Functional Nanocomposite Films of Poly(Lactic Acid) with Well-Dispersed Chitin Nanocrystals Achieved Using a Dispersing Agent and Liquid-Assisted Extrusion Process.

ABSTRACT: The development of bio-based nanocomposites is of high scientific and industrial interest, since they offer excellent advantages in creating functional materials. However, dispersion and distribution of the nanomaterials inside the polymer matrix is a key challenge to achieve high-performance functional nanocomposites. In this context, for better dispersion, biobased triethyl citrate (TEC) as a dispersing agent in a liquid-assisted extrusion process was used to prepare the nanocomposites of poly (lactic acid) (PLA) and chitin nanocrystals (ChNCs). The aim was to identify the effect of the TEC content on the dispersion of ChNCs in the PLA matrix and the manufacturing of a functional nanocomposite. The nanocomposite film's optical properties; microstructure; migration of the additive and nanocomposites' thermal, mechanical and rheological properties, all influenced by the ChNC dispersion, were studied. The microscopy study confirmed that the dispersion of the ChNCs was improved with the increasing TEC content, and the best dispersion was found in the nanocomposite prepared with 15 wt% TEC. Additionally, the nanocomposite with the highest TEC content (15 wt%) resembled the mechanical properties of commonly used polymers like polyethylene and polypropylene. The addition of ChNCs in PLA-TEC15 enhanced the melt viscosity, as well as melt strength, of the polymer and demonstrated antibacterial activity.

SUBMITTER: Patel M

PROVIDER: S-EPMC8347658 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Nanocomposite hydrogels have found a wide scope in regenerative medicine, tissue engineering, and smart drug delivery applications. The present study reports the formulations of biocompatible nanocomposite hydrogel films using carboxymethyl cellulose-hydroxyethyl cellulose-acrylonitrile-linseed oil polyol (CHAP) plain hydrogel and Na-montmorillonite (NaMMT) dispersed CHAP nanocomposite hydrogel films (NaCHAP) using solution blending technique. The structural, morphological, and mechanical properties of resultant nanocomposite hydrogel films were further investigated to analyze the effects of polyol and NaMMT on the characteristic properties. The synergistic effect of polyol and nanofillers on the mechanical strength and sustained drug-release behavior of the resultant hydrogel films was studied, which revealed that the increased cross-link density of hydrogels enhanced the elastic modulus (up to 99%) and improved the drug retention time (up to 72 h at both pHs 7.4 and 4.0). The release rate of cisplatin in nanocomposite hydrogel films was found to be higher in CHAP-1 (83 and 69%) and CHAP-3 (79 and 64%) than NaCHAP-3 (77 and 57%) and NaCHAP-4 (73 and 54%) at both pHs 4.0 and 7.4, respectively. These data confirmed that the release rate of cisplatin in nanocomposite hydrogel films was pH-responsive and increased with decrease of pH. All nanocomposite hydrogel films have exhibited excellent pH sensitivity under buffer solution of various pHs (1.0, 4.0, 7.4, and 9.0). The in vitro biocompatibility and cytotoxicity tests of these films were also conducted using 3-(4,5-dimethylthiazole-2-yl-2,5-diphenyl tetrazolium bromide) assay of human embryonic kidney (HEK-293) and human breast cancer (MCF-7) cell lines up to 48 h, which shows their biocompatible nature. However, cisplatin-loaded nanocomposite hydrogel films effectively inhibited the growth of human breast MCF-7 cancer cells. These studies suggested that the proposed nanocomposite hydrogel films have shown promising application in therapeutics, especially for anticancer-targeted drug delivery.

Dataset Information

Functional Nanocomposite Films of Poly(Lactic Acid) with Well-Dispersed Chitin Nanocrystals Achieved Using a Dispersing Agent and Liquid-Assisted Extrusion Process.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets