Light-induced levitation of ultralight carbon aerogels via temperature control.

ABSTRACT: We demonstrate that ultralight carbon aerogels with skeletal densities lesser than the air density can levitate in air, based on Archimedes' principle, when heated with light. Porous materials, such as aerogels, facilitate the fabrication of materials with density less than that of air. However, their apparent density increases because of the air inside the materials, and therefore, they cannot levitate in air under normal conditions. Ultralight carbon aerogels, fabricated using carbon nanotubes, have excellent light absorption properties and can be quickly heated by a lamp owing to their small heat capacity. In this study, an ultralight carbon aerogel was heated with a halogen lamp and levitated in air by expanding the air inside as well as selectively reducing its density. We also show that the levitation of the ultralight carbon aerogel can be easily controlled by turning the lamp on and off. These findings are expected to be useful for various applications of aerogels, such as in communication and transportation through the sky.

SUBMITTER: Yanagi R

PROVIDER: S-EPMC8203743 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Ultralight and fire-resistant ceramic nanofibrous aerogels with temperature-invariant superelasticity.

Project description:Ultralight aerogels that are both highly resilient and compressible have been fabricated from various materials including polymer, carbon, and metal. However, it has remained a great challenge to realize high elasticity in aerogels solely based on ceramic components. We report a scalable strategy to create superelastic lamellar-structured ceramic nanofibrous aerogels (CNFAs) by combining SiO2 nanofibers with aluminoborosilicate matrices. This approach causes the random-deposited SiO2 nanofibers to assemble into elastic ceramic aerogels with tunable densities and desired shapes on a large scale. The resulting CNFAs exhibit the integrated properties of flyweight densities of >0.15 mg cm-3, rapid recovery from 80% strain, zero Poisson's ratio, and temperature-invariant superelasticity to 1100°C. The integral ceramic nature also provided the CNFAs with robust fire resistance and thermal insulation performance. The successful synthesis of these fascinating materials may provide new insights into the development of ceramics in a lightweight, resilient, and structurally adaptive form.

| S-EPMC5922795 | biostudies-literature

Ultralight boron nitride aerogels via template-assisted chemical vapor deposition.

Project description:Boron nitride (BN) aerogels are porous materials with a continuous three-dimensional network structure. They are attracting increasing attention for a wide range of applications. Here, we report the template-assisted synthesis of BN aerogels by catalyst-free, low-pressure chemical vapor deposition on graphene-carbon nanotube composite aerogels using borazine as the B and N sources with a relatively low temperature of 900?(°)C. The three-dimensional structure of the BN aerogels was achieved through the structural design of carbon aerogel templates. The BN aerogels have an ultrahigh specific surface area, ultralow density, excellent oil absorbing ability, and high temperature oxidation resistance. The specific surface area of BN aerogels can reach up to 1051?m(2) g(-1), 2-3 times larger than the reported BN aerogels. The mass density can be as low as 0.6?mg cm(-3), much lower than that of air. The BN aerogels exhibit high hydrophobic properties and can absorb up to 160 times their weight in oil. This is much higher than porous BN nanosheets reported previously. The BN aerogels can be restored for reuse after oil absorption simply by burning them in air. This is because of their high temperature oxidation resistance and suggests broad utility as water treatment tools.

| S-EPMC4432566 | biostudies-literature

Ultralight covalent organic framework/graphene aerogels with hierarchical porosity.

Project description:The fabrication of macroscopic objects from covalent organic frameworks (COFs) is challenging but of great significance to fully exploit their chemical functionality and porosity. Herein, COF/reduced graphene oxide (rGO) aerogels synthesized by a hydrothermal approach are presented. The COFs grow in situ along the surface of the 2D graphene sheets, which are stacked in a 3D fashion, forming an ultralight aerogel with a hierarchical porous structure after freeze-drying, which can be compressed and expanded several times without breaking. The COF/rGO aerogels show excellent absorption capacity (uptake of >200 g organic solvent/g aerogel), which can be used for removal of various organic liquids from water. Moreover, as active material of supercapacitor devices, the aerogel delivers a high capacitance of 269 F g-1 at 0.5 A g-1 and cycling stability over 5000 cycles.

| S-EPMC7501297 | biostudies-literature

A synthetic route to ultralight hierarchically micro/mesoporous Al(III)-carboxylate metal-organic aerogels.

Project description:Developing a synthetic methodology for the fabrication of hierarchically porous metal-organic monoliths that feature high surface area, low density and tunable porosity is imperative for mass transfer applications, including bulky molecule capture, heterogeneous catalysis and drug delivery. Here we report a versatile and facile synthetic route towards ultralight micro/mesoporous metal-organic aerogels based on the two-step gelation of metal-organic framework nanoparticles. Heating represents a key factor in the control of gelation versus crystallization of Al(III)-multicarboxylate systems. The porosity of the resulting metal-organic aerogels can be readily tuned, leading to the formation of well-ordered intraparticle micropores and aerogel-specific interparticle mesopores, thereby integrating the merits of both crystalline metal-organic frameworks and light aerogels. The hierarchical micro/mesoporosity of the Al-metal-organic aerogels is thoroughly evaluated by N? sorption. The good accessibility of the micro/mesopores is verified by vapour/dye uptake, and their potential for utilization as effective fibre-coating absorbents is tested in solid-phase microextraction analyses.

| S-EPMC3644084 | biostudies-other

Boron nitride colloidal solutions, ultralight aerogels and freestanding membranes through one-step exfoliation and functionalization.

Project description:Manufacturing of aerogels and membranes from hexagonal boron nitride (h-BN) is much more difficult than from graphene or graphene oxides because of the poor dispersibility of h-BN in water, which limits its exfoliation and preparation of colloidal solutions. Here, a simple, one-step mechano-chemical process to exfoliate and functionalize h-BN into highly water-dispersible, few-layer h-BN containing amino groups is presented. The colloidal solutions of few-layer h-BN can have unprecedentedly high concentrations, up to 30?mg?ml(-1), and are stable for up to several months. They can be used to produce ultralight aerogels with a density of 1.4?mg?cm(-3), which is ?1,500 times less than bulk h-BN, and freestanding membranes simply by cryodrying and filtration, respectively. The material shows strong blue light emission under ultraviolet excitation, in both dispersed and dry state.

| S-EPMC4674780 | biostudies-literature

Ultralight Industrial Bamboo Residue-Derived Holocellulose Thermal Insulation Aerogels with Hydrophobic and Fire Resistant Properties.

Project description:In this study, water-soluble ammonium polyphosphate- (APP) and methyl trimethoxysilane (MTMS)-modified industrial bamboo residue (IBR)-derived holocellulose nanofibrils (HCNF/APP/MTMS) were used as the raw materials to prepare aerogels in a freeze-drying process. Synthetically modified aerogels were confirmed by Fourier transform infrared spectroscopy, X-ray diffraction, and thermal stability measurements. As-prepared HCNF/APP/MTMS aerogels showed themselves to be soft and flexible. The scanning electron microscopy (SEM) analysis showed that the foam-like structure translates into a 3D network structure from HCNF aerogels to HCNF/APP/MTMS aerogels. The compressive modules of the HCNF/APP/MTMS aerogels were decreased from 38 kPa to 8.9 kPa with a density in the range of 12.04-28.54 kg/m3, which was due to the structural change caused by the addition of APP and MTMS. Compared with HCNF aerogels, HCNF/APP/MTMS aerogels showed a high hydrophobicity, in which the water contact angle was 130°, and great flame retardant properties. The peak of heat release rate (pHRR) and total smoke production (TSP) decreased from 466.6 to 219.1 kW/m2 and 0.18 to 0.04 m2, respectively, meanwhile, the fire growth rate (FIGRA) decreased to 8.76 kW/s·m2. The thermal conductivity of the HCNF/APP/MTMS aerogels was 0.039 W/m·K. All results indicated the prepared aerogels should be expected to show great potential for thermally insulative materials.

| S-EPMC7013456 | biostudies-literature

Ultralight hybrid silica aerogels derived from supramolecular hydrogels self-assembled from insoluble nano building blocks.

Project description:Supramolecular hydrogels are a type of hydrogel cross-linked by non-chemical bonds and they have been widely applied in the field of smart systems, sensors, tissue engineering, and controlled drug delivery. Most supramolecular hydrogels are formed by soluble molecules, polymers, and metal ions. In this work, supramolecular hydrogels self-assembled between two insoluble nano building blocks (ISNBBs), graphene oxide (GO) and amino-functionalized silica nanoparticles (SiO2-NH2), have been discovered and synthesized. The gelation conditions of the two ISNBBs have been investigated. A step further, ultralight hybrid silica aerogels are obtained by supercritical drying of the physical hydrogels. No visible volume shrinkage is observed, due to the fact that the hydrogel networks are formed by rigid ISNBBs. Thus the hybrid aerogels possess ultralow density (down to 7.5 mg cm-3), high specific surface areas (178.6 m2 g-1), and extremely high porosity (99.6%). The present work shows an alternative strategy to design and synthesize supramolecular hydrogels and aerogels using predetermined building blocks, together with designable morphology and physical properties for the target aerogels.

| S-EPMC8695017 | biostudies-literature

Grafting Polymers onto Carbon Nitride via Visible-Light-Induced Photofunctionalization.

Project description:Metal-free graphitic carbon nitride (g-CN) has attracted significant attention recently due to its multiple applications, such as photocatalysis, energy storage and conversion, and biomaterials, albeit formation of g-CN films is challenging. Herein, a "grafting to" route to graft polymer brushes onto g-CN via visible-light irradiation is described. Afterward, g-CN/polymer films can be obtained through spin coating on glass substrates. As such, the present material provides an improved process toward further application of g-CN in thin films. Moreover, an improved dispersibility in organic solvent was realized after grafting and functional groups (such as epoxides) were introduced to g-CN. Subsequently, the epoxy groups were utilized for further functionalization to adjust the surface polarity.

| S-EPMC6750929 | biostudies-literature

Starch-Based Aerogels Obtained via Solvent-Induced Gelation.

Project description:In this work, the ability of several solvents to induce gel formation from amylomaize starch solubilized in dimethyl sulfoxide (DMSO) was investigated. The formed gels were subjected to solvent exchange using ethanol and dried with supercritical carbon dioxide (sc-CO2) to obtain the aerogels. The influence of starch concentration (3-15 wt%) and solvent content (20-80 wt%) on gel formation was also studied. It was demonstrated that the gelation of starch in binary mixtures of solvents can be rationalized by Hansen Solubility Parameters (HSP) revealing a crucial hole of hydrogen bonding for the gel's strength, which is in agreement with rheological measurements. Only the addition of water or propylene glycol to starch/DMSO solutions resulted in strong gels at a minimum starch and solvent content of 7.5 wt% and 50 wt%, respectively. The resulting aerogels showed comparably high specific surface areas (78-144 m2 g-1) and low envelope densities (0.097-0.203 g cm-3). The results of this work indicate that the HSP parameters could be used as a tool to guide the rational selection of water-free gelation in starch/DMSO systems. In addition, it opens up an attractive opportunity to perform starch gelation in those solvents that are miscible with sc-CO2, avoiding the time-consuming step of solvent exchange.

| S-EPMC7559039 | biostudies-literature

Highly stretchable carbon aerogels.

Project description:Carbon aerogels demonstrate wide applications for their ultralow density, rich porosity, and multifunctionalities. Their compressive elasticity has been achieved by different carbons. However, reversibly high stretchability of neat carbon aerogels is still a great challenge owing to their extremely dilute brittle interconnections and poorly ductile cells. Here we report highly stretchable neat carbon aerogels with a retractable 200% elongation through hierarchical synergistic assembly. The hierarchical buckled structures and synergistic reinforcement between graphene and carbon nanotubes enable a temperature-invariable, recoverable stretching elasticity with small energy dissipation (~0.1, 100% strain) and high fatigue resistance more than 106 cycles. The ultralight carbon aerogels with both stretchability and compressibility were designed as strain sensors for logic identification of sophisticated shape conversions. Our methodology paves the way to highly stretchable carbon and neat inorganic materials with extensive applications in aerospace, smart robots, and wearable devices.

| S-EPMC5830400 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data