Temperate UV-Accelerated Weathering Cycle Combined with HT-GPC Analysis and Drop Point Testing for Determining the Environmental Instability of Polyethylene Films.
Ontology highlight
ABSTRACT:
SUBMITTER: Moreira C
PROVIDER: S-EPMC8309575 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:Accelerated UV-weathering cycles are predominately used for evaluating the durability of plastic materials, particularly polyethylene (PE) films. The point of failure for this testing is usually the loss of a physical property, such as the loss of tensile strength over time. For plastics designed to be instable under environmental conditions, the accelerated weathering cycles are yet to be defined and their correlation to outdoor exposure has yet to be made. This study demonstrates the utility of a newly defined temperate accelerated UV-weathering cycle, recently codified in the British Standard PAS 9017:2020. In addition, the effectiveness of the laboratory weathering cycle has been correlated to real-world outdoor exposure through simultaneous testing of the same samples at a specialist outdoor exposure site in Florida. The utility of the testing methodology and the performance of the polyethylene samples was demonstrated through the use of High Temperature Gel Permeation Chromatography (HT-GPC) analysis. The data led to a detailed insight into the physico-chemical changes occurring in the PE films upon exposure to environmental stimuli. By comparison, and surprisingly, the techniques employed appear to provide an insight into the processes in which secondary micro-particles of PE are formed from macro-polyethylene samples. The temperate accelerated UV-weathering cycle over 14 days demonstrated an approximate correlation to 90 days of outdoor exposure in Florida for the PE film studied.
| S-EPMC7920266 | biostudies-literature
Project description:Samples of polycarbonate (PC), poly(butylene terephthalate) (PBT), a PC/PBT blend, and poly(styrene-co-acrylonitrile) (SAN), all containing 3% TiO2 (by mass), were exposed in the NIST (National Institutes of Standards and Technology) SPHERE (Simulated Photodegradation via High Energy Radiant Exposure) to determine the effects of UV intensity (irradiance), temperature, relative humidity (RH), and UV wavelength on yellowing and gloss loss. There was no effect of irradiance, such that the samples obeyed reciprocity and doubling the irradiance doubled the rate of degradation. The activation energy for yellowing was determined to be ≈ 20 kJ/mol for PC, PC/PBT, and SAN and ≈ 16 kJ/mol for PBT. The activation energy for gloss loss was determined to be 9-16 kJ/mol. Thus, a 10 °C increase in temperature results in a 20%-30% increase in degradation rate. There was no consistent effect of RH on PC or PC/PBT yellowing or gloss loss. SAN degraded rapidly under dry conditions but showed little effect for RH > 10%. PBT lost gloss more slowly under dry conditions but displayed no RH effect with yellowing. Shorter wavelength UV had a greater effect on PC/PBT compared to PC or PBT.
| S-EPMC7539635 | biostudies-literature
Project description:The biocatalytic degradation of polyethylene terephthalate (PET) emerged recently as a promising alternative plastic recycling method. However, limited activity of previously known enzymes against post-consumer PET materials still prevents the application on an industrial scale. In this study, the influence of ultraviolet (UV) irradiation as a potential pretreatment method for the enzymatic degradation of PET was investigated. Attenuated total reflection Fourier transform infrared (ATR-FTIR) and 1H solution nuclear magnetic resonance (NMR) analysis indicated a shortening of the polymer chains of UV-treated PET due to intra-chain scissions. The degradation of UV-treated PET films by a polyester hydrolase resulted in significantly lower weight losses compared to the untreated sample. We also examined site-specific and segmental chain dynamics over a time scale of sub-microseconds to seconds using centerband-only detection of exchange, rotating-frame spin-lattice relaxation (T 1 ? ), and dipolar chemical shift correlation experiments which revealed an overall increase in the chain rigidity of the UV-treated sample. The observed dynamic changes are most likely associated with the increased crystallinity of the surface, where a decreased accessibility for the enzyme-catalyzed hydrolysis was found. Moreover, our NMR study provided further knowledge on how polymer chain conformation and dynamics of PET can mechanistically influence the enzymatic degradation.
| S-EPMC7199389 | biostudies-literature
Project description:Mycelium, as the root of fungi, is composed of filamentous strands of fine hyphae that bind discrete substrate particles into a block material. With advanced processing, dense mycelium-bound composites (DMCs) resembling commercial particleboards can be formed. However, their mechanical properties and performance under the working conditions of particleboards are unknown. Here, we show how weathering conditions affect the DMC stress and elastic modulus. DMC was made using Ganoderma lucidum mycelium grown on a substrate of sawdust and empty fruit bunch. The DMC was then subjected to weathering under tropical conditions over 35 days and tested under flexural, tensile, and compressive loading with reference to international standards. After exposure to specified weathering conditions, the maximum stress in flexure, tension, and compression decreased substantially. The addition of a protective coating improved the resistance of DMC to weathering conditions; however, the difference between coated and uncoated samples was only found to be statistically significant in tensile strength.
| S-EPMC8586338 | biostudies-literature
Project description:Applications of cyanoacrylate monomers are generally limited to adhesives/glues (instant or superglues) and forensic sciences. They tend to polymerize rapidly into rigid structures when exposed to trace amounts of moisture. Transforming cyanoacrylate monomers into transparent polymeric films or coatings can open up several new applications, as they are biocompatible, biodegradable and have surgical uses. Like other acrylics, cyanoacrylate polymers are glassy and rigid. To circumvent this, we prepared transparent cyanoacrylate films by solvent casting from a readily biodegrade solvent, cyclopentanone. To improve the ductility of the films, poly(propylene carbonate) (PPC) biopolymer was used as an additive (maximum 5 wt.%) while maintaining transparency. Additionally, ductile films were functionalized with caffeic acid (maximum 2 wt.%), with no loss of transparency while establishing highly effective double functionality, i.e., antioxidant effect and effective UV-absorbing capability. Less than 25 mg antioxidant caffeic acid release per gram film was achieved within a 24-h period, conforming to food safety regulations. Within 2 h, films achieved 100% radical inhibition levels. Films displayed zero UVC (100-280 nm) and UVB (280-315 nm), and ~15% UVA (315-400 nm) radiation transmittance comparable to advanced sunscreen materials containing ZnO nanoparticles or quantum dots. Transparent films also exhibited promising water vapor and oxygen barrier properties, outperforming low-density polyethylene (LPDE) films. Several potential applications can be envisioned such as films for fatty food preservation, biofilms for sun screening, and biomedical films for free-radical inhibition.
| S-EPMC7564323 | biostudies-literature
Project description:Nano-fillers are increasingly incorporated into polymeric materials to improve the mechanical, barrier or other matrix properties of nanocomposites used for consumer and industrial applications. However, over the life cycle, these nanocomposites could degrade due to exposure to environmental conditions, resulting in the release of embedded nanomaterials from the polymer matrix into the environment. This paper presents a rigorous study on the degradation and the release of nanomaterials from food packaging composites. Films of nano-clay-loaded low-density polyethylene (LDPE) composite for food packaging applications were prepared with the spherilene technology and exposed to accelerated weathering of ultraviolet (UV) irradiation or low concentration of ozone at 40 °C. The changes in the structural, surface morphology, chemical and physical properties of the films during accelerated weathering were investigated. Qualitative and quantitative changes in properties of pristine and aged materials and the release of nano-clay proceeded slowly until 130 hr irradiation and then accelerated afterward resulting complete degradation. Although nano-clay increased the stability of LDPE and improved thermal and barrier properties, they accelerated the UV oxidation of LDPE. With increasing exposure to UV, the surface roughness, chemiluminescence index, and carbonyl index of the samples increased while decreasing the intensity of the wide-angle X-ray diffraction pattern. Nano-clay particles with sizes ranging from 2-8 nm were released from UV and ozone weathered composite. The concentrations of released nanoparticles increased with an increase in aging time. Various toxicity tests, including reactive oxygen species generation and cell activity/viability were also performed on the released nano-clay and clay polymer. The released nano-clays basically did not show toxicity. Our combined results demonstrated the degradation properties of nano-clay particle-embedded LDPE composites toxicity of released nano-clay particles to A594 adenocarcinomic human alveolar basal epithelial cells was observed, which will help with future risk based-formulations of exposure.
| S-EPMC5716355 | biostudies-literature
Project description:In the past five decades, reinforced coated textile membranes have been used increasingly as building materials, which are environmentally exposed. Thus, their weathering degradation over the service life must be taken into account in design, fabrication, and construction. Regarding such structural membranes, PVC (polyvinylchloride)-coated PET (polyethylene terephthalate) fabric is one of the most common commercially available types. This paper focuses on the backbone of it, i.e., the woven PET fabric. Herein, weathering of uncoated PET, as the load-bearing component of the composite PET-PVC, was studied. This study assessed the uniaxial tensile strength degradation mechanisms of uncoated PET fabric during artificial accelerated weathering tests. For this purpose, exploratory data analysis was carried out to analyze the chemical and physical changes which were traced by Fourier transform infrared spectroscopy and molecular weight measurements. Finally, with the help of degradation mechanisms determined from the aforementioned evaluations, a degradation pathway network model was constructed. With that, the relationship between applied stress, mechanistic variables, structural changes, and performance level responses (tensile strength degradation) was assessed.
| S-EPMC7866265 | biostudies-literature
Project description:The effect of accelerated weathering on poly(lactic acid) (PLA) and a PLA nanocomposite with rutile titanium (IV) dioxide (rutile-TiO2) was investigated. The accelerated weathering test applied consecutive steps of ultraviolet (UV) (at 340 nm and 0.76 W m-2 irradiance) and moisture at 50 °C for 2000 h, following the ASTM D4329 standard. The morphology, chemical structure, molecular weight, crystallization, as well as mechanical and thermal properties were thoroughly studied. Samples were characterized after 500 h, 1000 h and 2000 h exposure. Different degradation mechanisms were proposed to happen during the weathering exposure and confirmed based on the experimental data. The PLA and PLA/TiO2 surfaces presented holes and increasing roughness over the exposure time. The molecular weight of the weathered samples decreased due to chain scission during the degradation processes. Thermal stability decreased in the presence of TiO2 and a double melting peak was observed for the PLA/TiO2 nanocomposite. A general improvement in the mechanical properties of the PLA/TiO2 nanocomposite was observed over time during the accelerated weathering analysis up to 1000 h of exposure time. After 2000 h of weathering exposure, the PLA and PLA/TiO2 became extremely brittle and lost their ductile properties. This was ascribed to a significant increase in the degree of crystallinity upon weathering, which was accelerated in the presence of TiO2. Atomic force microscopy (AFM) using amplitude modulation-frequency modulation (AM-FM) tool confirmed the mechanical changes in the surface area of the PLA samples after accelerated weathering exposure. The stiffness and Young's modulus achieved higher values than the unweathered ones up to 1000 h of exposure time. The changes in the physical and chemical properties of PLA/TiO2 over the ageing time confirm the photocatalytic activity of rutile-TiO2.
| S-EPMC7285358 | biostudies-literature
Project description:The present study focuses on the effect of two novel carbon fibre surface treatments, electropolymerisation of methacrylic acid and air pressure plasma, on the mechanical properties and structural integrity of carbon-fibre-reinforced composites under operational conditions. Extensive mechanical testing was applied, both in nano- and macro-scale, to assess the performance of the composites and the interphase properties after ultraviolet/humidity weathering. The results of the mechanical assessment are supported by structure, surface, and chemistry examination in order to reveal the failure mechanism of the composites. Composites with the electropolymerisation treatment exhibited an increase of 11.8% in interlaminar shear strength, while APP treatment improved the property of 23.9%, rendering both surface treatments effective in increasing the fibre-matrix adhesion. Finally, it was proven that the developed composites can withstand operational conditions in the long term, rendering them suitable for a wide variety of structural and engineering applications.
| S-EPMC8658828 | biostudies-literature
Project description:Temperate forests provide favorable conditions for carbonate bedrock weathering as the soil CO2 partial pressure is high and soil water is regularly available. As a result of weathering, abiotic CO2 can be released and contribute to the soil CO2 efflux. We used the distinct isotopic signature of the abiotic CO2 to estimate its contribution to the total soil CO2 efflux. Soil cores were sampled from forests on dolomite and limestone and were incubated under the exclusion of atmospheric CO2. Efflux and isotopic signatures of CO2 were repeatedly measured of cores containing the whole mineral soil and bedrock material (heterotrophic respiration + CO2 from weathering) and of cores containing only the mineral top-soil layer (A-horizon; heterotrophic respiration). An aliquot of the cores were let dry out during incubation to assess effects of soil moisture. Although the ?13C values of the CO2 efflux from the dolomite soil cores were within a narrow range (A-horizon -26.2 ± 0.1 ‰; whole soil profile wet -25.8 ± 0.1 ‰; whole soil profile dry -25.5 ± 0.1 ‰) the CO2 efflux from the separated A-horizons was significantly depleted in 13C when compared to the whole soil profiles (p = 0.015). The abiotic contribution to the total CO2 efflux from the dolomite soil cores was 2.0 ± 0.5 % under wet and 3.4 ± 0.5 % under dry conditions. No abiotic CO2 efflux was traceable from the limestone soil cores. An overall low contribution of CO2 from weathering was affirmed by the amount and 13C signature of the leached dissolved inorganic carbon (DIC) and the radiocarbon signature of the soil CO2 efflux in the field. Together, our data point towards no more than 1-2 % contribution of abiotic CO2 to the growing season soil CO2 efflux in the field.
| S-EPMC4512732 | biostudies-literature