Up-Scalable Fabrication of SnO₂ with Multifunctional Interface for High Performance Perovskite Solar Modules.

ABSTRACT: Tin dioxide (SnO₂) has been demonstrated as one of the promising electron transport layers for high-efficiency perovskite solar cells (PSCs). However, scalable fabrication of SnO₂ films with uniform coverage, desirable thickness and a low defect density in perovskite solar modules (PSMs) is still challenging. Here, we report preparation of high-quality large-area SnO₂ films by chemical bath deposition (CBD) with the addition of KMnO₄. The strong oxidizing nature of KMnO₄ promotes the conversion from Sn(II) to Sn(VI), leading to reduced trap defects and a higher carrier mobility of SnO₂. In addition, K ions diffuse into the perovskite film resulting in larger grain sizes, passivated grain boundaries, and reduced hysteresis of PSCs. Furthermore, Mn ion doping improves both the crystallinity and the phase stability of the perovskite film. Such a multifunctional interface engineering strategy enabled us to achieve a power conversion efficiency (PCE) of 21.70% with less hysteresis for lab-scale PSCs. Using this method, we also fabricated 5 × 5 and 10 × 10 cm² PSMs, which showed PCEs of 15.62% and 11.80% (active area PCEs are 17.26% and 13.72%), respectively. For the encapsulated 5 × 5 cm² PSM, we obtained a T₈₀ operation lifetime (the lifespan during which the solar module PCE drops to 80% of its initial value) exceeding 1000 h in ambient condition.

SUBMITTER: Tong G

PROVIDER: S-EPMC8271052 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Tailoring the Interface with a Multifunctional Ligand for Highly Efficient and Stable FAPbI3 Perovskite Solar Cells and Modules.

Project description:Perovskite solar cells (PeSCs) using FAPbI3 perovskite films often exhibit unfavorable phase transitions and defect-induced nonradiative interfacial recombination, resulting in considerable energy loss and impairing the performance of PeSCs in terms of efficiency, stability, and hysteresis. In this work, a facile interface engineering strategy to control the surface structure and energy-level alignment of perovskite films by tailoring the interface between the FAPbI3 film and hole-transporting layer using 4-hydroxypicolinic acid (4HPA) is reported. According to density functional theory studies, 4HPA has prominent electron delocalization distribution properties that enable it to anchor to the perovskite film surface and facilitate charge transfer at the interface. By enabling multiple bonding interactions with the perovskite layer, including hydrogen bonds, PbO, and PbN dative bonds, 4HPA passivation significantly reduces the trap density and efficiently suppresses nonradiative recombination. The obtained perovskite films exhibit superior optoelectronic properties with improved crystallinity, pure α-phase FAPbI3 , and favorable energy band bending. Following this strategy, 4HPA post-treatment PeSCs achieve a champion power conversion efficiency of 23.28% in 0.12 cm2 cells and 19.26% in 36 cm2 modules with excellent environmental and thermal stabilities.

| S-EPMC10375111 | biostudies-literature

Laser-Scribing Optimization for Sprayed SnO2-Based Perovskite Solar Modules on Flexible Plastic Substrates.

Project description:Flexible perovskite solar cells (FPSCs) are prime candidates for applications requiring a highly efficient, low-cost, lightweight, thin, and even foldable power source. Despite record efficiencies of lab-scale flexible devices (19.5% on a 0.1 cm2 area), scalability represents a critical factor toward commercialization of FPSCs. Large-area automized deposition techniques and efficient laser scribing procedures are required to enable a high-throughput production of flexible perovskite modules (FPSMs), with the latter being much more challenging compared to glass substrates. In this work, we introduce the combined concept of laser scribing optimization and automatized spray-coating of SnO2 layers. Based on a systematic variation of the incident laser power and a comprehensive morphological and electrical analysis of laser-based cell interconnections, optimal scribing parameters are identified. Furthermore, spray-coating is used to deposit uniform compact SnO2 films on large-area (>120 cm2) plastic substrates. FPSCs with spray-coated SnO2 show comparable performance as spin-coated cells, delivering up to 15.3% efficiency on small areas under 1 sun illumination. When upscaling to large areas, FPSMs deliver 12% power conversion efficiency (PCE) and negligible hysteresis on 16.8 cm2 and 11.7% PCE on a 21.8 cm2 active area. Our perovskite devices preserved 78% efficiency when the active area increased from 0.1 to 16.8 cm2, demonstrating that our combined approach is an effective strategy for large-area manufacturing of perovskite devices on flexible substrates.

| S-EPMC8288912 | biostudies-literature

Yb-doped SnO2 electron transfer layer assisting the fabrication of high-efficiency and stable perovskite solar cells in air.

Project description:To date, most preparation processes of polycrystalline perovskite films still have to be performed in a glovebox filled with inert gas, limiting the application due to their high cost and complexity. In this work, we exploit a facile processing technique for the preparation of perovskite solar cells (PSCs) under ambient conditions by the Yb3+ doping effect for SnO2 electron transfer layer. This remarkable and facile interface doping strategy promotes all-air processed planar PSCs, giving enhanced power conversion efficiency (PCE) from 15.69% to 17.31% with a decreasing hysteresis effect. Moreover, the heating and illumination stability of modified devices by virtue of defect suppression located at electron transfer layer (ETL)/perovskite interface has been effectively improved, retaining over 85% of its initial PCE after 7 h heating at 100 °C in ambient condition and 85% of its initial PCE under 7 h continuous light illumination without any encapsulation. Therefore, it is believed that this Yb-doping strategy for SnO2 ETL can provide a novel way of promoting the efficiency and stability of devices prepared in the air.

| S-EPMC9108972 | biostudies-literature

Dual Passivation of Perovskite and SnO2 for High-Efficiency MAPbI3 Perovskite Solar Cells.

Project description:So far, most techniques for modifying perovskite solar cells (PSCs) focus on either the perovskite or electron transport layer (ETL). For the sake of comprehensively improving device performance, a dual-functional method of simultaneously passivating trap defects in both the perovskite and ETL films is proposed that utilizes guidable transfer of Eu3+ in SnO2 to perovskite. Europium ions are distributed throughout the SnO2 film during the formation process of SnO2, and they can diffuse directionally through the SnO2/perovskite interface into the perovskite, while most of the europium ions remain at the interface. Under the synergistic effect of distributed Eu3+ in the SnO2 and aggregated Eu3+ at the interface, the electron mobilities of ETLs are evidently improved. Meanwhile, diffused Eu3+ ions passivate the perovskite to reduce trap densities at the grain boundaries, which can dramatically elevate the open-circuit voltage (V oc) of PSCs. Finally, the mainly PSCs coated on SnO2:Eu3+ ETL achieve a power conversion efficiency of 20.14%. Moreover, an unsealed device degrades by only 13% after exposure to ambient atmosphere for 84 days.

| S-EPMC7927604 | biostudies-literature

MDACl2-Modified SnO2 Film for Efficient Planar Perovskite Solar Cells.

Project description:The electron transport layer (ETL) with excellent charge extraction and transport ability is one of the key components of high-performance perovskite solar cells (PSCs). SnO2 has been considered as a more promising ETL for the future commercialization of PSCs due to its excellent photoelectric properties and easy processing. Herein, we propose a facile and effective ETL modification strategy based on the incorporation of methylenediammonium dichloride (MDACl2) into the SnO2 precursor colloidal solution. The effects of MDACl2 incorporation on charge transport, defect passivation, perovskite crystallization, and PSC performance are systematically investigated. First, the surface defects of the SnO2 film are effectively passivated, resulting in the increased conductivity of the SnO2 film, which is conducive to electron extraction and transport. Second, the MDACl2 modification contributes to the formation of high-quality perovskite films with improved crystallinity and reduced defect density. Furthermore, a more suitable energy level alignment is achieved at the ETL/perovskite interface, which facilitates the charge transport due to the lower energy barrier. Consequently, the MDACl2-modified PSCs exhibit a champion efficiency of 22.30% compared with 19.62% of the control device, and the device stability is also significantly improved.

| S-EPMC10056177 | biostudies-literature

cPCN-Regulated SnO2 Composites Enables Perovskite Solar Cell with Efficiency Beyond 23.

Project description:Efficient electron transport layers (ETLs) not only play a crucial role in promoting carrier separation and electron extraction in perovskite solar cells (PSCs) but also significantly affect the process of nucleation and growth of the perovskite layer. Herein, crystalline polymeric carbon nitrides (cPCN) are introduced to regulate the electronic properties of SnO2 nanocrystals, resulting in cPCN-composited SnO2 (SnO2-cPCN) ETLs with enhanced charge transport and perovskite layers with decreased grain boundaries. Firstly, SnO2-cPCN ETLs show three times higher electron mobility than pristine SnO2 while offering better energy level alignment with the perovskite layer. The SnO2-cPCN ETLs with decreased wettability endow the perovskite films with higher crystallinity by retarding the crystallization rate. In the end, the power conversion efficiency (PCE) of planar PSCs can be boosted to 23.17% with negligible hysteresis and a steady-state efficiency output of 21.98%, which is one of the highest PCEs for PSCs with modified SnO2 ETLs. SnO2-cPCN based devices also showed higher stability than pristine SnO2, maintaining 88% of the initial PCE after 2000 h of storage in the ambient environment (with controlled RH of 30% ± 5%) without encapsulation.

| S-EPMC8017043 | biostudies-literature

Photoexcitation-induced passivation of SnO2 thin film for efficient perovskite solar cells.

Project description:A high-quality tin oxide electron transport layer (ETL) is a key common factor to achieve high-performance perovskite solar cells (PSCs). However, the conventional annealing technique to prepare high-quality ETLs by continuous heating under near-equilibrium conditions requires high temperatures and a long fabrication time. Alternatively, we present a non-equilibrium, photoexcitation-induced passivation technique that uses multiple ultrashort laser pulses. The ultrafast photoexcitation and following electron-electron and electron-phonon scattering processes induce ultrafast annealing to efficiently passivate surface and bulk defects, and improve the crystallinity of SnO2, resulting in suppressing the carrier recombination and facilitating the charge transport between the ETL and perovskite interface. By rapidly scanning the laser beam, the annealing time is reduced to several minutes, which is much more efficient compared with conventional thermal annealing. To demonstrate the university and scalability of this technique, typical antisolvent and antisolvent-free processed hybrid organic-inorganic metal halide PSCs have been fabricated and achieved the power conversion efficiency (PCE) of 24.14% and 22.75% respectively, and a 12-square-centimeter module antisolvent-free processed perovskite solar module achieves a PCE of 20.26%, with significantly enhanced performance both in PCE and stability. This study establishes a new approach towards the commercialization of efficient low-temperature manufacturing of PSCs.

| S-EPMC10583279 | biostudies-literature

SnO x Atomic Layer Deposition on Bare Perovskite-An Investigation of Initial Growth Dynamics, Interface Chemistry, and Solar Cell Performance.

Project description:High-end organic-inorganic lead halide perovskite semitransparent p-i-n solar cells for tandem applications use a phenyl-C61-butyric acid methyl ester (PCBM)/atomic layer deposition (ALD)-SnO x electron transport layer stack. Omitting the PCBM would be preferred for manufacturing, but has in previous studies on (FA,MA)Pb(Br,I)3 and (Cs,FA)Pb(Br,I)3 and in this study on Cs0.05FA0.79MA0.16PbBr0.51I2.49 (perovskite) led to poor solar cell performance because of a bias-dependent light-generated current. A direct ALD-SnO x exposure was therefore suggested to form a nonideal perovskite/SnO x interface that acts as a transport barrier for the light-generated current. To further investigate the interface formation during the initial ALD SnO x growth on the perovskite, the mass dynamics of monitor crystals coated by partial p-i-n solar cell stacks were recorded in situ prior to and during the ALD using a quartz crystal microbalance. Two major finds were made. A mass loss was observed prior to ALD for growth temperatures above 60 °C, suggesting the decomposition of the perovskite. In addition, a mostly irreversible mass gain was observed during the first exposure to the Sn precursor tetrakis(dimethylamino)tin(IV) that is independent of growth temperature and that disrupts the mass gain of the following 20-50 ALD cycles. The chemical environments of the buried interface were analyzed by soft and hard X-ray photoelectron spectroscopy for a sample with 50 ALD cycles of SnO x on the perovskite. Although measurements on the perovskite bulk below and the SnO x film above did not show chemical changes, additional chemical states for Pb, Br, and N as well as a decrease in the amount of I were observed in the interfacial region. From the analysis, these states and not the heating of the perovskite were concluded to be the cause of the barrier. This strongly suggests that the detrimental effects can be avoided by controlling the interfacial design.

| S-EPMC7885702 | biostudies-literature

MgO Nanoparticle Modified Anode for Highly Efficient SnO2-Based Planar Perovskite Solar Cells.

Project description:Reducing the energy loss and retarding the carrier recombination at the interface are crucial to improve the performance of the perovskite solar cell (PSCs). However, little is known about the recombination mechanism at the interface of anode and SnO2 electron transfer layer (ETL). In this work, an ultrathin wide bandgap dielectric MgO nanolayer is incorporated between SnO2:F (FTO) electrode and SnO2 ETL of planar PSCs, realizing enhanced electron transporting and hole blocking properties. With the use of this electrode modifier, a power conversion efficiency of 18.23% is demonstrated, an 11% increment compared with that without MgO modifier. These improvements are attributed to the better properties of MgO-modified FTO/SnO2 as compared to FTO/SnO2, such as smoother surface, less FTO surface defects due to MgO passivation, and suppressed electron-hole recombinations. Also, MgO nanolayer with lower valance band minimum level played a better role in hole blocking. When FTO is replaced with Sn-doped In2O3 (ITO), a higher power conversion efficiency of 18.82% is demonstrated. As a result, the device with the MgO hole-blocking layer exhibits a remarkable improvement of all J-V parameters. This work presents a new direction to improve the performance of the PSCs based on SnO2 ETL by transparent conductive electrode surface modification.

| S-EPMC5604382 | biostudies-literature

MXene-based novel nanocomposites doped SnO2 for boosting the performance of perovskite solar cells.

Project description:Since being first published in 2018, the use of two-dimensional MXene in solar cells has attracted significant interest. This study presents, for the first time, the synthesis of an efficient hybrid electrocatalyst in the form of a nanocomposite (MXene/CoS)-SnO2 designed to function as a high-performance electron transfer layer (ETL). The study can be divided into three distinct parts. The first part involves the synthesis of single-layer Ti3C2Tx MXene nanosheets, followed by the preparation of a CoS solution. Subsequently, in the second part, the fabrication of MXene/CoS heterostructure nanocomposites is carried out, and a comprehensive characterization is conducted to evaluate the physical, structural, and optical properties. In the third part, the attention is on the crucial characterizations of the novel nanocomposite-electron transport layer (ETL) solution, significantly contributing to the evolution of perovskite solar cells. Upon optimising the composition, an exceptional power conversion efficiency of more than 17.69% is attained from 13.81% of the control devices with fill factor (FF), short-circuit current density (Jsc), and open-circuit voltage (Voc) were 66.51%, 20.74 mA/cm2, and 1.282 V. Therefore, this PCE is 21.93% higher than the control device. The groundbreaking MXene/CoS (2 mg mL-1) strategy reported in this research represents a promising and innovative avenue for the realization of highly efficient perovskite solar cells.

| S-EPMC11199647 | biostudies-literature