Insights into the Mechanochemical Synthesis of MOF-74.

ABSTRACT: Mechanochemical synthesis has recently emerged as a scalable "green" approach for the preparation of MOFs, but current understanding of the underlying reaction mechanisms is limited. In this work, an investigation of the reaction pathway of the mechanochemical synthesis of MOF-74 from ZnO and 2,5-dihydroxyterephthalic acid (H₄HDTA), using DMF as a liquid additive, is presented. The complex reaction pathway involves the formation of four short-lived intermediate phases, prior to the crystallization of MOF-74. The crystal structures of three of these intermediates have been determined using a combination of single-crystal and powder X-ray diffraction methods and are described here. The initial stages of the reaction are very fast, with a DMF solvate of H₄HDTA forming after only 2 min of milling. This is followed by crystallization, after only 4 min of milling, of a triclinic one-dimensional coordination polymer, Zn(H₂DHTA)(DMF)₂(H₂O)₂, which converts into a monoclinic polymorph on additional milling. Highly crystalline MOF-74 appears after prolonged milling, for at least 70 min.

SUBMITTER: Beamish-Cook J

PROVIDER: S-EPMC8273859 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The stability of functional materials in water-containing environments is critical for their industrial applications. A wide variety of metal-organic frameworks (MOFs) synthesized in the past decade have strikingly different apparent stabilities in contact with liquid or gaseous H2O, ranging from rapid hydrolysis to persistence over days to months. Here, we show using newly determined thermochemical data obtained by high-temperature drop combustion calorimetry that these differences are thermodynamically driven rather than primarily kinetically controlled. The formation reaction of a MOF from metal oxide (MO) and a linker generally liberates water by the reaction MO + linker = MOF + H2O. Newly measured enthalpies of formation of Mg-MOF-74(s) + H2O(l) and Ni-MOF-74(s) + H2O(l) from their crystalline dense components, namely, the divalent MO (MgO or NiO) and 2,5-dihydroxyterephthalic acid, are 303.9 ± 17.2 kJ/mol of Mg for Mg-MOF-74 and 264.4 ± 19.4 kJ/mol of Ni for Ni-MOF-74. These strongly endothermic enthalpies of formation indicate that the reverse reaction, namely, the hydrolysis of these MOFs, is highly exothermic, strongly suggesting that this large thermodynamic driving force for hydrolysis is the reason why the MOF-74 family cannot be synthesized via hydrothermal routes and why these MOFs decompose on contact with moist air or water even at room temperature. In contrast, other MOFs studied previously, namely, zeolitic imidazolate frameworks (ZIF-zni, ZIF-1, ZIF-4, Zn(CF3Im)2, and ZIF-8), show enthalpies of formation in the range 20-40 kJ per mole of metal atom. These modest endothermic enthalpies of formation can be partially compensated by positive entropy terms arising from water release, and these materials do not react appreciably with H2O under ambient conditions. Thus, these differences in reactivity with water are thermodynamically controlled and energetics of formation, either measured or predicted, can be used to assess the extent of water sensitivity for different possible MOFs.

Dataset Information

Insights into the Mechanochemical Synthesis of MOF-74.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets