In Vivo Animal Study of a Highly Viscous N-butyl Cyanoacrylate Medical Adhesive for Intravenous Embolization.

ABSTRACT: N-butyl cyanoacrylate (NBCA) is a liquid monomer that undergoes an exothermic polymerization reaction to form a solid upon initiation with hydroxyl anions. Recently, EGpresto, a highly viscous NBCA-based adhesive, has been developed for vascular-occlusion purposes. In this study, we investigated the heat of polymerization of EGpresto and compared the results with those of a low-viscosity NBCA glue. Results show that EGpresto exhibited a lower heat of polymerization (64 ± 7 °C vs. 34 ± 1 °C). This was due to its high viscosity, which resulted in a delayed polymerization time. To investigate the efficacy and safety of EGpresto for intravenous embolization, a 14 d in vivo animal test was conducted using three pigs. Five cc of EGpresto was injected into the epigastric vein of each animal. Complete postoperative vein occlusion was confirmed at 7 and 14 d by ultrasonographic visualization. After the animals were sacrificed, the operated and unoperated veins were exposed, and the injected adhesive was found without migration. During the histology, the injected adhesive was not found in the inner or outer vein walls, and the immune reactions seemed to be the only foreign-body reaction, showing that EGpresto is a non-toxic and safe intravascular embolic agent.

SUBMITTER: Seo JW

PROVIDER: S-EPMC8269526 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Background Aneurysmal rupture in the aortoiliac segment is a severe, life-threatening condition. Nowadays, in addition to surgical treatment, the implantation of a covered stent graft constitutes a feasible, minimally invasive treatment option. A novel approach is the add-on of transarterial aneurysm sac embolization with N-butyl-cyanoacrylate (NBCA). Here, we report our experience of performing this add-on embolization procedure after endovascular aneurysm repair for complex ruptured aneurysms of the aortoiliac segment. Material and Methods We describe six patients (mean age of 75.2 years; all male) with ruptured aneurysms in the visceral aortic and aortoiliac segment in whom a high-volume transarterial aneurysm sac embolization was performed as an add-on therapy to the implantation of an aortic prosthesis. The aim of this add-on intervention was to achieve the definite embolization of the aneurysmal rupture site and to ensure the best possible aneurysmal sealing. We report the feasibility, technical success, and considerations of using NBCA as well as clinical and follow-up imaging results, given their availability. Results Technical success was achieved in all cases. Clinical success was achieved in four cases. No periprocedural complications or reinterventions were reported. The mean full procedure time was 107.8 min. The mean radiation dose was 12,966.1 cGy/cm2. A mean amount of 10.7 mL of NBCA mixed with lipiodol in a 1:3 to 1:5 ratio was used for all patients. Available follow-up imaging up to 36 months after the procedure showed no aneurysm progression or endoleaks. In two patients, the NBCA cast had almost fully dissolved over the course of follow-up. Conclusions Our study underscores the notion that aneurysm sac embolization using high volumes of NBCA with ethiodized oil as an embolic agent is a feasible and add-on treatment option for optimizing the exclusion of the aneurysm from patients with ruptured aneurysms in the aortoiliac segment.

Project description:Tendon disorders are common medical conditions that could lead to significant disability, pain, healthcare costs, and a loss of productivity. Traditional approaches require long periods of treatment, and they largely fail due to the tissues weakening and the postoperative alterations of the normal joint mechanics. To overcome these limitations, innovative strategies for the treatment of these injuries need to be explored. The aim of the present work was the design of nano-fibrous scaffolds based on poly(butyl cyanoacrylate) (PBCA), a well-known biodegradable and biocompatible synthetic polymer, doped with copper oxide nanoparticles and caseinphosphopeptides (CPP), able to mimic the hierarchical structure of the tendon and to improve the tissue healing potential. These were developed as implants to be sutured to reconstruct the tendons and the ligaments during surgery. PBCA was synthetized, and then electrospun to produce aligned nanofibers. The obtained scaffolds were characterized for their structure and physico-chemical and mechanical properties, highlighting that CuO and CPP loading, and the aligned conformation determined an increase in the scaffold mechanical performance. Furthermore, the scaffolds loaded with CuO showed antioxidant and anti-inflammatory properties. Moreover, human tenocytes adhesion and proliferation to the scaffolds were assessed in vitro. Finally, the antibacterial activity of the scaffolds was evaluated using Escherichia coli and Staphylococcus aureus as representative of Gram-negative and Gram-positive bacteria, respectively, demonstrating that the CuO-doped scaffolds possessed a significant antimicrobial effect against E. coli. In conclusion, scaffolds based on PBCA and doped with CuO and CPP deserve particular attention as enhancers of the tendon tissue regeneration and able to avoid bacterial adhesion. Further investigation on the scaffold efficacy in vivo will assess their capability for enhancing the tendon ECM restoration in view of accelerating their translation to the clinic.

Dataset Information

In Vivo Animal Study of a Highly Viscous N-butyl Cyanoacrylate Medical Adhesive for Intravenous Embolization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets