Evaluation on Structural Properties and Performances of Graphene Oxide Incorporated into Chitosan/Poly-Lactic Acid Composites: CS/PLA versus CS/PLA-GO.

ABSTRACT: In this work, to fabricate a novel composite consisting of chitosan/poly-lactic acid doped with graphene oxide (CS/PLA-GO), composites were prepared via solution blending method to create various compositions of CS and PLA (90/10, 70/30 and 50/50CS/PLA-GO). Graphene oxide (GO) was added into a PLA solution prior to blending it with chitosan (CS). The surface morphology and structural properties of synthesized composites were characterized using FT-IR, SEM and XRD analysis. The performances of synthesized composites on thermal strength, mechanical strength, water absorption, and microbial activity were also evaluated through standard testing methods. The morphology of 70/30CS/PLA-GO became smoother with the addition of GO due to enhanced interfacial adhesion between CS, PLA and GO. The presence of GO has also improved the miscibility of CS and PLA and has superior properties compared to CS/PLA composites. Moreover, the addition of GO has boosted the thermal stability of the composite, with a significant enhancement of T_d and T_g. The highest T_d and T_g were accomplished at 389 °C and 76.88 °C, respectively, for the 70/30CS/PLA-GO composite in comparison to the CS and PLA that recorded T_d at 272 °C and 325 °C and T_g at 61 °C and 60 °C, respectively. In addition, as reinforcement, GO provided a significant influence on the tensile strength of composites where the tensile modulus showed remarkable improvement compared to pure CS and CS/PLA composites. Furthermore, CS/PLA-GO composites showed excellent water-barrier properties. Among other compositions, 70/30CS/PLA revealed the greatest decrement in water absorption. From the antibacterial results, it was observed that 90/10CS/PLA-GO and 70/30CS/PLA-GO showed an inhibitory effect and had wide inhibition zones which were 8.0 and 8.5 mm, respectively, against bacteria Bacillus Subtillis B29.

SUBMITTER: Mohamad SNK

PROVIDER: S-EPMC8199591 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The purpose of the present study is to develop new multifunctional environmentally friendly materials having applications both in medical and food packaging fields. New poly(lactic acid) (PLA)-based multifunctional materials containing additives derived from natural resources like chitosan (CS) and rosemary extract (R) were obtained by melt mixing. Each of the selected components has its own specific properties such as: PLA is a biodegradable thermoplastic aliphatic polyester derived from renewable biomass, heat-resistant, with mechanical properties close to those of polystyrene and polyethylene terephthalate, and CS offers good antimicrobial activity and biological functions, while R significantly improves antioxidative action necessary in all applications. A synergy of their combination, an optimum choice of their ratio, and processing parameters led to high performance antimicrobial/antioxidant/biocompatible/environmentally degradable materials. The polyethylene glycol (PEG)-plasticized PLA/chitosan/powdered rosemary extract biocomposites of various compositions were characterized in respect to their mechanical and rheological properties, structure by spectroscopy, antioxidant and antimicrobial activities, and in vitro and in vivo biocompatibility. Scanning electron microscopy images evidence the morphology features added by rosemary powder presence in polymeric materials. Incorporation of additives improved elongation at break, antibacterial and antioxidant activity and also biocompatibility. Migration of bioactive components into D1 simulant is slower for PEG-plasticized PLA containing 6 wt % chitosan and 0.5 wt % rosemary extract (PLA/PEG/6CS/0.5 R) biocomposite and it occurred by a diffusion-controlled mechanism. The biocomposites show high hydrophilicity and good in vitro and in vivo biocompatibility. No hematological, biochemical and immunological modifications are induced by subcutaneous implantation of biocomposites. All characteristics of the PEG-plasticized PLA-based biocomposites recommend them as valuable materials for biomedical implants, and as well as for the design of innovative drug delivery systems. Also, the developed biocomposites could be a potential nature-derived active packaging with controlled release of antimicrobial/antioxidant compounds.

Project description:Lignin, being one of the main structural components of lignocellulosic biomass, is considered the most abundant natural source of phenolics and aromatics. Efforts for its valorisation were recently explored as it is mostly treated as waste from heat/energy production via combustion. Among them, polymer-based lignin composites are a promising approach to both valorise lignin and to fine tune the properties of polymers. In this work, organosolv lignin, from beech wood, was used as fillers in a poly (lactic acid) (PLA) matrix. The PLA/lignin composites were prepared using melt mixing of masterbatches with neat PLA in three different lignin contents: 0.5, 1.0 and 2.5 wt%. Lignin was used as-isolated, via the organosolv biomass pretreatment/fractionation process and after 8 h of ball milling. The composites were characterised with Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR) spectroscopy, X-ray Diffraction (XRD), and Differential Scanning Calorimetry (DSC). Additionally, their antioxidant activity was assessed with the 2,2-Diphenyil-1-picrylhydrazyl (DPPH) method, the colour was measured with a colorimeter and the mechanical properties were evaluated with tensile testing. Ball milling, at least under the conditions applied in this study, did not induce a further substantial decrease in the already relatively small organosolv lignin primary particles of ~1 μm. All the produced PLA/lignin composites had a uniform dispersion of lignin. Compression-moulded films were successfully prepared, and they were coloured brown, with ball-milled lignin, giving a slightly lighter colour in comparison with the as-received lignin. Hydrogen bonding was detected between the components of the composites, and crystallization of the PLA was suppressed by both lignin, with the suppression being less pronounced by the ball-milled lignin. All composites showed a significantly improved antioxidant activity, and their mechanical properties were maintained for filler content 1 wt%.

Dataset Information

Evaluation on Structural Properties and Performances of Graphene Oxide Incorporated into Chitosan/Poly-Lactic Acid Composites: CS/PLA versus CS/PLA-GO.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets