Synthesis, Structure, Crystallization and Mechanical Properties of Isodimorphic PBS-ran-PCL Copolyesters.

ABSTRACT: Isodimorphic behavior is determined by partial inclusion of comonomer segments within the crystalline structure and arises from the comparatively similar repeating chain units of the parental homopolymers. Isodimorphic random copolymers are able to crystallize irrespective of their composition and exhibit a pseudo-eutectic behavior when their melting point values are plotted as a function of comonomer content. At the pseudo-eutectic point or region, two crystalline phases can coexist. On the right-hand and the left-hand side of the pseudo-eutectic point or region, only one single crystalline phase can form which is very similar to the crystalline structures of the parent homopolymers. This article aims to study the synthesis method, structure, crystallization behavior and mechanical properties of isodimorphic random PBS-ran-PCL copolyesters. Moreover, this study provides a comprehensive analysis of our main recent results on PBS-ran-PCL random copolyesters with three different molecular weights. The results show that the comonomer composition and crystallization conditions are the major factors responsible for the crystalline morphology, crystallization kinetics and mechanical performance of isodimorphic random copolyesters. Our studies demonstrate that in the pseudo-eutectic region, where both crystalline phases can coexist, the crystallization conditions determine the crystalline phase or phases of the copolymer. The relationships between the comonomer composition and mechanical properties are also addressed in this work.

SUBMITTER: Safari M

PROVIDER: S-EPMC8309441 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:BackgroundScaffolds are of great importance in tissue engineering applications as they provide a mechanically supportive environment for cellular activity, which is particularly necessary for hard tissues such as bone. Notably, the mechanical properties of a scaffold vary with differing design parameters such as those related to scaffold height and internal structure. Thus, the present study aimed to explore the relationship between design parameters and mechanical properties of composite polycaprolactone (PCL) and nano-hydroxyapatite (nHAp) scaffolds fabricated by three-dimensional (3D) printing.MethodsWe designed and printed scaffolds with different internal structures (lattice and staggered) and varying heights (4, 6, 8 and 10 layers), and consistent porosity (50%) for the purpose of comparison. Then, we examined the scaffold microstructure (pore size and penetration between layers) using scanning electron microscopy (SEM) and mechanical properties (elastic modulus and yield strength) using compressive testing.ResultsOur results illustrated that the microstructural parameters were related to scaffold design. At higher heights, pore size increased while penetration between layers decreased; thus, mechanical properties were affected. Results of mechanical testing demonstrated that for lattice scaffolds, elastic modulus was similar for 6 vs 4, and 8 vs 4 layers but ~33% lower for 10 layers vs 4 layers. Similarly, yield strength was comparable for 6 vs 4, and 8 vs 4 layers but ~27% lower for 10 layers vs 4 layers. With staggered scaffolds, when compared to 4-layer results, elastic modulus was similar for 6 layers but was ~43% lower for 8 layers and ~38% lower for 10 layers. Staggered scaffolds had ~38%, ~51%, and ~76% lower yield strength when the number of layers were increased from 4 to 6, 8, and 10 layers, respectively. When comparing lattice and staggered scaffolds with the same layer number, elastic modulus was similar, apart from 8-layer scaffolds where the staggered design was ~42% lower than lattice. Yield strength was similar between 4-layer staggered and lattice scaffolds, while staggered scaffolds with 6, 8, and 10 number of layers showed ~43%, ~45%, ~68% lower strength, respectively, than those found in lattice scaffolds with the same layer numbers.ConclusionsMechanical properties of 3D printed scaffolds depended on scaffold height for both lattice and staggered internal structures. Staggered scaffolds had lower mechanical properties than the lattice scaffolds with the same height and were more sensitive to the change in scaffold height. Taken together, lattice scaffolds demonstrated the advantages of more stable mechanical properties over staggered scaffolds. Also, scaffolds with lower height were more promising in terms of mechanical properties compared to scaffolds with greater height.

Dataset Information

Synthesis, Structure, Crystallization and Mechanical Properties of Isodimorphic PBS-ran-PCL Copolyesters.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets