Polyvinyl Alcohol/Chitosan Single-Layered and Polyvinyl Alcohol/Chitosan/Eudragit RL100 Multi-layered Electrospun Nanofibers as an Ocular Matrix for the Controlled Release of Ofloxacin: an In Vitro and In Vivo Evaluation.

ABSTRACT: A novel nanofiber insert was prepared with a modified electrospinning method to enhance the ocular residence time of ofloxacin (OFX) and to provide a sustained release pattern by covering hydrophilic polymers, chitosan/polyvinyl alcohol (CS/PVA) nanofibers, with a hydrophobic polymer, Eudragit RL100 in layers, and by glutaraldehyde (GA) cross-linking of CS-PVA nanofibers for the treatment of infectious conjunctivitis. The morphology of the prepared nanofibers was studied using scanning electron microscopy (SEM). The average fiber diameter was found to be 123 ± 23 nm for the single electrospun nanofiber with no cross-linking (OFX-O). The single nanofibers, cross-linked for 10 h with GA (OFX-OG), had an average fiber diameter of 159 ± 30 nm. The amount of OFX released from the nanofibers was measured in vitro and in vivo using UV spectroscopy and microbial assay methods against Staphylococcus aureus, respectively. The antimicrobial efficiency of OFX formulated in cross-linked and non-cross-linked nanofibers was affirmed by observing the inhibition zones of Staphylococcus aureus and Escherichia coli. In vivo studies using the OFX nanofibrous inserts on a rabbit eye confirmed a sustained release pattern for up to 96 h. It was found that the cross-linking of the nanofibers by GA vapor could reduce the burst release of OFX from OFX-loaded CS/PVA in one layer and multi-layered nanofibers. In vivo results showed that the AUC_0-96 for the nanofibers was 9-20-folds higher compared to the OFX solution. This study thus demonstrates the potential of the nanofiber technology is being utilized to sustained drug release in ocular drug delivery systems.

SUBMITTER: Mirzaeei S

PROVIDER: S-EPMC8175245 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Chitosan nanofibrous membranes have immense potential in tissue engineering and drug delivery applications because of their increased surface area, high degree of biocompatibility, and their ability to mimic the extracellular matrix. However, their use is often limited due to their extreme hydrophilic nature causing them to lose their nanofibrous structure in vivo. In the present study, chitosan membranes were modified either by acylation reactions using fatty acids of different chain lengths or tert-butyloxycarbonyl (tBOC) protecting groups to increase the hydrophobicity of the membranes and protect the nanofibrous structure. The modified membranes were characterized using scanning electron microscopy, attenuated total reflectance Fourier transform infrared spectroscopy, water contact angle and elemental analysis to confirm the addition of the modification groups. These membranes were then evaluated to control the release of a hydrophobic osteogenic drug-simvastatin (SMV). The interaction between SMV and the polymer was determined using molecular modeling. Pure SMV and SMV loaded membranes were examined for their in vitro cytotoxicity and osteogenic potential using preosteoblast mouse bone marrow stromal cells. From results, it was evident that as the fatty acid chain length increased from two to six methylene groups, the hydrophobicity of the membranes increased (59.2 ± 8.2° to 94.3 ± 8.5° water contact angle). The amount of drug released from the membranes could be controlled by changing the amount of initial drug loaded and/or the type of modifications. After 4 weeks, for a 500 μg loading, the short chain fatty acid modified membranes released 17.8 ± 3.2% of the drug whereas a long chain fatty acid released only 4.8 ± 0.8%. Similarly, for a 50 μg loading, short chain modified membranes released more (73.3 ± 33.3%) of the loaded drug as compared to the long chain membranes (43.0 ± 3.5%). The long chain fatty acid membranes released SMV for extended time periods of up to 90 days. This data was further supported by molecular modeling, which revealed that SMV was more compatible with more hydrophobic membranes. Cell studies showed that pure SMV from 75 to 600 ng/ml range possessed osteogenic potential in a dose dependent manner and the amount of SMV released from the most hydrophobic FA treated membranes was not cytotoxic and supported osteogenic differentiation. Therefore, this study demonstrates our ability to control the release of a hydrophobic drug from modified chitosan membranes as per the clinical need.

Dataset Information

Polyvinyl Alcohol/Chitosan Single-Layered and Polyvinyl Alcohol/Chitosan/Eudragit RL100 Multi-layered Electrospun Nanofibers as an Ocular Matrix for the Controlled Release of Ofloxacin: an In Vitro and In Vivo Evaluation.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets