Effect of New Eco-Polyols Based on PLA Waste on the Basic Properties of Rigid Polyurethane and Polyurethane/Polyisocyanurate Foams.

ABSTRACT: The aim of the presented research was to obtain two new eco-polyols based on waste polylactide (PLA) and to check the effect on the properties of rigid polyurethane (RPU) foams and, based on these, rigid polyurethane/polyisocyanurate (RPU/PIR) foams. The synthesis of eco-polyols was based on the transesterification reaction of melted PLA with diethylene glycol in the presence of an organometallic catalyst. Properties of the obtained eco-polyols were examined for their potential as raw materials for synthesis of rigid polyurethane and polyisocyanurate foams, i.e., hydroxyl value, acid value, density, viscosity, pH, water content. Spectroscopic studies (FTIR, ¹H NMR and ¹³C NMR) were also carried out. Results of these tests confirmed the assumed chemical structure of the new polyols. RPU and RPU/PIR foam formulations were developed based on the obtained analytical results. Partial replacement of petrochemical polyol by eco-polyols in RPU and RPU/PIR foams decreased the value of apparent density, compressive strength, brittleness and water absorption. Moreover, all foams modified by eco-polyols showed higher resistance to aging. All RPU/PIR foams and most PRU foams modified by eco-polyols from waste PLA had better functional properties than the reference foams based on petrochemical polyol.

SUBMITTER: Borowicz M

PROVIDER: S-EPMC8396538 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Rigid Polyurethane Foams with Various Isocyanate Indices Based on Polyols from Rapeseed Oil and Waste PET.

Project description:Developing polyols derived from natural sources and recycling materials attracts great interest for use in replacing petroleum-based polyols in polyurethane production. In this study, rigid polyurethane (PUR) foams with various isocyanate indices were obtained from polyols based on rapeseed oil and polyethylene terephthalate (RO/PET). The various properties of the prepared PUR foams were investigated, and the effect of the isocyanate index was evaluated. The closed-cell content and water absorption were not impacted by the change of the isocyanate index. The most significant effect of increasing the isocyanate index was on the dimensional stability of the resulting foams. This is due to the increased crosslink density, as evidenced by the increased formation of isocyanurate and increase of the glass transition temperature. Additionally, the influence on compression strength, modulus, and long-term thermal conductivity were evaluated and compared with reference PUR foams from commercially available polyols. Rigid PUR foams from RO/PET polyol were found to be competitive with reference materials and could be used as thermal insulation material.

| S-EPMC7240454 | biostudies-literature

Biodegradable, Flame-Retardant, and Bio-Based Rigid Polyurethane/Polyisocyanurate Foams for Thermal Insulation Application.

Project description:This article raised the issue of studies on the use of new bio-polyol based on white mustard seed oil and 2,2'-thiodiethanol (3-thiapentane-1,5-diol) for the synthesis of rigid polyurethane/polyisocyanurate (RPU/PIR) foams. For this purpose, new formulations of polyurethane materials were prepared. Formulations contained bio-polyol content from 0 to 0.4 chemical equivalents of hydroxyl groups. An industrial flame retardant, tri(2-chloro-1-methylethyl) phosphate (Antiblaze TCMP), was added to half of the formulations. Basic foaming process parameters and functional properties, such as apparent density, compressive strength, brittleness, absorbability and water absorption, aging resistance, thermal conductivity coefficient λ, structure of materials, and flammability were examined. The susceptibility of the foams to biodegradation in soil was also examined. The increase in the bio-polyol content caused a slight increase in processing times. Also, it was noted that the use of bio-polyol had a positive effect on the functional properties of obtained RPU/PIR foams. Foams modified by bio-polyol based on mustard seed oil showed lower apparent density, brittleness, compressive strength, and absorbability and water absorption, as well as thermal conductivity, compared to the reference (unmodified) foams. Furthermore, the obtained materials were more resistant to aging and more susceptible to biodegradation.

| S-EPMC6918136 | biostudies-literature

High Functionality Bio-Polyols from Tall Oil and Rigid Polyurethane Foams Formulated Solely Using Bio-Polyols.

Project description:High-quality rigid polyurethane (PU) foam thermal insulation material has been developed solely using bio-polyols synthesized from second-generation bio-based feedstock. High functionality bio-polyols were synthesized from cellulose production side stream-tall oil fatty acids by oxirane ring-opening as well as esterification reactions with different polyfunctional alcohols, such as diethylene glycol, trimethylolpropane, triethanolamine, and diethanolamine. Four different high functionality bio-polyols were combined with bio-polyol obtained from tall oil esterification with triethanolamine to develop rigid PU foam formulations applicable as thermal insulation material. The developed formulations were optimized using response surface modeling to find optimal bio-polyol and physical blowing agent: c-pentane content. The optimized bio-based rigid PU foam formulations delivered comparable thermal insulation properties to the petro-chemical alternative.

| S-EPMC7215456 | biostudies-literature

Use of a Mixture of Polyols Based on Metasilicic Acid and Recycled PLA for Synthesis of Rigid Polyurethane Foams Susceptible to Biodegradation.

Project description:Two polyol raw materials were obtained in the conducted research, one based on metasilicic acid (MSA), the other based on poly(lactic acid) (PLA) waste. The obtained polyols were characterized in terms of their applicability for the production of rigid polyurethane foams (RPUFs). Their basic analytical properties (hydroxyl number, acid number, elemental analysis) and physicochemical properties (density, viscosity) were determined. The assumed chemical structure of the obtained new compounds was confirmed by performing FTIR and 1H NMR spectroscopic tests. Formulations for the synthesis of RPUFs were developed on the basis of the obtained research results. A mixture of polyols based on MSA and PLA in a weight ratio of 1:1 was used as the polyol component in the polyurethane formulation. The reference foam in these tests was a foam that was synthesized only on the basis of MSA-polyol. The obtained RPUFs were tested for basic functional properties (apparent density, compressive strength, water absorption, thermal conductivity coefficient etc.). Susceptibility to biodegradation in soil environment was also tested. It was found that the use of mixture of polyols based on MSA and PLA positively affected the properties of the obtained foam. The polyurethane foam based on this polyol mixture showed good thermal resistance and significantly reduced flammability in comparison with the foam based MSA-polyol. Moreover, it showed higher compressive strength, lower thermal conductivity and biodegradability in soil. The results of the conducted tests confirmed that the new foam was characterized by very good performance properties. In addition, this research provides information on new waste management opportunities and fits into the doctrine of sustainable resource management offered by the circular economy.

| S-EPMC7795053 | biostudies-literature

Recovery of Green Polyols from Rigid Polyurethane Waste by Catalytic Depolymerization.

Project description:Polyurethane (PU) is one of the most versatile polymers available and can be found in an infinite number of formats ranging from rigid or flexible foams to elastomers. Currently, most Rigid PU Foam (RPUF) waste is landfilled, even though a small amount is mechanically recycled, in which the material is conditioned in size to a very fine powder, which is introduced as a filler. In this work, chemical recycling of two types of rigid PU foams is studied, the major difference being the aliphatic or aromatic nature of the isocyanate used in the synthesis. A solvolysis process is developed, a chemical depolymerization that breaks the chains by means of a chemical agent, a solvent, in the presence of a catalyst and under controlled process conditions. The glycolysis products are purified by vacuum distillation, centrifugation, and acid water treatment, depending on the most suitable process for each waste type. Optimal process conditions are established to obtain high-purity green polyols by performing a set of catalytic glycolysis reactions at laboratory scale with the previously conditioned RPUF waste samples. The physicochemical properties of the polyols, such as hydroxyl value, acid value, average molecular weight (Mn), and viscosity, are analyzed. The chemical structure and thermal stability of the polyols are studied by means of FTIR and TGA, respectively. Partial substitution of the commercial polyol (up to 15 wt.%) by the recycled polyols for RPUF synthesis is studied and characterized.

| S-EPMC9319047 | biostudies-literature

Comparing the Properties of Bio-Polyols Based on White Mustard (<i>Sinapis alba</i>) Oil Containing Boron and Sulfur Atoms Obtained by Various Methods and Checking Their Influence on the Flammability of Rigid Polyurethane/Polyisocyanurate Foams.

Project description:The article compares the properties of bio-polyols obtained from white mustard (Sinapis alba) seed oil, which contain boron and sulfur atoms. Each of the bio-polyols was prepared by a different method of testing the efficiency of the incorporation of boron and sulfur atoms. All synthesis methods were based on the epoxidation of unsaturated bonds followed by the opening of epoxy rings by compounds containing heteroatoms. Two of the bio-polyols were subjected to additional esterification reactions of hydroxyl groups with boric acid or its ester. Three new bio-polyols were obtained as a result of the performed syntheses. The synthesized compounds were subjected to detailed physicochemical (physical state, color, smell, density, viscosity and pH), analytical (hydroxyl number, acid number, water content, content of C, H, N, S, O, B elements and GPC analysis), spectroscopic (FTIR, 1H NMR and 13C NMR) and thermal (DSC) tests. The obtained results allowed for a detailed characterization of the synthesized bio-polyol raw materials. Their suitability for obtaining polyurethane materials was also determined. The synthesized compounds have been found to be an interesting alternative to petrochemical polyols. The influence of the synthesized compounds on the flammability of polyurethane materials was tested experimentally. On the basis of this testing, a number of rigid polyurethane/polyisocyanurate foams were obtained, which were then subjected to flammability tests with the methods of horizontal and vertical burning, limiting oxygen index (LOI) and using the cone calorimeter. Based on this research, it was found that the presence of sulfur and boron heteroatoms reduced the flammability of polyurethane materials based on synthesized bio-polyols.

| S-EPMC10180400 | biostudies-literature

Life Cycle Assessment of Polyurethane Foams from Polyols Obtained through Chemical Recycling.

Project description:In this research, the results of the life cycle assessment of polyurethane (PUR) foams with different recycled polyol contents are presented. A methodological framework implementing laboratory activities directly into the life cycle assessment has been developed. Laboratory activities made the primary data related to the recycled polyol production available through the glycolysis of polyurethane scraps and the subsequent production and characterization of the foams. Five different formulations were analyzed with glycolyzed polyol content ranging from 0 to 100%. A comprehensive set of impact categories was considered. To ensure the robustness of the results, the influence of two different end-of-life allocation approaches was investigated, and the model was subjected to sensitivity and uncertainty analyses. Formulations with recycled content of 50 and 75% scored better environmental impacts compared to others. The main contributions to the overall impact resulted to be related to the production of isocyanate and virgin polyol. Physical characteristics such as density and thermal conductivity emerged as the main variables to be considered to minimize the overall environmental impacts of PUR foams.

| S-EPMC7818590 | biostudies-literature

Light Microscopy of Medium-Density Rigid Polyurethane Foams Filled with Nanoclay.

Project description:Practical applications and mathematical modelling of the physical and mechanical properties of medium-density rigid polyurethane foams require knowledge of their structure. It is necessary to determine structural characteristics without destroying the foams and measuring each element. A methodology is described for the use of light microscopy on environmentally sustainable, medium-density rigid polyurethane foams (in the density region of ≈210-230 kg/m3), by the analysis of two types of light microscopy images: (1) Cutting surface images; and (2) Through-cutting surface images. The dimensions of structural elements of polyurethane foams, filled with the nanoclay Cloisite-30B at concentrations of 0.0%, 0.25%, 0.50%, 1.0%, 2.0%, 3.0%, and 5.0% from the mass of the filled reacting mixture, are estimated. Probability density functions of projections of bubbles' diameters and struts' length are determined using images in three mutually perpendicular planes. A mathematical model is developed for the restoration of the actual dimensions of bubbles' diameters using data of cutting circles' diameters. Intercalation and exfoliation of the filler's Cloisite-30B mono-layers is evaluated via the basal spacing by X-ray diffraction at a 5 wt.% concentration of nanoclay.

| S-EPMC8955111 | biostudies-literature

Polyols from Microwave Liquefied Bagasse and Its Application to Rigid Polyurethane Foam.

Project description:Bagasse flour (BF) was liquefied using bi-component polyhydric alcohol (PA) as a solvent and phosphoric acid as a catalyst in a microwave reactor. The effect of BF to solvent ratio and reaction temperatures on the liquefaction extent and characteristics of liquefied products were evaluated. The results revealed that almost 75% of the raw bagasse was converted into liquid products within 9 min at 150 °C with a BF to solvent ratio of 1/4. The hydroxyl and acid values of the liquefied bagasse (LB) varied with the liquefied conditions. High reaction temperature combining with low BF to solvent ratio resulted in a low hydroxyl number for the LB. The molecular weight and polydispersity of the LB from reactions of 150 °C was lower compared to that from 125 °C. Rigid polyurethane (PU) foams were prepared from LB and methylene diphenyl diisocyanate (MDI), and the structural, mechanical and thermal properties of the PU foam were evaluated. The PU foams prepared using the LB from high reaction temperature showed better physical and mechanical performance in comparison to those from low reaction temperature. The amount of PA in the LB has the ability of increasing thermal stability of LB-PU foams. The results in this study may provide fundamental information on integrated utilizations of sugarcane bagasse via microwave liquefaction process.

| S-EPMC5458812 | biostudies-other

Producing Lignin-Based Polyols through Microwave-Assisted Liquefaction for Rigid Polyurethane Foam Production.

Project description:Lignin-based polyols were synthesized through microwave-assisted liquefaction under different microwave heating times (5-30 min). The liquefaction reactions were carried out using polyethylene glycol (PEG-400)/glycerol as liquefying solvents and 97 wt% sulfur acid as a catalyst at 140 °C. The polyols obtained were analyzed for their yield, composition and structural characteristics using gel permeation chromatography (GPC), Fourier transform infrared (FT-IR) and nuclear magnetic resonance (NMR) spectra. FT-IR and NMR spectra showed that the liquefying solvents reacted with the phenol hydroxyl groups of the lignin in the liquefied product. With increasing microwave heating time, the viscosity of polyols was slightly increased and their corresponding molecular weight (MW) was gradually reduced. The optimal condition at the microwave heating time (5 min) ensured a high liquefaction yield (97.47%) and polyol with a suitable hydroxyl number (8.628 mmol/g). Polyurethane (PU) foams were prepared by polyols and methylene diphenylene diisocyanate (MDI) using the one-shot method. With the isocyanate/hydroxyl group ([NCO]/[OH]) ratio increasing from 0.6 to 1.0, their mechanical properties were gradually increased. This study provided some insight into the microwave-assisted liquefied lignin polyols for the production of rigid PU foam.

| S-EPMC5455266 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data