Kidney-Protector Lipidic Cilastatin Derivatives as Structure-Directing Agents for the Synthesis of Mesoporous Silica Nanoparticles for Drug Delivery.

ABSTRACT: Mesoporous silica nanomaterials have emerged as promising vehicles in controlled drug delivery systems due to their ability to selectively transport, protect, and release pharmaceuticals in a controlled and sustained manner. One drawback of these drug delivery systems is their preparation procedure that usually requires several steps including the removal of the structure-directing agent (surfactant) and the later loading of the drug into the porous structure. Herein, we describe the preparation of mesoporous silica nanoparticles, as drug delivery systems from structure-directing agents based on the kidney-protector drug cilastatin in a simple, fast, and one-step process. The concept of drug-structure-directing agent (DSDA) allows the use of lipidic derivatives of cilastatin to direct the successful formation of mesoporous silica nanoparticles (MSNs). The inherent pharmacological activity of the surfactant DSDA cilastatin-based template permits that the MSNs can be directly employed as drug delivery nanocarriers, without the need of extra steps. MSNs thus synthesized have shown good sphericity and remarkable textural properties. The size of the nanoparticles can be adjusted by simply selecting the stirring speed, time, and aging temperature during the synthesis procedure. Moreover, the release experiments performed on these materials afforded a slow and sustained drug release over several days, which illustrates the MSNs potential utility as drug delivery system for the cilastatin cargo kidney protector. While most nanotechnology strategies focused on combating the different illnesses this methodology emphasizes on reducing the kidney toxicity associated to cancer chemotherapy.

SUBMITTER: Martinez-Erro S

PROVIDER: S-EPMC8348040 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Tunable glutathione (GSH)-sensitive hollow mesoporous silica nanoparticles (HMSiO2 NPs) were developed using a structural difference-based selective etching strategy. These organosilica hollow nanoparticles contained disulfide linkages (S-S) in the outer shell which were degraded by GSH. The particles were compared with their nonGSH-sensitive tetraethyl orthosilicate (TEOS) HMSiO2 counterparts in terms of their synthesis method, characterization, doxorubicin (DOX) release profile, and in vitro cytotoxicity in MCF-7 breast cancer cells. Transmission electron microscopy (TEM) of the particles indicated that the fabricated HMSiO2 NPs had an average diameter of 130?±?5?nm. Thermogravimetric analysis (TGA) revealed that GSH-sensitive particles had approximately 5.3% more weight loss than TEOS HMSiO2 NPs. Zeta potential of these redox-responsive particles was -23?±?1?mV at pH?6 in deionized (DI) water. Nitrogen adsorption-desorption isotherm revealed that the surface area of the hollow mesoporous nanoreservoirs was roughly 446?±?6?m2?g-1 and the average diameter of the pores was 2.3?±?0.5?nm. TEM images suggest that the nanoparticles started to lose mass integrity from Day 1. The particles showed a high loading capacity for DOX (8.9?±?0.5%) as a model drug, due to the large voids existing in the hollow structures. Approximately 58% of the incorporated DOX released within 14?days in phosphate buffered saline (PBS) at pH?6 and in the presence of 10?mM of GSH, mimicking intracellular tumor microenvironment while release from TEOS HMSiO2 NPs was only c.a. 18%. The uptake of these hollow nanospheres by MCF-7 cells and RAW 264.7 macrophages was evaluated using TEM and confocal microscopy. The nanospheres were shown to accumulate in the endolysosomal compartments after incubation for 24?h with the maximum uptake of c.a. 2.1?±?0.3% and 5.2?±?0.4%, respectively. Cytotoxicity of the nanospheres was investigated using CCK-8 assay. Results indicate that intact hollow particles (both GSH-sensitive and TEOS HMSiO2 NPs) were nontoxic to MCF-7 cells after incubation for 24?h within the concentration range of 0-1000??g?ml-1. DOX-loaded GSH-sensitive nanospheres containing 6??g?ml-1 of DOX killed c.a. 51% of MCF-7 cells after 24?h while TEOS HMSiO2 NPs killed c.a. 20% with the difference being statistically significant. Finally, cytotoxicity data in RAW 264.7 macrophages and NIH 3?T3 fibroblasts shows that intact GSH-sensitive HMSiO2 NPs did not show any toxic effects on these cells with the concentrations equal or <125??g?ml-1.

Dataset Information

Kidney-Protector Lipidic Cilastatin Derivatives as Structure-Directing Agents for the Synthesis of Mesoporous Silica Nanoparticles for Drug Delivery.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets