Controlling Calcium Carbonate Particle Morphology, Size, and Molecular Order Using Silicate.

ABSTRACT: Calcium carbonate (CaCO₃) is one of the most abundant substances on earth and has a large array of industrial applications. Considerable research has been conducted in an effort to synthesize calcium carbonate microparticles with controllable and specific morphologies and sizes. CaCO₃ produced by a precipitation reaction of calcium nitrate and sodium carbonate solution was found to have high polymorphism and batch to batch variability. In this study, we investigated the polymorphism of the precipitated material and analyzed the chemical composition, particle morphology, and crystalline state revealing that the presence of silicon atoms in the precipitant is a key factor effecting particle shape and crystal state. An elemental analysis of single particles within a polymorphic sample, using energy-dispersive X-ray spectroscopy (EDS) conjugated microscopy, showed that only spherical particles, but not irregular shaped one, contained traces of silicon atoms. In agreement, silicon-containing additives lead to homogenous, amorphous nanosphere particles, verified by X-ray powder diffraction (XRD). Our findings provide important insights into the mechanism of calcium carbonate synthesis, as well as introducing a method to control the precipitants at the micro-scale for many diverse applications.

SUBMITTER: Minkowicz L

PROVIDER: S-EPMC8269534 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Post-tilleyite, a dense calcium silicate-carbonate phase.

Project description:Calcium carbonate is a relevant constituent of the Earth's crust that is transferred into the deep Earth through the subduction process. Its chemical interaction with calcium-rich silicates at high temperatures give rise to the formation of mixed silicate-carbonate minerals, but the structural behavior of these phases under compression is not known. Here we report the existence of a dense polymorph of Ca5(Si2O7)(CO3)2 tilleyite above 8 GPa. We have structurally characterized the two phases at high pressures and temperatures, determined their equations of state and analyzed the evolution of the polyhedral units under compression. This has been possible thanks to the agreement between our powder and single-crystal XRD experiments, Raman spectroscopy measurements and ab-initio simulations. The presence of multiple cation sites, with variable volume and coordination number (6-9) and different polyhedral compressibilities, together with the observation of significant amounts of alumina in compositions of some natural tilleyite assemblages, suggests that post-tilleyite structure has the potential to accommodate cations with different sizes and valencies.

| S-EPMC6536543 | biostudies-literature

Controlling the calcium carbonate microstructure of engineered living building materials.

Project description:The fabrication of responsive soft materials that enable the controlled release of microbial induced calcium carbonate (CaCO3) precipitation (MICP) would be highly desirable for the creation of living materials that can be used, for example, as self-healing construction materials. To obtain a tight control over the mechanical properties of these materials, needed for civil engineering applications, the amount, location, and structure of the forming minerals must be precisely tuned; this requires good control over the dynamic functionality of bacteria. Despite recent advances in the self-healing of concrete cracks and the understanding of the role of synthesis conditions on the CaCO3 polymorphic regulation, the degree of control over the CaCO3 remains insufficient to meet these requirements. We demonstrate that the amount and location of CaCO3 produced within a matrix, can be controlled through the concentration and location of bacteria; these parameters can be precisely tuned if bacteria are encapsulated, as we demonstrate with the soil-dwelling bacterium Sporosarcina pasteurii that is deposited within biocompatible alginate and carboxymethyl cellulose (CMC) hydrogels. Using a competitive ligand exchange mechanism that relies on the presence of yeast extract, we control the timing of the release of calcium ions that crosslink the alginate or CMC without compromising bacterial viability. With this novel use of hydrogel encapsulation of bacteria for on-demand release of MICP, we achieve control over the amount and structure of CaCO3-based composites and demonstrate that S. pasteurii can be stored for up to 3 months at an accessible storage temperature of 4 °C, which are two important factors that currently limit the applicability of MICP for the reinforcement of construction materials. These composites thus have the potential to sense, respond, and heal without the need for external intervention.

| S-EPMC8577622 | biostudies-literature

Higher-generation type III-B rotaxane dendrimers with controlling particle size in three-dimensional molecular switching.

Project description:Type III-B rotaxane dendrimers (T3B-RDs) are hyperbranched macromolecules with mechanical bonds on every branching unit. Here we demonstrate the design, synthesis, and characterization of first to third (G1-G3), and up to the fourth (G4) generation (MW?>?22,000?Da) of pure organic T3B-RDs and dendrons through the copper-catalyzed alkyne-azide cycloaddition (CuAAC) reaction. By utilizing multiple molecular shuttling of the mechanical bonds within the sphere-like macromolecule, a collective three-dimensional contract-extend molecular motion is demonstrated by diffusion ordered spectroscopy (DOSY) and atomic force microscopy (AFM). The discrete T3B-RDs are further observed and characterized by AFM, dynamic light scattering (DLS), and mass spectrometry (MS). The binding of chlorambucil and pH-triggered switching of the T3B-RDs are also characterized by 1H-NMR spectroscopy.

| S-EPMC5799186 | biostudies-literature

Particle size fractions

Project description:Prokaryotic communities of soil particle size fractions and their responsiveness to long-term fertilisation

| PRJEB11366 | ENA

Influence of Fraction Particle Size of Pure Straw and Blends of Straw with Calcium Carbonate or Cassava Starch on Pelletising Process and Pellet.

Project description:The aim of this study was to investigate the pressure agglomeration process of wheat straw (WS) and the blends of WS with calcium carbonate (CC) or cassava straw (CS) with a ratio of 6% wt./wt. from seven separate fractions with sizes in the range of 0.21-2.81 mm. The agglomeration was performed at a moisture of 30% wb and a material temperature of 78 °C, with a dose of 0.1 g, in a die of diameter 8 mm and height 80 mm. The effects of the process were evaluated based on the compaction parameters and the pellets' density, tensile strength, and water absorption. The incorporation of additives into the WS improved the pellet process and quality. Refined results were achieved after adding CC, as compared to those achieved after adding CS, and the preferred particle size was in the range of 1.00-1.94 mm. This was because, under the given conditions, the back pressure in the die chamber significantly increased, allowing the achievement of a single pellet density of 800 kg·m-3. The pellets were resistant to compressive loads and cracked only at tensile strength of 6 MPa and a specific compression work of 6.5 mJ·mm-2. The addition of CC to the WS improved the strength of the adhesive and the cohesive bonds between the particles. The water absorption for the uncrushed pellets was considerably less than that for crushed pellets, which results in the safer storage of uncrushed pellets and excellent moisture absorption of crushed pellets. The addition of CC to the WS offers benefits in the form of pellet strength with a high water absorption capability. Notably, a study of crushed pellet litter under broiler rearing conditions and an analysis of the operational costs of using WS additives are required for implementing this study.

| S-EPMC7602947 | biostudies-literature

Interparticle and Brownian forces controlling particle aggregation and rheology of silicate melts containing platinum-group element particles.

Project description:We study the rheology of silicate melts containing platinum-group element (PGE) particles. They exhibit a shear-thinning behaviour, an intense aggregation tendency, and an anomalously high apparent viscosity in the low shear rate limit, even at very low particle volume fraction. Using a compilation of published experimental data, we analyse these effects in three steps. Firstly, we observe that the viscosities of these suspensions are much higher than those of natural silicate crystal-bearing melts for low shear rate regimes. Secondly, we demonstrate that the viscosities at low shear rate limit cannot be estimated by classical rheological models but rather may be understood as the result of particle aggregation, trapping dead fluid, and thereby increasing the effective particle volume fraction. Finally, we scale the critical shear rates for shear-thinning using a Peclet number analysis-invoking a competition between random thermal particle motion and hydrodynamic shearing motion-and, using an empirical extension, we additionally account for the particle-particle interaction energetics. We propose a framework in which the rheology of this family of particle-bearing melts can be predicted, and demonstrate that at low Peclet numbers, PGE-bearing particle aggregation is driven by interparticle forces and Brownian motion.

| S-EPMC9163177 | biostudies-literature

Morphology Change of Calcium Carbonate in the Presence of Two-Dimensional DNA Lattices.

Project description:Two-dimensional DNA lattices are grown under conditions that also are suitable for the magnesium-free growth of three-dimensional calcium carbonate crystals. These lattices are used to template morphology changes in calcium carbonate. The effects of DNA lattices, sub-assemblies, duplexes, single strands, dinucleotides, and mononucleotides on calcium carbonate morphology are studied. A "rotated" morphology of calcite is found to predominate when a critical concentration of any polynucleotide is reached in the templating solution.

| S-EPMC3915517 | biostudies-literature

Nanoindentation Study of Calcium-Silicate-Hydrate Gel via Molecular Dynamics Simulations.

Project description:The mechanical properties of calcium-silicate-hydrate (C-S-H) gels in cementitious materials are mainly realized by nanoindentation experiments. There is limited research on the dynamic response of the molecular structure of C-S-H under nanoindentation conditions. This study simulated the nanoindentation on the C-S-H gel samples by the molecular dynamics method considering the essential factors of modeling and loading process. The results demonstrate that the averaged elastic moduli we obtained had slight differences from those by experiments. In contrast to the experimental results, the gels showed bi-modulus and transverse isotropic with the material principal direction perpendicular to the C-S-H layers. The modulus in a direction increased with the loading speed, which indicates that C-S-H behaves viscous due to the water motion in the sample and the propagation of stress wave. The saturation of water influenced the moduli differently because more water in C-S-H will reduce the polymerization of silicon chains and then weaken the local stiffness. The conclusions provide a deeper understanding of the mechanism on the unique mechanical response of C-S-H gels.

| S-EPMC10536101 | biostudies-literature

Nanoscale analysis of the morphology and surface stability of calcium carbonate polymorphs.

Project description:Under earth surface conditions, in ocean and natural water, calcium carbonate is ubiquitous, forming anhydrous and hydrous minerals. These hydrous phases are of considerable interest for their role as precursors to stable carbonate minerals. Atomistic simulation techniques have been employed here to perform a comprehensive and quantitative study of the structural and energetic stability of dry and hydrous surfaces of calcium carbonate polymorphs using two recently developed forcefields. Results show that the dry forms are prone to ductility; while hydrous phases are found to be brittle. The (001) surface of monohydrocalcite appears to be the most stable (0.99 J/m(2)) whereas for the ikaite phase, the (001) surface is the most stable. The corresponding value is 0.2 J/m(2), i.e. even lower than the surface energy of the Beautiful computed morphology pictures are obtained with Xiao's model and are very similar to the observed SEM images.

| S-EPMC3613796 | biostudies-other

Luminescence reveals variations in local structural order of calcium carbonate polymorphs formed by different mechanisms.

Project description:In nature, calcium carbonate (CaCO3) in the form of calcite and aragonite nucleates through different pathways including geogenic and biogenic processes. It may also occur as pyrogenic lime plaster and laboratory-precipitated crystals. All of these formation processes are conducive to different degrees of local structural order in CaCO3 crystals, with the pyrogenic and precipitated forms being the least ordered. These variations affect the manner in which crystals interact with electromagnetic radiation, and thus formation processes may be tracked using methods such as X-ray diffraction and infrared spectroscopy. Here we show that defects in the crystal structure of CaCO3 may be detected by looking at the luminescence of crystals. Using cathodoluminescence by scanning electron microscopy (SEM-CL) and laser-induced fluorescence (LIF), it is possible to discern different polymorphs and their mechanism of formation. We were thus able to determine that pyrogenic calcite and aragonite exhibit blue luminescence due to the incorporation of distortions in the crystal lattice caused by heat and rapid precipitation, in agreement with infrared spectroscopy assessments of local structural order. These results provide the first detailed reference database of SEM-CL and LIF spectra of CaCO3 standards, and find application in the characterization of optical, archaeological and construction materials.

| S-EPMC6838102 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data