Halogen-Free Flame Retardant Polypropylene Fibers with Modified Intumescent Flame Retardant: Preparation, Characterization, Properties and Mode of Action.

ABSTRACT: A novel intumescent flame retardant (IFR) agent designated as Dohor-6000A has been used to prepare halogen-free flame retardant polypropylene (PP) fibers via melting spinning. Before being blended with PP resin, a surface modification of Dohor-6000A was carried out to improve its compatibility with the PP matrix. The rheological behavior of flame retardant Dohor-6000A/PP resin, the structure, morphology, mechanical properties, flammability of the Dohor-6000A/PP fibers were studied in detail, as well as the action mode of flame retardant. X-ray diffraction (XRD) showed that the addition of Dohor-6000A did not damage the crystal as well as the orientation structure of PP matrix, which was helpful to the maintenance of mechanical properties. The presence of the IFR significantly improved the flame retardant performance and thermal stability of PP fibers. When the content of Dohor-6000A reached 25%, the fibers displayed a limiting oxygen index (LOI) value of 29.1% and good melt-drop resistance. Moreover, the peak heat release rate (PHRR) and total heat release (THR) from microscale combustion colorimetry (MCC) tests were decreased by 26.0% and 16.0% in comparison with the same conditions for pure PP fibers. In the condensed phase, the IFR promoted a carbonization process and promoted the formation of a glassy or stable foam protective layer on the surface of the polymer matrix. In addition, the IFR decomposed endothermically to release of non-combustible gases such as NH₃ and CO₂ which dilutes the combustible gases in the combustion zone.

SUBMITTER: Xu Q

PROVIDER: S-EPMC8347993 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

The Synergistic Effect of Ionic Liquid-Modified Expandable Graphite and Intumescent Flame-Retardant on Flame-Retardant Rigid Polyurethane Foams.

Project description:In this study, a nitrogen-phosphorus intumescent flame-retardant 3-(N-diphenyl phosphate) amino propyl triethoxy silane (DPES), the ionic liquid (IL) of 1-butyl-3-methyl-imidazole phosphate, and a phosphorous-containing ionic liquid-modified expandable graphite (IL-EG), were synthesized, and their molecular structures were characterized. The flame-retardant rigid polyurethane foams (RPUFs) were compounded with synergistic flame-retardant IL-EG/DPES to study the effects of the combination IL-EG and DPES on the pore structure, mechanical properties, thermal decomposition behavior and thermal decomposition mechanism of RPUF. The results showed that IL-EG/DPES had good thermal stability, and an excellent expansibility and char yield. The flame-retardant RPUF, modified with IL-EG and DPES at the ratio of 1:1, had a relatively uniform pore size, the highest compressive strength, and an excellent flame-retardant performance due to the form interwoven hydrogen bonds between IL-EG and DPES, as well as the new synergistic flame-retardant coating on the RPUF surface to restrict the transfer of gas or heat into the PU matrix.

| S-EPMC7411720 | biostudies-literature

Synergistic Flame Retardant Effect of an Intumescent Flame Retardant Containing Boron and Magnesium Hydroxide.

Project description:In this study, to develop an organic/inorganic synergistic flame retardant and to reduce the dosage and cost of flame retardants, organic/inorganic synergistic flame retardants, hexakis(4-boronic acid-phenoxy)-cyclophosphazene (CP-6B), and magnesium hydroxide (MH) were chosen. The flame retardant properties of CP-6B/MH in epoxy resin (EP) were discussed. EP/CP-6B/MH had better flame retardancy and heat resistance compared with EP/CP-6B and EP/MH. A limiting oxygen index of EP/3.0%CP-6B/0.5%MH of 31.9% was achieved, and vertical burning V-0 rating was achieved. Compared with EP, the cone calorimeter dates of EP/CP-6B/MH decreased. CP-6B/MH inhibited combustion and did little to damage mechanical properties. Besides, the flame retardant mechanism was studied by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and pyrolysis-gas chromatography-mass spectrometry. CP-6B/MH exerted good synergistic effects.

| S-EPMC6648587 | biostudies-literature

Self-intumescent polyelectrolyte for flame retardant poly (lactic acid) nonwovens.

Project description:The demand for eco-friendly poly (lactic acid) (PLA) nonwovens grows at a high rate in the past several decades, however, only a little attention has been received for flame retardant PLA nonwoven fabrics. In this work, a novel halogen-free self-intumescent polyelectrolyte tris (hydroxymethyl)-aminomethane polyphosphate (APTris) was synthesized by reacting ammonium polyphosphate with tris (hydroxymethyl) aminomethane, and was then used to improve the fire resistance of PLA nonwovens via a dip-nip process. The flammability characterization indicated the limiting oxygen index value was increased to 30.0% from 18.3%, and the damaged area in the vertical burning test was reduced by about 87.0% by the presence of APTris. The cone calorimeter test results revealed that the peak heat release rate and total heat release of the treated sample were decreased by 41.0% and 28.2% respectively compared with that of the control PLA nonwoven sample. The char residue was increased to 12.3 from 1.7 wt % at 800 °C. It is suggested that the dense char barrier formed at the presence of APTris prevents heat, smoke, and gas transfer, and hence enhance thermal dilatability and flame retardancy of PLA nonwovens. This simple sustainable halogen-free treatment has great potential to produce cleaner commercialized flame-retardant PLA nonwovens.

| S-EPMC7529633 | biostudies-literature

Intumescent Phosphorus and Triazole-Based Flame-Retardant Polyurethane Foams from Castor Oil.

Project description:Synthesis of a novel phosphorus and triazole-functionalized flame-retardant (FR) monomer (PTFM) using azide-alkyne "click" reaction between triprop-2-ynyl phosphate and 2-azidoethanol that can impart intumescent FR property to polyurethane foams (PUFs) has been reported. Polyurethane triazole foams (PUTFs) were prepared using the as-synthesized PTFM and a hydroxylated castor polyol with a hydroxyl value of ∼310 mg KOH/g for application as reactive FR rigid foams. PTFM and the castor polyol were characterized for structural elucidation using Fourier transform infrared and 1H, 13C, and 31P NMR. PUTFs with a varying loading content of PTFM were subjected to the lab-scale flame test, cone calorimetry test, Underwriters Laboratory 94 Vertical burning test (UL 94V), and limiting oxygen index (LOI) test. A significant increase in the char yields, reduction in heat release rates, V-1 rating, and 27% of LOI were observed for PUTFs compared to PUFs and proportional to the percentage loading of PTFM. The cumulative effect of nitrogen and phosphorus in PUTFs on their intumescent behavior was evident from the thermogravimetric analysis and scanning electron microscopy micrographs, which were further supplemented by X-ray photoelectron spectroscopy studies, indicating expulsion of N2 and overall improvement in compression strength as well. Such environment-friendly reactive FRs can be good replacements to the halogenated ones.

| S-EPMC6647972 | biostudies-literature

Influence of Zinc Oxide Nanoparticles and Char Forming Agent Polymer on Flame Retardancy of Intumescent Flame Retardant Coatings.

Project description:Zinc oxide nanoparticles (ZnO NPs) were synthesized by a precipitation method, and a new charring-foaming agent (CFA) N-ethanolamine triazine-piperazine, melamine polymer (ETPMP) was synthesized via nucleophilic substitution reaction by using cyanuric chloride, ethanolamine, piperazine, and melamine as precursor molecules. FTIR and energy-dispersive X-ray spectroscopy (EDS) studies were employed to characterize and confirm the synthesized ETPMP structure. New intumescent flame retardant epoxy coating compositions were prepared by adding ammonium polyphosphate (APP), ETPMP, and ZnO NPs into an epoxy resin. APP and ETPMP were fixed in a 2:1 w/w ratio and used as an intumescent flame-retardant (IFR) system. ZnO NPs were loaded as a synergistic agent in different amounts into the IFR coating system. The synergistic effects of ZnO NPs on IFR coatings were systematically evaluated by limited oxygen index (LOI) tests, vertical burning tests (UL-94 V), TGA, cone calorimeter tests, and SEM. The obtained results revealed that a small amount of ZnO NPs significantly increased the LOI values of the IFR coating and these coatings had a V-0 ratings in UL-94 V tests. From the TGA data, it is clear that the addition of ZnO NPs could change the thermal degradation behaviors of coatings with increasing char residue percentage at high temperatures. Cone calorimeter data reported that ZnO NPs could decrease the combustion parameters including peak heat release rates (PHRRs), and total heat release (THR) rates. The SEM results showed that ZnO NPs could enhance the strength and the compactness of the intumescent char, which restricted the flow of heat and oxygen.

| S-EPMC7022803 | biostudies-literature

Expanded Polystyrene Beads Coated with Intumescent Flame Retardant Material to Achieve Fire Safety Standards.

Project description:The compatibility and coating ratio between flame retardant materials and expanded polystyrene (EPS) foam is a major impediment to achieving satisfactory flame retardant performance. In this study, we prepared a water-based intumescent flame retardant system and methylene diphenyl diisocyanate (MDI)-coated expandable polystyrene microspheres by a simple coating approach. We investigated the compatibility, coating ratio, and fire performance of EPS- and MDI-coated EPS foam using a water-based intumescent flame retardant system. The microscopic study revealed that the water-based intumescent flame retardant materials were successfully incorporated with and without MDI-coated EPS microspheres. The cone calorimeter tests (CCTs) of the MDI-coated EPS containing water-based intumescent flame retardant materials exhibited better flame retardant performance with a lower total heat release (THR) 7.3 MJ/m2, peak heat release rate (PHRR) 57.6 kW/m2, fire growth rate (FIGRA) 2027.067 W/m2.s, and total smoke production (TSP) 0.133 m2. Our results demonstrated that the MDI-coated EPS containing water-based intumescent flame retardant materials achieved flame retarding properties as per fire safety standards.

| S-EPMC8398555 | biostudies-literature

The Efficiency of Biobased Carbonization Agent and Intumescent Flame Retardant on Flame Retardancy of Biopolymer Composites and Investigation of their Melt-Spinnability.

Project description:The objective of this study is to assess the efficiency of biobased carbonization agent in intumescent formulations (IFRs) to examine the flame retardant properties of polylactic acid (PLA) composites and to investigate their melt-spinnability. We used phosphorous-based halogen free flame retardant (FR) and kraft lignin (KL) as bio-based carbonization agent. After melt compounding and molding into sheets by hot pressing various fire related characteristics of IFR composites were inspected and were characterized by different characterization methods. It was fascinating to discover that the introduction of 5-20 wt% FR increased the limiting oxygen index (LOI) of PLA composites from 20.1% to 23.2-33.5%. The addition of KL with content of 3-5 wt% further increased the LOI up to 36.6-37.8% and also endowed PLA/FR/KL composites with improved anti-dripping properties. Cone calorimetry revealed a 50% reduction in the peak heat release rate of the IFR composites in comparison to 100% PLA and confirmed the development of an intumescent char structure containing residue up to 40%. For comparative study, IFR composites containing pentaerythritol (PER) as a carbonization agent were also prepared and their FR properties were compared. IFR composites were melt spun and mechanical properties of multifilament yarns were tested. The analysis of char residues by energy dispersive X-ray spectrometry (EDS) and SEM images confirmed that PLA/FR/KL composites developed a thicker and more homogeneous char layer with better flame retardant properties confirming that the fire properties of PLA can be enhanced by using KL as a carbonization agent.

| S-EPMC6515164 | biostudies-literature

Halogen-Free Flame-Retardant Compounds. Thermal Decomposition and Flammability Behavior for Alternative Polyethylene Grades.

Project description:The effect of six halogen-free flame retardant (FR) formulations was investigated on the thermal stability of two low-density polyethylenes (LDPE) and one linear low-density polyethylene (LLDPE), by means of thermogravimetric analysis (TGA) under nitrogen and air atmosphere. The relative data were combined with flammability properties and the overall performance of the FRs was correlated with the type of branching in the polyethylene grades and to their processing behavior. The thermal degradation kinetics was further determined based on the Kissinger and Coats-Redfern methods. In terms of flammability, the addition of a triazine derivative and ammonium polyphosphate at a loading of 35 wt. %. was found to be the most efficient, leading to UL 94 V0 ranking in the case of the LDPE grade produced in an autoclave reactor.

| S-EPMC6780580 | biostudies-literature

Layered double hydroxide-oxidized carbon nanotube hybrids as highly efficient flame retardant nanofillers for polypropylene.

Project description:Aqueous miscible organic layered double hydroxides (AMO-LDHs) can act as organophilic inorganic flame retardant nanofillers for unmodified non-polar polymers. In this contribution, AMO [Mg3Al(OH)8](CO3)0.5·yH2O LDH-oxidized carbon nanotube (AMO-LDH-OCNT) hybrids are shown to perform better than the equivalent pure AMO-LDH. A synergistic effect between the AMO-LDH and OCNT was observed; this endows the hybrid material with enhanced flame retardancy, thermal stability, and mechanical properties. The thermal stability of polypropylene (PP) was significantly enhanced by adding AMO-LDH-OCNT hybrids. For PP mixed with AMO-LDH-OCNT hybrids to produce a composite with 10 wt% LDH and 2 wt% OCNT, the 50% weight loss temperature was increased by 43?°C. Further, a system with 10?wt% of AMO-LDH and 1?wt% OCNT showed a peak heat release rate (PHRR) reduction of 40%, greater than the PHRR reduction with PP/20?wt% AMO-LDH (31%). The degree of dispersion (mixability) between AMO-LDH and OCNT has a significant effect on the flame retardant performance of the hybrids. In addition, the incorporation of AMO-LDH-OCNT hybrids led to better mechanical properties, such as higher tensile strength (27.5?MPa) and elongation at break (17.9%), than those composites containing only AMO-LDH (25.6?MPa and 7.5%, respectively).

| S-EPMC5067659 | biostudies-literature

In Situ Nanofibrillar Polypropylene-Based Composite Microcellular Foams with Enhanced Mechanical and Flame-Retardant Performances.

Project description:With the increasing demand for plastic components, the development of lightweight, high strength and functionalized polypropylene (PP) from a cost-effective and environmentally friendly process is critical for resource conservation. In situ fibrillation (INF) and supercritical CO2 (scCO2) foaming technology were combined in this work to fabricate PP foams. Polyethylene terephthalate (PET) and poly(diaryloxyphosphazene)(PDPP) particles were applied to fabricate in situ fibrillated PP/PET/PDPP composite foams with enhanced mechanical properties and favorable flame-retardant performance. The existence of PET nanofibrils with a diameter of 270 nm were uniformly dispersed in PP matrix and served multiple roles by tuning melt viscoelasticity for improving microcellular foaming behavior, enhancing crystallization of PP matrix and contributing to improving the uniformity of PDPP's dispersion in INF composite. Compared to pure PP foam, PP/PET(F)/PDPP foam exhibited refined cellular structures, thus the cell size of PP/PET(F)/PDPP foam was decreased from 69 to 23 μm, and the cell density increased from 5.4 × 106 to 1.8 × 108 cells/cm3. Furthermore, PP/PET(F)/PDPP foam showed remarkable mechanical properties, including a 975% increase in compressive stress, which was attributed to the physical entangled PET nanofibrils and refined cellular structure. Moreover, the presence of PET nanofibrils also improved the intrinsic flame-retardant nature of PDPP. The synergistical effect of the PET nanofibrillar network and low loading of PDPP additives inhibited the combustion process. These gathered advantages of PP/PET(F)/PDPP foam make it promising for lightweight, strong, and fire-retardant polymeric foams.

| S-EPMC10056583 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data