Covalent Triazine Frameworks Based on the First Pseudo-Octahedral Hexanitrile Monomer via Nitrile Trimerization: Synthesis, Porosity, and CO₂ Gas Sorption Properties.

ABSTRACT: Herein, we report the first synthesis of covalent triazine-based frameworks (CTFs) based on a hexanitrile monomer, namely the novel pseudo-octahedral hexanitrile 1,4-bis(tris(4'-cyano-phenyl)methyl)benzene 1 using both ionothermal reaction conditions with ZnCl₂ at 400 °C and the milder reaction conditions with the strong Brønsted acid trifluoromethanesulfonic acid (TFMS) at room temperature. Additionally, the hexanitrile was combined with different di-, tri-, and tetranitriles as a second linker based on recent work of mixed-linker CTFs, which showed enhanced carbon dioxide captures. The obtained framework structures were characterized via infrared (IR) spectroscopy, elemental analysis, scanning electron microscopy (SEM), and gas sorption measurements. Nitrogen adsorption measurements were performed at 77 K to determine the Brunauer-Emmett-Teller (BET) surface areas range from 493 m²/g to 1728 m²/g (p/p₀ = 0.01-0.05). As expected, the framework CTF-hex6 synthesized from 1 with ZnCl₂ possesses the highest surface area for nitrogen adsorption. On the other hand, the mixed framework structure CTF-hex4 formed from the hexanitrile 1 and 1,3,5 tricyanobenzene (4) shows the highest uptake of carbon dioxide and methane of 76.4 cm³/g and 26.6 cm³/g, respectively, at 273 K.

SUBMITTER: Wessely ID

PROVIDER: S-EPMC8230500 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Rigid Nanoporous Urea-Based Covalent Triazine Frameworks for C2/C1 and CO2/CH4 Gas Separation.

Project description:C2/C1 hydrocarbon separation is an important industrial process that relies on energy-intensive cryogenic distillation methods. The use of porous adsorbents to selectively separate these gases is a viable alternative. Highly stable covalent triazine frameworks (urea-CTFs) have been synthesized using 1,3-bis(4-cyanophenyl)urea. Urea-CTFs exhibited gas uptakes of C2H2 (3.86 mmol/g) and C2H4 (2.92 mmol/g) at 273 K and 1 bar and is selective over CH4. Breakthrough simulations show the potential of urea-CTFs for C2/C1 separation.

| S-EPMC8235060 | biostudies-literature

Influenza A virus hemagglutinin trimerization completes monomer folding and antigenicity.

Project description:Influenza A virus (IAV) remains an important human pathogen largely because of antigenic drift, the rapid emergence of antibody escape mutants that precludes durable vaccination. The most potent neutralizing antibodies interact with cognate epitopes in the globular "head" domain of hemagglutinin (HA), a homotrimeric glycoprotein. The H1 HA possesses five distinct regions defined by a large number of mouse monoclonal antibodies (MAbs), i.e., Ca1, Ca2, Cb, Sa, and Sb. Ca1-Ca2 sites require HA trimerization to attain full antigenicity, consistent with their locations on opposite sides of the trimer interface. Here, we show that full antigenicity of Cb and Sa sites also requires HA trimerization, as revealed by immunofluorescence microscopy of IAV-infected cells and biochemically by pulse-chase radiolabeling experiments. Surprisingly, epitope antigenicity acquired by HA trimerization persists following acid triggering of the globular domains dissociation and even after proteolytic release of monomeric heads from acid-treated HA. Thus, the requirement for HA trimerization by trimer-specific MAbs mapping to the Ca, Cb, and Sa sites is not dependent upon the bridging of adjacent monomers in the native HA trimer. Rather, complete antigenicity of HA (and, by inference, immunogenicity) requires a final folding step that accompanies its trimerization. Once this conformational change occurs, HA trimers themselves would not necessarily be required to induce a highly diverse neutralizing response to epitopes in the globular domain.

| S-EPMC3754138 | biostudies-literature

Advances in the Synthesis of Covalent Triazine Frameworks.

Project description:Covalent triazine frameworks (CTFs) are a class of organic polymer materials constructed by aromatic 1,3,5-triazine rings with planar π-conjugation properties. CTFs are highly stable and porous with N atoms in the frameworks, possessing semiconductive properties; thus they are widely used in gas adsorption and separation as well as catalysis. The properties of CTFs strongly depend on the type of monomers and the synthesis process. Synthesis methods including ionothermal polymerization, amino-aldehyde synthesis, trifluoromethanesulfonic acid catalyzed synthesis, and aldehyde-amidine condensation have been intensively studied in recent years. In this review, we discuss the recent advances and future developments of CTFs synthesis.

| S-EPMC9909813 | biostudies-literature

Tailoring topology and bio-interactions of triazine frameworks.

Project description:The construction of covalent organic frameworks with special geometery and optical properties is of high interest, due to their unique physicochemical and biological properties. In this work, we report on a new method for the construction of triazine frameworks with defined topologies using coordination chemistry. Ball milling and wet chemical reactions between cyanuric chloride and melamine were directed in spatial arrangements and opposite optical activity. Cobalt was used as a directing agent to drive reactions into special morphologies, optical properties and biological activity. The enantiorecognition ability of triazine frameworks that was manifested in their activities against bacteria, demonstrated a new way for the construction of materials with specific interactions at biointerfaces.

| S-EPMC11208503 | biostudies-literature

Covalent Triazine Frameworks via a Low-Temperature Polycondensation Approach.

Project description:Covalent triazine frameworks (CTFs) are normally synthesized by ionothermal methods. The harsh synthetic conditions and associated limited structural diversity do not benefit for further development and practical large-scale synthesis of CTFs. Herein we report a new strategy to construct CTFs (CTF-HUSTs) via a polycondensation approach, which allows the synthesis of CTFs under mild conditions from a wide array of building blocks. Interestingly, these CTFs display a layered structure. The CTFs synthesized were also readily scaled up to gram quantities. The CTFs are potential candidates for separations, photocatalysis and for energy storage applications. In particular, CTF-HUSTs are found to be promising photocatalysts for sacrificial photocatalytic hydrogen evolution with a maximum rate of 2647 μmol h-1 g-1 under visible light. We also applied a pyrolyzed form of CTF-HUST-4 as an anode material in a sodium-ion battery achieving an excellent discharge capacity of 467 mAh g-1 .

| S-EPMC5698698 | biostudies-literature

Coupling fullerene into porous aromatic frameworks for gas selective sorption.

Project description:A lot of investigations calculate that fullerene would be an excellent unit for porous adsorbents for gas sorption and separation. Although the conjugated structure and symmetrical shape of fullerene makes it an ideal building block, there is no facile strategy to achieve fullerene-based porous materials. Herein, we adopt a novel acid catalyzed coupling reaction to bind the fullerene molecules together in a one-step synthesis. After synthesizing the adducts as models, the atomic connectivity between the fullerene molecules is determined clearly. We then prepared a series of fullerene-based porous aromatic frameworks (PAFs). The targeted products adsorb H2 and CO2, and they exhibit some selectivity of CO2 over N2 and CH4. The good performance of the PAFs indicates that we could combine the gas binding ability of the building block and the porous nature of PAF materials together to give a better adsorbent.

| S-EPMC6008602 | biostudies-literature

Topology and porosity control of metal-organic frameworks through linker functionalization.

Project description:Tetratopic organic linkers have been extensively used in Zr-based metal-organic frameworks (MOFs) where diverse topologies have been observed. Achieving meticulous control over the topologies to tune the pore sizes and shapes of the resulting materials, however, remains a great challenge. Herein, by introducing substituents to the backbone of tetratopic linkers to affect the linker conformation, phase-pure Zr-MOFs with different topologies and porosity were successfully obtained under the same synthetic conditions. The conversion of CO2 to valuable cyclic carbonates is a promising route for the mitigation of the greenhouse gas. Owing to the presence of substrate accessible Lewis acidic Zr(iv) sites in the 8-connected Zr6 nodes, the Zr-MOFs in this study have been investigated as heterogenous acid catalysts for CO2 cycloaddition to styrene oxide. The MOFs exhibited drastically different catalytic activities depending on their distinct pore structures. Compared to previously reported MOF materials, a superior catalytic activity was observed with the mesoporous NU-1008, giving an almost 100% conversion under mild conditions.

| S-EPMC6349059 | biostudies-literature

Porosity and surface properites of SBA-15 with grafted PNIPAAM: a water sorption calorimetry study.

Project description:Mesoporous silica SBA-15 was modified in a three-step process to obtain a material with poly-N-isopropylacrylamide (PNIPAAM) grafted onto the inner pore surface. Water sorption calorimetry was implemented to characterize the materials obtained after each step regarding the porosity and surface properties. The modification process was carried out by (i) increasing the number of surface silanol groups, (ii) grafting 1-(trichlorosilyl)-2-(m-/p-(chloromethylphenyl) ethane, acting as an anchor for (iii) the polymerization of N-isopropylacrylamide. Water sorption isotherms and the enthalpy of hydration are presented. Pore size distributions were calculated on the basis of the water sorption isotherms by applying the BJH model. Complementary measurements with nitrogen sorption and small-angle X-ray diffraction are presented. The increase in the number of surface silanol groups occurs mainly in the intrawall pores, the anchor is mainly located in the intrawall pores, and the intrawall pore volume is absent after the surface grafting of PNIPAAM. Hence, PNIPAAM seals off the intrawall pores. Water sorption isotherms directly detect the presence of intrawall porosity. Pore size distributions can be calculated from the isotherms. Furthermore, the technique provides information regarding the hydration capability (i.e., wettability of different chemical surfaces) and thermodynamic information.

| S-EPMC3324985 | biostudies-literature

Influence of hydrothermal carbonization conditions on the porosity, functionality, and sorption properties of microalgae hydrochars.

Project description:Green microalgae is a possible feedstock for the production of biofuels, chemicals, food/feed, and medical products. Large-scale microalgae production requires large quantities of water and nutrients, directing the attention to wastewater as a cultivation medium. Wastewater-cultivated microalgae could via wet thermochemical conversion be valorised into products for e.g., water treatment. In this study, hydrothermal carbonization was used to process microalgae polycultures grown in municipal wastewater. The objective was to perform a systematic examination of how carbonization temperature, residence time, and initial pH affected solid yield, composition, and properties. Carbonization temperature, time and initial pH all had statistically significant effects on hydrochar properties, with temperature having the most pronounced effect; the surface area increased from 8.5 to 43.6 m2 g-1 as temperature was increased from 180 to 260 °C. However, hydrochars produced at low temperature and initially neutral pH generally had the highest capacity for methylene blue adsorption. DRIFTS analysis of the hydrochar revealed that the pH conditions changed the functional group composition, implying that adsorption was electrostatic interactions driven. This study concludes that un-activated hydrochars from wastewater grown microalgae produced at relatively low hydrothermal carbonization temperatures adsorb methylene blue, despite having low surface area.

| S-EPMC10219968 | biostudies-literature

Photocurable 3D-Printable Systems with Controlled Porosity towards CO2 Air Filtering Applications.

Project description:Porous organic polymers are versatile platforms, easily adaptable to a wide range of applications, from air filtering to energy devices. Their fabrication via vat photopolymerization enables them to control the geometry on a multiscale level, obtaining hierarchical porosity with enhanced surface-to-volume ratio. In this work, a photocurable ink based on 1,6 Hexanediol diacrylate and containing a high internal phase emulsion (HIPE) is presented, employing PLURONIC F-127 as a surfactant to generate stable micelles. Different parameters were studied to assess the effects on the morphology of the pores, the printability and the mechanical properties. The tests performed demonstrates that only water-in-oil emulsions were suitable for 3D printing. Afterwards, 3D complex porous objects were printed with a Digital Light Processing (DLP) system. Structures with large, interconnected, homogeneous porosity were fabricated with high printing precision (300 µm) and shape fidelity, due to the addition of a Radical Scavenger and a UV Absorber that improved the 3D printing process. The formulations were then used to build scaffolds with complex architecture to test its application as a filter for CO2 absorption and trapping from environmental air. This was obtained by surface decoration with NaOH nanoparticles. Depending on the surface coverage, tested specimens demonstrated long-lasting absorption efficiency.

| S-EPMC9740396 | biostudies-literature