Responsive Polyesters with Alkene and Carboxylic Acid Side-Groups for Tissue Engineering Applications.

ABSTRACT: Main chain polyesters have been extensively used in the biomedical field. Despite their many advantages, including biocompatibility, biodegradability, and others, these materials are rather inert and lack specific functionalities which will endow them with additional biological and responsive properties. In this work, novel pH-responsive main chain polyesters have been prepared by a conventional condensation polymerization of a vinyl functionalized diol with a diacid chloride, followed by a photo-induced thiol-ene click reaction to attach functional carboxylic acid side-groups along the polymer chains. Two different mercaptocarboxylic acids were employed, allowing to vary the alkyl chain length of the polymer pendant groups. Moreover, the degree of modification, and as a result, the carboxylic acid content of the polymers, was easily tuned by varying the irradiation time during the click reaction. Both these parameters, were shown to strongly influence the responsive behavior of the polyesters, which presented adjustable pKα values and water solubilities. Finally, the difunctional polyesters bearing the alkene and carboxylic acid functionalities enabled the preparation of cross-linked polyester films by chemically linking the pendant vinyl bonds on the polymer side groups. The biocompatibility of the cross-linked polymers films was assessed in L929 fibroblast cultures and showed that the cell viability, proliferation, and attachment were greatly promoted on the polyester surface, bearing the shorter alkyl chain length side groups and the higher fraction of carboxylic acid functionalities.

SUBMITTER: Mountaki SA

PROVIDER: S-EPMC8158382 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Immobilization of cell adhesive proteins on the scaffold surface has become a widely reported method that can improve the interaction between scaffold and cells. In this study, three nanofibrous scaffolds obtained by electrospinning of poly(caprolactone) (PCL), poly(L-lactide-co-caprolactone) (PLCL) 70:30, or poly(L-lactide) (PLLA) were subjected to chemical immobilization of gelatin based on aminolysis and glutaraldehyde cross-linking, as well as physisorption of gelatin. Two sets of aminolysis conditions were applied to evaluate the impact of amine group content. Based on the results of the colorimetric bicinchoninic acid (BCA) assay, it was shown that the concentration of gelatin on the surface is higher for the chemical modification and increases with the concentration of free NH2 groups. XPS (X-ray photoelectron spectroscopy) analysis confirmed this outcome. On the basis of XPS results, the thickness of the gelatin layer was estimated to be less than 10 nm. Initially, hydrophobic scaffolds are completely wettable after coating with gelatin, and the time of waterdrop absorption was correlated with the surface concentration of gelatin. In the case of all physically and mildly chemically modified samples, the decrease in stress and strain at break was relatively low, contrary to strongly aminolyzed PLCL and PLLA samples. Incubation testing performed on the PCL samples showed that a chemically immobilized gelatin layer is more stable than a physisorbed one; however, even after 90 days, more than 60% of the initial gelatin concentration was still present on the surface of physically modified samples. Mouse fibroblast L929 cell culture on modified samples indicates a positive effect of both physical and chemical modification on cell morphology. In the case of PCL and PLCL, the best morphology, characterized by stretched filopodia, was observed after stronger chemical modification, while for PLLA, there was no significant difference between modified samples. Results of metabolic activity indicate the better effect of chemical immobilization than of physisorption of gelatin.

Dataset Information

Responsive Polyesters with Alkene and Carboxylic Acid Side-Groups for Tissue Engineering Applications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets