Large-Area Fabrication of Vertical Silicon Nanotube Arrays via Toroidal Micelle Self-Assembly.

ABSTRACT: We present a highly scalable, room-temperature strategy for fabricating vertical silicon nanotube arrays derived from a toroidal micelle pattern via a water vapor-induced block copolymer (BCP) self-assembly mechanism. A polystyrene-b-poly(ethylene oxide) (PS-b-PEO) BCP system can be self-assembled into toroidal micelle structures (diameter: 400-600 nm) on a PS-OH-modified substrate in a facile manner contrasting with other complex processes described in the literature. It was found that a minimum PS-b-PEO thickness of ∼86 nm is required for the toroidal self-assembly. Furthermore, a water vapor annealing treatment at room conditions (∼25 °C, 60 min) is shown to vastly enhance the ordering of micellar structures. A liquid-phase infiltration process was used to generate arrays of iron and nickel oxide nanorings. These oxide structures were used as templates for pattern transfer into the underlying silicon substrate via plasma etching, resulting in large-area 3D silicon nanotube arrays. The overall simplicity of this technique, as well as the wide potential versatility of the resulting metal structures, proves that such room-temperature synthesis routes are a viable pathway for complex nanostructure fabrication, with potential applicability in fields such as optics or catalysis.

SUBMITTER: Prochukhan N

PROVIDER: S-EPMC8280740 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Bottom-up assembly of large-area nanowire resonator arrays.

Project description:Directed-assembly of nanowire-based devices will enable the development of integrated circuits with new functions that extend well beyond mainstream digital logic. For example, nanoelectromechanical resonators are very attractive for chip-based sensor arrays because of their potential for ultrasensitive mass detection. In this letter, we introduce a new bottom-up assembly method to fabricate large-area nanoelectromechanical arrays each having over 2,000 single-nanowire resonators. The nanowires are synthesized and chemically functionalized before they are integrated onto a silicon chip at predetermined locations. Peptide nucleic acid probe molecules attached to the nanowires before assembly maintain their binding selectivity and recognize complementary oligonucleotide targets once the resonator array is assembled. The two types of cantilevered resonators we integrated here using silicon and rhodium nanowires had Q-factors of approximately 4,500 and approximately 1,150, respectively, in vacuum. Taken together, these results show that bottom-up nanowire assembly can offer a practical alternative to top-down fabrication for sensitive chip-based detection.

| S-EPMC2656674 | biostudies-literature

Fabrication of Large-Area Molybdenum Disulfide Device Arrays Using Graphene/Ti Contacts.

Project description:Two-dimensional (2D) molybdenum disulfide (MoS2) is the most mature material in 2D material fields owing to its relatively high mobility and scalability. Such noticeable properties enable it to realize practical electronic and optoelectronic applications. However, contact engineering for large-area MoS2 films has not yet been established, although contact property is directly associated to the device performance. Herein, we introduce graphene-interlayered Ti contacts (graphene/Ti) into large-area MoS2 device arrays using a wet-transfer method. We achieve MoS2 devices with superior electrical and photoelectrical properties using graphene/Ti contacts, with a field-effect mobility of 18.3 cm2/V∙s, on/off current ratio of 3 × 107, responsivity of 850 A/W, and detectivity of 2 × 1012 Jones. This outstanding performance is attributable to a reduction in the Schottky barrier height of the resultant devices, which arises from the decreased work function of graphene induced by the charge transfer from Ti. Our research offers a direction toward large-scale electronic and optoelectronic applications based on 2D materials.

| S-EPMC8348625 | biostudies-literature

Large Area Fabrication of Semiconducting Phosphorene by Langmuir-Blodgett Assembly.

Project description:Phosphorene is a recently new member of the family of two dimensional (2D) inorganic materials. Besides its synthesis it is of utmost importance to deposit this material as thin film in a way that represents a general applicability for 2D materials. Although a considerable number of solvent based methodologies have been developed for exfoliating black phosphorus, so far there are no reports on controlled organization of these exfoliated nanosheets on substrates. Here, for the first time to the best of our knowledge, a mixture of N-methyl-2-pyrrolidone and deoxygenated water is employed as a subphase in Langmuir-Blodgett trough for assembling the nanosheets followed by their deposition on substrates and studied its field-effect transistor characteristics. Electron microscopy reveals the presence of densely aligned, crystalline, ultra-thin sheets of pristine phosphorene having lateral dimensions larger than hundred of microns. Furthermore, these assembled nanosheets retain their electronic properties and show a high current modulation of 104 at room temperature in field-effect transistor devices. The proposed technique provides semiconducting phosphorene thin films that are amenable for large area applications.

| S-EPMC5037434 | biostudies-literature

System design of large-area vertical photothermoelectric detectors based on carbon nanotube forests with MXene electrodes.

Project description:Photothermoelectric (PTE) detectors that combine photothermal and thermoelectric conversion have emerged in recent years. They can overcome bandgap limitations and achieve effective infrared detection. However, the development of PTE detectors and the related system design are in the early phases. Herein, we present vertical PTE detectors utilizing the active layer of carbon nanotube forests with MXenes acting as top electrodes. The detector demonstrates its capacity for sensitive infrared detection and rapid infrared response. We also investigated the relationship between photoresponse and different MXene electrode types as well as their thickness, which guides the PTE detector configuration design. Furthermore, we packed the PTE detectors with a polytetrafluoroethylene (PTFE, Teflon) cavity. The photoresponse is improved and the degradation is significantly delayed. We also applied this PTE detector system for non-destructive tracking (NDT) applications, where the photovoltage mapping pattern proves the viability of the imaging track. This work paves the way toward infrared energy harvesters and customized industrial NDT measurement.

| S-EPMC9926910 | biostudies-literature

Fabrication of sharp silicon arrays to wound Caenorhabditis elegans.

Project description:Understanding how animals respond to injury and how wounds heal remains a challenge. These questions can be addressed using genetically tractable animals, including the nematode Caenorhabditis elegans. Given its small size, the current methods for inflicting wounds in a controlled manner are demanding. To facilitate and accelerate the procedure, we fabricated regular arrays of pyramidal features ("pins") sharp enough to pierce the tough nematode cuticle. The pyramids were made from monocrystalline silicon wafers that were micro-structured using optical lithography and alkaline wet etching. The fabrication protocol and the geometry of the pins, determined by electron microscopy, are described in detail. We also used electron microscopy to characterize the different types of injury caused by these pins. Upon wounding, C. elegans expresses genes encoding antimicrobial peptides. A comparison of the induction of antimicrobial peptide gene expression using traditional needles and the pin arrays demonstrates the utility of this new method.

| S-EPMC7046703 | biostudies-literature

Optically transparent vertical silicon nanowire arrays for live-cell imaging.

Project description:Programmable nano-bio interfaces driven by tuneable vertically configured nanostructures have recently emerged as a powerful tool for cellular manipulations and interrogations. Such interfaces have strong potential for ground-breaking advances, particularly in cellular nanobiotechnology and mechanobiology. However, the opaque nature of many nanostructured surfaces makes non-destructive, live-cell characterization of cellular behavior on vertically aligned nanostructures challenging to observe. Here, a new nanofabrication route is proposed that enables harvesting of vertically aligned silicon (Si) nanowires and their subsequent transfer onto an optically transparent substrate, with high efficiency and without artefacts. We demonstrate the potential of this route for efficient live-cell phase contrast imaging and subsequent characterization of cells growing on vertically aligned Si nanowires. This approach provides the first opportunity to understand dynamic cellular responses to a cell-nanowire interface, and thus has the potential to inform the design of future nanoscale cellular manipulation technologies.

| S-EPMC7890818 | biostudies-literature

Fabrication of Durable Ordered Ta2O5 Nanotube Arrays Decorated with Bi2S3 Quantum Dots.

Project description:One of the most important challenges in the fabrication of ordered tantalum pentaoxide (Ta2O5) nanotube arrays (NTs) via the electrochemical method is the formation of nanotubes that adhere well to the Ta substrate. In this paper, we propose a new protocol that allows tight-fitting Ta2O5 nanotubes to be obtained through the anodic oxidation of tantalum foil. Moreover, to enhance their activity in the photocatalytic reaction, in this study, they have been decorated by nontoxic bismuth sulfide (Bi2S3) quantum dots (QDs) via a simple successive ionic layer adsorption and reaction (SILAR) method. Transmission electron microscopy (TEM) analysis revealed that quantum dots with a size in the range of 6-11 nm were located both inside and on the external surfaces of the Ta2O5 NTs. The effect of the anodization time and annealing conditions, as well as the effect of cycle numbers in the SILAR method, on the surface properties and photoactivity of Ta2O5 nanotubes and Bi2S3/Ta2O5 composites have been investigated. The Ta2O5 nanotubes decorated with Bi2S3 QDs exhibit high photocatalytic activity in the toluene degradation reaction, i.e., 99% of toluene (C0 = 200 ppm) was degraded after 5 min of UV-Vis irradiation. Therefore, the proposed anodic oxidation of tantalum (Ta) foil followed by SILAR decorating allows a photocatalytic surface, ready to use for pollutant degradation in the gas phase, to be obtained.

| S-EPMC6835939 | biostudies-literature

Quick Fabrication of Large-area Organic Semiconductor Single Crystal Arrays with a Rapid Annealing Self-Solution-Shearing Method.

Project description:In this paper, we developed a new method to produce large-area single crystal arrays by using the organic semiconductor 9, 10-bis (phenylethynyl) anthracene (BPEA). This method involves an easy operation, is efficient, meets the demands of being low-cost and is independent of the substrate for large-area arrays fabrication. Based on these single crystal arrays, the organic field effect transistors exhibit the superior performance with the average mobility extracting from the saturation region of 0.2 cm(2) V(-1)s(-1) (the highest 0.47 cm(2) V(-1)s(-1)) and on/off ratio exceeding 10(5). In addition, our single crystal arrays also show a very high photoswitch performance with an on/off current ratio up to 4.1 × 10(5), which is one of the highest values reported for organic materials. It is believed that this method provides a new way to fabricate single crystal arrays and has the potential for application to large area organic electronics.

| S-EPMC4539534 | biostudies-literature

Anodic Fabrication of Ti-Ni-O Nanotube Arrays on Shape Memory Alloy.

Project description:Surface modification with oxide nanostructures is one of the efficient ways to improve physical or biomedical properties of shape memory alloys. This work reports a fabrication of highly ordered Ti-Ni-O nanotube arrays on Ti-Ni alloy substrates through pulse anodization in glycerol-based electrolytes. The effects of anodization parameters and the annealing process on the microstructures and surface morphology of Ti-Ni-O were studied using scanning electron microscope and Raman spectroscopy. The electrolyte type greatly affected the formation of nanotube arrays. A formation of anatase phase was found with the Ti-Ni-O nanotube arrays annealed at 450 °C. The oxide nanotubes could be crystallized to rutile phase after annealing treatment at 650 °C. The Ti-Ni-O nanotube arrays demonstrated an excellent thermal stability by keeping their nanotubular structures up to 650 °C.

| S-EPMC5453335 | biostudies-other

Transfer Tiling of Nanostructures for Large-Area Fabrication.

Project description:The fabrication of nanoscale patterns over a large area has been considered important but difficult, because there are few ways to satisfy both conditions. Previously, visually tolerable tiling (VTT) for fabricating nanopatterns for optical applications has been reported as a candidate for large area fabrication. The essence of VTT is the inevitable stitching of the nanoscale optical component, which is not seen by the naked eye if the boundary is very narrow while the tiles are overlapped. However, it had been difficult to control the shape of the spread of liquid prepolymers in the previous work, and there was room for the development of tiling. Here, we propose a method for transferring various shapes of tiles, which can be defined with a shadow mask. The method of using a transparent shadow mask can provide a wide process window, because it allows the spreading of a liquid prepolymer to be more easily controlled. We optimize the coating condition of a liquid prepolymer and the ultraviolet (UV) exposure time. Using this method, we can attach tiles of various shapes without a significant visible trace in the overlapped region.

| S-EPMC6266267 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data