Anomalous Loss of Stiffness with Increasing Reinforcement in a Photo-Activated Nanocomposite.

ABSTRACT: Hydrogels are commonly doped with stiff nanoscale fillers to endow them with the strength and stiffness needed for engineering applications. Although structure-property relations for many polymer matrix nanocomposites are well established, modeling the new generation of hydrogel nanocomposites requires the study of processing-structure-property relationships because subtle differences in chemical kinetics during their synthesis can cause nearly identical hydrogels to have dramatically different mechanical properties. The authors therefore assembled a framework to relate synthesis conditions (including hydrogel and nanofiller mechanical properties and light absorbance) to gelation kinetics and mechanical properties. They validated the model against experiments on a graphene oxide (GO) doped oligo (ethylene glycol) diacrylate (OEGDA), a system in which, in apparent violation of laws from continuum mechanics, doping can reduce rather than increase the stiffness of the resulting hydrogel nanocomposites. Both model and experiment showed a key role light absorbance-dominated gelation kinetics in determining nanocomposite mechanical properties in conjunction with nanofiller reinforcement, with the nanofiller's attenuation of chemical kinetics sometimes outweighing stiffening effects to explain the observed, anomalous loss of stiffness. By bridging the chemical kinetics and mechanics of nanocomposite hydrogels, the authors' modeling framework shows promise for broad applicability to design of hydrogel nanocomposites.

SUBMITTER: Zhu H

PROVIDER: S-EPMC8298289 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Embedding nanomaterials into polymer hydrogels enables the design of functional materials with tailored chemical, mechanical, and optical properties. Nanocapsules that protect interior cargo and disperse readily through a polymeric matrix have drawn particular interest for their ability to integrate chemically incompatible systems and to further expand the parameter space for polymer nanocomposite hydrogels. The properties of polymer nanocomposite hydrogels depend on the material composition and processing route, which were explored systematically in this work. The gelation kinetics of network-forming polymer solutions with and without silica-coated nanocapsules bearing polyethylene glycol (PEG) surface ligands were investigated using in situ dynamic rheology measurements. Network-forming polymers comprised either 4-arm or 8-arm star PEG with terminal anthracene groups, which dimerize upon irradiation with ultraviolet (UV) light. The PEG-anthracene solutions exhibited rapid gel formation upon UV exposure (365 nm); gel formation was observed as a crossover from liquid-like to solid-like behavior during in situ small-amplitude oscillatory shear rheology. This crossover time was non-monotonic with polymer concentration. Far below the overlap concentration (c/c* ≪ 1), spatially separated PEG-anthracene molecules were subject to forming intramolecular loops over intermolecular cross-links, thereby slowing the gelation process. Near the polymer overlap concentration (c/c* ∼ 1), rapid gelation was attributed to the ideal proximity of anthracene end groups from neighboring polymer molecules. Above the overlap concentration (c/c* > 1), increased solution viscosities hindered molecular diffusion, thereby reducing the frequency of dimerization reactions. Adding nanocapsules to PEG-anthracene solutions resulted in faster gelation than nanocapsule-free PEG-anthracene solutions with equivalent effective polymer concentrations. The final elastic modulus of nanocomposite hydrogels increased with nanocapsule volume fraction, signifying synergistic mechanical reinforcement by nanocapsules despite not being cross-linked into the polymer network. Overall, these findings quantify the impact of nanocapsule addition on the gelation kinetics and mechanical properties of polymer nanocomposite hydrogels, which are promising materials for applications in optoelectronics, biotechnology, and additive manufacturing.

Dataset Information

Anomalous Loss of Stiffness with Increasing Reinforcement in a Photo-Activated Nanocomposite.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets