Stable and Durable Conductive Superhydrophobic Coatings Prepared by Double-Layer Spray Coating Method.

ABSTRACT: Herein, a low cost, durable, and stable conductive superhydrophobic composite coating (CSC coating) was fabricated on a Q345 steel surface by simple double-layer spray coating. The water contact angle (WCA) of the CSC coating was 160° and the sliding angle (SA) was 3°. In addition to its excellent conductivity (3.10 × 10³ Ω), the fabricated composite coating had good durability and wear resistance. After 10 sand-washing cycles, the CSC coating surface still exhibited stable superhydrophobicity (149° WCA, 9.5° SA). At 200 g pressure, the surface of the optimized CSC coating still maintained fine superhydrophobicity (150° WCA, 9.2° SA) and conductivity (1.86 × 10⁴ Ω) after 10 abrasion cycles. In addition, it also exhibited fine adhesion (0.307 MPa) between the composite coating and the substrate. This functional superhydrophobic surface can be applied in specialty fields with harsh conditions such as coal mining and petrochemical activities. This new coating may also expand the application fields of superhydrophobic surfaces and have broad practical application prospects.

SUBMITTER: Liu X

PROVIDER: S-EPMC8228788 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Superhydrophobic Ceramic Coatings by Solution Precursor Plasma Spray.

Project description:This work presents a novel coating technique to manufacture ceramic superhydrophobic coatings rapidly and economically. A rare earth oxide (REO) was selected as the coating material due to its hydrophobic nature, chemical inertness, high temperature stability, and good mechanical properties, and deposited on stainless steel substrates by solution precursor plasma spray (SPPS). The effects of various spraying conditions including standoff distance, torch power, number of torch passes, types of solvent and plasma velocity were investigated. The as-sprayed coating demonstrated a hierarchically structured surface topography, which closely resembles superhydrophobic surfaces found in nature. The water contact angle on the SPPS superhydrophobic coating was up to 65% higher than on smooth REO surfaces.

| S-EPMC4835754 | biostudies-literature

Mechanically durable, superoleophobic coatings prepared by layer-by-layer technique for anti-smudge and oil-water separation.

Project description:Superoleophobic surfaces are of interest for anti-fouling, self-cleaning, anti-smudge, low-drag, anti-fog, and oil-water separation applications. Current bioinspired surfaces are of limited use due to a lack of mechanical durability. A so-called layer-by-layer approach, involving charged species with electrostatic interactions between layers, can provide the flexibility needed to improve adhesion to the substrate while providing a low surface tension coating at the air interface. In this work, a polyelectrolyte binder, SiO2 nanoparticles, and a fluorosurfactant are spray deposited separately to create a durable, superoleophobic coating. Polydiallyldimethylammonium chloride (PDDA) polyelectrolyte was complexed with a fluorosurfactant layer (FL), which provides oil repellency while being hydrophilic. This oleophobic/superhydrophilic behavior was enhanced through the use of roughening with SiO2 particles resulting in a superoleophobic coating with hexadecane contact angles exceeding 155° and tilt angles of less than 4°. The coating is also superhydrophilic, which is desirable for oil-water separation applications. The durability of these coatings was examined through the use of micro- and macrowear experiments. These coatings currently display characteristics of transparency. Fabrication of these coatings via the layer-by-layer technique results in superoleophobic surfaces displaying improved durability compared to existing work where either the durability or the oil-repellency is compromised.

| S-EPMC4346800 | biostudies-other

Fabrication of Water Jet Resistant and Thermally Stable Superhydrophobic Surfaces by Spray Coating of Candle Soot Dispersion.

Project description:A facile synthesis method for highly stable carbon nanoparticle (CNP) dispersion in acetone by incomplete combustion of paraffin candle flame is presented. The synthesized CNP dispersion is the mixture of graphitic and amorphous carbon nanoparticles of the size range of 20-50 nm and manifested the mesoporosity with an average pore size of 7 nm and a BET surface area of 366 m2g-1. As an application of this material, the carbon nanoparticle dispersion was spray coated (spray-based coating) on a glass surface to fabricate superhydrophobic (water contact angle > 150° and sliding angle < 10 °) surfaces. The spray coated surfaces were found to exhibit much improved water jet resistance and thermal stability up to 400 °C compared to the surfaces fabricated from direct candle flame soot deposition (candle-based coating). This study proved that water jet resistant and thermally stable superhydrophobic surfaces can be easily fabricated by simple spray coating of CNP dispersion gathered from incomplete combustion of paraffin candle flame and this technique can be used for different applications with the potential for the large scale fabrication.

| S-EPMC5548922 | biostudies-literature

Durable Anti-Icing Coatings Based on Self-Sustainable Lubricating Layer.

Project description:A versatile, convenient, and cost-effective method that can be used for grafting anti-icing materials onto different surfaces is highly desirable. Based on mussel-inspired chemistry, the anti-icing coating with extremely low ice adhesion is enabled by constructing a self-sustainable lubricating layer, achieved via modifying solid substrates with a highly hydrophilic conjugate of poly(acrylic acid)-dopamine. Both unfreezable and freezable water remain liquidlike at subzero conditions and synergistically fulfill the role of lubrication for reducing the ice adhesion. The anti-icing coatings show excellent stability in harsh environments and durability after the cross-linking. More importantly, this coating can be applied to various substrates and is of great promise for practical applications.

| S-EPMC6640938 | biostudies-literature

A Cost-Effective Method for Preparing Robust and Conductive Superhydrophobic Coatings Based on Asphalt.

Project description:The wide application of superhydrophobic materials is mainly hindered by the poor mechanical robustness and complicated preparation method. To overcome these problems, we tried to make a combination of hierarchical and self-similar structure by the means of a simple spraying method. By adding nanofiller (carbon nanotube) and microfiller (graphite powder and expanded graphite), the hierarchical structure was constructed. By further doping the fillers in the commercial asphalt uniformly, the self-similar structure was prepared. Based on the aforementioned work, the as-prepared sample could withstand the sandpaper abrasion for 12.00 m under 4.90 kPa. Moreover, this superhydrophobic coating demonstrated good conductivity, superior self-cleaning property, and excellent corrosion resistance. The integration of conductivity with the superhydrophobicity might open new avenues for ground grid applications.

| S-EPMC7775183 | biostudies-literature

The effect of composition and thermodynamics on the surface morphology of durable superhydrophobic polymer coatings.

Project description:Durable superhydrophobic coatings were synthesized using a system of silica nanoparticles (NPs) to provide nanoscale roughness, fluorosilane to give hydrophobic chemistry, and three different polymer binders: urethane acrylate, ethyl 2-cyanoacrylate, and epoxy. Coatings composed of different binders incorporating NPs in various concentrations exhibited different superhydrophobic attributes when applied on polycarbonate (PC) and glass substrates and as a function of coating composition. It was found that the substrate surface characteristics and wettability affected the superhydrophobic characteristics of the coatings. Interfacial tension and spreading coefficient parameters (thermodynamics) of the coating components were used to predict the localization of the NPs for the different binders' concentrations. The thermodynamic analysis of the NPs localization was in good agreement with the experimental observations. On the basis of the thermodynamic analysis and the experimental scanning electron microscopy, X-ray photoelectron spectroscopy, profilometry, and atomic force microscopy results, it was concluded that localization of the NPs on the surface was critical to provide the necessary roughness and resulting superhydrophobicity. The durability evaluated by tape testing of the epoxy formulations was the best on both glass and PC. Several coating compositions retained their superhydrophobicity after the tape test. In summary, it was concluded that thermodynamic analysis is a powerful tool to predict the roughness of the coating due to the location of NPs on the surface, and hence can be used in the design of superhydrophobic coatings.

| S-EPMC5317333 | biostudies-literature

An Environmentally Friendly Approach for the Fabrication of Conductive Superhydrophobic Coatings with Sandwich-Like Structures.

Project description:A large amount of research has been devoted to developing novel superhydrophobic coatings. However, it is still a great challenge to pursuean environmentally friendly method that leads to superhydrophobic coatings. Herein, we demonstrate for the first time, an environmentally friendly method for the preparation of conductive superhydrophobic coatings with sandwich-like structures by using aminoethylaminopropyl polydimethylsiloxane modified waterborne polyurethane (SiWPU) and N-octadecylamine functionalized multi-wall carbon nanotubes. These environmentally friendly coatings with the sheet resistance of 1.1 ± 0.1 kΩ/sq exhibit a high apparent contact angle of 158.1° ± 2° and a low sliding angle below 1°. The influence of the surface texture before and after heat treatment on the wetting properties is discussed. In addition, the coatings can be electrically heated by 3~113 °C with a voltage of 12~72 V, and thus, can be used for deicing. Furthermore, the resulting coatings demonstrate good performance of wear resistance and ultraviolet resistance, which will have broad application potential in harsh environments.

| S-EPMC6415204 | biostudies-literature

Robust Superhydrophobic Cotton Fibers Prepared by Simple Dip-Coating Approach Using Chemical and Plasma-Etching Pretreatments.

Project description:The preparation of superhydrophobic textiles with high mechanical and chemical durability is challenging. Here, facile and fluorine-free methods, using alkali and plasma-etching treatments, followed by the addition of silica nanoparticles and tetraethyl orthosilicate (TEOS), were used to prepare superhydrophobic cotton surfaces. With different input variables and etching techniques, superhydrophobic cotton fabrics with high chemical and mechanical durability were successfully prepared, with contact angles up to 173°. A control of the surface architecture at the nanoscale in combination with a homogeneous repellent layer of TEOS in the cotton surface was achieved. The repellent properties of the as-prepared cotton remain stable under accelerated laundering and abrasion test conditions. The etching pretreatment by alkali or plasma plays a key role in obtaining superhydrophobic cotton surfaces.

| S-EPMC6648567 | biostudies-literature

Near-Instantaneously Self-Healing Coating toward Stable and Durable Electromagnetic Interference Shielding.

Project description:Durable electromagnetic interference (EMI) shielding is highly desired, as electromagnetic pollution is a great concern for electronics' stable performance and human health. Although a superhydrophobic surface can extend the service lifespan of EMI shielding materials, degradation of its protection capability and insufficient self-healing are troublesome issues due to unavoidable physical/chemical damages under long-term application conditions. Here, we report, for the first time, an instantaneously self-healing approach via microwave heating to achieve durable shielding performance. First, a hydrophobic 1H,1H,2H,2H-perfluorooctyltriethoxysilane (POTS) layer was coated on a polypyrrole (PPy)-modified fabric (PPy@POTS), enabling protection against the invasion of water, salt solution, and corrosive acidic and basic solutions. Moreover, after being damaged, the POTS layer can, for the first time, be instantaneously self-healed via microwave heating for a very short time, i.e., 4 s, benefiting from the intense thermal energy generated by PPy under electromagnetic wave radiation. This self-healing ability is also repeatable even after intentionally severe plasma etching, which highlights the great potential to achieve robust and durable EMI shielding applications. Significantly, this approach can be extended to other EMI shielding materials where heat is a triggering stimulus for healing thin protection layers. We envision that this work could provide insights into fabricating EMI shielding materials with durable performance for portable and wearable devices, as well as for human health care.

| S-EPMC8426454 | biostudies-literature

Robust, Self-Healing Superhydrophobic Fabrics Prepared by One-Step Coating of PDMS and Octadecylamine.

Project description:A robust, self-healing superhydrophobic poly(ethylene terephthalate) (PET) fabric was fabricated by a convenient solution-dipping method using an easily available material system consisting of polydimethylsiloxane and octadecylamine (ODA). The surface roughness was formed by self-roughening of ODA coating on PET fibers without any lithography steps or adding any nanomaterials. The fabric coating was durable to withstand 120 cycles of laundry and 5000 cycles of abrasion without apparently changing the superhydrophobicity. More interestingly, the fabric can restore its super liquid-repellent property by 72?h at room temperature even after 20000 cycles of abrasion. Meanwhile, after being damaged chemically, the fabric can restore its superhydrophobicity automatically in 12?h at room temperature or by a short-time heating treatment. We envision that this simple but effective coating system may lead to the development of robust protective clothing for various applications.

| S-EPMC4893697 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data