Effective Solid Electrolyte Interphase Formation on Lithium Metal Anodes by Mechanochemical Modification.
Ontology highlight
ABSTRACT:
SUBMITTER: Wellmann J
PROVIDER: S-EPMC8397250 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:The notorious lithium dendrite growth, causing the safety concern, hinders the practical application of high-capacity Li metal anodes for rechargeable batteries. Here, a robust and highly ionic conductive solid electrolyte interphase (SEI) layer to protect Li metal anode is in-situ constructed by introducing trace additive of tetrapotassium heptaiodobismuthate (K4BiI7) into electrolyte. The K4BiI7-added electrolyte enables Li metal anode to display a stable cycling for over 600 cycles at 1.0 mA cm-2/1.0 mAh cm-2 and over 400 cycles at 5.0 mA cm-2/5.0 mAh cm-2. In situ optical microscopy observations also conform the suppression of Li dendrites at high current density. Moreover, the in-situ SEI layer modified Li anode exhibits an average Coulombic efficiency of 99.57% and less Li dendrite growth. The Li-S full sells with the modified electrolyte also show improved electrochemical performance. This research provides a cost-efficient method to achieve a highly ionic conductive and stable SEI layer toward advanced Li metal anodes.
| S-EPMC6990125 | biostudies-literature
Project description:Lithium stripping is a crucial process coupled with lithium deposition during the cycling of Li metal batteries. Lithium deposition has been widely studied, whereas stripping as a subsurface process has rarely been investigated. Here we reveal the fundamental mechanism of stripping on lithium by visualizing the interface between stripped lithium and the solid electrolyte interphase (SEI). We observed nanovoids formed between lithium and the SEI layer after stripping, which are attributed to the accumulation of lithium metal vacancies. High-rate dissolution of lithium causes vigorous growth and subsequent aggregation of voids, followed by the collapse of the SEI layer, i.e., pitting. We systematically measured the lithium polarization behavior during stripping and find that the lithium cation diffusion through the SEI layer is the rate-determining step. Nonuniform sites on typical lithium surfaces, such as grain boundaries and slip lines, greatly accelerated the local dissolution of lithium. The deeper understanding of this buried interface stripping process provides beneficial clues for future lithium anode and electrolyte design.
| S-EPMC6112724 | biostudies-literature
Project description:Lithium metal is a promising anode candidate for the next-generation rechargeable battery due to its highest specific capacity (3860?mA?h?g-1) and lowest potential, but low Coulombic efficiency and formation of lithium dendrites hinder its practical application. Here, we report a self-formed flexible hybrid solid-electrolyte interphase layer through co-deposition of organosulfides/organopolysulfides and inorganic lithium salts using sulfur-containing polymers as an additive in the electrolyte. The organosulfides/organopolysulfides serve as "plasticizer" in the solid-electrolyte interphase layer to improve its mechanical flexibility and toughness. The as-formed robust solid-electrolyte interphase layers enable dendrite-free lithium deposition and significantly improve Coulombic efficiency (99% over 400 cycles at a current density of 2?mA?cm-2). A lithium-sulfur battery based on this strategy exhibits long cycling life (1000 cycles) and good capacity retention. This study reveals an avenue to effectively fabricate stable solid-electrolyte interphase layer for solving the issues associated with lithium metal anodes.The practical application of lithium metal anodes suffers from the poor Coulombic efficiency and growth of lithium dendrites. Here, the authors report an approach to enable the self-formation of stable and flexible solid-electrolyte interphase layers which serve to address both issues.
| S-EPMC5636837 | biostudies-other
Project description:With increasing demand for high-capacity and rapidly rechargeable anodes, problems associated with unstable evolution of a solid-electrolyte interphase on the active anode surface become more detrimental. Here, we report the near fatigue-free, ultrafast, and high-power operations of lithium-ion battery anodes employing silicide nanowires anchored selectively to the inner surface of graphene-based micro-tubular conducting electrodes. This design electrically shields the electrolyte inside the electrode from an external potential load, eliminating the driving force that generates the solid-electrolyte interphase on the nanowire surface. Owing to this electric control, a solid-electrolyte interphase develops firmly on the outer surface of the graphene, while solid-electrolyte interphase-free nanowires enable fast electronic and ionic transport, as well as strain relaxation over 2000 cycles, with 84% capacity retention even at ultrafast cycling (>20C). Moreover, these anodes exhibit unprecedentedly high rate capabilities with capacity retention higher than 88% at 80C (vs. the capacity at 1C).
| S-EPMC6110779 | biostudies-literature
Project description:For Li-air batteries, dissolved gas can cross over from the air electrode to the Li metal anode and affect the solid-electrolyte interphase (SEI) formation, a phenomenon that has not been fully characterized. In this work, the impact of atmospheric gases on the SEI properties is studied using electrochemical methods and ex situ characterization techniques, including X-ray photoelectron spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and scanning electron microscopy. The presence of O2 significantly improved the lithium cyclability; less lithium is consumed to form the SEI or is lost because of electrical disconnects. However, the SEI resistivity and plating overpotentials increased. Lithium cycled in an "air-like" mixed O2/N2 environment also demonstrated improved cycling efficiency, suggesting that dissolved O2 participates in electrolyte reduction, forming a homogeneous SEI, even at low concentrations. The impact of gas environments on Li metal plating and SEI formation represents an additional parameter in designing future Li-metal batteries.
| S-EPMC7155172 | biostudies-literature
Project description:Aqueous lithium energy storage systems address environmental sustainability and safety issues. However, significant capacity fading after repeated cycles of charge-discharge and during float charge limit their practical application compared to their nonaqueous counterparts. We introduce an artificial solid electrolyte interphase (SEI) to the aqueous systems and report the use of graphene films as an artificial SEI (G-SEI) that substantially enhance the overall performance of an aqueous lithium battery and a supercapacitor. The thickness (1 to 50 nm) and the surface area (1 cm2 to 1 m2) of the G-SEI are precisely controlled on the LiMn2O4-based cathode using the Langmuir trough-based techniques. The aqueous battery with a 10-nm-thick G-SEI exhibits a discharge capacity as high as 104 mA·hour g-1 after 600 cycles and a float charge current density as low as 1.03 mA g-1 after 1 day, 26% higher (74 mA·hour g-1) and 54% lower (1.88 mA g-1) than the battery without the G-SEI, respectively. We propose that the G-SEI on the cathode surface simultaneously suppress the structural distortion of the LiMn2O4 (the Jahn-Teller distortion) and the oxidation of conductive carbon through controlled diffusion of Li+ and restricted permeation of gases (O2 and CO x ), respectively. The G-SEI on both small (~1 cm2 in 1.15 mA·hour cell) and large (~9 cm2 in 7 mA·hour cell) cathodes exhibit similar property enhancement, demonstrating excellent potential for scale-up and manufacturing.
| S-EPMC5590782 | biostudies-literature
Project description:Lithium metal anodes have attracted extensive attention owing to their high theoretical specific capacity. However, the notorious reactivity of lithium prevents their practical applications, as evidenced by the undesired lithium dendrite growth and unstable solid electrolyte interphase formation. Here, we develop a facile, cost-effective and one-step approach to create an artificial lithium metal/electrolyte interphase by treating the lithium anode with a tin-containing electrolyte. As a result, an artificial solid electrolyte interphase composed of lithium fluoride, tin, and the tin-lithium alloy is formed, which not only ensures fast lithium-ion diffusion and suppresses lithium dendrite growth but also brings a synergistic effect of storing lithium via a reversible tin-lithium alloy formation and enabling lithium plating underneath it. With such an artificial solid electrolyte interphase, lithium symmetrical cells show outstanding plating/stripping cycles, and the full cell exhibits remarkably better cycling stability and capacity retention as well as capacity utilization at high rates compared to bare lithium.
| S-EPMC6941966 | biostudies-literature
Project description:Lithium metal is strongly regarded as a promising electrode material in next-generation rechargeable batteries due to its extremely high theoretical specific capacity and lowest reduction potential. However, the safety issue and short lifespan induced by uncontrolled dendrite growth have hindered the practical applications of lithium metal anodes. Hence, we propose a flexible anion-immobilized ceramic-polymer composite electrolyte to inhibit lithium dendrites and construct safe batteries. Anions in the composite electrolyte are tethered by a polymer matrix and ceramic fillers, inducing a uniform distribution of space charges and lithium ions that contributes to a dendrite-free lithium deposition. The dissociation of anions and lithium ions also helps to reduce the polymer crystallinity, rendering stable and fast transportation of lithium ions. Ceramic fillers in the electrolyte extend the electrochemically stable window to as wide as 5.5 V and provide a barrier to short circuiting for realizing safe batteries at elevated temperature. The anion-immobilized electrolyte can be applied in all-solid-state batteries and exhibits a small polarization of 15 mV. Cooperated with LiFePO4 and LiNi0.5Co0.2Mn0.3O2 cathodes, the all-solid-state lithium metal batteries render excellent specific capacities of above 150 mAh?g-1 and well withstand mechanical bending. These results reveal a promising opportunity for safe and flexible next-generation lithium metal batteries.
| S-EPMC5651763 | biostudies-literature
Project description:Li+ transport within a solid electrolyte interphase (SEI) in lithium ion batteries has challenged molecular dynamics (MD) studies due to limited compositional control of that layer. In recent years, experiments and ab initio simulations have identified dilithium ethylene dicarbonate (Li2EDC) as the dominant component of SEI layers. Here, we adopt a parameterized, non-polarizable MD force field for Li2EDC to study transport characteristics of Li+ in this model SEI layer at moderate temperatures over long times. The observed correlations are consistent with recent MD results using a polarizable force field, suggesting that this non-polarizable model is effective for our purposes of investigating Li+ dynamics. Mean-squared displacements distinguish three distinct Li+ transport regimes in EDC - ballistic, trapping, and diffusive. Compared to liquid ethylene carbonate (EC), the nanosecond trapping times in EDC are significantly longer and naturally decrease at higher temperatures. New materials developed for fast-charging Li-ion batteries should have a smaller trapping region. The analyses implemented in this paper can be used for testing transport of Li+ ion in novel battery materials. Non-Gaussian features of van Hove self -correlation functions for Li+ in EDC, along with the mean-squared displacements, are consistent in describing EDC as a glassy material compared with liquid EC. Vibrational modes of Li+ ion, identified by MD, characterize the trapping and are further validated by electronic structure calculations. Some of this work appeared in an extended abstract and has been reproduced with permission from ECS Transactions, 77, 1155-1162 (2017).
| S-EPMC6048109 | biostudies-literature
Project description:Extremely fast charging (i.e. 80% of storage capacity within 15 min) is a pressing requirement for current lithium-ion battery technology and also affects the planning of charging infrastructure. Accelerating lithium ion transport through the solid-electrolyte interphase (SEI) is a major obstacle in boosting charging rate; in turn, limited kinetics at the SEI layer negatively affect the cycle life and battery safety as a result of lithium metal plating on the electrode surface. Here, we report a γ-ray-driven SEI layer that allows a battery cell to be charged to 80% capacity in 10.8 min as determined for a graphite full-cell with a capacity of 2.6 mAh cm-2. This exceptional charging performance is attributed to the lithium fluoride-rich SEI induced by salt-dominant decomposition via γ-ray irradiation. This study highlights the potential of non-electrochemical approaches to adjust the SEI composition toward fast charging and long-term stability, two parameters that are difficult to improve simultaneously in typical electrochemical processes owing to the trade-off relation.
| S-EPMC8611023 | biostudies-literature