Single-Step Production of a TiO₂@MoS₂ Heterostructure and Its Applications as a Supercapacitor Electrode and Photocatalyst for Reduction of Cr(VI) to Cr(III).

ABSTRACT: In this study, we have reported a one-step synthesis of a TiO₂@MoS₂ heterostructure. TiO₂@MoS₂ was synthesized using a facile and cost-effective method. The as-synthesized TiO₂@MoS₂ heterostructure was characterized by suitable spectroscopic techniques. The obtained TiO₂@MoS₂ was utilized as a supercapacitor electrode material. Electrochemical studies show that the TiO₂@MoS₂ heterostructure possesses a specific capacitance of 337 F/g at a current density of 1 A/g in an aqueous solution. Furthermore, an application as a photocatalyst for the photoreduction of toxic hexavalent chromium was reported for the first time. This heterostructure showed the photoreduction of Cr⁶⁺ to Cr³⁺ in 120 min with formic acid as a scavenger under direct sunlight. A plausible mechanism of photoreduction of Cr⁶⁺ to Cr³⁺ under natural sunlight irradiation using TiO₂@MoS₂ is proposed.

SUBMITTER: Lathe A

PROVIDER: S-EPMC8158794 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

CdIn2S4/In(OH)3/NiCr-LDH Multi-Interface Heterostructure Photocatalyst for Enhanced Photocatalytic H2 Evolution and Cr(VI) Reduction.

Project description:The development of highly active and stable photocatalysts, an effective way to remediate environment pollution and alleviate energy shortages, remains a challenging issue. In this work, a CdIn2S4/In(OH)3 nanocomposite was deposited in-situ on NiCr-LDH nanosheets by a simple hydrothermal method, and the obtained CdIn2S4/In(OH)3/NiCr-LDH heterostructure photocatalysts with multiple intimate-contact interfaces exhibited better photocatalytic activity. The photocatalytic H2 evolution rate of CdIn2S4/In(OH)3/NiCr-LDH increased to 10.9 and 58.7 times that of the counterparts CdIn2S4 and NiCr-LDH, respectively. Moreover, the photocatalytic removal efficiency of Cr(VI) increased from 6% for NiCr-LDH and 75% for CdIn2S4 to 97% for CdIn2S4/In(OH)3/NiCr-LDH. The enhanced photocatalytic performance was attributed to the formation of multi-interfaces with strong interfacial interactions and staggered band alignments, which offered multiple pathways for carrier migration, thus promoting the separation efficiency of photo-excited electrons and holes. This study demonstrates a facile method to fabricate inexpensive and efficient heterostructure photocatalysts for solving environmental problems.

| S-EPMC8619374 | biostudies-literature

TiO2 Nanomembranes Fabricated by Atomic Layer Deposition for Supercapacitor Electrode with Enhanced Capacitance.

Project description:TiO2 is a promising environment friendly, low cost, and high electrochemical performance material. However, impediments like high internal ion resistance and low electrical conductivity restrict its applications as electrode for supercapacitor. In the present work, atomic layer deposition was used to fabricate TiO2 nanomembranes (NMs) with accurately controlled thicknesses. The TiO2 NMs were then used as electrodes for high-performance pseudocapacitors. Experimental results demonstrated that the TiO2 NM with 100 ALD cycles had the highest capacitance of 2332 F/g at 1 A/g with energy density of 81 Wh/kg. The enhanced performance was ascribed to the large surface area and the interconnectivity in the case of ultra-thin and flexible NMs. Increased ALD cycles led to stiffer NMs and decreased capacitance. Moreover, one series of two supercapacitors can light up one light-emitting diode with a working voltage of ~ 1.5 V, sufficiently describing its application values.

| S-EPMC6419636 | biostudies-literature

Enhanced Electrochemical Performance of Self-Assembled Nanoflowers of MoS2 Nanosheets as Supercapacitor Electrode Materials.

Project description:As supercapacitor electrode materials, their structures, including specific surface area, instability, and interconnection, determine the electrochemical performances (specific capacitance, cycle stability, and rate performance). In this study, 1T-MoS2 nanosheets were self-assembled into nanoflowers via a one-pot facile hydrothermal reaction. The nanoflowers retain the excellent electrical conductive performance and the feature of inherent high specific surface area of the nanosheets. For the sheets are interconnected to each other in flower structure, the structure is more stable and the charges are more easily transferred. Thus, compared to the nanosheet electrode, the nanoflower electrode shows the remarkable advantage when used as the electrode of the energy-storage device, whether it is 1T phase or 2H phase in KCl or in KOH. When measured at 0.5 A g-1 in KOH electrolyte, the MoS2 nanoflower electrode exhibits a high specific capacitance of 1120 F g-1. At the same time, when cycling 2000 times at a current density of 10 A g-1, the capacitance retention ratio can reach up to 96%.

| S-EPMC6776964 | biostudies-literature

Photocatalytic Reduction of Cr(VI) on a 3.0% Au/Sr0.70Ce0.20WO4 Photocatalyst.

Project description:Herein, a 3.0%-Au/Sr0.70Ce0.20WO4 sample was prepared for the photocatalytic reduction of the Cr2O7 2- ion. The photocatalyst was characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, and ultraviolet-visible diffuse reflectance spectra. The Sr0.70Ce0.20WO4 sample presented a photocatalytic reduction activity that is better than those of the Ce-doped sample and the intrinsic sample. Thereafter, different metal elements, Cu, Ag, Au, and Pt, were used as cocatalysts, which were loaded on the Sr0.70Ce0.20WO4 sample. The 3.0%-Au/Sr0.70Ce0.20WO4 photocatalyst showed optimal photocatalytic reduction activity in a 8 vol % methanol solution (pH = 7) under visible light irradiation. The kinetic constant of the optimal one is 0.0039 min-1, which is 1.86 times that of the Sr0.70Ce0.20WO4 sample. The photocatalyst is stable enough after a 24 h photocatalytic experiment.

| S-EPMC7581225 | biostudies-literature

Development of Efficient Photocatalyst MIL-68(Ga)_NH2 Metal-Organic Framework for the Removal of Cr(VI) and Cr(VI)/RhB from Wastewater under Visible Light.

Project description:Severe environmental pollution is caused by the massive discharge of complex industrial wastewater. The photocatalytic technology has been proved as an effective way to solve the problem, while an efficient photocatalyst is the most critical factor. Herein, a new photocatalyst MIL-68(Ga)_NH2 was obtained by hydrothermal synthesis and were characterized by PXRD, FTIR, 1H NMR, and TGA systematically. The result demonstrates that MIL-68(Ga)_NH2 crystallized in orthorhombic system and Cmcm space group with the unit cell parameters: a = 36.699 Å, b = 21.223 Å, c = 6.75 Å, V = 5257.6 Å3, which sheds light on the maintenance of the crystal structure of the prototype material after amino modification. The conversion of Cr(VI) and binary pollutant Cr(VI)/RhB in wastewater under visible light stimulation was characterized by the UV-vis DRS. Complementary experimental results indicate that MIL-68(Ga)_NH2 exhibits remarkable photocatalytic activity for Cr(VI) and the degradation rate reaches as high as 98.5% when pH = 2 and ethanol as hole-trapping agent under visible light irradiation with good reusability and stability. Owing to the synergistic effect between Cr(VI) and RhB in the binary pollutant system, MIL-68(Ga)_NH2 exhibits excellent catalytic activity for both the pollutants, the degradation efficiency of Cr(VI) and RhB was up to 95.7% and 94.6% under visible light irradiation for 120 min, respectively. The possible removal mechanism of Cr(VI)/RhB based on MIL-68(Ga)_NH2 was explored. In addition, Ga-based MOF was applied in the field of photocatalytic treatment of wastewater for the first time, which broadened the application of MOF materials in the field of photocatalysis.

| S-EPMC9181230 | biostudies-literature

MoS2 Nanosheet Arrays Rooted on Hollow rGO Spheres as Bifunctional Hydrogen Evolution Catalyst and Supercapacitor Electrode.

Project description:MoS2 has attracted attention as a promising hydrogen evolution reaction (HER) catalyst and a supercapacitor electrode material. However, its catalytic activity and capacitive performance are still hindered by its aggregation and poor intrinsic conductivity. Here, hollow rGO sphere-supported ultrathin MoS2 nanosheet arrays (h-rGO@MoS2) are constructed via a dual-template approach and employed as bifunctional HER catalyst and supercapacitor electrode material. Because of the expanded interlayer spacing in MoS2 nanosheets and more exposed electroactive S-Mo-S edges, the constructed h-rGO@MoS2 architectures exhibit enhanced HER performance. Furthermore, benefiting from the synergistic effect of the improved conductivity and boosted specific surface areas (144.9 m2 g-1, ca. 4.6-times that of pristine MoS2), the h-rGO@MoS2 architecture shows a high specific capacitance (238 F g-1 at a current density of 0.5 A g-1), excellent rate capacitance, and remarkable cycle stability. Our synthesis method may be extended to construct other vertically aligned hollow architectures, which may serve both as efficient HER catalysts and supercapacitor electrodes.

| S-EPMC6199108 | biostudies-literature

Hexagonal 2H-MoSe2 broad spectrum active photocatalyst for Cr(VI) reduction.

Project description:To make full use of the solar energy, exploring broad spectrum active photocatalysts has become one of the core issues for photocatalysis. Here we report a novel hexagonal 2H-MoSe2 photocatalyst with ultraviolet (UV)-visible-near infrared (NIR) light response for the first time. The results indicate that the MoSe2 displays excellent photo-absorption and photocatalytic activity in the reduction of Cr(VI) under UV and visible even NIR light irradiation. MoSe2 synthesized at pH value of 2 achieves the highest Cr(VI) reduction rates of 99%, 91% and 100% under UV, visible and NIR light irradiation, respectively, which should be attributed to its comparatively higher light absorption, efficient charge separation and transfer as well as relatively large number of surface active sites. The excellent broad spectrum active photocatalytic activity makes the MoSe2 to be a promising photocatalyst for the effective utilization of solar energy.

| S-EPMC5062113 | biostudies-literature

Facile synthesis and defect optimization of 2D-layered MoS2 on TiO2 heterostructure for industrial effluent, wastewater treatments.

Project description:Current research is paying much attention to heterojunction nanostructures. Owing to its versatile characteristics such as stimulating morphology, affluent surface-oxygen-vacancies and chemical compositions for enhanced generation of reactive oxygen species. Herein, we report the hydrothermally synthesized TiO2@MoS2 heterojunction nanostructure for the effective production of photoinduced charge carriers to enhance the photocatalytic capability. XRD analysis illustrated the crystalline size of CTAB capped TiO2, MoS2@TiO2 and L-Cysteine capped MoS2@TiO2 as 12.6, 11.7 and 10.2 nm, respectively. The bandgap of the samples analyzed by UV-Visible spectroscopy are 3.57, 3.66 and 3.94 eV. PL spectra of anatase phase titania shows the peaks present at and above 400 nm are ascribed to the defects in the crystalline structure in the form of oxygen vacancies. HRTEM reveals the existence of hexagonal layered MoS2 formation on the spherical shaped TiO2 nanoparticles at the interface. X-ray photoelectron spectroscopy recommends the chemical interactions between MoS2 and TiO2, specifically, oxygen vacancies. In addition, the electrochemical impedance spectroscopy studies observed that L-MT sample performed low charge transfer resistance (336.7 Ω cm2) that promotes the migration of electrons and interfacial charge separation. The photocatalytic performance is evaluated by quantifying the rate of Congo red dye degradation under visible light irradiation, and the decomposition efficiency was found to be 97%. The electron trapping recombination and plausible photocatalytic mechanism are also explored, and the reported work could be an excellent complement for industrial wastewater treatment.

| S-EPMC7728806 | biostudies-literature

Synthesis and Characterization of Two-Dimensional Transition Metal Dichalcogenide Magnetic MoS2@Fe3O4 Nanoparticles for Adsorption of Cr(VI)/Cr(III).

Project description:Recently, two-dimensional transition metal dichalcogenides (TMDs) have received tremendous attention in many fields including environmental remediation. Magnetic nanoparticles (Fe3O4NPs) decorated with MoS2 (MoS2@Fe3O4NPs) have been synthesized via a new one-step synthesis route and utilized as an efficient adsorbent for removal of Cr(VI)/Cr(III) from aqueous solutions. The obtained MoS2@Fe3O4NPs with numerous surface hydroxyl groups show uniform size and shape, excellent water-dispersibility, and superior magnetic property to enhance the adsorption. The physicochemical properties of the adsorbent prior to and after adsorption of Cr(VI)/Cr(III) were extensively characterized using several advanced instrumental techniques.The adsorption of Cr(VI)/Cr(III) on MoS2@Fe3O4NPs was performed under batch conditions aiming at identification of optimal contact time, pH value of chromium solution, and influence of the presence of competitive ions. This study was supported by modeling of adsorption equilibrium and kinetics by using empirical equations.

| S-EPMC6644607 | biostudies-literature

Heterostructure of two different 2D materials based on MoS2 nanoflowers@rGO: an electrode material for sodium-ion capacitors.

Project description:Sodium ion capacitors are under extensive investigation as companionable pre-existing lithium ion batteries and sodium ion batteries. Finding a suitable host for sodium ion storage is still a major challenge. In this context, here we report a MoS2 nanoflowers@rGO composite produced via a hydrothermal method followed by an ultra sonication process as a sodium ion symmetric hybrid supercapacitor. The structural and electrochemical performances of the electrode material were investigated to establish its applicability in sodium ion capacitors. The electrochemical performance was evaluated using metallic sodium in a half cell configuration which delivered a maximum specific capacitance of 226 F g-1 at 0.03 A g-1. When examined as a symmetric hybrid electrode (full cell) it delivered a maximum capacitance of 55 F g-1 at 0.03 A g-1. This combination may be a new gateway for upcoming research work which deals with sodium ion storage applications. The results confirmed that the as-synthesized MoS2 nanoflowers@rGO heterostructure electrode exhibited notable electrochemical behaviour.

| S-EPMC9473256 | biostudies-literature