Characterization of Composition and Structure-Property Relationships of Commercial Post-Consumer Polyethylene and Polypropylene Recyclates.

ABSTRACT: The current efforts in moving closer towards a circular plastics economy puts massive pressure on recycled plastics, especially recycled polyethylene (rPE) and recycled polypropylene (rPP) to enter new markets. Their market penetration remained low so far, despite PE and PP constituting the largest share of plastic wastes. However, with the current imperative of more circularity comes a new focus on performance of recyclates. Hence, a detailed understanding of composition and structure-property relationships of post-consumer recyclates has to be developed. Five recycling companies from the Austrian and German markets were asked to supply their purest high-quality rPE and rPP grades. These were characterized by differential scanning calorimetry (DSC), thermo-gravimetric analysis (TGA), and Fourier-transform infrared (FTIR) spectroscopy, and micro-imaging. Technological characterization included density measurements, determination of the melt flow rate (MFR), and Charpy impact testing. All recyclates contained diverse contaminants and inclusions ranging from legacy fillers like calcium carbonate to polymeric contaminants like polyamides or polyolefin cross-contamination. The overall amount, size, and distribution of contaminants varied significantly among suppliers. Furthermore, first structure-property relationships for polyolefin recyclates that link inorganic content and polymeric purity with density and impact performance could be derived.

SUBMITTER: Gall M

PROVIDER: S-EPMC8156794 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Our studies of amorphous calcium phosphate (ACP)-based materials over the last decade have yielded bioactive polymeric composites capable of protecting teeth from demineralization or even regenerating lost tooth mineral. The anti-cariogenic/re-mineralizing potential of these ACP composites originates from their propensity, when exposed to the oral environment, to release in a sustained manner sufficient levels of mineral-forming calcium and phosphate ions to promote formation of stable apatitic tooth mineral. However, the less than optimal ACP filler/resin matrix cohesion, excessive polymerization shrinkage and water sorption of these experimental materials can adversely affect their physicochemical and mechanical properties, and, ultimately, limit their lifespan. This study demonstrates the effects of chemical structure and composition of the methacrylate monomers used to form the matrix phase of composites on degree of vinyl conversion (DVC) and water sorption of both copolymers and composites and the release of mineral ions from the composites. Modification of ACP surface via introducing cations and/or polymers ab initio during filler synthesis failed to yield mechanically improved composites. However, moderate improvement in composite's mechanical stability without compromising its remineralization potential was achieved by silanization and/or milling of ACP filler. Using ethoxylated bisphenol A dimethacrylate or urethane dimethacrylate as base monomers and adding moderate amounts of hydrophilic 2-hydroxyethyl methacrylate or its isomer ethyl-α-hydroxymethacrylate appears to be a promising route to maximize the remineralizing ability of the filler while maintaining high DVC. Exploration of the structure/composition/property relationships of ACP fillers and polymer matrices is complex but essential for achieving a better understanding of the fundamental mechanisms that govern dissolution/re-precipitation of bioactive ACP fillers, and, ultimately, the suitability of the composites for clinical evaluation.

Dataset Information

Characterization of Composition and Structure-Property Relationships of Commercial Post-Consumer Polyethylene and Polypropylene Recyclates.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets