Highly Ordered SnO₂ Nanopillar Array as Binder-Free Anodes for Long-Life and High-Rate Li-Ion Batteries.

ABSTRACT: SnO₂, a typical transition metal oxide, is a promising conversion-type electrode material with an ultrahigh theoretical specific capacity of 1494 mAh g^-1. Nevertheless, the electrochemical performance of SnO₂ electrode is limited by large volumetric changes (~300%) during the charge/discharge process, leading to rapid capacity decay, poor cyclic performance, and inferior rate capability. In order to overcome these bottlenecks, we develop highly ordered SnO₂ nanopillar array as binder-free anodes for LIBs, which are realized by anodic aluminum oxide-assisted pulsed laser deposition. The as-synthesized SnO₂ nanopillar exhibit an ultrahigh initial specific capacity of 1082 mAh g^-1 and maintain a high specific capacity of 524/313 mAh g^-1 after 1100/6500 cycles, outperforming SnO₂ thin film-based anodes and other reported binder-free SnO₂ anodes. Moreover, SnO₂ nanopillar demonstrate excellent rate performance under high current density of 64 C (1 C = 782 mA g^-1), delivering a specific capacity of 278 mAh g^-1, which can be restored to 670 mAh g^-1 after high-rate cycling. The superior electrochemical performance of SnO₂ nanoarray can be attributed to the unique architecture of SnO₂, where highly ordered SnO₂ nanopillar array provided adequate room for volumetric expansion and ensured structural integrity during the lithiation/delithiation process. The current study presents an effective approach to mitigate the inferior cyclic performance of SnO₂-based electrodes, offering a realistic prospect for its applications as next-generation energy storage devices.

SUBMITTER: Dai L

PROVIDER: S-EPMC8156522 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

The Effects of the Binder and Buffering Matrix on InSb-Based Anodes for High-Performance Rechargeable Li-Ion Batteries.

Project description:C-decorated intermetallic InSb (InSb-C) was developed as a novel high-performance anode material for lithium-ion batteries (LIBs). InSb nanoparticles synthesized via a mechanochemical reaction were characterized using X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and energy-dispersive X-ray spectroscopy (EDX). The effects of the binder and buffering matrix on the active InSb were investigated. Poly(acrylic acid) (PAA) was found to significantly improve the cycling stability owing to its strong hydrogen bonding. The addition of amorphous C to InSb further enhanced mechanical stability and electronic conductivity. As a result, InSb-C demonstrated good electrochemical Li-ion storage performance: a high reversible specific capacity (878 mAh·g-1 at 100 mA·g-1 after 140 cycles) and good rate capability (capacity retention of 98% at 10 A·g-1 as compared to 0.1 A·g-1). The effects of PAA and C were comprehensively studied using cyclic voltammetry, differential capacity plots, ex-situ SEM, and electrochemical impedance spectroscopy (EIS). In addition, the electrochemical reaction mechanism of InSb was revealed using ex-situ XRD. InSb-C exhibited a better performance than many recently reported Sb-based electrodes; thus, it can be considered as a potential anode material in LIBs.

| S-EPMC8707395 | biostudies-literature

Lignin as a Binder Material for Eco-Friendly Li-Ion Batteries.

Project description:The industrial lignin used here is a byproduct from Kraft pulp mills, extracted from black liquor. Since lignin is inexpensive, abundant and renewable, its utilization has attracted more and more attention. In this work, lignin was used for the first time as binder material for LiFePO₄ positive and graphite negative electrodes in Li-ion batteries. A procedure for pretreatment of lignin, where low-molecular fractions were removed by leaching, was necessary to obtain good battery performance. The lignin was analyzed for molecular mass distribution and thermal behavior prior to and after the pretreatment. Electrodes containing active material, conductive particles and lignin were cast on metal foils, acting as current collectors and characterized using scanning electron microscopy (SEM), electrochemical impedance spectroscopy (EIS) and galvanostatic charge-discharge cycles. Good reversible capacities were obtained, 148 mAh·g-1 for the positive electrode and 305 mAh·g-1 for the negative electrode. Fairly good rate capabilities were found for both the positive electrode with 117 mAh·g-1 and the negative electrode with 160 mAh·g-1 at 1C. Low ohmic resistance also indicated good binder functionality. The results show that lignin is a promising candidate as binder material for electrodes in eco-friendly Li-ion batteries.

| S-EPMC5456705 | biostudies-other

Bio-Derived, Binderless, Hierarchically Porous Carbon Anodes for Li-ion Batteries.

Project description:Here we explore the electrochemical performance of pyrolyzed skins from the species A. bisporus, also known as the Portobello mushroom, as free-standing, binder-free, and current collector-free Li-ion battery anodes. At temperatures above 900 °C, the biomass-derived carbon nanoribbon-like architectures undergo unique processes to become hierarchically porous. During heat-treatment, the oxygen and heteroatom-rich organics and potassium compounds naturally present in the mushroom skins play a mutual role in creating inner void spaces throughout the resulting carbon nanoribbons, which is a process analogous to KOH-activation of carbon materials seen in literature. The pores formed in the pyrolytic carbon nanoribbons range in size from sub-nanometer to tens of nanometers, making the nanoribbons micro, meso, and macroporous. Detailed studies were conducted on the carbon nanoribbons using SEM and TEM to study morphology, as well as XRD and EDS to study composition. The self-supporting nanoribbon anodes demonstrate significant capacity increase as they undergo additional charge/discharge cycles. After a pyrolysis temperature of 1100 °C, the pristine anodes achieve over 260 mAh/g after 700 cycles and a Coulombic efficiency of 101.1%, without the use of harmful solvents or chemical activation agents.

| S-EPMC4586494 | biostudies-other

Controlling Li Dendritic Growth in Graphite Anodes by Potassium Electrolyte Additives for Li-Ion Batteries.

Project description:Fast charging promotes Li dendrite formation and its growth on graphite anodes, which affects cell performance in Li-ion batteries (LIBs). This work reports the formation of a robust SEI layer by introducing a KPF6 inorganic additive into the electrolyte. An optimal concentration of 0.001 M KPF6 effectively inhibits the growth of Li dendrites at 2C charging rates, compared with a commercial electrolyte. Electrolytes containing a KPF6 additive are shown here to deliver dual effects to mitigate the growth of dendrites. A thin LiF-rich SEI layer is formed on graphite, which blocks the electron leakage pathways. Additionally, K+ resides at defect sites (such as particle boundaries) due to its faster diffusion rate and blocks the incoming Li+ and restricts the growth of Li dendrites. The electrolyte with optimum concentration of KPF6, i.e., 0.001 M, effectively directs Li+ transport through the thin, durable, and low resistance LiF-rich SEI layer. This has implications for fast charging through optimization of the electrode/electrolyte interphase by controlling additive concentrations.

| S-EPMC9501903 | biostudies-literature

Hierarchically ordered mesoporous Co3O4 materials for high performance Li-ion batteries.

Project description:Highly ordered mesoporous Co3O4 materials have been prepared via a nanocasting route with three-dimensional KIT-6 and two-dimensional SBA-15 ordered mesoporous silicas as templates and Co(NO3)2 · 6H2O as precursor. Through changing the hydrothermal treating temperature of the silica template, ordered mesoporous Co3O4 materials with hierarchical structures have been developed. The larger pores around 10 nm provide an efficient transport for Li ions, while the smaller pores between 3-5 nm offer large electrochemically active areas. Electrochemical impedance analysis proves that the hierarchical structure contributes to a lower charge transfer resistance in the mesoporous Co3O4 electrode than the mono-sized structure. High reversible capacities around 1141 mAh g(-1) of the hierarchically mesoporous Co3O4 materials are obtained, implying their potential applications for high performance Li-ion batteries.

| S-EPMC4726024 | biostudies-other

Confined SnO2 quantum-dot clusters in graphene sheets as high-performance anodes for lithium-ion batteries.

Project description:Construction of metal oxide nanoparticles as anodes is of special interest for next-generation lithium-ion batteries. The main challenge lies in their rapid capacity fading caused by the structural degradation and instability of solid-electrolyte interphase (SEI) layer during charge/discharge process. Herein, we address these problems by constructing a novel-structured SnO2-based anode. The novel structure consists of mesoporous clusters of SnO2 quantum dots (SnO2 QDs), which are wrapped with reduced graphene oxide (RGO) sheets. The mesopores inside the clusters provide enough room for the expansion and contraction of SnO2 QDs during charge/discharge process while the integral structure of the clusters can be maintained. The wrapping RGO sheets act as electrolyte barrier and conductive reinforcement. When used as an anode, the resultant composite (MQDC-SnO2/RGO) shows an extremely high reversible capacity of 924?mAh g(-1) after 200 cycles at 100?mA g(-1), superior capacity retention (96%), and outstanding rate performance (505?mAh g(-1) after 1000 cycles at 1000?mA g(-1)). Importantly, the materials can be easily scaled up under mild conditions. Our findings pave a new way for the development of metal oxide towards enhanced lithium storage performance.

| S-EPMC4867637 | biostudies-literature

One-Pot Synthesis of High-Performance Tin Chalcogenides/C Anodes for Li-Ion Batteries.

Project description:Tin chalcogenides are considered as promising anode materials for lithium-ion batteries (LIBs) due to their high theoretical lithium-storage capacity. Herein, we have successfully synthesized the composites of tin chalcogenides and graphite, that is, SnS/C, SnSe/C, and SnS0.5Se0.5/C, via a simple one-pot solid-state method. During the electrochemical test, they exhibit excellent lithium-storage ability and cyclic performance as the anode electrodes of LIBs due to the introduction of carbon. In particular, (i) SnS/C displayed a high specific capacity of 875 mAh g-1 at 0.2 A g-1 over 200 cycles; (ii) SnSe/C presents 734 mAh g-1 at 0.2 A g-1 after 100 cycles, and it delivers 690 mAh g-1 at 1.0 A g-1 over 300 cycles; and (iii) the SnS0.5Se0.5/C composite electrode delivers a specific capacity of 643 mAh g-1 at 0.5 A g-1 over 150 cycles. Furthermore, another series of tin-based composites have also been successfully fabricated (i.e., Sn/C, SnS2/C, SnSe2/C, and SnTe/C), showing the general applicability of the synthetic route applied here. Our synthetic approach demonstrates a promising route for the large-scale production of high-performance tin chalcogenides/C anode materials for LIBs and other battery systems (e.g., Na-ion and K-ion batteries).

| S-EPMC8280710 | biostudies-literature

Nanoscale Heterogeneity of Multilayered Si Anodes with Embedded Nanoparticle Scaffolds for Li-Ion Batteries.

Project description:A new approach on the synthesis of Si anodes for Li-ion batteries is reported, combining advantages of both nanoparticulated and continuous Si films. A multilayered configuration prototype is proposed, comprising amorphous Si arranged in nanostructured, mechanically heterogeneous films, interspersed with Ta nanoparticle scaffolds. Particular structural features such as increased surface roughness, nanogranularity, and porosity are dictated by the nanoparticle scaffolds, boosting the lithiation process due to fast Li diffusion and low electrode polarization. Consequently, a remarkable charge/discharge speed is reached with the proposed anode, in the order of minutes (1200 mAh g-1 at 10 C). Moreover, nanomechanical heterogeneity self-limits the capacity at intermediate charge/discharge rates; as a consequence, exceptional cycleability is observed at 0.5 C, with 100% retention over 200 cycles with 700 mAh g-1. Higher capacity can be obtained when the first cycles are performed at 0.2 C, due to the formation of microislands, which facilitate the swelling of the active Si. This study indicates a method to tune the mechanical, morphological, and electrochemical properties of Si electrodes via engineering nanoparticle scaffolds, paving the way for a novel design of nanostructured Si electrodes for high-performance energy storage devices.

| S-EPMC5644243 | biostudies-literature

Long-term Cyclability of Substoichiometric Silicon Nitride Thin Film Anodes for Li-ion Batteries.

Project description:Silicon has been the subject of an extensive research effort aimed at developing new anode materials for lithium ion batteries due to its large specific and volumetric capacity. However, commercial use is limited by a number of degradation problems, many of which are related to the large volume change the material undergoes during cycling in combination with limited lithium-diffusivity. Silicon rich silicon oxides (SiOx), which converts into active silicon and inactive lithium oxide during the initial lithiation, have attracted some attention as a possible solution to these issues. In this work we present an investigation of silicon rich amorphous silicon nitride (a-SiNx) as an alternative convertible anode material. Amorphous SiN0.89 thin films deposited by plasma enhanced chemical vapour deposition show reversible reactions with lithium when cycled between 0.05 and 1.0 V vs. Li+/Li. This material delivers a reversible capacity of approximately 1,200 mAh/g and exhibits excellent cycling stability, with 41 nm a-SiN0.89 thin film electrodes showing negligible capacity degradation over more than 2,400 cycles.

| S-EPMC5645470 | biostudies-literature

A conductive self healing polymeric binder using hydrogen bonding for Si anodes in lithium ion batteries.

Project description:A ureido-pyrimidinone (UPy)-functionalized poly(acrylic acid) grafted with poly(ethylene glycol)(PEG), designated PAU-g-PEG, was developed as a high performance polymer binder for Si anodes in lithium-ion batteries. By introducing both a ureido-pyrimidinone (UPy) unit, which is capable of self-healing through dynamic hydrogen bonding within molecules as well as with Si, and an ion-conducting PEG onto the side chain of the poly(acrylic acid), this water-based self-healable and conductive polymer binder can effectively accommodate the volume changes of Si, while maintaining electronic integrity, in an electrode during repeated charge/discharge cycles. The Si@PAU-g-PEG electrode retained a high capacity of 1,450.2 mAh g-1 and a Coulombic efficiency of 99.4% even after 350 cycles under a C-rate of 0.5 C. Under a high C-rate of 3 C, an outstanding capacity of 2,500 mAh g-1 was also achieved, thus demonstrating its potential for improving the electrochemical performance of Si anodes.

| S-EPMC7486292 | biostudies-literature