Poly(aryl cyanurate)-Based Thin-Film Composite Nanofiltration Membranes.

ABSTRACT: The successful synthesis of poly(aryl cyanurate) nanofiltration membranes via the interfacial polymerization reaction between cyanuric chloride and 1,1,1-tris(4-hydroxyphenyl)ethane (TPE), atop a polyethersulfone ultrafiltration support, is demonstrated. The use of cyanuric chloride allows for the formation of a polymer that does not contain hydrolysis-susceptible amide bonds that inherently limit the stability of polyamide nanofiltration membranes. In order to achieve a thin defect-free cross-linked film via interfacial polymerization, a sufficient number of each monomer should react. However, the reactivities of the second and third chloride groups of the cyanuric chloride are moderate. Here, this difficulty is overcome by the high functionality and the high reactivity of TPE. The membranes demonstrate a typical nanofiltration behavior, with a molecular weight cutoff of 400 ± 83 g·mol^-1 and a permeance of 1.77 ± 0.18 L·m^-2 h^-1 bar^-1. The following retention behavior Na₂SO₄ (97.1%) > MgSO₄ (92.8%) > NaCl (51.3%) > MgCl₂ (32.1%) indicates that the membranes have a negative surface charge. The absence of amide bonds in the membranes was expected to result in superior pH stability as compared to polyamide membranes. However, it was found that under extremely acidic conditions (pH = 1), the performance showed a pronounced decline over the course of 2 months. Under extremely alkaline conditions (pH = 13), after 1 month, the performance was lost. After 2 months of exposure to moderate alkaline conditions (pH = 12), the MgSO₄ retention decreased by 14% and the permeance increased by 2.5-fold. This degradation was attributed to the hydrolysis of the aryl cyanurate bond that behaves like an ester bond.

SUBMITTER: Elshof MG

PROVIDER: S-EPMC8154205 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Given the huge significance of organic solvents in several industrial processes, the use of membranes for recovering the solvents has evolved into an industrially viable process. The current work has been focused on studying the effect of minor changes in the chemistry of the reacting monomers on the organic solvent nanofiltration/solvent resistance nanofiltration (OSN/SRNF) performance of the membranes. The two aliphatic amines with varying aliphatic chain lengths between primary and secondary amines were selected for this purpose. Based on the structure of the resultant active layer, the Janus nanofiltration performance of the membrane was evaluated. The two membranes, 4A-TPC@crosslinked PAN and 4A-3P@crosslinked PAN were fabricated by using two different tetra-amines, 4A (N,N'-bis(3-aminopropyl)ethylenediamine) and 4A-3P (N,N'-Bis(2-aminoethyl)-1,3-propanediamine) crosslinked with terephthaloyl chloride (TPC) on a crosslinked polyacryonitrile (PAN) support through interfacial polymerization (IP). The presence of multiple hydrophobic -CH2- groups in the structures of the aliphatic amines 4A and 4A-3P develops hydrophobic sites in the hydrophilic polyamide active layers of the membranes. In addition, 4A has two secondary amino groups separated by ethylene (-CH2-CH2-) groups, whereas in 4A-3P, the two secondary amino groups are separated by propylene (-CH2-CH2-CH2-) leading to variation in the structural features and performance of the two membranes. Both membranes were fully characterized by several membrane characterization techniques and applied for OSN/SRNF using both polar (methanol, ethanol, and isopropanol) and non-polar (n-hexane and toluene) solvents. Different dyes (Congo red, Eriochrome black T, and Methylene blue) were used as model solutes during the filtration experiment. The 4A-3P-TPC@crosslinked PAN showed n-hexane and toluene flux of 109.9 LMH and 95.5 LMH, respectively. The Congo red (CR) showed the highest rejection, reaching 99.1% for the 4A-TPC@Crosslinked PAN membrane and 98.8% for the 4A-3P-TPC@Crosslinked PAN membrane.

Dataset Information

Poly(aryl cyanurate)-Based Thin-Film Composite Nanofiltration Membranes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets