Spherulitic and rotational crystal growth of Quartz thin films.

ABSTRACT: To obtain crystalline thin films of alpha-Quartz represents a challenge due to the tendency for the material towards spherulitic growth. Thus, understanding the mechanisms that give rise to spherulitic growth can help regulate the growth process. Here the spherulitic type of 2D crystal growth in thin amorphous Quartz films was analyzed by electron back-scatter diffraction (EBSD). EBSD was used to measure the size, orientation, and rotation of crystallographic grains in polycrystalline SiO₂ and GeO₂ thin films with high spatial resolution. Individual spherulitic Quartz crystal colonies contain primary and secondary single crystal fibers, which grow radially from the colony center towards its edge, and fill a near circular crystalline area completely. During their growth, individual fibers form so-called rotational crystals, when some lattice planes are continuously bent. The directions of the lattice rotation axes in the fibers were determined by an enhanced analysis of EBSD data. A possible mechanism, including the generation of the particular type of dislocation(s), is suggested.

SUBMITTER: Lutjes NR

PROVIDER: S-EPMC8295350 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Tailoring the crystal growth of quartz on silicon for patterning epitaxial piezoelectric films.

Project description:Epitaxial films of piezoelectric α-quartz could enable the fabrication of sensors with unprecedented sensitivity for prospective applications in electronics, biology and medicine. However, the prerequisites are harnessing the crystallization of epitaxial α-quartz and tailoring suitable film microstructures for nanostructuration. Here, we bring new insights into the crystallization of epitaxial α-quartz films on silicon (100) from the devitrification of porous silica and the control of the film microstructures: we show that by increasing the quantity of devitrifying agent (Sr) it is possible to switch from an α-quartz microstructure consisting of a porous flat film to one dominated by larger, fully dense α-quartz crystals. We also found that the film thickness, relative humidity and the nature of the surfactant play an important role in the control of the microstructure and homogeneity of the films. Via a multi-layer deposition method, we have extended the maximum thickness of the α-quartz films from a few hundreds of nm to the μm range. Moreover, we found a convenient method to combine this multilayer approach with soft lithography to pattern silica films while preserving epitaxial crystallization. This improved control over crystallization and the possibility of preparing patterned films of epitaxial α-quartz on Si substrates pave the path to future developments in applications based on electromechanics, optics and optomechanics.

| S-EPMC9419616 | biostudies-literature

Wafer-scale single-crystal perovskite patterned thin films based on geometrically-confined lateral crystal growth.

Project description:We report a facile roll-printing method, geometrically confined lateral crystal growth, for the fabrication of large-scale, single-crystal CH3NH3PbI3 perovskite thin films. Geometrically confined lateral crystal growth is based on transfer of a perovskite ink solution via a patterned rolling mould to a heated substrate, where the solution crystallizes instantly with the immediate evaporation of the solvent. The striking feature of this method is that the instant crystallization of the feeding solution under geometrical confinement leads to the unidirectional lateral growth of single-crystal perovskites. Here, we fabricated single-crystal perovskites in the form of a patterned thin film (3 × 3 inch) with a high carrier mobility of 45.64?cm2?V-1?s-1. We also used these single-crystal perovskite thin films to construct solar cells with a lateral configuration. Their active-area power conversion efficiency shows a highest value of 4.83%, which exceeds the literature efficiency values of lateral perovskite solar cells.

| S-EPMC5508126 | biostudies-literature

Vapor Sorption–Desorption Phenomena of HD and GB Simulants from Polyurethane Thin Films on Aluminum Oxide via a Quartz Crystal Microbalance

Project description:Protection and decontamination

| S-EPMC9260914 | biostudies-literature

Electron Irradiation-Induced Degradation of TiN Thin Films on Quartz and Sapphire Substrates.

Project description:In this contribution, we investigated the properties of magnetron-sputtered TiN thin films on sapphire and quartz substrates before and after 5 MeV electron irradiation with a fluence of 7 × 1013 e/cm2. Structural, morphological, optical, and electrical properties were analyzed to observe the impact of electron irradiation on the TiN thin films. The results showed improved electrical properties of the TiN thin films due to high-energy electron irradiation, resulting in increased specific conductivity compared to the as-deposited thin films on both sapphire and quartz substrates. The structural features of the TiN thin films on the sapphire substrate transformed from polycrystalline to amorphous, while the TiN thin films deposited on the quartz substrate remained unchanged. Chemical state analysis indicated changes in the metallic bonding between Ti and N in the deposited TiN on the sapphire substrate, while TiN deposited on the quartz substrate retained its Ti-N bonding. This study provides insights into the effects of electron irradiation on TiN thin films, emphasizing the importance of investigating radiation resistance for the reliable operation of optoelectronic devices and photovoltaic systems in extreme ionizing radiation environments.

| S-EPMC10785614 | biostudies-literature

Growth of Epitaxial Oxide Thin Films on Graphene.

Project description:The transfer process of graphene onto the surface of oxide substrates is well known. However, for many devices, we require high quality oxide thin films on the surface of graphene. This step is not understood. It is not clear why the oxide should adopt the epitaxy of the underlying oxide layer when it is deposited on graphene where there is no lattice match. To date there has been no explanation or suggestion of mechanisms which clarify this step. Here we show a mechanism, supported by first principles simulation and structural characterisation results, for the growth of oxide thin films on graphene. We describe the growth of epitaxial SrTiO3 (STO) thin films on a graphene and show that local defects in the graphene layer (e.g. grain boundaries) act as bridge-pillar spots that enable the epitaxial growth of STO thin films on the surface of the graphene layer. This study, and in particular the suggestion of a mechanism for epitaxial growth of oxides on graphene, offers new directions to exploit the development of oxide/graphene multilayer structures and devices.

| S-EPMC4981861 | biostudies-literature

ZnO Thin Films Growth Optimization for Piezoelectric Application.

Project description:The piezoelectric response of ZnO thin films in heterostructure-based devices is strictly related to their structure and morphology. We optimize the fabrication of piezoelectric ZnO to reduce its surface roughness, improving the crystalline quality, taking into consideration the role of the metal electrode underneath. The role of thermal treatments, as well as sputtering gas composition, is investigated by means of atomic force microscopy and x-ray diffraction. The results show an optimal reduction in surface roughness and at the same time a good crystalline quality when 75% O2 is introduced in the sputtering gas and deposition is performed between room temperature and 573 K. Subsequent annealing at 773 K further improves the film quality. The introduction of Ti or Pt as bottom electrode maintains a good surface and crystalline quality. By means of piezoelectric force microscope, we prove a piezoelectric response of the film in accordance with the literature, in spite of the low ZnO thickness and the reduced grain size, with a unipolar orientation and homogenous displacement when deposited on Ti electrode.

| S-EPMC8472809 | biostudies-literature

Water Content of Polyelectrolyte Multilayer Films Measured by Quartz Crystal Microbalance and Deuterium Oxide Exchange.

Project description:Water content of natural and synthetic, thin, polymer films is of considerable interest to a variety of fields because it governs properties such as ion conductivity, rigidity, porosity, and mechanical strength. Measuring thin film water content typically requires either complicated and expensive instrumentation or use of multiple instrumental techniques. However, because a quartz crystal microbalance (QCM) is sensitive to changes in mass and viscosity, deuterated solvent exchange has emerged as a simple, single-instrument, in situ method to quantify thin film water content. Relatively few studies, though, have employed this technique to measure water content of polyelectrolyte multilayers formed by layer-by-layer (LbL) assembly. In this work, poly (allyl amine) (PAH) and poly (styrene sulfonate) (PSS) films of up to nine layers were formed and the water content for each layer was measured via QCM with deuterium oxide exchange. The well-characterized nature of PAH/PSS films facilitated comparisons of the technique used in this work to other instrumental methods. Water content results showed good agreement with the literature and good precision for hydrated films thicker than 20 nm. Collectively, this work highlights the utility, repeatability, and limitations of this deuterated exchange technique in measuring the solvent content of thin films.

| S-EPMC7866239 | biostudies-literature

Post-Growth Dynamics and Growth Modeling of Organic Semiconductor Thin Films.

Project description:The ability to control the properties of organic thin films is crucial for obtaining highly performant thin-film devices. However, thin films may experience post-growth processes, even when the most sophisticated and controlled growth techniques such as organic molecular beam epitaxy (OMBE) are used. Such processes can modify the film structure and morphology and, thus, the film properties ultimately affecting device performances. For this reason, probing the occurrence of post-growth evolution is essential. Equally importantly, the processes responsible for this evolution should be addressed in view of finding a strategy to control and, possibly, leverage them for driving film properties. Here, nickel-tetraphenylporphyrin (NiTPP) thin films grown by OMBE on highly oriented pyrolytic graphite (HOPG) are selected as an exemplary system exhibiting a remarkable post-growth morphology evolution consistent with Ostwald-like ripening. To quantitatively describe the growth, the height-height correlation function (HHCF) analysis of the atomic force microscopy (AFM) images is carried out, clarifying the role of the post-growth evolution as an integral part of the whole growth process. The set of scaling exponents obtained confirms that the growth is mainly driven by diffusion combined with the presence of step-edge barriers, in agreement with the observed ripening phenomenon. Finally, the results together with the overall approach adopted demonstrate the reliability of the HHCF analysis in systems displaying post-growth evolution.

| S-EPMC9996818 | biostudies-literature

Growth and superconductivity of niobium titanium alloy thin films on strontium titanate (001) single-crystal substrates for superconducting joints.

Project description:Aiming to introduce NbTi alloy superconducting joints for REBa2Cu3O7-δ (REBCO, RE: rare-earth element) superconducting wires, NbTi alloy thin films were deposited at room temperature on SrTiO3 (STO) (001) single-crystal substrates, which have a high lattice matching with REBCO (001). The strain, crystallinity, surface morphology, and superconducting property of the films with various thicknesses were investigated. The NbTi films grew in the orientation with (110)NbTi//(001)STO:[001]NbTi and [11-0] NbTi//[100]STO; that is, the NbTi lattices had two directions in the (110) of NbTi. The strain decreased and the crystallinity improved as the film thickness increased. The films were found to crystallize immediately at the interface between the films and substrates by cross-sectional scanning transmission electron microscopy. The flat surfaces of the films have mesh-like morphologies due to the growth of elongated NbTi grains along the [100] and [010] of the STO, reflecting the in-plane two directions of the NbTi lattices. The superconducting transition temperature of the films increased with improvement in the crystallinity of the films. The preparation of superconducting NbTi alloy thin films with sufficient crystallinity at room temperature suggested the possibility of forming the films on REBCO and the applicability of the films as superconducting joints.

| S-EPMC6181932 | biostudies-literature

Mechanisms of classical crystal growth theory explain quartz and silicate dissolution behavior.

Project description:The central control of mineral weathering rates on biogeochemical systems has motivated studies of dissolution for more than 50 years. A complete physical picture that explains widely observed variations in dissolution behavior is lacking, and some data show apparent serious inconsistencies that cannot be explained by the largely empirical kinetic "laws." Here, we show that mineral dissolution can, in fact, be understood through the same mechanistic theory of nucleation developed for mineral growth. In principle, this theory should describe dissolution but has never been tested. By generalizing nucleation rate equations to include dissolution, we arrive at a model that predicts how quartz dissolution processes change with undersaturation from step retreat, to defect-driven and homogeneous etch pit formation. This finding reveals that the "salt effect," recognized almost 100 years ago, arises from a crossover in dominant nucleation mechanism to greatly increase step density. The theory also explains the dissolution kinetics of major weathering aluminosilicates, kaolinite and K-feldspar. In doing so, it provides a sensible origin of discrepancies reported for the dependence of kaolinite dissolution and growth rates on saturation state by invoking a temperature-activated transition in the nucleation process. Although dissolution by nucleation processes was previously unknown for oxides or silicates, our mechanism-based findings are consistent with recent observations of dissolution (i.e., demineralization) in biological minerals. Nucleation theory may be the missing link to unifying mineral growth and dissolution into a mechanistic and quantitative framework across the continuum of driving force.

| S-EPMC1266142 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data