The Synthesis of Poly(Vinyl Alcohol) Grafted with Fluorinated Protic Ionic Liquids Containing Sulfo Functional Groups.

ABSTRACT: There has been an ongoing need to develop polymer materials with increased performance as proton exchange membranes (PEMs) for middle- and high-temperature fuel cells. Poly(vinyl alcohol) (PVA) is a highly hydrophilic and chemically stable polymer bearing hydroxyl groups, which can be further altered. Protic ionic liquids (proticILs) have been found to be an effective modifying polymer agent used as a proton carrier providing PEMs' desirable proton conductivity at high temperatures and under anhydrous conditions. In this study, the novel synthesis route of PVA grafted with fluorinated protic ionic liquids bearing sulfo groups (-SO3H) was elaborated. The polymer functionalization with fluorinated proticILs was achieved by the following approaches: (i) the PVA acylation and subsequent reaction with fluorinated sultones and (ii) free-radical polymerization reaction of vinyl acetate derivatives modified with 1-methylimidazole and sultones. These modifications resulted in the PVA being chemically modified with ionic liquids of protic character. The successfully grafted PVA has been characterized using 1H, 19F, and 13C-NMR and FTIR-ATR. The presented synthesis route is a novel approach to PVA functionalization with imidazole-based fluorinated ionic liquids with sulfo groups.

SUBMITTER: Glinska P

PROVIDER: S-EPMC8306934 | biostudies-literature | 2021 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The Synthesis of Poly(Vinyl Alcohol) Grafted with Fluorinated Protic Ionic Liquids Containing Sulfo Functional Groups.

Glińska Patrycja P Wolan Andrzej A Kujawski Wojciech W Rynkowska Edyta E Kujawa Joanna J

Molecules (Basel, Switzerland) 20210708 14

There has been an ongoing need to develop polymer materials with increased performance as proton exchange membranes (PEMs) for middle- and high-temperature fuel cells. Poly(vinyl alcohol) (PVA) is a highly hydrophilic and chemically stable polymer bearing hydroxyl groups, which can be further altered. Protic ionic liquids (proticILs) have been found to be an effective modifying polymer agent used as a proton carrier providing PEMs' desirable proton conductivity at high temperatures and under anh ...[more]

PMID: 34299436

Similar Datasets

Project description:This study aimed to develop poly (vinyl alcohol) grafted glycidyl methacrylate/cellulose nanofiber (PVA-g-GMA/CNF) injectable hydrogels for meniscus tissue engineering. PVA-g-GMA is an interesting polymer for preparing cross-linking injectable hydrogels with UV radiation, but it has poor mechanical properties and low cell proliferation. In this study, CNF as a reinforcing agent was selected to improve mechanical properties and cell proliferation in PVA-g-GMA injectable hydro-gels. The effect of CNF concentration on hydrogel properties was investigated. Both PVA-g-GMA and PVA-g-GMA hydrogels incorporating 0.3, 0.5, and 0.7% (w/v) CNF can be formed by UV curing at a wavelength of 365 nm, 6 mW/cm2 for 10 min. All hydrogels showed substantial microporosity with interconnected tunnels, and a pore size diameter range of 3-68 µm. In addition, all hydrogels also showed high physicochemical properties, a gel fraction of 81-82%, porosity of 83-94%, water content of 73-87%, and water swelling of 272-652%. The water content and swelling of hydrogels were increased when CNF concentration increased. It is worth noting that the reduction of porosity in the hydrogels occurred with increasing CNF concentration. With increasing CNF concentration from 0.3% to 0.7% (w/v), the compressive strength and compressive modulus of the hydrogels significantly increased from 23 kPa to 127 kPa and 27 kPa to 130 kPa, respectively. All of the hydrogels were seeded with human cartilage stem/progenitor cells (CSPCs) and cultured for 14 days. PVA-g-GMA hydrogels incorporating 0.5% and 0.7% (w/v) CNF demonstrated a higher cell proliferation rate than PVA-g-GMA and PVA-g-GMA hydrogels incorporating 0.3% (w/v) CNF, as confirmed by MTT assay. At optimum formulation, 10%PVA-g-GMA/0.7%CNF injectable hydrogel met tissue engineering requirements, which showed excellent properties and significantly promoted cell proliferation, and has a great potential for meniscus tissue engineering application.

Dataset Information

The Synthesis of Poly(Vinyl Alcohol) Grafted with Fluorinated Protic Ionic Liquids Containing Sulfo Functional Groups.

Publications

The Synthesis of Poly(Vinyl Alcohol) Grafted with Fluorinated Protic Ionic Liquids Containing Sulfo Functional Groups.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets