Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.

ABSTRACT: Degradation in the polymeric insulators is caused due to the environmental stresses. The main aim of this paper is to explore the improved aging characteristics of hybrid samples by adding nano/micro silica in High Temperature Vulcanized Silicone Rubber (HTV-SiR) under long term accelerated aging conditions for 9000 hours. As HTV-SiR is unable to sustain environmental stresses for a long time, thus a long term accelerated aging behavior is an important phenomenon to be considered for field application. The aging characteristics of nano/micro filled HTV-SiR are analyzed by using techniques such as Scanning Electron Microscopy (SEM), Leakage Current (LC), Fourier Transform Infrared Microscopy (FTIR), Hydrophobicity Classification (HC), and breakdown strength for the aging time of 9000 hours. FTIR and leakage currents are measured after every cycle. All the co-filled samples revealed escalated aging characteristics as compared to the neat sample except the SN8 sample (8% nano-silica+20% micro-silica) after 9000 hours of aging. The highest loading of 6% and 8% nano-silica with 20% micro-silica do not contribute to the improved performance when compared with the neat and hybrid samples. However, from the critical experimental analysis, it is deduced that SN2 sample (2% nano-silica+20% micro-silica) is highly resistant to the long term accelerated aging conditions. SN2 has no cracks, lower loss percentages in the important FTIR absorption peaks, higher breakdown strength and superior HC after aging as compared to the unfilled and hybrid samples.

SUBMITTER: Rashid A

PROVIDER: S-EPMC8318273 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Although natural rubber was regarded as biodegradable, the degradation is a time-consuming process that could take weeks or months for any degradation or substantial weight loss to be observable, resulting in the need for novel processes/methods to accelerate the rubber degradation. As a result, this work investigated the potential utilization of chitosan (CS) as a biodegradation enhancer for radiation-vulcanized natural rubber latex (R-VNRL) and hybrid radiation and peroxide-vulcanized natural rubber latex (RP-VNRL) composites, with varying CS contents (0, 2, 4, or 6 phr). The R-VNRL samples were prepared using 15 kGy gamma irradiation, while the RP-VNRL samples were prepared using a combination of 0.1 phr tert-butyl hydroperoxide (t-BHPO) and 10 kGy gamma irradiation. The properties investigated were biodegradability in the soil and the morphological, chemical, mechanical, and physical properties, both before and after undergoing thermal aging. The results indicated that the biodegradability of both the R-VNRL and RP-VNRL composites was enhanced with the addition of CS, as evidenced by increases in the percentage weight loss (% weight loss) after being buried in soil for 8 weeks from 6.5 ± 0.1% and 6.4 ± 0.1% in a pristine R-VNRL and RP-VNRL samples, respectively, to 10.5 ± 0.1% and 10.2 ± 0.1% in 6-pph CS/R-VNRL and 6-pph CS/RP-VNRL composites, respectively, indicating the biodegradation enhancement of approximately 60%. In addition, the results revealed that the addition of CS could increase the value of tensile modulus by 119%, while decrease the values of tensile strength and elongation at break by 50% and 43%, respectively, in the specimens containing 6-phr CS. In terms of the color appearances, the samples were lighter and yellower after the addition of CS, as evidenced by the noticeably increased L* and b* values, based on the CIE L*a*b* color space system. Furthermore, the investigation into the effects of thermal aging showed that the overall tensile properties for both curing systems were reduced, while varying degrees of color change were observed, with the pristine R-VNRL and RP-VNRL samples having more pronounced degradation/changes for both properties. In conclusion, the overall results suggested that CS had great potential to be applied as a bio-filler in R-VNRL and RP-VNRL composites to effectively promote the biodegradability, environmental friendliness, and resistance to thermal degradation of the composites.

Project description:Photocatalytic oxidation purposes an economical and environmental friendly process to remove benzene from indoor air pollution. However, the process efficiency is primarily dependent on catalytic-film. The main purpose of this study is to synthesize pre-vulcanized latex impregnated with TiO2 (PVL-TiO2 thin film) from natural rubber to be used in photo-catalytic oxidation for benzene removal in a reactor. PVL-TiO2 thin films were synthesized for 3 different dosages of TiO2, which were 5%, 15%, and 25% The outcome of this study offers the new application of modified natural rubber in terms of environmental and health care protection. Morphology of the synthesized films was analyzed by SEM. The results showed that TiO2 particles could be well dispersed all over the surface of the film, in which the best distribution could be found for the PVL-TiO2 15% thin film. Tensile stress of the films was analyzed using ASTM D412. Results showed that the stress of the films got higher with the increasing amount of TiO2 content. This indicates that TiO2 strengthened the PVL-TiO2 film because the uniformly distribution of TiO2 on the inner surface increased the strength of the film. The decomposition of PVL and PVL-TiO2 thin films was analyzed using thermo gravimetric analysis. The maximum weight loss rates in the range of 1.536-1.145 wt%/°C attained at between 380 - 382 °C TiO2 particles enhanced thermal stability of PVL-TiO2 thin films due to the high decomposition temperature of its properties and also acted as barrier for the heat transfer of the films. Specific surface area (SSA) of the films was analyzed using Brunauer-Emmett-Teller. Specific surface area increased as the increasing content of TiO2, which corresponded to the morphology analysis by SEM. The analysis of chemical functional group of thin films was performed using ATR-FTIR. The results of Crystal identification using XRD clearly showed good attachment of rutile TiO2 on the films. Finally, results of absorbance spectrums and band gap energy showed that PVL not only peg TiO2 particles but also reducing band gap energy which induced by S and ZnO. Therefore, PVL-TiO2 thin films could be used under visible light condition. The films were then used in the study of benzene removal in annular reactor. The highest removal efficiency (83%)for the PVL-TiO2 15% thin film was obtained. Comparing to the maximum removal efficiency for PVL film (28%), roughly 60% increase in efficiency was achieved. The PCO kinetics were well fit by a first order Langmuir-Hinshelwood model. The calculation of oxidation rate and percentage of residual intermediates indicated that accumulation of residual intermediates can occur on the active site and the gas phase, resulting in increasing of residual intermediates. The successful synthesis of PVL-TiO2 thin film provides new opportunity to use natural rubber in terms of environmental and health care protection.

Dataset Information

Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets