Effect of Esterification Conditions on the Physicochemical Properties of Phosphorylated Potato Starch.

ABSTRACT: The aim of this study was to evaluate the effect of the temperature (15 or 45 °C) and the duration (15-120 min) of the modification process on the selected physicochemical, thermal, and rheological properties of phosphorylated potato starch. The modified starches contained 93.6-98.2 mg P/100 g (dry weight basis, d.w.b.). Phosphorylation caused color changes with a total color difference between the starches below 0.55, but these changes were less than those that were recognizable by the human eye. The thermal analysis showed two opposite processes appearing during the modification: the loosening of the structure (dominant among starches obtained at 15 °C) and the strengthening of the structure (dominant among starches obtained at 45 °C). The higher phosphorylation temperature reduced native starch recovery from 140% to 87-116% and increased the hysteresis loop area from -169 to 1040. All of the pastes made from the modified starches showed a weaker tendency for retrogradation (during 21 days of storage) than native starches. The results of the regression analysis conducted between the properties of the starch pastes obtained at 45 °C indicated that the modification time appeared to be a better indicator of the rate of modification progress than the phosphorus content. The PCA (principal component analysis) results made it possible to distinguish starch phosphates obtained at 15 °C from those obtained at 45 °C and those from natural starch.

SUBMITTER: Roznowski J

PROVIDER: S-EPMC8347770 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Effects of Variety and Growing Location on Physicochemical Properties of Starch from Sweet Potato Root Tuber.

Project description:Three sweet potato varieties with purple-, yellow-, and white-fleshed root tubers were planted in four growing locations. Starches were isolated from their root tubers, their physicochemical properties (size, iodine absorption, amylose content, crystalline structure, ordered degree, lamellar thickness, swelling power, water solubility, and pasting, thermal and digestion properties) were determined to investigate the effects of variety and growing location on starch properties in sweet potato. The results showed that granule size (D[4,3]) ranged from 12.1 to 18.2 μm, the iodine absorption parameters varied from 0.260 to 0.361 for OD620, from 0.243 to 0.326 for OD680 and from 1.128 to 1.252 for OD620/550, and amylose content varied from 16.4% to 21.2% among starches from three varieties and four growing locations. Starches exhibited C-type X-ray diffraction patterns, and had ordered degrees from 0.634 to 0.726 and lamellar thicknesses from 9.72 to 10.21 nm. Starches had significantly different swelling powers, water solubilities, pasting viscosities, and thermal properties. Native starches had rapidly digestible starch (RDS) from 2.2% to 10.9% and resistant starch (RS) from 58.2% to 89.1%, and gelatinized starches had RDS from 70.5% to 81.4% and RS from 10.8% to 23.3%. Two-way ANOVA analysis showed that starch physicochemical properties were affected significantly by variety, growing location, and their interaction in sweet potato.

| S-EPMC8659240 | biostudies-literature

Impacts of nitrogen fertilization rate on the root yield, starch yield and starch physicochemical properties of the sweet potato cultivar Jishu 25.

Project description:In recent years, the sweet potato cultivar Jishu 25 has exhibited good characteristics for starch processing in northern China. The storage root dry matter yields of this cultivar can exceed one ton per mu (1/15 of a hectare) at nitrogen (N) rates of 60-90 kg ha-1 based on soil nutrient content. However, the effect of N fertilizer on the physicochemical properties of starches isolated from this cultivar has not been reported. In order to evaluate these effects, three different N rates, 0 (control, N0), 75 (N1), and 150 kg ha-1 (N2), were selected for a field experiment in 2017. The results showed that N1 exhibited the highest storage root yield and starch yield. Compared to the control group, N fertilizer significantly increased the total starch content while no significant difference was found in these between the N1 and N2 groups. The amylose (AM) content was highest in the N2 group and lowest in the N0 group. In addition, N fertilizer exhibited no significant effects on the values of [D(v, 0.9)], D [4, 3] and D [3, 2]. Compared to the control group, N1 demonstrated significantly higher setback viscosity (SV), while N2 showed significantly higher peak viscosity (PV), cold paste viscosity (CPV) and SV. However, there were no significant differences in the hot paste viscosity (HPV), peak time and pasting temperature between the N1 and N2 groups. For the thermal properties of starch, there were no significant differences in peak temperature (Tp), conclusion temperature (Tc) or gelatinization enthalpy (?H) between the N1 and N2 groups. Overall, for the starch samples of cultivar Jishu 25, N fertilizer exerts significant effects on the starch content, AM content and viscosity properties but little effect on the particle size distribution and ?H. 75 kg N ha-1 can easily lead to substantial planting benefits from the high storage root yield, dry matter yield and total starch content of this cultivar.

| S-EPMC6705776 | biostudies-literature

Physicochemical and Structural Characterization of Potato Starch with Different Degrees of Gelatinization.

Project description:Starch gelatinization has been widely studied previously, but there is still a lack of systematical research on the relationship between the degree of starch gelatinization (DSG) and its physicochemical and structural properties. In this study, potato starch samples with DSG ranging from 39.41% to 90.56% were obtained by hydrothermal treatment. The thermal, rheological, and structural properties, as well as the water-binding capacity of samples were investigated. A starch solution with a DSG of 39.41% was partially sedimented at room temperature, while starch with a DSG of 56.11% can form a stable paste with a fine shear-thinning property, as well as samples with a DSG larger than 56.11%. The endothermic enthalpy, gelatinization range, and short-range ordered structure of starch were negatively correlated with DSG, whereas onset gelatinization temperature, apparent viscosity, and water-binding capacity were positively correlated. The viscoelasticity of starch gels was negatively correlated with the DSG after full gelatinization (DSG > 39.41%). Starch granules gradually lose their typical shape and less birefringence can be observed with increasing DSG. Hydrothermal treatment has a more significant effect on the amount of exposed hydroxyl groups than the ordered and amorphous structures of partially gelatinized starch. This study built linear correlations between starch physicochemical properties and the DSG and provided comprehensive insight into the characteristics of partially gelatinized potato starch.

| S-EPMC8156876 | biostudies-literature

Comparison of Physicochemical Properties of Silver and Gold Nanocomposites Based on Potato Starch in Distilled and Cold Plasma-Treated Water.

Project description:Nanometal-containing biocomposites find wide use in many industries and fields of science. The physicochemical properties of these materials depend on the character of the polymer, the size and shape of the metallic nanoparticles, and the interactions between the biopolymer and the nanoparticles. The aim of the work was to synthesise and study the effect of plasma-treated water on the properties of the obtained metallic nanoparticles as well as the physicochemical and functional properties of nanocomposites based on potato starch. The metallic nanoparticles were synthesised within a starch paste made in distilled water and in distilled water exposed to low-temperature, low-pressure plasma. The materials produced were characterised in terms of their physicochemical properties. Studies have shown that gold and silver nanoparticles were successfully obtained in a matrix of potato starch in distilled water and plasma water. SEM (Scanning Electron Microscopy) images and UV-Vis spectra confirmed the presence of nanosilver and nanosilver in the obtained composites. On the basis of microscopic images, the size of nanoparticles was estimated in the range from 5 to 20 nm for nanoAg and from 15 to 40 nm for nanoAu. The analysis of FTIR-ATR spectra showed that the type of water used and the synthesis of gold and silver nanoparticles did not lead to changes in the chemical structure of potato starch. DLS analysis showed that the nanoAg obtained in the plasma water-based starch matrix were smaller than the Ag particles obtained using distilled water. Colour analysis showed that the nanocomposites without nanometals were colourless, while those containing nanoAg were yellow, while those with nanoAu were dark purple. This work shows the possibility of using plasma water in the synthesis of nanometals using potato starch, which is a very promising polysaccharide in terms of many potential applications.

| S-EPMC9916708 | biostudies-literature

Structural, Physicochemical, and Functional Properties of Electrolyzed Cassava Starch.

Project description:Cassava starch was oxidized using the electrolysis system. Sodium chloride was added to this system at various concentrations from 0.5 to 5.0 % (w/v). The whiteness of modified starches proportionally increased based on the NaCl concentration and human eyes could recognize the difference of color. Under treatment, dents occurred on the surface of starch granule. Concentration of carbonyl and carboxyl groups was increased compared to native starch. Based on X-ray diffraction pattern, oxidized starch kept its A-type. Besides, the ratios of alpha-helix/amorphous regions remained indicating oxidation reaction mainly subjected on amorphous region. Intrinsic viscosity was used to indirectly calculate the average molecular weight of sample. Furthermore, results showed that average molecular weight was significantly reduced (from 2.09-fold to 13.22-fold) based on the reacting NaCl concentration. The increase of NaCl content related to the increase of retrogradation of treated starches. At various temperatures (30-95°C), swelling factor and clarity reflected negative and positive correlations to NaCl concentration.

| S-EPMC6525864 | biostudies-literature

Structural characterization and physicochemical properties of grain amaranth starch

Project description: Not available

| S-EPMC11375243 | biostudies-literature

Highly phosphorylated functionalized rice starch produced by transgenic rice expressing the potato GWD1 gene.

Project description:Starch phosphorylation occurs naturally during starch metabolism in the plant and is catalysed by glucan water dikinases (GWD1) and phosphoglucan water dikinase/glucan water dikinase 3 (PWD/GWD3). We generated six stable individual transgenic lines by over-expressing the potato GWD1 in rice. Transgenic rice grain starch had 9-fold higher 6-phospho (6-P) monoesters and double amounts of 3-phospho (3-P) monoesters, respectively, compared to control grain. The shape and topography of the transgenic starch granules were moderately altered including surface pores and less well defined edges. The gelatinization temperatures of both rice flour and extracted starch were significantly lower than those of the control and hence negatively correlated with the starch phosphate content. The 6-P content was positively correlated with amylose content and relatively long amylopectin chains with DP25-36, and the 3-P content was positively correlated with short chains of DP6-12. The starch pasting temperature, peak viscosity and the breakdown were lower but the setback was higher for transgenic rice flour. The 6-P content was negatively correlated with texture adhesiveness but positively correlated with the cohesiveness of rice flour gels. Our data demonstrate a way forward to employ a starch bioengineering approach for clean modification of starch, opening up completely new applications for rice starch.

| S-EPMC5469863 | biostudies-literature

Properties of Potato Starch Roasted with Apple Distillery Wastewater.

Project description:This study aimed to produce starch esters by roasting potato starch with apple distillery wastewater at various temperatures and aimed to determine the effects of esterification conditions on selected properties of the modified preparations. Apple distillery wastewater was concentrated, mixed with starch (30 g of dry matter per 100 g of starch), dried, and roasted at temperatures of 110, 130 or 150 °C for 3 h. The resulting preparations were rinsed 30 times with a 60% ethanol solution, dried, and disintegrated. After that, the following analyses were performed: content of substituted acids (after alkaline de-esterification) with high performance liquid chromatography (HPLC); thermal characteristics with differential scanning calorimetry (DSC); swelling power and solubility in water at 80 °C; color changes with a colorimeter; rheology of the pastes based on the plotted flow curves; and the pastes' resistance to amyloglucosidase. Starch treatments with apple distillery wastewater at 130 and 150 °C caused significant changes to its properties when compared to the control samples of native starch and starch roasted without wastewater, including: a lower temperature and heat of pasting, lower swelling power and solubility in water, darker color, higher resistance to amyloglucosidase, and the formation of pastes with a lower viscosity.

| S-EPMC7465239 | biostudies-literature

Effect of Potato Starch Hydrogel:Glycerol Monostearate Oleogel Ratio on the Physico-Rheological Properties of Bigels.

Project description:Bigel (BG) has been shown to be promising for the food industry due to the possibility to manipulate the properties of the system by adjusting the ratio of each individual phase, namely the hydrogel (H) and oleogel (O) phases. This work aimed to evaluate the influence of the O:H ratio on the physical-rheological properties of BG produced with potato starch (PS) and glycerol monostearate (GM). The hydrogel hardness (i.e., 1423.47 g) directly influenced the viscosity of the BG samples, as BG with a higher H-phase presented the highest viscosity and firmness. All BG samples presented shear-thinning behavior and structural breakdown at ~50 °C. BG with a higher O-phase had superior results for thermal stability, softer texture, and yield stress values, representative of good plasticity and spreadability, as compared to BG with less O-phase. The BG with 80% H-phase was less stable during the 21 days of storage in relation to the other BG samples. This study showed the role that the O:H ratio plays in the development of PS-GM-based BGs with tailor-made physical-rheological properties. In addition, the BG is an easily reproduced system with great potential to be used as a trans and saturated fat substitute in food applications.

| S-EPMC9689572 | biostudies-literature

Correlation analysis on physicochemical and structural properties of sorghum starch.

Project description:This manuscript analyzed physicochemical and structural properties of 30 different types of sorghum starches based on their apparent amylose content (AAC). Current results confirmed that sorghum starch exhibited irregular spherical or polygonal granule shape with 14.5 μm average particle size. The AAC of sorghum starch ranged from 7.42 to 36.44% corresponding to relative crystallinities of 20.5 to 32.4%. The properties of enthalpy of gelatinization (ΔH), peak viscosity (PV), relative crystallinity (RC), degree of double helix (DD), degree of order (DO), and swelling power (SP) were negatively correlated with AAC, while the cool paste viscosity (CPV) and setback (SB) were positively correlated with AAC. Correlations analyzed was conducted on various physicochemical parameters. Using principal component analysis (PCA) with 20 variables, the difference between 30 different types of sorghum starch was displayed. Results of current study can be used to guide the selection and breeding of sorghum varieties and its application in food and non-food industries.

| S-EPMC9873550 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data