High-Tribological-Performance Polymer Nanocomposites: An Approach Based on the Superlubricity State of the Graphene Oxide Agglomerates.

ABSTRACT: Here, nanocomposites of high-molecular-weight polyethylene (HMWPE) and HMWPE-UHMWPE (80/20 wt.%) containing a low amount of multilayer graphene oxide (mGO) (≤0.1 wt.%) were produced via twin-screw extrusion to produce materials with a higher tribological performance than UHMWPE. Due to the high viscosity of both polymers, the nanocomposites presented a significant concentration of agglomerates. However, the mechanical (tensile) and tribological (volumetric loss) performances of the nanocomposites were superior to those of UHMWPE. The morphology of the nanocomposites was investigated using differential scanning calorimetry (DSC), microtomography, and transmission electron microscopy (TEM). The explanation for these results is based on the superlubricity phenomenon of mGO agglomerates. It was also shown that the well-exfoliated mGO also contained in the nanocomposite was of fundamental importance as a mechanical reinforcement for the polymer. Even with a high concentration of agglomerates, the nanocomposites displayed tribological properties superior to UHMWPE's (wear resistance up to 27% higher and friction coefficient up to 57% lower). Therefore, this manuscript brings a new exception to the rule, showing that agglomerates can act in a beneficial way to the mechanical properties of polymers, as long as the superlubricity phenomenon is present in the agglomerates contained in the polymer.

SUBMITTER: Ferreira EHC

PROVIDER: S-EPMC8309333 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Model Approach to Thermal Conductivity in Hybrid Graphene-Polymer Nanocomposites.

Project description:The thermal conductivity of epoxy nanocomposites filled with self-assembled hybrid nanoparticles composed of multilayered graphene nanoplatelets and anatase nanoparticles was described using an analytical model based on the effective medium approximation with a reasonable amount of input data. The proposed effective thickness approach allowed for the simplification of the thermal conductivity simulations in hybrid graphene@anatase TiO2 nanosheets by including the phenomenological thermal boundary resistance. The sensitivity of the modeled thermal conductivity to the geometrical and material parameters of filling particles and the host polymer matrix, filler's mass concentration, self-assembling degree, and Kapitza thermal boundary resistances at emerging interfaces was numerically evaluated. A fair agreement of the calculated and measured room-temperature thermal conductivity was obtained.

| S-EPMC10647783 | biostudies-literature

Tribological Performance Investigation of a Commercial Engine Oil Incorporating Reduced Graphene Oxide as Additive.

Project description:We investigated the tribological behavior of commercialized, fully synthetic engine oil upon the incorporation of reduced graphene oxide in seven different concentrations between 0.01 and 0.2 wt %. Stability of the prepared samples was assessed by turbidimetry and dynamic light scattering measurements, and their tribological properties through a reciprocating tribometer, using a steel ball on special cut steel blocks. The addition of 0.02 wt % of reduced graphene oxide led to an improvement of the tribological behavior compared to the pristine engine oil, by significantly lowering the friction coefficient by 5% in the boundary lubrication regime. Both the surfaces and the reduced graphene oxide additive were thoroughly characterized by microscopic and optical spectroscopy techniques. We also verified that a protective layer was formed between the worn surfaces, due to the presence of reduced graphene oxide. Carbon accumulation and various additive elements such as Ca, Zn, S and P were detected on the rubbing surfaces of both the ball and the block through energy-dispersive X-ray spectroscopy. Finally, it was shown that the wear scar diameter on the surface of the steel ball was lower by 3%, upon testing the engine oil sample containing reduced graphene oxide at concentration 0.02 wt %, compared to the control sample.

| S-EPMC7913578 | biostudies-literature

High-Performance PEDOT:PSS/Hexamethylene Diisocyanate-Functionalized Graphene Oxide Nanocomposites: Preparation and Properties.

Project description:Graphene oxide (GO) has emerged as an ideal filler to reinforce polymeric matrices owing to its large specific surface area, transparency, flexibility, and very high mechanical strength. Nonetheless, functionalization is required to improve its solubility in common solvents and expand its practical uses. In this work, hexamethylene diisocyanate (HDI)-functionalized GO (HDI-GO) has been used as filler of a conductive polymer matrix, poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS). The nanocomposites have been prepared via a simple solution casting method, and have been characterized by scanning electron microscopy (SEM), UV⁻Vis and Raman spectroscopies, X-ray diffraction (XRD), thermogravimetric analysis (TGA), tensile tests, and four-point probe measurements to get information about how the HDI-GO functionalization degree (FD) and the HDI-GO concentration in the nanocomposite influence the final properties. SEM analysis showed a very homogenous dispersion of the HDI-GO nanosheets with the highest FD within the matrix, and the Raman spectra revealed the existence of very strong HDI-GO-PEDOT:PSS interactions. A gradual improvement in thermal stability was found with increasing HDI-GO concentration, with only a small loss in transparency. A reduction in the sheet resistance of PEDOT:PSS was found at low HDI-GO contents, whilst increasing moderately at the highest loading tested. The nanocomposites showed a good combination of stiffness, strength, ductility, and toughness. The optimum balance of properties was attained for samples incorporating 2 and 5 wt % HDI-GO with the highest FD. These solution-processed nanocomposites show considerably improved performance compared to conventional PEDOT:PSS nanocomposites filled with raw GO, and are highly suitable for applications in various fields, including flexible electronics, thermoelectric devices, and solar energy applications.

| S-EPMC6403542 | biostudies-literature

The Impacts of Moisture and Ultraviolet Light on the Degradation of Graphene Oxide/Polymer Nanocomposites.

Project description:The extent to which hydrophilic GO nanofillers regulate polymer degradation during exposure to a combination of ultraviolet (UV) radiation and moisture is presently unknown. Accordingly, this study systematically evaluated the effect of GO on polymer degradability under both humid UV and dry UV conditions. Both GO accumulation at the polymer nanocomposite (PNC) surface and GO release following degradation were also investigated. Different mass loadings of GO were incorporated into waterborne polyurethane (WBPU), a commonly used exterior coating, and the resulting GO/WBPU nanocomposites were exposed to precisely controlled accelerated weathering conditions using the NIST Simulated Photodegradation via High Energy Radiant Exposure (SPHERE) device. Thickness loss and infrared spectroscopy measurements indicated GO slightly improved the durability of WBPU under dry UV conditions but not under humid UV conditions. Raman spectroscopy, scanning electron microscopy, and atomic force microscopy modulus measurements indicated that GO accumulation occurred at and near the PNC surface under both conditions but to a more rapid extent under humid UV conditions. Minimal GO release occurred under dry UV conditions as measured with Raman spectroscopy of aqueous run-off from a simulated rain spray applied to degraded PNCs. In contrast, PNC surface transformations under humid UV conditions suggested that GO release occurred.

| S-EPMC7836096 | biostudies-literature

Enhanced Thermal Conductivity of Polyamide-Based Nanocomposites Containing Graphene Oxide Sheets Decorated with Compatible Polymer Brushes.

Project description:Polyamide-based nanocomposites containing graphene platelets decorated with poly(acrylamide) brushes were prepared and characterized. The brushes were grafted from the surface of graphene oxide (GO), a thermally conductive additive, using atom transfer radical polymerization, which led to the formation of the platelets coated with covalently tethered polymer layers (GO_PAAM), accounting for ca. 31% of the total mass. Polyamide-6 (PA6) nanocomposites containing 1% of GO_PAAM were formed by extrusion followed by injection molding. The thermal conductivity of the nanocomposite was 54% higher than that of PA6 even for such a low content of GO. The result was assigned to strong interfacial interactions between the brushes and PA6 matrix related to hydrogen bonding. Control nanocomposites containing similarly prepared GO decorated with other polymer brushes that are not able to form hydrogen bonds with PA6 revealed no enhancement of the conductivity. Importantly, the nanocomposite containing GO_PAAM also demonstrated larger tensile strength without deteriorating the elongation at break value, which was significantly decreased for the other coated platelets. The proposed approach enhances the interfacial interactions thanks to the covalent tethering of dense polymer brushes on 2D fillers and may be used to improve thermal properties of other polymer-based nanocomposites with simultaneous enhancement of their mechanical properties.

| S-EPMC7914667 | biostudies-literature

SnO2/Graphene Nanoplatelet Nanocomposites: Solid-State Method Synthesis With High Ethanol Gas-Sensing Performance.

Project description: Not available

| S-EPMC6095040 | biostudies-literature

β-Cyclodextrin⁻Hyaluronic Acid Polymer Functionalized Magnetic Graphene Oxide Nanocomposites for Targeted Photo-Chemotherapy of Tumor Cells.

Project description:A multifunctional targeted drug delivery platform (CDHA⁻MGO) has been successfully constructed by grafting β-cyclodextrin⁻hyaluronic acid polymers (CDHA) to Fe₃O₄⁻graphene oxide (MGO). The obtained CDHA⁻MGO nanocomposite has good water-dispersibility, easy magnetic separation, high near-infrared (NIR) photothermal heating, and excellent biocompatibility. The β-cyclodextrin-hyaluronic acid polymers efficaciously enhance the doxorubicin (DOX) loading amount up to 485.43 mg·g-1. Meanwhile, the Fe₃O₄⁻graphene oxide provides a facile photothermal response mechanism to handle the NIR-triggered release of DOX in weak acidic solvent environments. Significantly, the DOX-loaded nanocomposite (DOX@CDHA⁻MGO) has displayed CD44 receptor-mediated active targeting recognition and chemo-photothermal synergistic therapy of hepatoma cells. These findings suggest that the as-prepared drug delivery platform would be of valuable potential for cancer-targeted photo-chemotherapy.

| S-EPMC6401939 | biostudies-literature

Enhanced Osteogenesis by Reduced Graphene Oxide/Hydroxyapatite Nanocomposites.

Project description:Recently, graphene-based nanomaterials, in the form of two dimensional substrates or three dimensional foams, have attracted considerable attention as bioactive scaffolds to promote the differentiation of various stem cells towards specific lineages. On the other hand, the potential advantages of using graphene-based hybrid composites directly as factors inducing cellular differentiation as well as tissue regeneration are unclear. This study examined whether nanocomposites of reduced graphene oxide (rGO) and hydroxyapatite (HAp) (rGO/HAp NCs) could enhance the osteogenesis of MC3T3-E1 preosteoblasts and promote new bone formation. When combined with HAp, rGO synergistically promoted the spontaneous osteodifferentiation of MC3T3-E1 cells without hindering their proliferation. This enhanced osteogenesis was corroborated from determination of alkaline phosphatase activity as early stage markers of osteodifferentiation and mineralization of calcium and phosphate as late stage markers. Immunoblot analysis showed that rGO/HAp NCs increase the expression levels of osteopontin and osteocalcin significantly. Furthermore, rGO/HAp grafts were found to significantly enhance new bone formation in full-thickness calvarial defects without inflammatory responses. These results suggest that rGO/HAp NCs can be exploited to craft a range of strategies for the development of novel dental and orthopedic bone grafts to accelerate bone regeneration because these graphene-based composite materials have potentials to stimulate osteogenesis.

| S-EPMC4685392 | biostudies-literature

Effect of thiophene S on the enhanced ORR electrocatalytic performance of sulfur-doped graphene quantum dot/reduced graphene oxide nanocomposites.

Project description:In this study, a novel and simple hydrothermal method was developed to synthesize sulfur-doped graphene quantum dots (S-GQDs) with a diameter of 1-6 nm and S-GQD/reduced graphene oxide hybrids. The results indicated that an increase in the sulfur content led to superior ORR electrocatalytic activity. Moreover, it is found that thiophene S plays a significant role in the electrocatalytic activity. In addition, the average electron transfer number depends on the content of thiophene S. It is believed that the proposed synthesis strategy is a general and effective method for designing high-performance metal-free electrocatalytic materials.

| S-EPMC9080651 | biostudies-literature

Enhanced Electrochemical performance at high temperature of Cobalt Oxide/Reduced Graphene Oxide Nanocomposites and its application in lithium-ion batteries.

Project description:We report a microwave irradiation method for the preparation of reduced graphene oxide (RGO) based Co3O4 nanocomposites as anodes for lithium-ion (li-ion) batteries. The Co3O4/RGO nanocomposites displayed good electrochemical behavior as anodic materials for li-ion batteries when compared to pure Co3O4. The Co3O4/RGO nanocomposites with low RGO content resulted in stable electrochemical performance with 100% coulombic efficiency at a high current density of 500?mA/g for 50 cycles. The enhanced capacity of the Co3O4/RGO nanocomposites is due to the incorporation of RGO, which resulted in a four times larger surface area than that of Co3O4. This increased surface area could facilitate the absorption of more lithium ions, resulting in excellent electrochemical performance. Interestingly, the novelty of this work is that the designed li-ion batteries showed stable electrochemical performance even at a high temperature of 100?°C, which might be useful for rechargeable battery applications in a wide temperature range.

| S-EPMC6328569 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data