Scalable Solution-Processed Fabrication Approach for High-Performance Silver Nanowire/MXene Hybrid Transparent Conductive Films.

ABSTRACT: The transparent conductive films (TCFs) based on silver nanowires are expected to be a next-generation electrode for flexible electronics. However, their defects such as easy oxidation and high junction resistance limit its wide application in practical situations. Herein, a method of coating Ti₃C₂T_x with different sizes was proposed to prepare silver nanowire/MXene composite films. The solution-processed silver nanowire (AgNW) networks were patched and welded by capillary force effect through the double-coatings of small and large MXene nanosheets. The sheet resistance of the optimized AgNW/MXene TCFs was 15.1 Ω/sq, the optical transmittance at 550 nm was 89.3%, and the figure of merit value was 214.4. Moreover, the AgNW/MXene TCF showed higher stability at 1600 mechanical bending, annealing at 100 °C for 50 h, and exposure to ambient air for 40 days. These results indicate that the novel AgNW/MXene TCFs have a great potential for high-performance flexible optoelectronic devices.

SUBMITTER: Wang P

PROVIDER: S-EPMC8224074 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Tackling the Stability Issues of Silver Nanowire Transparent Conductive Films through FeCl₃ Dilute Solution Treatment.

Project description:Silver nanowires (AgNWs) have been investigated as alternatives to indium tin oxide in transparent conductive films (TCFs) for electronics. However, AgNW TCFs still pose stability issues when exposed to thermal, chemical, and mechanical stimuli. Herein, we demonstrate a facile and effective route to improve stability by treating the films with dilute ferric chloride solution. Our results indicate that after treatment the films exhibit a dramatically enhanced stability against aging, high temperature oxidation, chemical etching, sulfurization, and mechanical straining. Size-dependent instability is fully explored and explained regarding surface atomic diffusion, which could be blocked by enhancing the activation energy of surface diffusion through forming a AgCl cap under ferric chloride solution treatment. Chemisorption-related Fermi level shift of silver nanowires is applied to tune their chemical reactivity to ferric chloride solution for balancing between size-dependent stability improvement and maintaining optoelectrical properties. Owing to the dilute treatment solution, the treated films exhibit a negligible change in light transmittance, whereas sheet resistance decreases by 30% and flexibility increases because of capillary-force-induced welding of contacting AgNWs and AgCl layer mediated tightening. These findings are significant for real-world applications of AgNW TCFs.

| S-EPMC6523130 | biostudies-literature

Solution-processed transparent ferroelectric nylon thin films.

Project description:Ferroelectricity, a bistable ordering of electrical dipoles in a material, is widely used in sensors, actuators, nonlinear optics, and data storage. Traditional ferroelectrics are ceramic based. Ferroelectric polymers are inexpensive lead-free materials that offer unique features such as the freedom of design enabled by chemistry, the facile solution-based low-temperature processing, and mechanical flexibility. Among engineering polymers, odd nylons are ferroelectric. Since the discovery of ferroelectricity in polymers, nearly half a century ago, a solution-processed ferroelectric nylon thin film has not been demonstrated because of the strong tendency of nylon chains to form hydrogen bonds. We show the solution processing of transparent ferroelectric thin film capacitors of odd nylons. The demonstration of ferroelectricity, as well as the way to obtain thin films, makes odd nylons attractive for applications in flexible devices, soft robotics, biomedical devices, and electronic textiles.

| S-EPMC6697430 | biostudies-literature

Screen-Printed Fabrication of PEDOT:PSS/Silver Nanowire Composite Films for Transparent Heaters.

Project description:A transparent and flexible film heater was fabricated; based on a hybrid structure of poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) and silver nanowires (Ag NWs) using a screen printing; which is a scalable production technology. The resulting film integrates the advantages of the two conductive materials; easy film-forming and strong adhesion to the substrate of the polymer PEDOT:PSS; and high conductivity of the Ag NWs. The fabricated composite films with different NW densities exhibited the transmittance within the range from 82.3% to 74.1% at 550 nm. By applying 40 V potential on the films; a stable temperature from 49 °C to 99 °C was generated within 30 s to 50 s. However; the surface temperature of the pristine PEDOT:PSS film did not increase compared to the room temperature. The composite film with the transmittance of 74.1% could be heated to the temperatures from 41 °C to 99 °C at the driven voltages from 15 V to 40 V; indicating that the film heater exhibited uniform heating and rapid thermal response. Therefore; the PEDOT:PSS/Ag NW composite film is a promising candidate for the application of the transparent and large-scale film heaters.

| S-EPMC5503381 | biostudies-other

Inkjet-Printed Silver Nanowire Ink for Flexible Transparent Conductive Film Applications.

Project description:The development of flexible transparent conductive electrodes has been considered as a key issue in realizing flexible functional electronics. Inkjet printing provides a new opportunity for the manufacture of FFE due to simple process, cost-effective, environmental friendliness, and digital method to circuit pattern. However, obtaining high concentration of inkjet- printed silver nanowires (AgNWs) conductive ink is a great challenge because the high aspect ratio of AgNWs makes it easy to block the jetting nozzle. This study provides an inkjet printing AgNWs conductive ink with low viscosity and high concentration of AgNWs and good printing applicability, especially without nozzle blockage after printing for more than 4 h. We discussed the effects of the components of the ink on surface tension, viscosity, contact angle as well as droplet spreading behavior. Under the optimized process and formulation of ink, flexible transparent conductive electrode with a sheet resistance of 32 Ω·sq-1-291 nm·sq-1 and a transmittancy at 550 nm of 72.5-86.3% is achieved. We investigated the relationship between the printing layer and the sheet resistance and the stability of the sheet resistance under a bending test as well as the infrared thermal response of the AgNWs-based flexible transparent conductive electrode. We successfully printed the coupling electrodes and demonstrated the excellent potential of inkjet-printed AgNWs-based flexible transparent conductive electrode for developing flexible functional electronics.

| S-EPMC8912571 | biostudies-literature

Silver nanowires decorated with silver nanoparticles for low-haze flexible transparent conductive films.

Project description:Silver nanowires have attracted much attention for use in flexible transparent conductive films (TCFs) due to their low sheet resistance and flexibility. However, the haze was too high for replacing indium-tin-oxide in high-quality display devices. Herein, we report flexible TCFs, which were prepared using a scalable bar-coating method, with a low sheet resistance (24.1 ?/sq at 96.4% transmittance) and a haze (1.04%) that is comparable to that of indium-tin-oxide TCFs. To decrease the haze and maintain a low sheet resistance, small diameter silver nanowires (~20 nm) were functionalized with low-temperature surface-sintering silver nanoparticles (~5 nm) using bifunctional cysteamine. The silver nanowire-nanoparticle ink stability was excellent. The sheet resistance of the TCFs was decreased by 29.5% (from 34.2 to 24.1 ?/sq) due to the functionalization at a low curing temperature of 85?°C. The TCFs were highly flexible and maintained their stability for more than 2 months and 10,000 bending cycles after coating with a protective layer.

| S-EPMC4648094 | biostudies-literature

Sandwich-Structured Silver Nanowire Transparent Conductive Films with 3H Hardness and Robust Flexibility for Potential Applications in Curved Touch Screens.

Project description:A sandwich-structured bottom hard-coat/silver nanowire/top hard-coat (BHC/AgNW/THC) transparent conductive film (TCF) has been prepared by embedding the functional AgNW layer between two HC layers. The BHC/AgNW/THC TCFs show high scratch resistance with a hardness of 3H due to the enhanced adhesion to the substrate. In addition, the BHC/AgNW/THC TCFs exhibit a transmittance of 90.6% and a haze of 1% at 550 nm under a sheet resistance of 72 Ω/sq. Furthermore, highly enhanced long-term stability has been guaranteed by the HC layers due to their excellent gas barrier property. The amazing fact is that hard coating has little effect on the flexibility of AgNW films especially under extreme bending conditions and negligible resistance change could be observed after bending over thousands of times. Consequently, the greatly improved performance of BHC/AgNW/THC TCFs provided by employing hard coating layers paves the way for real-world applications of flexible AgNWs in vast areas that rigid indium tin oxide is not suitable.

| S-EPMC6523603 | biostudies-literature

Optoelectronic and Electrothermal Properties of Transparent Conductive Silver Nanowires Films.

Project description:Silver nanowires (AgNWs) show promise for fabricating flexible transparent conductors owing to their excellent conductivity, high transparency, and good mechanical properties. Here, we present the fabrication of transparent films composed of AgNWs with diameters of 20-30 nm and lengths of 25-30 μm on polyethylene terephthalate substrates and glass slides substrates using the Meyer rod method. We systematically investigated the films' optoelectronic and electrothermal properties. The morphology remained intact when heated at 25-150 °C and the AgNWs film showed high conductivity (17.6-14.3 Ω∙sq-1), excellent transmittance (93.9-91.8%) and low surface roughness values (11.2-14.7 nm). When used as a heater, the transparent AgNW conductive film showed rapid heating at low input voltages owing to a uniform heat distribution across the whole substrate surface. Additionally, the conductivity of the film decreased with increasing bending cycle numbers; however, the film still exhibited a good conductivity and heating performances after repeated bending.

| S-EPMC6631837 | biostudies-other

Inkjet Printing of Flexible Transparent Conductive Films with Silver Nanowires Ink.

Project description:The inkjet printing process is a promising electronic printing technique for large-scale, printed, flexible and stretchable electronics because of features such as its high manufacturing speed, environmental friendliness, simple process, low cost, accurate positioning, and so on. As the base material of printed conductive patterns, conductive ink is the foundation of the development of printed electronics technology, and directly affects the performance and the quality of electronic products. In this paper, conductive ink with silver nanowires (AgNWs) was prepared, with AgNWs of lengths of 2-5 µm and diameters of 20 nm or so, isopropyl alcohol and ethylene glycol as the mixed solvents, and modified polysilane as the wetting agent. We discussed the relationship between the formula of the AgNWs ink and the surface tension, viscosity, contact angle between ink droplet and poly(ethylene) terephthalate (PET) surface, as well as the film-forming properties of the ink. Further, we analyzed the effects of the number of printed layers and the ink concentration of the AgNWs on the microstructures, photoelectric properties and accuracy of the printed patterns, as well as the change in the sheet resistance of the film during different bending cycles. The experimental results show that flexible transparent conductive patterns with a light transmittance of 550 nm of 83.1-88.4% and a sheet resistance of 34.0 Ω∙sq-1-78.3 nm∙sq-1 can be obtained by using AgNWs ink of 0.38 mg∙mL-1 to 0.57 mg∙mL-1, a poly (ethylene terephthalate) (PET) substrate temperature of 40 °C, a nozzle temperature of 35 °C, and heat treated at 60 °C for 10 min. These performances indicate the excellent potential of the inkjet printing of AgNWs networks for developing flexible transparent conductive film.

| S-EPMC8232118 | biostudies-literature

Novel Insights into Inkjet Printed Silver Nanowires Flexible Transparent Conductive Films.

Project description:Silver nanowire (AgNWs) inks for inkjet printing were prepared and the effects of the solvent system, wetting agent, AgNWs suspension on the viscosity, surface tension, contact angle between ink droplet and poly(ethylene) terephthalate (PET) surface, and pH value of AgNWs ink were discussed. Further, AgNWs flexible transparent conductive films were fabricated by using inkjet printing process on the PET substrate, and the effects of the number printing layer, heat treatment temperature, drop frequency, and number of nozzle on the microstructures and photoelectric properties of AgNWs films were investigated in detail. The experimental results demonstrated that the 14-layer AgNWs printed film heated at 60 °C and 70 °C had an average sheet resistance of 13 Ω∙sq-1 and 23 Ω∙sq-1 and average transparency of 81.9% and 83.1%, respectively, and displayed good photoelectric performance when the inkjet printing parameters were set to the voltage of 20 V, number of nozzles of 16, drop frequency of 7000 Hz, droplet spacing of 15 μm, PET substrate temperatures of 40 °C and nozzles of 35 °C during printing, and heat treatment at 60 °C for 20 min. The accumulation and overflow of AgNWs at the edges of the linear pattern were observed, which resulted in a decrease in printing accuracy. We successfully printed the heart-shaped pattern and then demonstrated that it could work well. This showed that the well-defined pattern with good photoelectric properties can be obtained by using an inkjet printing process with silver nanowires ink as inkjet material.

| S-EPMC8307527 | biostudies-literature

Silver Nanowire Transparent Conductive Electrodes for High-Efficiency III-Nitride Light-Emitting Diodes.

Project description:Silver nanowires (AgNWs) have been successfully demonstrated to function as next-generation transparent conductive electrodes (TCEs) in organic semiconductor devices owing to their figures of merit, including high optical transmittance, low sheet resistance, flexibility, and low-cost processing. In this article, high-quality, solution-processed AgNWs with an excellent optical transmittance of 96.5% at 450 nm and a low sheet resistance of 11.7 Ω/sq were demonstrated as TCEs in inorganic III-nitride LEDs. The transmission line model applied to the AgNW contact to p-GaN showed that near ohmic contact with a specific contact resistance of ~10(-3) Ωcm(2) was obtained. The contact resistance had a strong bias-voltage (or current-density) dependence: namely, field-enhanced ohmic contact. LEDs fabricated with AgNW electrodes exhibited a 56% reduction in series resistance, 56.5% brighter output power, a 67.5% reduction in efficiency droop, and a approximately 30% longer current spreading length compared to LEDs fabricated with reference TCEs. In addition to the cost reduction, the observed improvements in device performance suggest that the AgNWs are promising for application as next-generation TCEs, to realise brighter, larger-area, cost-competitive inorganic III-nitride light emitters.

| S-EPMC4558582 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data