Enhanced thermoelectric performance of UV-curable silver (I) selenide-based composite for energy harvesting.

ABSTRACT: Thermoelectric (TE) composites, with photocured resin as the matrix and Ag₂Se (AS) as the filler, are synthesized by a digital-light-processing (DLP) based 3D printer. The mixture of diurethane dimethacrylate (DUDMA) and isobornyl acrylate (IBOA) is used as a UV-curable resin because of their low viscosity and high miscibility. Scanning electron microscopy (FE-SEM) images confirm that the filler retains its shape and remains after the UV-curing process. After completing curing, the mechanical and thermoelectric properties of the composite with different AS contents were measured. The addition of the AS filler increases the thermoelectric properties of the cured resin. When the AS contents increase by 30 wt.%, the maximum power factor was obtained (~ 51.5 μW/m·K² at room temperature). Additionally, due to the phonon scattering effect between the interfaces, the thermal conductivity of composite is lower than that of pristine photoresin. The maximum thermoelectric figure of merit (ZT) is ~ 0.12, which is achieved with 30 wt.% of AS at 300 K with the enhanced power factor and reduced thermal conductivity. This study presents a novel manufacturing method for a thermoelectric composite using 3D printing.

SUBMITTER: Park D

PROVIDER: S-EPMC8371107 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

High-performance thermoelectric silver selenide thin films cation exchanged from a copper selenide template.

Project description:Over the past decade, Ag2Se has attracted increasing attention due to its potentially excellent thermoelectric (TE) performance as an n-type semiconductor. It has been considered a promising alternative to Bi-Te alloys and other commonly used yet toxic and/or expensive TE materials. To optimize the TE performance of Ag2Se, recent research has focused on fabricating nanosized Ag2Se. However, synthesizing Ag2Se nanoparticles involves energy-intensive and time-consuming techniques with poor yield of final product. In this work, we report a low-cost, solution-processed approach that enables the formation of Ag2Se thin films from Cu2-x Se template films via cation exchange at room temperature. Our simple two-step method involves fabricating Cu2-x Se thin films by the thiol-amine dissolution of bulk Cu2Se, followed by soaking Cu2-x Se films in AgNO3 solution and annealing to form Ag2Se. We report an average power factor (PF) of 617 ± 82 μW m-1 K-2 and a corresponding ZT value of 0.35 at room temperature. We obtained a maximum PF of 825 μW m-1 K-2 and a ZT value of 0.46 at room temperature for our best-performing Ag2Se thin-film after soaking for 5 minutes. These high PFs have been achieved via full solution processing without hot-pressing.

| S-EPMC9416934 | biostudies-literature

3D extruded composite thermoelectric threads for flexible energy harvesting.

Project description:Whereas the rigid nature of standard thermoelectrics limits their use, flexible thermoelectric platforms can find much broader applications, for example, in low-power, wearable energy harvesting for internet-of-things applications. Here we realize continuous, flexible thermoelectric threads via a rapid extrusion of 3D-printable composite inks (Bi2Te3 n- or p-type micrograins within a non-conducting polymer as a binder) followed by compression through a roller-pair, and we demonstrate their applications in flexible, low-power energy harvesting. The thermoelectric power factors of these threads are enhanced up to 7 orders-of-magnitude after lateral compression, principally due to improved conductivity resulting from reduced void volume fraction and partial alignment of thermoelectric micrograins. This dependence is quantified using a conductivity/Seebeck vise for pressure-controlled studies. The resulting grain-to-grain conductivity is well explained with a modified percolation theory to model a pressure-dependent conductivity. Flexible thermoelectric modules are demonstrated to utilize thermal gradients either parallel or transverse to the thread direction.

| S-EPMC6897922 | biostudies-literature

Screen-Printed Flexible Thermoelectric Device Based on Hybrid Silver Selenide/PVP Composite Films.

Project description:In recent years, the preparation of flexible thermoelectric generators by screen printing has attracted wide attention due to easy processing and high-volume production. In this work, we propose an n-type Ag2Se/polymer polyvinylpyrrolidone (PVP) film based on screen printing and investigate the effect of PVP on thermoelectric performance by varying the ratio of PVP. When the content ratio of Ag2Se to PVP is 30:1, i.e., PI30, the fabricated PI30 film has the best thermoelectric property. The maximum power factor (PF) of the PI30 is 4.3 μW·m-1·K-2, and conductivity reaches 81% of its initial value at 1500 bending cycles. Then, the film thermoelectric generator (F-TEG) fabricated by PI30 is tested for practical application; the output voltage and the maximum output power are 21.6 mV and 233.3 nW at the temperature difference of 40 K, respectively. This work demonstrates that the use of PVP combined with screen printing to prepare F-TEG is a simple and rapid method, which provides an efficient preparation solution for the development of environmentally friendly and wearable flexible thermoelectric devices.

| S-EPMC8401139 | biostudies-literature

Thermoelectric Flexible Silver Selenide Films: Compositional and Length Optimization.

Project description:Silver selenide is considered as a promising room temperature thermoelectric material due to its excellent performance and high abundance. However, the silver selenide-based flexible film is still behind in thermoelectric performance compared with its bulk counterpart. In this work, the composition of paper-supported silver selenide film was successfully modulated through changing reactant ratio and annealing treatment. In consequence, the power factor value of 2450.9 ± 364.4 ?W/(mK2) at 303 K, which is close to that of state-of-the-art bulk Ag2Se has been achieved. Moreover, a thermoelectric device was fabricated after optimizing the length of annealed silver selenide film via numerical simulation. At temperature difference of 25 K, the maximum power density of this device reaches 5.80 W/m2, which is superior to that of previous film thermoelectric devices. Theoretically and experimentally, this work provides an effective way to achieve silver-selenide-based flexible thermoelectric film and device with high performance.

| S-EPMC6941873 | biostudies-literature

Multifunctional Magnetic Nanocolloids for Hybrid Solar-Thermoelectric Energy Harvesting.

Project description:Present environmental issues force the research to explore radically new concepts in sustainable and renewable energy production. In the present work, a functional fluid consisting of a stable colloidal suspension of maghemite magnetic nanoparticles in water was characterized from the points of view of thermoelectrical and optical properties, to evaluate its potential for direct electricity generation from thermoelectric effect enabled by the absorption of sunlight. These nanoparticles were found to be an excellent solar radiation absorber and simultaneously a thermoelectric power-output enhancer with only a very small volume fraction when the fluid was heated from the top. These findings demonstrate the investigated nanofluid's high promise as a heat transfer fluid for co-generating heat and power in brand new hybrid flat-plate solar thermal collectors where top-heating geometry is imposed.

| S-EPMC8074063 | biostudies-literature

Preparation of UV-Curable Low Surface Energy Polyurethane Acrylate/Fluorinated Siloxane Resin Hybrid Coating with Enhanced Surface and Abrasion Resistance Properties.

Project description:Low surface energy coatings have gained considerable attention due to their superior surface hydrophobic properties. However, their abrasion resistance and sustainability of surface hydrophobicity are still not very satisfactory and need to be improved. In this work, a series of utraviolet (UV)-curable fluorosiloxane copolymers were synthesized and used as reactive additives to prepare polyurethane acrylate coatings with low surface energy. The effect of the addition of the fluorinated graft copolymers on the mechanical durability and surface hydrophobicity of the UV-cured hybrid films during the friction-annealing treatment cycles was investigated. The results show that introducing fluorosiloxane additives can greatly enhance surface hydrophobicity of the hybrid film. With addition of 2 wt.% fluorosiloxane copolymers, the water contact angle (WCA) value of the hybrid film was almost tripled compared to that of the pristine PU film, increasing from 58° to 144°. The hybrid film also showed enhanced abrasion resistance and could withstand up to about 60 times of friction under a pressure of 20 kPa. The microstructure formed in the annealed film was found to contribute much to achieve better surface hydrophobicity. The polyurethane acrylate/fluorinated siloxane resin hybrid film prepared in this study exhibits excellent potential for applications in the low surface energy field.

| S-EPMC7143720 | biostudies-literature

Compliant and stretchable thermoelectric coils for energy harvesting in miniature flexible devices.

Project description:With accelerating trends in miniaturization of semiconductor devices, techniques for energy harvesting become increasingly important, especially in wearable technologies and sensors for the internet of things. Although thermoelectric systems have many attractive attributes in this context, maintaining large temperature differences across the device terminals and achieving low-thermal impedance interfaces to the surrounding environment become increasingly difficult to achieve as the characteristic dimensions decrease. Here, we propose and demonstrate an architectural solution to this problem, where thin-film active materials integrate into compliant, open three-dimensional (3D) forms. This approach not only enables efficient thermal impedance matching but also multiplies the heat flow through the harvester, thereby increasing the efficiencies for power conversion. Interconnected arrays of 3D thermoelectric coils built using microscale ribbons of monocrystalline silicon as the active material demonstrate these concepts. Quantitative measurements and simulations establish the basic operating principles and the key design features. The results suggest a scalable strategy for deploying hard thermoelectric thin-film materials in harvesters that can integrate effectively with soft materials systems, including those of the human body.

| S-EPMC6214638 | biostudies-literature

High-Performance, UV-Curable Crosslinked Films via Grafting of Hydroxyethyl Methacrylate Methylene Malonate.

Project description:Thermoset coatings have been used extensively to protect and enhance the appearance of substrates for industrial maintenance and architectural applications. Here, we demonstrate that anionic polymerization can be used to first graft hydroxyethyl methacrylate methylene malonate (HEMA-MM) onto a latex particle at ambient conditions, while subsequent ultraviolet (UV) exposure enabled their crosslinking into robust coatings. At room temperature, in the presence of air and water, the polymerization of HEMA-MM was initiated by anionic carboxyl groups present on the MAA latex particles and subsequently grafted onto the surface of particles. The pendent hydroxyethyl methacrylate (HEMA) group enabled UV-curing via free radical polymerization and the formation of a crosslinked network. Systematic investigations were conducted to study the formation and performance of the crosslinked coatings as a function of HEMA-MM incorporation. The incorporation of 10 wt% HEMA-MM into MAA latex yielded crosslinked coatings with decreased swelling, a heightened glass transition temperature (by ~20 °C) and a 2.9-fold improvement in the Young's moduli compared to controls (without HEMA-MM). Here, we demonstrate a facile method that provides a one-step grafting-functionalization approach using functional methylene malonates to produce UV-curable and high-performance coatings at room temperature and under atmospheric environments.

| S-EPMC8153410 | biostudies-literature

Ultrastable and High-Performance Silk Energy Harvesting Textiles.

Project description:Energy harvesting textiles (EHTs) have attracted much attention in wearable electronics and the internet-of-things for real-time mechanical energy harvesting associated with human activities. However, to satisfy practical application requirements, especially the demand for long-term use, it is challenging to construct an energy harvesting textile with elegant trade-off between mechanical and triboelectric performance. In this study, an energy harvesting textile was constructed using natural silk inspired hierarchical structural designs combined with rational material screening; this design strategy provides multiscale opportunities to optimize the mechanical and triboelectric performance of the final textile system. The resulting EHTs with traditional advantages of textiles showed good mechanical properties (tensile strength of 237 ± 13 MPa and toughness of 4.5 ± 0.4 MJ m-3 for single yarns), high power output (3.5 mW m-2), and excellent structural stability (99% conductivity maintained after 2.3 million multi-type cyclic deformations without severe change in appearance), exhibiting broad application prospects in integrated intelligent clothing, energy harvesting, and human-interactive interfaces.

| S-EPMC7770758 | biostudies-literature

Thermoelectric coupling effect in BNT-BZT-xGaN pyroelectric ceramics for low-grade temperature-driven energy harvesting.

Project description:Pyroelectric energy harvesting has received increasing attention due to its ability to convert low-grade waste heat into electricity. However, the low output energy density driven by low-grade temperature limits its practical applications. Here, we show a high-performance hybrid BNT-BZT-xGaN thermal energy harvesting system with environmentally friendly lead-free BNT-BZT pyroelectric matrix and high thermal conductivity GaN as dopant. The theoretical analysis of BNT-BZT and BNT-BZT-xGaN with x = 0.1 wt% suggests that the introduction of GaN facilitates the resonance vibration between Ga and Ti, O atoms, which not only contributes to the enhancement of the lattice heat conduction, but also improves the vibration of TiO6 octahedra, resulting in simultaneous improvement of thermal conductivity and pyroelectric coefficient. Therefore, a thermoelectric coupling enhanced energy harvesting density of 80 μJ cm-3 has been achieved in BNT-BZT-xGaN ceramics with x = 0.1 wt% driven by a temperature variation of 2 oC, at the optical load resistance of 600 MΩ.

| S-EPMC10689474 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data