Facet controlled growth mechanism of SnO₂ (101) nanosheet assembled film via cold crystallization.

ABSTRACT: Cold crystallization of SnO₂ was realized in aqueous solutions, where crystal growth was controlled to form SnO₂ (101) nanosheet assembled films for devices such as chemical sensors. The nanosheets grew directly on a fluorine-doped tin oxide substrate without a seed layer or a buffer layer. The nanosheets had a thickness of 5-10 nm and an in-plane size of 100-1600 nm. Moreover, the large flat surface of the (101) facet was metastable. The thickness of the SnO₂ (101) nanosheet assembled film was approximately 800 nm, and the film had a gradient structure that contained many connected nanosheets. TEM results revealed that the predominate branch angles between any two connected nanosheets were 90° and 46.48°, corresponding to type I and type II connections, respectively. These connections were consistent with the calculations based on crystallography. Crystallographic analysis clarified the characteristic crystal growth of the SnO₂ (101) nanosheet assembled film in the aqueous solution. Furthermore, we demonstrate that the metastable (101) facet can be exploited to control the rate of crystal growth by adjusting the etching condition.

SUBMITTER: Masuda Y

PROVIDER: S-EPMC8163760 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

A Metal-Organic Framework Nanosheet-Assembled Frame Film with High Permeability and Stability.

Project description:The engineering of metal-organic frameworks (MOFs) into membranes and films is being investigated, to transform laboratory-synthesized MOFs into industrially viable products for a range of attractive applications. However, rational design and construction of highly permeable MOF thin films, without trade-offs in terms of structural mechanical stability, remains a significant challenge. Herein, a simple, general strategy is reported to prepare thin MOF nanosheet (NS)-assembled frame film via heteroepitaxial growth from metal hydroxide film. As the thin MOF NS-assembled film significantly enhances the permeability of mass though the film, the resultant gold nanoparticle (Au NP)@MOF film exhibits much higher catalytic efficiency than the Au NP@MOF bulk film. Meanwhile, the unique framework of the MOF NS-assembled film resists torsion and collapse, so the composite catalyst exhibits long-term stability.

| S-EPMC7175284 | biostudies-literature

Extremely Sensitive Dependence of SnOx Film Properties on Sputtering Power.

Project description:An extremely sensitive dependence of the electronic properties of SnOx film on sputtering deposition power is discovered experimentally. The carrier transport sharply switches from n-type to p-type when the sputtering power increases by less than 2%. The best n-type carrier transport behavior is observed in thin-film transistors (TFTs) produced at a sputtering power just below a critical value (120 W). In contrast, at just above the critical sputtering power, the p-type behavior is found to be the best with the TFTs showing the highest on/off ratio of 1.79 × 104 and the best subthreshold swing among all the sputtering powers that we have tested. A further increase in the sputtering power by only a few percent results in a drastic drop in on/off ratio by more than one order of magnitude. Scanning electron micrographs, x-ray diffraction spectra, x-ray photoelectron spectroscopy, as well as TFT output and transfer characteristics are analyzed. Our studies suggest that the sputtering power critically affects the stoichiometry of the SnOx film.

| S-EPMC5099937 | biostudies-literature

Experimental and Density Functional Theory Simulation Research on PdO-SnO2 Nanosheet Ethanol Gas Sensors.

Project description:Pure SnO2 and 1 at.% PdO-SnO2 materials were prepared using a simple hydrothermal method. The micromorphology and element valence state of the material were characterized using XRD, SEM, TEM, and XPS methods. The SEM results showed that the prepared material had a two-dimensional nanosheet morphology, and the formation of PdO and SnO2 heterostructures was validated through TEM. Due to the influence of the heterojunction, in the XPS test, the energy spectrum peaks of Sn and O in PdO-SnO2 were shifted by 0.2 eV compared with SnO2. The PdO-SnO2 sensor showed improved ethanol sensing performance compared to the pure SnO2 sensor, since it benefited from the large specific surface area of the nanosheet structure, the modulation effect of the PdO-SnO2 heterojunction on resistance, and the catalyst effect of PdO on the adsorption of oxygen. A DFT calculation study of the ethanol adsorption characteristics of the PdO-SnO2 surface was conducted to provide a detailed explanation of the gas-sensing mechanism. PdO was found to improve the reducibility of ethanol, enhance the adsorption of ethanol's methyl group, and increase the number of adsorption sites. A synergistic effect based on the continuous adsorption sites was also deduced.

| S-EPMC11314670 | biostudies-literature

MDACl2-Modified SnO2 Film for Efficient Planar Perovskite Solar Cells.

Project description:The electron transport layer (ETL) with excellent charge extraction and transport ability is one of the key components of high-performance perovskite solar cells (PSCs). SnO2 has been considered as a more promising ETL for the future commercialization of PSCs due to its excellent photoelectric properties and easy processing. Herein, we propose a facile and effective ETL modification strategy based on the incorporation of methylenediammonium dichloride (MDACl2) into the SnO2 precursor colloidal solution. The effects of MDACl2 incorporation on charge transport, defect passivation, perovskite crystallization, and PSC performance are systematically investigated. First, the surface defects of the SnO2 film are effectively passivated, resulting in the increased conductivity of the SnO2 film, which is conducive to electron extraction and transport. Second, the MDACl2 modification contributes to the formation of high-quality perovskite films with improved crystallinity and reduced defect density. Furthermore, a more suitable energy level alignment is achieved at the ETL/perovskite interface, which facilitates the charge transport due to the lower energy barrier. Consequently, the MDACl2-modified PSCs exhibit a champion efficiency of 22.30% compared with 19.62% of the control device, and the device stability is also significantly improved.

| S-EPMC10056177 | biostudies-literature

The Formation Mechanism of (001) Facet Dominated α-FAPbI3 Film by Pseudohalide Ions for High-Performance Perovskite Solar Cells.

Project description:Formamidinium lead triiodide (α-FAPbI3 ) has been widely used in high-efficiency perovskite solar cells due to its small band gap and excellent charge-transport properties. Recently, some additives show facet selectivity to generate a (001) facet-dominant film during crystallization. However, the mechanism to realize such (001) facet selectivity is not fully understood. Here, the authors attempted to use three ammonia salts NH4 X (X are pseudohalide anions) to achieve better (001) facet selectivity in perovskite crystallization and improved crystallinity. After addition, the (001) facet dominance is generally increased with the best effect from SCN- anions. The theoretical calculation revealed three mechanisms of such improvements. First, pseudohalide anions have larger binding energy than the iodine ion to bind the facets including (110), (210), and (111), slowing down the growth of these facets. The large binding energy also reduces nucleation density and improves crystallinity. Second, pseudohalide ions improve phase purity by increasing the formation energies of the δ-phase and other hexagonal polytypes, retarding the α- to δ-phase transition. Third, the strong binding of these anions can also effectively passivate the iodine vacancies and suppress nonradiative recombination. As a result, the devices show a power conversion efficiency of 24.11% with a Voc of 1.181 V.

| S-EPMC10288232 | biostudies-literature

Two-dimensional SnO2 anchored biomass-derived carbon nanosheet anode for high-performance Li-ion capacitors.

Project description:Lithium-ion capacitors (LICs) combine the advantages of both batteries and supercapacitors; they have attracted intensive attention among energy conversion and storage fields, and one of the key points of their research is the exploration of suitable battery-type electrode materials. Herein, a simple and low-cost strategy is proposed, in which SnO2 particles are anchored on the conductive porous carbon nano-sheets (PCN) derived from coffee grounds. This method can inhibit the grain coarsening of Sn and the volume change of SnO2 effectively, thus improving the electrochemical reversibility of the materials. In the lithium half cell (0-3.0 V vs. Li/Li+), the as-prepared SnO2/PCN electrode yields a reversible capacity of 799 mA h g-1 at 0.1 A g-1 and decent long-term cyclability of 313 mA h g-1 at 1 A g-1 after 500 cycles. The excellent Li+ storage performance of SnO2/PCN is beneficial from the hierarchical structure as well as the robust carbonaceous buffer layer. Besides, a LIC hybrid device with the as-prepared SnO2/PCN anode exhibits outstanding energy and power density of 138 W h kg-1 and 53 kW kg-1 at a voltage window of 1.0-4.0 V. These promising results open up a new way to develop advanced anode materials with high rate and long life.

| S-EPMC8695415 | biostudies-literature

Regioselective Friedel-Crafts Acylation Reaction Using Single Crystalline and Ultrathin Nanosheet Assembly of Scrutinyite-SnO2.

Project description:Peculiar physicochemical properties of two-dimensional (2D) nanomaterials have attracted research interest in developing new synthetic technology and exploring their potential applications in the field of catalysis. Moreover, ultrathin metal oxide nanosheets with atomic thickness exhibit abnormal surficial properties because of the unique 2D confinement effect. In this work, we present a facile and general approach for the synthesis of single crystalline and ultrathin 2D nanosheets assembly of scrutinyite-SnO2 through a simple solvothermal method. The structural and compositional characterization using X-ray diffraction (Rietveld refinement analysis), high-resolution transmission electron microscopy, atomic force microscopy, X-ray photoelectron spectroscopy, and so on reveal that the as-synthesized 2D nanosheets are ultrathin and single crystallized in the scrutinyite-SnO2 phase with high purity. The ultrathin SnO2 nanosheets show predominant growth in the [011] direction on the main surface having a thickness of ca. 1.3 nm. The SnO2 nanosheets are further employed for the regioselective Friedel-Crafts acylation to synthesize aromatic ketones that have potential significance in chemical industry as synthetic intermediates of pharmaceuticals and fine chemicals. A series of aromatic substrates acylated over the SnO2 nanosheets have afforded the corresponding aromatic ketones with up to 92% yield under solvent-free conditions. Comprehensive catalytic investigations display the SnO2 nanosheet assembly as a better catalytic material compared to the heterogeneous metal oxide catalysts used so far in the view of its activity and reusability in solvent-free reaction conditions.

| S-EPMC9476169 | biostudies-literature

Photoexcitation-induced passivation of SnO2 thin film for efficient perovskite solar cells.

Project description:A high-quality tin oxide electron transport layer (ETL) is a key common factor to achieve high-performance perovskite solar cells (PSCs). However, the conventional annealing technique to prepare high-quality ETLs by continuous heating under near-equilibrium conditions requires high temperatures and a long fabrication time. Alternatively, we present a non-equilibrium, photoexcitation-induced passivation technique that uses multiple ultrashort laser pulses. The ultrafast photoexcitation and following electron-electron and electron-phonon scattering processes induce ultrafast annealing to efficiently passivate surface and bulk defects, and improve the crystallinity of SnO2, resulting in suppressing the carrier recombination and facilitating the charge transport between the ETL and perovskite interface. By rapidly scanning the laser beam, the annealing time is reduced to several minutes, which is much more efficient compared with conventional thermal annealing. To demonstrate the university and scalability of this technique, typical antisolvent and antisolvent-free processed hybrid organic-inorganic metal halide PSCs have been fabricated and achieved the power conversion efficiency (PCE) of 24.14% and 22.75% respectively, and a 12-square-centimeter module antisolvent-free processed perovskite solar module achieves a PCE of 20.26%, with significantly enhanced performance both in PCE and stability. This study establishes a new approach towards the commercialization of efficient low-temperature manufacturing of PSCs.

| S-EPMC10583279 | biostudies-literature

A Nanosheet-Assembled SnO2-Integrated Anode.

Project description:There is an ever-increasing trend toward bendable and high-energy-density electrochemical storage devices with high strength to fulfil the rapid development of flexible electronics, but they remain a great challenge to be realised by the traditional slurry-casting fabrication processes. To overcome these issues, herein, a facile strategy was proposed to design integrating an electrode with flexible, high capacity, and high tensile strength nanosheets with interconnected copper micro-fibre as a collector, loaded with a novel hierarchical SnO2 nanoarchitecture, which were assembled into core-shell architecture, with a 1D micro-fibre core and 2D nanosheets shell. When applied as anode materials for LIBs, the resultant novel electrode delivers a large reversible specific capacity of 637.2 mAh g-1 at a high rate of 1C. Such superior capacity may benefit from rational design based on structural engineering to boost synergistic effects of the integrated electrode. The outer shell with the ultrathin 2D nanoarchitecture blocks can provide favourable Li+ lateral intercalation lengths and more beneficial transport routes for electrolyte ions, with sufficient void space among the nanosheets to buffer the volume expansion. Furthermore, the interconnected 1D micro-fibre core with outstanding metallic conductivity can offer an efficient electron transport pathway along axial orientation to shorten electron transport. More importantly, the metal's remarkable flexibility and high tensile strength provide the hybrid integrated electrode with strong bending and stretchability relative to sintered carbon or graphene hosts. The presented strategy demonstrates that this rational nanoarchitecture design based on integrated engineering is an effective route to maintain the structural stability of electrodes in flexible LIBs.

| S-EPMC8538835 | biostudies-literature

High-Pressure Behavior of Ca2SnO4, Sr2SnO4, and Zn2SnO4.

Project description:The pressure-induced structural evolution of Ca2SnO4, Sr2SnO4, and Zn2SnO4 has been characterized by powder X-ray diffraction up to 20 GPa using the ALBA synchrotron radiation source and density functional theory calculations. No phase transition was observed in Ca2SnO4 and Zn2SnO4 in the investigated pressure range. The observation in Zn2SnO4 solves contradictions existing in the literature. In contrast, a phase transition was observed in Sr2SnO4 at a pressure of 9.09 GPa. The transition was characterized as from the ambient-condition tetragonal polymorph (space group I4/mmm) to the low-temperature tetragonal polymorph (space group P42/ncm). The linear compressibility of crystallographic axes and room-temperature pressure-volume equation of state are reported for the three compounds studied. Calculated elastic constants and moduli are also reported as well as a systematic discussion of the high-pressure behavior and bulk modulus of M2SnO4 stannates.

| S-EPMC10823467 | biostudies-literature