Migration Behavior of Lubricants in Polypropylene Composites under Accelerated Thermal Aging.

ABSTRACT: The surface migration of lubricants degrades the quality of thermoplastic polymer composites. In this study, the surface migration of lubricants in polypropylene composites were studied to improve the quality of the composites. Polypropylene (PP)/lubricant composites were manufactured using a co-rotating twin-screw extruder and injection molding, and the migration phenomena of the lubricant in the PP/lubricant composites were investigated under accelerated aging conditions with temperatures in the range of 20 to 90 °C and humidity of 100% for 72 h. The interrelation between the surface migration properties of PP/lubricant composites were investigated by considering their microstructural and morphological features, which were influenced by the thermal aging conditions. Further, the microstructural and morphological features were examined by contact angle, surface energy, attenuated total reflectance Fourier-transform infrared spectrometry, X-ray photoelectron spectroscopy, close-up digital imaging, and atomic force microscopy analyses. The polypropylene composites containing the magnesium stearate as the lubricant were found to exhibit a more stable migration behavior than the polypropylene composites containing a calcium stearate lubricant. This is attributed to multiple synergistic factors, such as interfacial tension and work of adhesion between PP and the lubricant. The findings of this study can be utilized to effectively manufacture high-quality thermoplastic composites for the fourth industrial revolution.

SUBMITTER: Bak MG

PROVIDER: S-EPMC8197380 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Nanomaterials (NM) are incorporated into polymers to enhance their properties. However, there are a limited number of studies on the aging of these nanocomposites and the resulting potential release of NM. To characterize NM at critical points in their life cycles, polypropylene (PP) and multiwall carbon nanotube filled PP (PP-MWCNT) plates with different thicknesses (from 0.25 mm to 2 mm) underwent accelerated weathering in a chamber that simulates solar irradiation and rainfall. The physicochemical changes of the plates depended on the radiation exposure, the plate thickness, and the presence of CNT fillers. Photodegradation increased with aging time, making the exposed surface more hydrophilic, decreasing the surface hardness and creating surface stress-cracks. Aged surface and cross-section showed crazing due to the polymer bond scission and the formation of carbonyls. The degradation was higher near the UV-exposed surface as the intensity of the radiation and oxygen diffusion decreased with increasing depth of the plates, resulting in an oxidation layer directly proportional to oxygen diffusion. Thus, sample thickness determines the kinetics of the degradation reaction and the transport of reactive species. Plastic fragments, which are less than 1 mm, and free CNTs were released from weathered MWCNT-PP. The concentrations of released NM that were estimated using ICP-MS, increased with prolonged aging time. Various toxicity tests, including reactive oxygen species generation and cell activity/viability, were performed on the released CNTs. The toxicity of the released fragments and CNTs to A594 adenocarcinomic human alveolar basal epithelial cells was observed. The released polymer fragments and CNTs did not show significant toxicity under the experimental conditions in this study. This study will help manufacturers, users of consumer products with nanocomposites and policymakers in the development of testing guidelines, predictive models, and risk assessments and risk based-formulations of NM exposure.

Dataset Information

Migration Behavior of Lubricants in Polypropylene Composites under Accelerated Thermal Aging.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets