Large tuning in the electrowetting behaviour on ferroelectric PVDF-HFP/Teflon AF bilayer.

ABSTRACT: Electrowetting (EW) response on a dielectric depends on its permittivity value, Young contact angle and voltage amplitude. We present a large change in EW contact angle, from 163° to 80°, on the bilayer dielectric made up of ferroelectric PVDF-HFP with a thin layer of fluoropolymer. The thickness values of both layers were separately optimized for high effective capacitance essential for the large EW response. It reveals that the bilayer with ~ 500 nm thick PVDF-HFP layer and ~ 50 nm thin layer of Teflon results in the maximum value of effective dielectric constant, ε ≈ 8. Besides this gain, dc-voltage EW response exhibits hysteresis mainly due to polarization in the ferroelectric layer such that, hysteretic offset voltage was found to depend on the applied voltage amplitude and thickness of the dielectrics. Finally, bilayer was subjected to ac-voltage EW in silicone oil for ambient temperature ranging from - 25 to 70 °C. The consistent EW response in this ambient without any degradation/delamination of polymer surface confirmed the durability of the bilayer on the transparent ITO electrodes.

Supplementary information

The online version contains supplementary material available at 10.1007/s10853-021-06308-z.

SUBMITTER: Wadhai SM

PROVIDER: S-EPMC8274264 | biostudies-literature | 2021

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Large tuning in the electrowetting behaviour on ferroelectric PVDF-HFP/Teflon AF bilayer.

Wadhai Sandip M SM Sawane Yogesh B YB Limaye Abhay V AV Banpurkar Arun G AG

Journal of materials science 20210712 28

Electrowetting (EW) response on a dielectric depends on its permittivity value, Young contact angle and voltage amplitude. We present a large change in EW contact angle, from 163° to 80°, on the bilayer dielectric made up of ferroelectric PVDF-HFP with a thin layer of fluoropolymer. The thickness values of both layers were separately optimized for high effective capacitance essential for the large EW response. It reveals that the bilayer with ~ 500 nm thick PVDF-HFP layer and ~ 50 nm thin layer ...[more]

PMID: 34276067

Similar Datasets

Project description:Fluorous media are the least polar and polarizable condensed phases known. Their use as membrane materials considerably increases the selectivity and robustness of ion-selective electrodes (ISEs). In this research, a fluorous amorphous perfluoropolymer was used for the first time as a matrix for an ISE membrane. Electrodes for pH measurements with membranes composed of poly[4,5-difluoro-2,2-bis(trifluoromethyl)-1,3-dioxole]-co-poly(tetrafluoroethylene) (87% dioxole monomer content; known as Teflon AF2400) as polymer matrix, a linear perfluorooligoether as plasticizer, sodium tetrakis[3,5-bis(perfluorohexyl)phenyl]borate providing for ionic sites, and bis[(perfluorooctyl)propyl]-2,2,2-trifluoroethylamine as H+ ionophore were investigated. All electrodes had excellent potentiometric selectivities, showed Nernstian responses to H+ over a wide pH range, exhibited enhanced mechanical stability, and maintained their selectivity over at least 4 weeks. For membranes of low ionophore concentration, the polymer affected the sensor selectivity noticeably at polymer concentrations exceeding 15%. Also, the membrane resistance increased quite strongly at high polymer concentrations, which cannot be explained by the Mackie-Meares obstruction model. The selectivities and resistances depend on the polymer concentration because of a functional group associated with Teflon AF2400, with a concentration of one functional group per 854 monomer units of the polymer. In the fluorous environment of these membranes, this functional group binds to Na+, K+, Ca2+, and the unprotonated ionophore with binding constants of 10(3.5), 10(1.8), 10(6.8), and 10(4.4) M(-1), respectively. Potentiometric and spectroscopic evidence indicates that these functional groups are COOH groups formed by the hydrolysis of carboxylic acid fluoride (COF) groups originally present in Teflon AF2400. The use of higher ionophore concentrations removes the undesirable effect of these COOH groups almost completely. Alternatively, the C(=O)F groups can be eliminated chemically, or they can be used to readily introduce new functionalities.

Project description:Electrospinning is a versatile technique to produce nanofibrous membranes with applications in filtration, biosensing, biomedical and tissue engineering. The structural and therefore physical properties of electrospun fibers can be finely tuned by changing the electrospinning parameters. The large parameter window makes it challenging to optimize the properties of fibers for a specific application. Therefore, a fundamental understanding of the multiscale structure of fibers and its correlation with their macroscopic behaviors is required for the design and production of systems with dedicated applications. In this study, we demonstrate that the properties of poly(vinylidene fluoride-co-hexafluoro propylene) (PVDF-HFP) electrospun fibers can be tuned by changing the rotating drum speed used as a collector during electrospinning. Indeed, with the help of multiscale characterization techniques such as scanning electron microscopy (SEM), small-angle X-ray scattering (SAXS), and wide-angle X-ray scattering (WAXS), we observe that increasing the rotating drum speed not only aligns the fibers but also induces polymeric chain rearrangements at the molecular scale. Such changes result in enhanced mechanical properties and an increase of the piezoelectric β-phase of the PVDF-HFP fiber membranes. We detect nanostructural deformation behaviors when the aligned fibrous membrane is uniaxially stretched along the fiber alignment direction, while an increase in the alignment of the fibers is observed for randomly aligned samples. This was analyzed by performing in situ SAXS measurements coupled with uniaxial tensile loading of the fibrous membranes along the fiber alignment direction. The present study shows that fibrous membranes can be produced with varying degrees of fiber orientation, piezoelectric β-phase content, and mechanical properties by controlling the speed of the rotating drum collector during the fiber production. Such aligned fiber membranes have potential applications for neural or musculoskeletal tissue engineering.

Dataset Information

Large tuning in the electrowetting behaviour on ferroelectric PVDF-HFP/Teflon AF bilayer.

Supplementary information

Publications

Large tuning in the electrowetting behaviour on ferroelectric PVDF-HFP/Teflon AF bilayer.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets