Novel Dealloying-Fabricated NiS/NiO Nanoparticles with Superior Cycling Stability for Supercapacitors.

ABSTRACT: NiS/NiO nanoparticles are successfully fabricated through a simple dealloying method and an ion-exchange process. X-ray diffraction demonstrates the existence of NiO and NiS phases, and scanning electron microscopy and transmission electron microscopy imply the nanopore distribution nature and the nanoparticle morphology of the produced material. The electrochemical behaviors are studied by cyclic voltammetry and galvanostatic charge-discharge measurements. The NiS/NiO electrode shows an enhanced specific capacitance of 1260 F g^-1 at a current density of 0.5 A g^-1. The NiS/NiO//AC device provides a maximum energy density of 17.42 W h kg^-1, a high power density of 4000 W kg^-1, and a satisfactory cycling performance of 93% capacitance retention after 30,000 cycles.

SUBMITTER: Wang H

PROVIDER: S-EPMC8296023 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Enhanced cycling stability of NiCo2S4@NiO core-shell nanowire arrays for all-solid-state asymmetric supercapacitors.

Project description:As a new class of pseudocapacitive material, metal sulfides possess high electrochemical performance. However, their cycling performance as conventional electrodes is rather poor for practical applications. In this article, we report an original composite electrode based on NiCo2S4@NiO core-shell nanowire arrays (NWAs) with enhanced cycling stability. This three-dimensional electrode also has a high specific capacitance of 12.2 F cm-2 at the current density of 1 mA cm-2 and excellent cycling stability (about 89% retention after 10,000 cycles). Moreover, an all-solid-state asymmetric supercapacitor (ASC) device has been assembled with NiCo2S4@NiO NWAs as the positive electrode and active carbon (AC) as the negative electrode, delivering a high energy density of 30.38?W h kg-1 at 0.288?KW kg-1 and good cycling stability (about 109% retention after 5000 cycles). The results show that NiCo2S4@NiO NWAs are promising for high-performance supercapacitors with stable cycling based on the unique core-shell structure and well-designed combinations.

| S-EPMC5141571 | biostudies-literature

Phase-controlled synthesis of ?-NiS nanoparticles confined in carbon nanorods for high performance supercapacitors.

Project description:A facile and phase-controlled synthesis of ?-NiS nanoparticles (NPs) embedded in carbon nanorods (CRs) is reported by in-situ sulfurating the preformed Ni/CRs. The nanopore confinement by the carbon matrix is essential for the formation of ?-NiS and preventing its transition to ?-phase, which is in strong contrast to large aggregated ?-NiS particles grown freely without the confinement of CRs. When used as electrochemical electrode, the hybrid electrochemical charge storage of the ultrasmall ?-NiS nanoparticels dispersed in CRs is benefit for the high capacitor (1092, 946, 835, 740?F g(-1) at current densities of 1, 2, 5, 10?A g(-1), respectively.). While the high electrochemical stability (approximately 100% retention of specific capacitance after 2000 charge/discharge cycles) is attributed to the supercapacitor-battery electrode, which makes synergistic effect of capacitor (CRs) and battery (NiS NPs) components rather than a merely additive composite. This work not only suggests a general approach for phase-controlled synthesis of nickel sulfide but also opens the door to the rational design and fabrication of novel nickel-based/carbon hybrid supercapacitor-battery electrode materials.

| S-EPMC4231331 | biostudies-literature

Non-Isothermal Decomposition as Efficient and Simple Synthesis Method of NiO/C Nanoparticles for Asymmetric Supercapacitors.

Project description:A series of NiO/C nanocomposites with NiO concentrations ranging from 10 to 90 wt% was synthesized using a simple and efficient two-step method based on non-isothermal decomposition of Nickel(II) bis(acetylacetonate). X-ray diffraction (XRD) measurements of these NiO/C nanocomposites demonstrate the presence of β-NiO. NiO/C nanocomposites are composed of spherical particles distributed over the carbon support surface. The average diameter of nickel oxide spheres increases with the NiO content and are estimated as 36, 50 and 205 nm for nanocomposites with 10, 50 and 80 wt% NiO concentrations, respectively. In turn, each NiO sphere contains several nickel oxide nanoparticles, whose average sizes are 7-8 nm. According to the tests performed using a three-electrode cell, specific capacitance (SC) of NiO/C nanocomposites increases from 200 to 400 F/g as the NiO content achieves a maximum of 60 wt% concentration, after which the SC decreases. The study of the NiO/C composite showing the highest SC in three- and two-electrode cells reveals that its SC remains almost unchanged while increasing the current density, and the sample demonstrates excellent cycling stability properties. Finally, NiO/C (60% NiO) composites are shown to be promising materials for charging quartz clocks with a power rating of 1.5 V (30 min).

| S-EPMC7828437 | biostudies-literature

Enhanced cycle stability of a NiCo2S4 nanostructured electrode for supercapacitors fabricated by the alternate-dip-coating method.

Project description:Nanostructured nickel cobalt sulfide (NiCo2S4) electrodes are successfully fabricated using a simple alternate-dip-coating method. The process involves dipping a TiO2 nanoparticles-covered substrate in a nickel/cobalt precursor solution and sulfur precursor solution alternately at room temperature. The fabricated bimetallic sulfide electrode exhibits a synergetic improvement compensating for the disadvantages of the two single metal sulfide electrodes, i.e. the poor cycle stability of the nickel sulfide electrode and the low specific capacitance (Csp) of the cobalt sulfide electrode. The two capacitive properties are optimized by adjusting the ratio of nickel and cobalt concentrations in the metal precursor solution, reaching a Csp of 516 F g-1 at a current density of 1 mA cm-2, with its retention being 99.9% even after 2000 galvanostatic charge-discharge cycles.

| S-EPMC6124026 | biostudies-literature

Free-Standing rGO-CNT Nanocomposites with Excellent Rate Capability and Cycling Stability for Na2SO4 Aqueous Electrolyte Supercapacitors.

Project description:Facing the increasing demand for various renewable energy storage devices and wearable and portable energy storage systems, the research on electrode materials with low costs and high energy densities has attracted great attention. Herein, free-standing rGO-CNT nanocomposites have been successfully synthesized by a facile hydrothermal method, in which the hierarchical porous network nanostructure is synergistically assembled by rGO nanosheets and CNT with interlaced network distribution. The rGO-CNT composite electrodes with synergistic enhancement of rGO and CNT exhibit high specific capacitance, excellent rate capability, exceptional conductivity and outstanding long-term cycling stability, especially for the optimal rGO-CNT30 electrode. Applied to a symmetric supercapacitor systems (SSS) assembled with an rGO-CNT30 electrode and with 1 M Na2SO4 aqueous solution as the electrolyte, the SSS possesses a high energy density of 12.29 W h kg-1 and an outstanding cycling stability, with 91.42% of initial specific capacitance after 18,000 cycles. Results from these electrochemical properties suggest that the rGO-CNT30 nanocomposite electrode is a promising candidate for the development of flexible and lightweight high-performance supercapacitors.

| S-EPMC8229913 | biostudies-literature

Controllable Synthesis of Three-Dimensional β-NiS Nanostructured Assembly for Hybrid-Type Asymmetric Supercapacitors.

Project description:The process of energy storage in supercapacitors via the surface reaction of the electrode can lead to a significant perfecting of the electrochemical performance of supercapacitors, for developing the morphologies of materials and increasing the specific surface areas of the electrodes. Three-dimensional nickel sulfide (NiS) superstructures with nanomorphologies, viz. coral-like, urchin-like, flake-like, and flower-like, are synthesized through simple solvothermal methods, without any template. The nanostructured flower-like β-NiS demonstrates, not only a remarkable specific capacitance of 2425.89 F·g-1 at the current densities of 1 A·g-1, but also an excellent cycling stability of approximately 100% (at the current density of 10 A·g-1 over 5000 cycles). Moreover, the hybrid-type asymmetric supercapacitor, constructed from the flower-like β-NiS positive electrode and active carbon negative electrode, exhibits an energy density of 42.12 Wh·kg-1 at a power density of 28.8 kW·kg-1.

| S-EPMC7153257 | biostudies-literature

Facile synthesis of Al-doped NiO nanosheet arrays for high-performance supercapacitors.

Project description:Electrode material design is the key to the development of asymmetric supercapacitors with high electrochemical performances and stability. In this work, Al-doped NiO nanosheet arrays were synthesized using a facile hydrothermal method followed by a calcination process, and the synthesized arrays exhibited a superior pseudocapacitive performance, including a favourable specific capacitance of 2253 ± 105 F g-1 at a current density of 1 A g-1, larger than that of an undoped NiO electrode (1538 ± 80 F g-1). More importantly, the arrays showed a high-rate capability (75% capacitance retention at 20 A g-1) and a high cycling stability (approx. 99% maintained after 5000 cycles). The above efficient capacitive performance benefits from the large electrochemically active area and enhanced conductivity of the arrays. Furthermore, an assembled asymmetric supercapacitor based on the Al-doped NiO arrays and N-doped multiwalled carbon nanotube ones delivered a high specific capacitance of 192 ± 23 F g-1 at 0.4 A g-1 with a high-energy density of 215 ± 15 Wh kg-1 and power density of 21.6 kW kg-1. Additionally, the asymmetric device exhibited a durable cyclic stability (approx. 100% retention after 5000 cycles). This work with the proposed doping method will be beneficial to the construction of high-performance supercapacitor systems.

| S-EPMC6281943 | biostudies-literature

NiO Nanoparticles for Electrochemical Insulin Detection.

Project description:Diabetes mellitus represents one of the most widespread diseases in civilization nowadays. Since the costs for treating and diagnosing of diabetes represent several billions of dollars per year, a cheap, fast, and simple sensor for diabetes diagnosis is needed. Electrochemical insulin sensors can be considered as a novel approach for diabetes diagnosis. In this study, carbon electrode with electrodeposited NiO nanoparticles was selected as a suitable electrode material for insulin determination. The morphology and surface composition were studied by scanning electron microscopy (SEM), energy dispersive X-ray (EDX) spectroscopy, and X-ray photoelectron spectroscopy (XPS). For a better understanding of insulin determination on NiO-modified electrodes, the mechanism of electrochemical reaction and the kinetic parameters were studied. They were calculated from both voltammetric and amperometric measurements. The modified carbon electrode displayed a wide linear range from 600 nM to 10 µM, a low limit of detection of 19.6 nM, and a high sensitivity of 7.06 µA/µM. The electrodes were stable for 30 cycles and were able to detect insulin even in bovine blood serum. Additionally, the temperature stability of this electrode and its storage conditions were studied with appropriate outcomes. The above results show the high promise of this electrode for detecting insulin in clinical samples.

| S-EPMC8347614 | biostudies-literature

Unique insights into the design of low-strain single-crystalline Ni-rich cathodes with superior cycling stability.

Project description:Micro-sized single-crystalline Ni-rich cathodes are emerging as prominent candidates owing to their larger compact density and higher safety compared with poly-crystalline counterparts, yet the uneven stress distribution and lattice oxygen loss result in the intragranular crack generation and planar gliding. Herein, taking LiNi0.83Co0.12Mn0.05O2 as an example, an optimal particle size of 3.7 µm is predicted by simulating the stress distributions at various states of charge and their relationship with fracture free-energy, and then, the fitted curves of particle size with calcination temperature and time are further built, which guides the successful synthesis of target-sized particles (m-NCM83) with highly ordered layered structure by a unique high-temperature short-duration pulse lithiation strategy. The m-NCM83 significantly reduces strain energy, Li/O loss, and cationic mixing, thereby inhibiting crack formation, planar gliding, and surface degradation. Accordingly, the m-NCM83 exhibits superior cycling stability with highly structural integrity and dual-doped m-NCM83 further shows excellent 88.1% capacity retention.

| S-EPMC10927491 | biostudies-literature

Two-dimensional β-MoO<sub>3</sub>@C nanosheets as high-performance negative materials for supercapacitors with excellent cycling stability.

Project description:MoO3 has gained a great deal of attention as a promising electrode material in energy storage devices. In particular, the low dimensional MoO3 nanosheets coated with carbon layers are desirable electrode materials in supercapacitors. However, the fabrication or construction of β-MoO3 with a special morphology is difficult. Here, we report a simple solvothermal treatment method to synthesize two-dimensional β-MoO3@C (2D β-MoO3@C) nanosheets. When used as electrode materials for supercapacitors, the as-prepared material displays an ultra-long lifespan with a 94% retention ratio after 50 000 cycles at 2 A g-1. The excellent cycling stability is mainly attributed to the unique 2D nanosheet structure and the presence of the carbon layer on the surface of the nanosheet. Specifically, the presence of the carbon layer increases the electric conductivity of MoO3, which facilitates a good access point for electrolyte ions and short ion diffusion paths. In addition, MoO3 that has been coated with a carbon layer can maintain a good structural stability due to the carbon layer restricting the volume expansion of MoO3 during the charge procedure. We believe that the present work opens a new way for designing the 2D layered materials with unique architectures for supercapacitor applications.

| S-EPMC9053513 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data