Approaching Highly Leaching-Resistant Fire-Retardant Wood by In Situ Polymerization with Melamine Formaldehyde Resin.

ABSTRACT: The objective of the work was to improve the leaching resistance of fire-retardant (FR) modified wood by the incorporation of a thermoset resin. Here, Scots pine (Pinus sylvestris L.) sapwood was impregnated with melamine formaldehyde (MF) resin and hydrophilic FRs guanyl-urea phosphate/boric acid by a vacuum-pressure treatment. Resistance to leaching of FR-modified wood was evaluated, after conducting an accelerated aging test according to European standard EN 84. Inductively coupled plasma analysis showed that the incorporation of MF resin significantly reduced the leachability of FRs. Scanning electron microscopy/energy-dispersive X-ray spectrometry revealed that the mechanism of water resistance was by doping the FRs into MF resin microspheres. Fourier transform infrared spectra showed the chemical functionality changes of FR-modified wood such as the formation of methylene bridges by drying the modified wood specimens. An increase in the thermal stability of FR-modified wood was confirmed by thermal gravimetric analysis. Excellent fire performance of FR-modified wood after leaching was affirmed by the limiting oxygen index and cone calorimeter tests.

SUBMITTER: Lin CF

PROVIDER: S-EPMC8154219 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Effective Insensitiveness of Melamine Urea-Formaldehyde Resin via Interfacial Polymerization on Nitramine Explosives.

Project description:To improve the safety of ammonium nitrate explosives, the melamine urea-formaldehyde resin (MUF resin) was selected for the preparation of three typical nitramine explosives (cyclotetramethylenetetranitramine, HMX; cryclo-trimethylenetrinitramine, RDX; and hexanitrohexaazaisowurtzitane, CL-20) based green polymer-bonded explosives (GPBXs) via interfacial polymerization. Meanwhile, the corresponding composite particles prepared by physical mixing and drying bath methods were studied and compared. The particle morphology, crystal structure, thermal stability, and safety performance of the resultant composite particles were characterized by scanning electron microscopy (SEM), powder X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectra, differential scanning calorimeter (DSC), and impact sensitivity test, respectively. SEM results showed that MUF was successfully coated on the surface of the three explosives, and different composite particles prepared by the same method have their own unique characteristics. Such effect is attributed to the resin's ability to isolate and buffer external stimuli. It is obvious that the interfacial polymerization is an effective desensitization technique to prepare core-shell composite particles for explosives.

| S-EPMC6288043 | biostudies-literature

Distribution and curing reactions of melamine formaldehyde resin in cells of impregnation-modified wood.

Project description:Wood modification improves the properties of wood as a building material by altering the wood structure on a cellular level. This study investigated how dimensional changes of wood on a macroscopic scale are related to the cellular level chemical changes on the micron level after impregnation modification with melamine formaldehyde (MF) resin under different heat curing conditions. Our results showed that the curing conditions affected the polycondensation reactions and the morphological structure of the MF resin within the cell lumen. The diffusion of the resin into the cell wall was estimated based on the triazine ring vibration of melamine in the Raman spectrum at 950-990?cm-1. Thereby, it was shown that macroscopic changes in wood dimensions do not provide a reliable estimate for the cell wall diffusion of the resin. The removal of cell wall constituents during the modification, which was facilitated by the alkaline pH of the impregnation solution, counterbalanced the cell wall bulking effect of the resin. This was particularly evident for wet cured samples, where diffusion of MF resin into the cell wall was observed by confocal Raman microscopy, despite a reduction in macroscopic wood dimensions.

| S-EPMC7042241 | biostudies-literature

Fabrication of CL-20/HMX Cocrystal@Melamine–Formaldehyde Resin Core–Shell Composites Featuring Enhanced Thermal and Safety Performance via In Situ Polymerization

Project description:Safety concerns remain a bottleneck for the application of 2,4,6,8,10,12-hexanitro- 2,4,6,8,10,12-hexaazaisowurtzitane (CL-20)/1,3,5,7-tetranitro-1,3,5,7-tetrazacyclooctane (HMX) cocrystal. Melamine–formaldehyde (MF) resin was chosen to fabricate CL-20/HMX cocrystal-based core–shell composites (CH@MF composites) via a facile in situ polymerization method. The resulted CH@MF composites were comprehensively characterized, and a compact core–shell structure was confirmed. The effects of the shell content on the properties of the composites were explored as well. As a result, we found that, except for CH@MF–2 with a 1% shell content, the increase in shell content led to a rougher surface morphology and more close-packed structure. The thermal decomposition peak temperature improved by 5.3 °C for the cocrystal enabled in 1.0 wt% MF resin. Regarding the sensitivity, the CH@MF composites exhibited a significantly reduced impact and friction sensitivity with negligible energy loss compared with the raw cocrystal and physical mixtures due to the cushioning and insulation effects of the MF coating. The formation mechanism of the core–shell micro-composites was further clarified. Overall, this work provides a green, facile and industrially potential strategy for the desensitization of energetic cocrystals. The CH@MF composites with high thermal stability and low sensitivity are promising to be applied in propellants and polymer-bonded explosive (PBX) formulations.

| S-EPMC9224366 | biostudies-literature

Self-Extinguishing Resin Transfer Molding Composites Using Non-Fire-Retardant Epoxy Resin.

Project description:Introducing fire-retardant additives or building blocks into resins is a widely adopted method used for improving the fire retardancy of epoxy composites. However, the increase in viscosity and the presence of insoluble additives accompanied by resin modification remain challenges for resin transfer molding (RTM) processing. We developed a robust approach for fabricating self-extinguishing RTM composites using unmodified and flammable resins. To avoid the effects on resin fluidity and processing, we loaded the flame retardant into tackifiers instead of resins. We found that the halogen-free flame retardant, a microencapsulated red phosphorus (MRP) additive, was enriched on fabric surfaces, which endowed the composites with excellent fire retardancy. The composites showed a 79.2% increase in the limiting oxygen index, a 29.2% reduction in heat release during combustion, and could self-extinguish within two seconds after ignition. Almost no effect on the mechanical properties was observed. This approach is simple, inexpensive, and basically applicable to all resins for fabricating RTM composites. This approach adapts insoluble flame retardants to RTM processing. We envision that this approach could be extended to load other functions (radar absorbing, conductivity, etc.) into RTM composites, broadening the application of RTM processing in the field of advanced functional materials.

| S-EPMC6315867 | biostudies-other

Optimizing Melamine Resin Microspheres with Excess Formaldehyde for the SERS Substrate.

Project description:Influence of the excess monomer within the synthetic reaction solution of melamine resin microspheres (MFMSs) on the surface-enhanced Raman spectroscopy (SERS) enhancement from Rhodamine 6G (R6G) was investigated, where the R6G was adsorbed on the silver nanoparticles (AgNPs) that were loaded on the MFMSs. Surface characteristics of the MFMSs were modified by the excess monomer (i.e., the excessive melamine or formaldehyde) through its terminal overreaction, which can be simply controlled by some of the synthetic reaction conditions, thus further allowing us to optimize the assembly of the loaded AgNPs for the SERS detection. These SERS substrates incorporating the optimized MFMSs with the excess formaldehyde can also be used for tracing analyses of more environmental and food contaminants.

| S-EPMC5618374 | biostudies-literature

Release of Melamine and Formaldehyde from Melamine-Formaldehyde Plastic Kitchenware.

Project description:The release of melamine and formaldehyde from kitchenware made of melamine resins is still a matter of great concern. To investigate the migration and release behavior of the monomers from melamine-based food contact materials into food simulants and food stuffs, cooking spoons were tested under so-called hot plate conditions at 100 °C. Release conditions using the real hot plate conditions with 3% acetic acid were compared with conditions in a conventional migration oven and with a release to deionized water. Furthermore, the kinetics of the release were studied using Arrhenius plots giving an activation energy for the release of melamine of 120 kJ/mol. Finally, a correlation between quality of the resins, specifically the kind of bridges between the monomers, and the release of melamine, was confirmed by CP/MAS 13C-NMR measurements of the melamine kitchenware. Obviously, the ratio of methylene bridges and dimethylene ether bridges connecting the melamine monomers during the curing process can be directly correlated with the amount of the monomers released into food.

| S-EPMC7463570 | biostudies-literature

The Effect of High-Energy Ionizing Radiation on the Mechanical Properties of a Melamine Resin, Phenol-Formaldehyde Resin, and Nitrile Rubber Blend.

Project description:Irradiation by ionizing radiation is a specific type of controllable modification of the physical and chemical properties of a wide range of polymers, which is, in comparison to traditional chemical methods, rapid, non-polluting, simple, and relatively cheap. In the presented paper, the influence of high-energy ionizing radiation on the basic mechanical properties of the melamine resin, phenol-formaldehyde resin, and nitrile rubber blend has been studied for the first time. The mechanical properties of irradiated samples were compared to those of non-irradiated materials. It was found that radiation doses up to 150 kGy improved the mechanical properties of the tested materials in terms of a significant increase in stress at break, tensile strength, and tensile modulus at 40% strain, while decreasing the value of strain at break. At radiation doses above 150 kGy, the irradiated polymer blend is already degrading, and its tensile characteristics significantly deteriorate. An radiation dose of 150 kGy thus appears to be optimal from the viewpoint of achieving significant improvement, and the radiation treatment of the given polymeric blend by a beam of accelerated electrons is a very promising alternative to the traditional chemical mode of treatment which impacts the environment.

| S-EPMC6317311 | biostudies-literature

Thermochromic microcapsules with highly transparent shells obtained through in-situ polymerization of urea formaldehyde around thermochromic cores for smart wood coatings.

Project description:In this paper, thermochromic microcapsules were synthesized in situ polymerization with urea formaldehyde as shell material and thermochromic compounds as core material. The effects of emulsifying agent and conditions on surface morphology and particle size of microcapsules were studied. It was found that the size and surface morphology of microcapsules were strongly depending on stirring rate and the ratio of core to shell. The stable and small size spherical microcapsules with excellent transparency can be obtained at an emulsifying agent to core to shell ratio as 1:5:7.5 under mechanical stirring at 12?krpm for 15?min. Finally, the thermochromic property was discussed by loading microcapsules in wood and wood coatings. Results indicate that microcapsules can realize the thermochromic property while incorporated with wood and coatings, and could have high potential in smart material fabrication.

| S-EPMC5838241 | biostudies-literature

Fire Retardancy and Leaching Resistance of Furfurylated Pine Wood (Pinus sylvestris L.) Treated with Guanyl-Urea Phosphate

Project description:Guanyl-urea phosphate (GUP) was introduced into furfurylated wood in order to improve fire retardancy. Modified wood was produced via vacuum-pressure impregnation of the GUP–furfuryl alcohol (FA) aqueous solution, which was then polymerized at elevated temperature. The water leaching resistance of the treated wood was tested according to European standard EN 84, while the leached water was analyzed using ultra-performance liquid chromatography (UPLC) and inductively coupled plasma–sector field mass spectrometry (ICP-SFMS). This new type of furfurylated wood was further characterized in the laboratory by evaluating its morphology and elemental composition using optical microscopy and electron microscopy coupled with energy-dispersive X-ray spectrometry (SEM-EDX). The chemical functionality was detected using infrared spectroscopy (FTIR), and the fire resistance was tested using cone calorimetry. The dimensional stability was evaluated in wet–dry soaking cycle tests, along with the mechanical properties, such as the Brinell hardness and bending strength. The fire retardancy of the modified furfurylated wood indicated that the flammability of wood can be depressed to some extent by introducing GUP. This was reflected in an observed reduction in heat release rate (HRR2) from 454.8 to 264.9 kW/m2, without a reduction in the material properties. In addition, this leaching-resistant furfurylated wood exhibited higher fire retardancy compared to conventional furfurylated wood. A potential method for producing fire-retardant treated furfurylated wood stable to water exposure has been suggested.

| S-EPMC9104981 | biostudies-literature

Thermomechanical and microhardness data of melamine-formaldehyde-based self-healing resin film able to undergo reversible crosslinking via Diels-Alder reaction.

Project description:The data presented in this article characterize the thermomechanical and microhardness properties of a novel melamine-formaldehyde resin (MF) intended for the use as a self-healing surface coating. The investigated MF resin is able to undergo reversible crosslinking via Diels Alder reactive groups. The microhardness data were obtained from nanoindentation measurements performed on solid resin film samples at different stages of the self-healing cycle. Thermomechanical analysis was performed under dynamic load conditions. The data provide supplemental material to the manuscript published by Urdl et al. 2020 (http://doi.org/10.1016/j.eurpolymj.2020.109601, [1]) on the self-healing performance of this resin, where a more thorough discussion on the preparation, the properties of this coating material and its application in impregnated paper-based decorative laminates can be found [1].

| S-EPMC7708790 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data