Simultaneously Regulating Uniform Zn²⁺ Flux and Electron Conduction by MOF/rGO Interlayers for High-Performance Zn Anodes.

ABSTRACT: Owing to the merits of low cost, high safety and environmental benignity, rechargeable aqueous Zn-based batteries (ZBs) have gained tremendous attention in recent years. Nevertheless, the poor reversibility of Zn anodes that originates from dendrite growth, surface passivation and corrosion, severely hinders the further development of ZBs. To tackle these issues, here we report a Janus separator based on a Zn-ion conductive metal-organic framework (MOF) and reduced graphene oxide (rGO), which is able to regulate uniform Zn²⁺ flux and electron conduction simultaneously during battery operation. Facilitated by the MOF/rGO bifunctional interlayers, the Zn anodes demonstrate stable plating/stripping behavior (over 500 h at 1 mA cm^-2), high Coulombic efficiency (99.2% at 2 mA cm^-2 after 100 cycles) and reduced redox barrier. Moreover, it is also found that the Zn corrosion can be effectively retarded through diminishing the potential discrepancy on Zn surface. Such a separator engineering also saliently promotes the overall performance of Zn|MnO₂ full cells, which deliver nearly 100% capacity retention after 2000 cycles at 4 A g^-1 and high power density over 10 kW kg^-1. This work provides a feasible route to the high-performance Zn anodes for ZBs.

SUBMITTER: Wang Z

PROVIDER: S-EPMC8187534 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

A hybrid polymer protective layer with uniform Li+ flux and self-adaption enabling dendrite-free Li metal anodes.

Project description:Lithium (Li) metal is considered as an ideal negative electrode material for next-generation secondary batteries; however, the hideous dendrite growth and parasitic reactions hinder the practical applications of Li metal batteries. Herein, a hybrid polymer film composed of polyvinyl alcohol (PVA) and polyacrylic acid (PAA) is adopted as an artificial protective layer to inhibit the dendritic formation and side reactions in Li metal anodes. PVA with large quantities of polar functional groups can induce even distribution of Li ions (Li+). Alternatively, PAA can in situ react with Li metal to form highly elastic and ionic conducting lithium polyacrylic acid (LiPAA), thereby enabling tight contact and flexible self-adaption with Li metal anodes. Therefore, such a rationally designed functional composite layer, with good binding ability and relatively high Li+ conductivity, as well as excellent capability of homogenizing Li+ flow, accordingly enables Li metal anodes to reveal dendrite-free plating/stripping behaviours and minimum volume variation. As a result, the PVA-PAA modified Li metal anode delivered stable cycling for 700 and 250 h, respectively, at current densities of 1 and 3 mA cm-2 under an areal capacity of 1 mA h cm-2, in a carbonate ester-based electrolyte without any additive, exhibiting boosted cycling and rate performances. The Li anode with a functional PVA-PAA hybrid interlayer can maintain the dense and smooth texture without dendrite formation after long cycles. The full cell of Li|LiFeO4 with our modified Li anode and a cathode with a high areal capacity of 2.45 mA h cm-2 delivers, change to achieved a long-term lifespan of 180 cycles at 1.0 C, with a capacity retention of 96.7%. This work demonstrates a simple and effective strategy of designing multi-functional artificial protective layers, targeting dendrite-free Li anodes.

| S-EPMC10496765 | biostudies-literature

Zeolitic Imidazolate Frameworks as Zn2+ Modulation Layers to Enable Dendrite-Free Zn Anodes.

Project description:Zinc (Zn) holds great promise as a desirable anode material for next-generation rechargeable batteries. However, the uncontrollable dendrite growth and low coulombic efficiency of the Zn plating/stripping process severely impede further practical applications of Zn-based batteries. Here, these roadblocks are removed by using in situ grown zeolitic imidazolate framework-8 (ZIF-8) as the ion modulation layer to tune the diffusion behavior of Zn2+ ions on Zn anodes. The well-ordered nanochannels and N species of ZIF-8 can effectively homogenize Zn2+ flux distribution and modulate the plating/stripping rate, ensuring uniform Zn deposition without dendrite growth. The Zn corrosion and hydrogen evolution are also alleviated by the insulating nature of ZIF-8, resulting in high coulombic efficiency. Therefore, the Zn@ZIF anode shows highly reversible, dendrite-free Zn plating/stripping behavior under a broad range of current densities, and a symmetric cell using this anode can work correctly up to 1200 h with a low polarization at 2 mA cm-2. Moreover, this ultrastable Zn@ZIF anode also enables a full Zn ion battery with outstanding cyclic stability (10 000 cycles).

| S-EPMC7610278 | biostudies-literature

Stable Zn Metal Anodes with Limited Zn-Doping in MgF2 Interphase for Fast and Uniformly Ionic Flux.

Project description:The practical applications of aqueous Zn metal batteries are currently restricted by the inherent drawbacks of Zn such as the hydrogen evolution reaction, sluggish kinetics, and dendrite formation. To address these problems, herein, a limitedly Zn-doped MgF2 interphase comprising an upper region of pure, porous MgF2 and a lower region of gradient Zn-doped MgF2 is achieved via radio frequency sputtering technique. The porous MgF2 region is a polar insulator whose high corrosion resistance facilitates the de-solvation of the solvated Zn ions and suppression of hydrogen evolution, resulting in Zn metal electrodes with a low interfacial resistance. The Zn-doped MgF2 region facilitates fast transfer kinetics and homogeneous deposition of Zn ions owing to the interfacial polarization between the Zn dopant and MgF2 matrix, and the high concentration of the Zn dopant on the surface of the metal substrate as fine nuclei. Consequently, a symmetric cell incorporating the proposed Zn metal exhibits low overpotentials of ~ 27.2 and ~ 99.7 mV without Zn dendrites over 250 to 8000 cycles at current densities of 1.0 and 10.0 mA cm-2, respectively. The developed Zn/MnO2 full cell exhibits superior capacity retentions of 97.5% and 84.0% with average Coulombic efficiencies of 99.96% after 1000 and 3000 cycles, respectively.

| S-EPMC8783935 | biostudies-literature

MOF-derived nitrogen-doped porous carbon nanofibers with interconnected channels for high-stability Li+/Na+ battery anodes.

Project description:Heteroatom-doped porous carbon materials have been widely used as anode materials for Li-ion and Na-ion batteries, however, improving the specific capacity and long-term cycling stability of ion batteries remains a major challenge. Here, we report a facile based metal-organic framework (MOFs) strategy to synthesize nitrogen-doped porous carbon nanofibers (NCNFs) with a large number of interconnected channels that can increase the contact area between the material and the electrolyte, shorten the diffusion distance between Li+/Na+ and the electrolyte, and relieve the volume expansion of the electrode material during cycling; the doping of nitrogen atoms can improve the conductivity and increase the active sites of the carbon material, can also affect the microstructure and electron distribution of the electrode material, thereby improving the electrochemical performance of the material. As expected, the obtained NCNFs-800 exhibited excellent electrochemical performance with high reversible capacity (for Li+ battery anodes: 1237 mA h g-1 at 100 mA g-1 after 200 cycles, for Na+ battery anodes: 323 mA h g-1 at 100 mA g-1 after 150 cycles) and long-term cycling stability (for Li+ battery anodes: 635 mA h g-1 at 2 A g-1 after 5000 cycles, for Na+ battery anodes: 194 mA h g-1 at 2 A g-1 after 5000 cycles).

| S-EPMC9926884 | biostudies-literature

Direct Proof of the Reversible Dissolution/Deposition of Mn2+/Mn4+ for Mild-Acid Zn-MnO2 Batteries with Porous Carbon Interlayers.

Project description:Mild-acid Zn-MnO2 batteries have been considered a promising alternative to Li-ion batteries for large scale energy storage systems because of their high safety. There have been remarkable improvements in the electrochemical performance of Zn-MnO2 batteries, although the reaction mechanism of the MnO2 cathode is not fully understood and still remains controversial. Herein, the reversible dissolution/deposition (Mn2+/Mn4+) mechanism of the MnO2 cathode through a 2e- reaction is directly evidenced using solution-based analyses, including electron spin resonance spectroscopy and the designed electrochemical experiments. Solid MnO2 (Mn4+) is reduced into Mn2+ (aq) dissolved in the electrolyte during discharge. Mn2+ ions are then deposited on the cathode surface in the form of the mixture of the poorly crystalline Zn-containing MnO2 compounds through two-step reactions during charge. Moreover, the failure mechanism of mild-acid Zn-MnO2 batteries is elucidated in terms of the loss of electrochemically active Mn2+. In this regard, a porous carbon interlayer is introduced to entrap the dissolved Mn2+ ions. The carbon interlayer suppresses the loss of Mn2+ during cycling, resulting in the excellent electrochemical performance of pouch-type Zn-MnO2 cells, such as negligible capacity fading over 100 cycles. These findings provide fundamental insights into strategies to improve the electrochemical performance of aqueous Zn-MnO2 batteries.

| S-EPMC7967064 | biostudies-literature

Functionalized rGO Interlayers Improve the Fill Factor and Current Density in PbS QDs-Based Solar Cells.

Project description:Graphene-quantum dot nanocomposites attract significant attention for novel optoelectronic devices, such as ultrafast photodetectors and third-generation solar cells. Combining the remarkable optical properties of quantum dots (QDs) with the exceptional electrical properties of graphene derivatives opens a vast perspective for further growth in solar cell efficiency. Here, we applied (3-mercaptopropyl) trimethoxysilane functionalized reduced graphene oxide (f-rGO) to improve the QDs-based solar cell active layer. The different strategies of f-rGO embedding are explored. When f-rGO interlayers are inserted between PbS QD layers, the solar cells demonstrate a higher current density and a better fill factor. A combined study of the morphological and electrical parameters of the solar cells shows that the improved efficiency is associated with better layer homogeneity, lower trap-state densities, higher charge carrier concentrations, and the blocking of the minor charge carriers.

| S-EPMC6947317 | biostudies-literature

A Water-Stable Zn-MOF Used as Multiresponsive Luminescent Probe for Sensing Fe3+/Cu2+, Trinitrophenol and Colchicine in Aqueous Medium.

Project description:A water-stable Zn-MOF was constructed based on H2PBA and 1, 10-phenanthroline under solvothermal conditions. The compound exhibited a 3D (2,3,8)-connected (43)2(46.66.815.12)(8) topology framework. The crystal structure and phase purity of the compound was verified by single crystal X-ray diffraction. Subsequently, some studies on the morphology, structure, and luminescent properties were carried out. The results showed that this compound could be used as a versatile chemosensor for Fe3+/Cu2+, trinitrophenol and colchicine via a luminescence quenching effect in an aqueous medium.

| S-EPMC9570702 | biostudies-literature

Flexible MnO nanoparticle-anchored N-doped porous carbon nanofiber interlayers for superior performance lithium metal anodes.

Project description:The mounting requirements for electric apparatus and vehicles stimulate the rapid progress of energy storage systems. Lithium (Li) metal is regarded as one of the most prospective anodes for high-performance cells. However, the uneven dendrite growth is one of the primary conundrums that hampers the use of the Li metal anode in rechargeable Li batteries. Achieving even Li deposition is crucial to solve this concern. In this study, a stable interlayer based on electrospun flexible MnO nanoparticle/nitrogen (N)-doped (polyimide) PI-based porous carbon nanofiber (MnO-PCNF) films was effectively prepared via electrospinning and in situ growth of MnO to reduce the growth of Li dendrites. It is revealed that the attraction of implanted MnO towards Li, the lithiophilic nature of N dopants and the capillary force of porous architectures are beneficial to the preeminent Li wettability of the MnO-PCNF interlayer. Furthermore, the wettable, stable and conductive structure of the MnO-PCNF interlayer can be retained well, offering rapid charge transfer to Li redox reactions, reduced local current density during the cycling process and homogeneous distribution of deposited Li. Consequently, anodes with MnO-PCNF interlayers can relieve the volume change and inhibit the growth of Li dendrites, demonstrating a remarkable lifetime for lithium metal cells at high current.

| S-EPMC9419476 | biostudies-literature

Towards the practical application of Zn metal anodes for mild aqueous rechargeable Zn batteries.

Project description:Rechargeable aqueous Zn batteries have been widely investigated in recent years due to the merits of high safety and low cost. However inevitable dendrite growth, corrosion and hydrogen evolution of Zn anodes severely compromise the practical lifespan of rechargeable Zn batteries. Despite the encouraging improvements for Zn anodes reported in the literature, the comprehensive understanding of Zn anodes under practical conditions is still often neglected. In this article, we focus on the "less-discussed" but critically important points for rechargeable aqueous Zn batteries, including revisit of the relationship between the coulombic efficiency and lifespan of Zn anodes, the rational control of the pH environment in the vicinity of Zn anodes, the design of appropriate aqueous separators and the relevant estimation of practical energy density for aqueous Zn batteries. It concludes that energy density of 60-80 W h kg-1 for aqueous Zn batteries should be realistic in practice with appropriate cell design. We also propose practical technical recommendations for the rational development of aqueous Zn batteries based on research experience from the community and our group. We hope this article offers readers more practical insights into the future development of aqueous Zn batteries as competitive technology for practical use.

| S-EPMC9297528 | biostudies-literature

Building Ohmic Contact Interfaces toward Ultrastable Zn Metal Anodes.

Project description:Zn metal holds grand promise as the anodes of aqueous batteries for grid-scale energy storage. However, the rampant zinc dendrite growth and severe surface side reactions significantly impede the commercial implementation. Herein, a universal Zn-metal oxide Ohmic contact interface model is demonstrated for effectively improving Zn plating/stripping reversibility. The high work function difference between Zn and metal oxides enables the building of an interfacial anti-blocking layer for dendrite-free Zn deposition. Moreover, the metal oxide layer can function as a physical barrier to suppress the pernicious side reactions. Consequently, the proof-of-concept CeO2 -modified Zn anode delivers ultrastable durability of over 1300 h at 0.5-5 mA cm-2 and improved Coulombic efficiency, the feasibility of which is also evidenced in MoS2 //Zn full cells. This study enriches the fundamental comprehension of Ohmic contact interfaces on the Zn deposition, which may shed light on the development of other metal battery anodes.

| S-EPMC8655195 | biostudies-literature