A Special Additive Enables All Cations and Anions Passivation for Stable Perovskite Solar Cells with Efficiency over 23.

ABSTRACT: Passivating undercoordinated ions is an effective way to reduce the defect densities at the surface and grain boundaries (GBs) of perovskite materials for enhanced photovoltaic performance and stability of perovskite solar cells (PSCs). Here, (BBF) complex is chosen as a multifunctional additive, which contains both C₇H₉N and BF₃ groups working as Lewis base and Lewis acid, respectively, can bond with Pb²⁺/I^- and FA⁺ on the surface and in the GBs in the perovskite film, affording passivation of both cation and anion defects. The synergistic effect of the C₇H₉N and BF₃ complex slows the crystallization during the perovskite film deposition to improve the crystalline quality, which reduces the trap density and the recombination in the perovskite film to suppress nonradiative recombination loss and minimizes moisture permeation to improve the stability of the perovskite material. Meanwhile, such an additive improves the energy-level alignment between the valence band of the perovskite and the highest occupied molecular orbital of the hole-transporting material, Spiro-OMeTAD. Consequently, our work achieves power conversion efficiency of 23.24%, accompanied by enhanced stability under ambient conditions and light illumination and opens a new avenue for improving the performance of PSCs through the use of a multifunctional complex.

SUBMITTER: Zhao W

PROVIDER: S-EPMC8346611 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

A binary 2D perovskite passivation for efficient and stable perovskite/silicon tandem solar cells.

Project description:To achieve high power conversion efficiency in perovskite/silicon tandem solar cells, it is necessary to develop a promising wide-bandgap perovskite absorber and processing techniques in relevance. To date, the performance of devices based on wide-bandgap perovskite is still limited mainly by carrier recombination at their electron extraction interface. Here, we demonstrate assembling a binary two-dimensional perovskite by both alternating-cation-interlayer phase and Ruddlesden-Popper phase to passivate perovskite/C60 interface. The binary two-dimensional strategy takes effects not only at the interface but also in the bulk, which enables efficient charge transport in a wide-bandgap perovskite solar cell with a stabilized efficiency of 20.79% (1 cm2). Based on this absorber, a monolithic perovskite/silicon tandem solar cell is fabricated with a steady-state efficiency of 30.65% assessed by a third party. Moreover, the tandem devices retain 96% of their initial efficiency after 527 h of operation under full spectral continuous illumination, and 98% after 1000 h of damp-heat testing (85 °C with 85% relative humidity).

| S-EPMC11327242 | biostudies-literature

Hole-Transport Management Enables 23%-Efficient and Stable Inverted Perovskite Solar Cells with 84% Fill Factor.

Project description:NiOx-based inverted perovskite solar cells (PSCs) have presented great potential toward low-cost, highly efficient and stable next-generation photovoltaics. However, the presence of energy-level mismatch and contact-interface defects between hole-selective contacts (HSCs) and perovskite-active layer (PAL) still limits device efficiency improvement. Here, we report a graded configuration based on both interface-cascaded structures and p-type molecule-doped composites with two-/three-dimensional formamidinium-based triple-halide perovskites. We find that the interface defects-induced non-radiative recombination presented at HSCs/PAL interfaces is remarkably suppressed because of efficient hole extraction and transport. Moreover, a strong chemical interaction, halogen bonding and coordination bonding are found in the molecule-doped perovskite composites, which significantly suppress the formation of halide vacancy and parasitic metallic lead. As a result, NiOx-based inverted PSCs present a power-conversion-efficiency over 23% with a high fill factor of 0.84 and open-circuit voltage of 1.162 V, which are comparable to the best reported around 1.56-electron volt bandgap perovskites. Furthermore, devices with encapsulation present high operational stability over 1,200 h during T90 lifetime measurement (the time as a function of PCE decreases to 90% of its initial value) under 1-sun illumination in ambient-air conditions.

| S-EPMC10149558 | biostudies-literature

Perfection of Perovskite Grain Boundary Passivation by Eu-Porphyrin Complex for Overall-Stable Perovskite Solar Cells.

Project description:The formation of defects at surfaces and grain boundaries (GBs) during the fabrication of solution-processed perovskite film are thought to be responsible for its instability. Herein, Eu-porphyrin complex (Eu-pyP) is directly doped into methylammonium lead triiodide (MAPbI3) precursor, perfectly fabricating 2D (Eu-pyP)0.5MA n -1Pb n I3 n +1 platelets inlaying the GBs of 3D polycrystalline interstices in this protocol. The device based on Eu-pyP doped perovskite film possesses a champion efficiency of 18.2%. More importantly, the doped perovskite solar cells device shows beyond 85% retention of its pristine efficiency value, whereas the pure MAPbI3 device has a rapid drop in efficiency down to 10% within 100 h under 45% humidity at 85 °C in AM 1.5 G. The above acquired perovskite films reveal an unpredictable thermodynamic self-healing ability. Consequently, the findings provide an avenue for defect passivation to synchronously improve resistibility to moisture, heat, and solar light including UV.

| S-EPMC6402397 | biostudies-literature

Bridging Effects of Sulfur Anions at Titanium Oxide and Perovskite Interfaces on Interfacial Defect Passivation and Performance Enhancement of Perovskite Solar Cells.

Project description:Interfacial defects at the electron transport layer (ETL) and perovskite (PVK) interface are critical to the power conversion efficiency (PCE) and stabilities of the perovskite solar cells (PSCs) via significantly affecting the quality of both interface contacts and PVK layers. Here, we demonstrate a simple ionic bond passivation method, employing Na2S solution treatment of the surface of titanium dioxide (TiO2) layers, to effectively passivate the traps at the TiO2/Cs0.05(MA0.15FA0.85)0.95Pb(Br0.15I0.85)3 PVK interface and enhance the performance of PSCs. X-ray photoelectron spectroscopy and other characterizations show that the Na2S treatment introduced S2- ions at the TiO2/PVK interface, where S2- ions effectively bridged the TiO2 ETL and the PVK layer via forming chemical bonds with Ti atoms and with uncoordinated Pb atoms and resulted in the reduced defect density and improved the crystallinity of PVK layers. In addition, the S2- ions can effectively enlarge the grain size of the PVK layers. The average PCE of solar cells is improved from 15.77 to 19.06% via employing the Na2S-treated TiO2 layers. This work demonstrates a simple and facile interface passivation method using ionic bond passivation to afford high-performance PSCs. The bridging effect of S2- ions may inspire the further exploration of the ionic bond passivation and sulfur-based passivation materials.

| S-EPMC8697378 | biostudies-literature

Moisture-triggered fast crystallization enables efficient and stable perovskite solar cells

Project description:Understanding the function of moisture on perovskite is challenging since the random environmental moisture strongly disturbs the perovskite structure. Here, we develop various N2-protected characterization techniques to comprehensively study the effect of moisture on the efficient cesium, methylammonium, and formamidinium triple-cation perovskite (Cs0.05FA0.75MA0.20)Pb(I0.96Br0.04)3. In contrast to the secondary measurements, the established air-exposure-free techniques allow us directly monitor the influence of moisture during perovskite crystallization. We find a controllable moisture treatment for the intermediate perovskite can promote the mass transportation of organic salts, and help them enter the buried bottom of the films. This process accelerates the quasi-solid-solid reaction between organic salts and PbI2, enables a spatially homogeneous intermediate phase, and translates to high-quality perovskites with much-suppressed defects. Consequently, we obtain a champion device efficiency of approaching 24% with negligible hysteresis. The devices exhibit an average T80-lifetime of 852 h (maximum 1210 h) working at the maximum power point. Perovskite structure is disturbed by environmental moisture, limiting the device performance. Here, Wei et al. monitor the effect of moisture during the growth by N2-protected characterization techniques, and obtain an operationally stable perovskite solar cell with efficiency approaching 24%.

| S-EPMC9391447 | biostudies-literature

Highly stable and efficient all-inorganic lead-free perovskite solar cells with native-oxide passivation.

Project description:There has been an urgent need to eliminate toxic lead from the prevailing halide perovskite solar cells (PSCs), but the current lead-free PSCs are still plagued with the critical issues of low efficiency and poor stability. This is primarily due to their inadequate photovoltaic properties and chemical stability. Herein we demonstrate the use of the lead-free, all-inorganic cesium tin-germanium triiodide (CsSn0.5Ge0.5I3) solid-solution perovskite as the light absorber in PSCs, delivering promising efficiency of up to 7.11%. More importantly, these PSCs show very high stability, with less than 10% decay in efficiency after 500 h of continuous operation in N2 atmosphere under one-sun illumination. The key to this striking performance of these PSCs is the formation of a full-coverage, stable native-oxide layer, which fully encapsulates and passivates the perovskite surfaces. The native-oxide passivation approach reported here represents an alternate avenue for boosting the efficiency and stability of lead-free PSCs.

| S-EPMC6318336 | biostudies-literature

Perfection of Perovskite Grain Boundary Passivation by Rhodium Incorporation for Efficient and Stable Solar Cells.

Project description:Organic cation and halide anion defects are omnipresent in the perovskite films, which will destroy perovskite electronic structure and downgrade the properties of devices. Defect passivation in halide perovskites is crucial to the application of solar cells. Herein, tiny amounts of trivalent rhodium ion incorporation can help the nucleation of perovskite grain and passivate the defects in the grain boundaries, which can improve efficiency and stability of perovskite solar cells. Through first-principle calculations, rhodium ion incorporation into the perovskite structure can induce ordered arrangement and tune bandgap. In experiment, rhodium ion incorporation with perovskite can contribute to preparing larger crystalline and uniform film, reducing trap-state density and enlarging charge carrier lifetime. After optimizing the content of 1% rhodium, the devices achieved an efficiency up to 20.71% without obvious hysteresis, from 19.09% of that pristine perovskite. In addition, the unencapsulated solar cells maintain 92% of its initial efficiency after 500 h in dry air. This work highlights the advantages of trivalent rhodium ion incorporation in the characteristics of perovskite solar cells, which will promote the future industrial application.

| S-EPMC7770677 | biostudies-literature

Synergetic surface charge transfer doping and passivation toward high efficient and stable perovskite solar cells.

Project description:Organic-inorganic lead halide perovskite solar cells (PSCs) have received much attention in the last few years due to the high power conversion efficiency (PCE). Generally, perovskite/charge transport layer interface and the defects at the surface and grain boundaries of perovskite film are important factors for the efficiency and stability of PSCs. Herein, we employ an extended benzopentafulvalenes compound (FDC-2-5Cl) with electron-withdrawing pentachlorophenyl group and favorable energy level as charge transfer molecule to treat the perovskite surface. The FDC-2-5Cl with pentachlorophenyl group could accept the electrons from perovskite as a p-type dopant, and passivate the surface defects. The p-type doping effect of FDC-2-5Cl on perovskite surface induced band bending at perovskite surface, which improves the hole extraction from perovskite. As a result, the PSC with FDC-2-5Cl treatment achieves a PCE of 21.16% with an enhanced open-circuit voltage (V oc) of 1.14 V and outstanding long-term stability.

| S-EPMC8005820 | biostudies-literature

Multifunctional succinate additive for flexible perovskite solar cells with more than 23% power-conversion efficiency.

Project description:Flexible perovskite solar cells (FPSCs) have emerged as power sources in versatile applications owing to their high-efficiency characteristics, excellent flexibility, and relatively low cost. Nevertheless, undesired strain in perovskite films greatly impacts the power-conversion efficiency (PCE) and stability of PSCs, particularly in FPSCs. Herein, a novel multifunctional organic salt, methylammonium succinate, which can alleviate strain and reinforce grain boundaries, was incorporated into the perovskite film, leading to relaxed microstrain and a lower defect concentration. As a result, a PCE of 25.4% for rigid PSCs and a record PCE of 23.6% (certified 22.5%) for FPSCs have been achieved. In addition, the corresponding FPSCs exhibited excellent bending durability, maintaining ∼85% of their initial efficiency after bending at a 6 mm radius for 10 000 cycles.

| S-EPMC9490203 | biostudies-literature

Interfacial Contact Passivation for Efficient and Stable Cesium-Formamidinium Double-Cation Lead Halide Perovskite Solar Cells.

Project description:Perovskite solar cells (PSCs) have achieved extremely high power conversion efficiencies (PCEs) of over 25%, but practical application still requires further improvement in the long-term stability of the device. Herein, we present an in situ interfacial contact passivation strategy to reduce the interfacial defects and extraction losses between the hole transporting layer and perovskite. The existence of PbS promotes the crystallization of perovskite, passivates the interface and grain boundary defects, and reduces the nonradiation recombination, thereby leading to a champion PCE of 21.07% with reduced hysteresis, which is one of the best results for the methylammonium (MA)-free, cesium formamidinium double-cation lead-based PSCs. Moreover, the unencapsulated device retains more than 93% and 82% of its original efficiencies after 1 year's storage under ambient conditions and thermal aging at 85°C for 1,000 h in a nitrogen atmosphere, likely due to the usage of MA-free perovskite and the enhanced surface hydrophobicity.

| S-EPMC6992903 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data