Mechanochemical Synthesis and Structure of Lithium Tetrahaloaluminates, LiAlX₄ (X = Cl, Br, I): A Family of Li-Ion Conducting Ternary Halides.

ABSTRACT: State-of-the-art oxides and sulfides with high Li-ion conductivity and good electrochemical stability are among the most promising candidates for solid-state electrolytes in secondary batteries. Yet emerging halides offer promising alternatives because of their intrinsic low Li⁺ migration energy barriers, high electrochemical oxidative stability, and beneficial mechanical properties. Mechanochemical synthesis has enabled the characterization of LiAlX₄ compounds to be extended and the iodide, LiAlI₄, to be synthesized for the first time (monoclinic P2₁/c, Z = 4; a = 8.0846(1) Å; b = 7.4369(1) Å; c = 14.8890(2) Å; β = 93.0457(8)°). Of the tetrahaloaluminates, LiAlBr₄ exhibited the highest ionic conductivity at room temperature (0.033 mS cm^-1), while LiAlCl₄ showed a conductivity of 0.17 mS cm^-1 at 333 K, coupled with the highest thermal and oxidative stability. Modeling of the diffusion pathways suggests that the Li-ion transport mechanism in each tetrahaloaluminate is closely related and mediated by both halide polarizability and concerted complex anion motions.

SUBMITTER: Flores-Gonzalez N

PROVIDER: S-EPMC8397468 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Li4.3AlS3.3Cl0.7: A Sulfide-Chloride Lithium Ion Conductor with Highly Disordered Structure and Increased Conductivity.

Project description:Mixed anion materials and anion doping are very promising strategies to improve solid-state electrolyte properties by enabling an optimized balance between good electrochemical stability and high ionic conductivity. In this work, we present the discovery of a novel lithium aluminum sulfide-chloride phase, obtained by substitution of chloride for sulfur in Li3AlS3 and Li5AlS4 materials. The structure is strongly affected by the presence of chloride anions on the sulfur site, as the substitution was shown to be directly responsible for the stabilization of a higher symmetry phase presenting a large degree of cationic site disorder, as well as disordered octahedral lithium vacancies. The effect of disorder on the lithium conductivity properties was assessed by a combined experimental-theoretical approach. In particular, the conductivity is increased by a factor 103 compared to the pure sulfide phase. Although it remains moderate (10-6 S·cm-1), ab initio molecular dynamics and maximum entropy (applied to neutron diffraction data) methods show that disorder leads to a 3D diffusion pathway, where Li atoms move thanks to a concerted mechanism. An understanding of the structure-property relationships is developed to determine the limiting factor governing lithium ion conductivity. This analysis, added to the strong step forward obtained in the determination of the dimensionality of diffusion, paves the way for accessing even higher conductivity in materials comprising an hcp anion arrangement.

| S-EPMC8613839 | biostudies-literature

Mechanochemical synthesis of Li?MnO? shell/LiMO? (M = Ni, Co, Mn) core-structured nanocomposites for lithium-ion batteries.

Project description:Core/shell-like nanostructured xLi2MnO3·(1-x)LiMO2 (M = Ni, Co, Mn) composite cathode materials are successfully synthesized through a simple solid-state reaction using a mechanochemical ball-milling process. The LiMO2 core is designed to have a high-content of Ni, which increases the specific capacity. The detrimental surface effects arising from the high Ni-content are countered by the Li2MnO3 shell, which stabilizes the nanoparticles. The electrochemical performances and thermal stabilities of the synthesized nanocomposites are compared with those of bare LiMO2. In particular, the results of time-resolved X-ray diffraction (TR-XRD) analyses of xLi2MnO3·(1-x)LiMO2 nanocomposites as well as their differential scanning calorimetry (DSC) profiles demonstrate that the Li2MnO3 shell is effective in stabilizing the LiMO2 core at high temperatures, making the nanocomposites highly suitable from a safety viewpoint.

| S-EPMC4007074 | biostudies-literature

Antiperovskite Chalco-Halides Ba3(FeS4)Cl, Ba3(FeS4)Br, and Ba3(FeSe4)Br with Spin Super-Super Exchange.

Project description:Perovskite-related materials have received increasing attention for their broad applications in photovoltaic solar cells and information technology due to their unique electrical and magnetic properties. Here we report three new antiperovskite chalco-halides: Ba3(FeS4)Cl, Ba3(FeS4)Br, and Ba3(FeSe4)Br. All of them were found to be good solar light absorbers. Remarkably, although the shortest Fe-Fe distance exceeds 6?Å, an unexpected anti-ferromagnetic phase transition near 100?K was observed in their magnetic susceptibility measurement. The corresponding complex magnetic structures were resolved by neutron diffraction experiments as well as investigated by first-principles electronic structure calculations. The spin-spin coupling between two neighboring Fe atoms along the b axis, which is realized by the Fe-S···S-Fe super-super exchange mechanism, was found to be responsible for this magnetic phase transition.

| S-EPMC4630630 | biostudies-literature

High Energy Density Single-Crystal NMC/Li6PS5Cl Cathodes for All-Solid-State Lithium-Metal Batteries.

Project description:To match the high capacity of metallic anodes, all-solid-state batteries require high energy density, long-lasting composite cathodes such as Ni-Mn-Co (NMC)-based lithium oxides mixed with a solid-state electrolyte (SSE). However in practice, cathode capacity typically fades due to NMC cracking and increasing NMC/SSE interface debonding because of NMC pulverization, which is only partially mitigated by the application of a high cell pressure during cycling. Using smart processing protocols, we report a single-crystal particulate LiNi0.83Mn0.06Co0.11O2 and Li6PS5Cl SSE composite cathode with outstanding discharge capacity of 210 mA h g-1 at 30 °C. A first cycle coulombic efficiency of >85, and >99% thereafter, was achieved despite a 5.5% volume change during cycling. A near-practical discharge capacity at a high areal capacity of 8.7 mA h cm-2 was obtained using an asymmetric anode/cathode cycling pressure of only 2.5 MPa/0.2 MPa.

| S-EPMC8397257 | biostudies-literature

Effect of current density on the solid electrolyte interphase formation at the lithium∣Li6PS5Cl interface.

Project description:Understanding the chemical composition and morphological evolution of the solid electrolyte interphase (SEI) formed at the interface between the lithium metal electrode and an inorganic solid-state electrolyte is crucial for developing reliable all-solid-state lithium batteries. To better understand the interaction between these cell components, we carry out X-ray photoemission spectroscopy (XPS) measurements during lithium plating on the surface of a Li6PS5Cl solid-state electrolyte pellet using an electron beam. The analyses of the XPS data highlight the role of Li plating current density on the evolution of a uniform and ionically conductive (i.e., Li3P-rich) SEI capable of decreasing the electrode∣solid electrolyte interfacial resistance. The XPS findings are validated via electrochemical impedance spectrsocopy measurements of all-solid-state lithium-based cells.

| S-EPMC9700819 | biostudies-literature

Mechanochemical synthesis of Si/Cu3Si-based composite as negative electrode materials for lithium ion battery.

Project description:Mechanochemical synthesis of Si/Cu3Si-based composite as negative electrode materials for lithium ion battery is investigated. Results indicate that CuO is decomposed and alloyed with Si forming amorphous Cu-Si solid solution due to high energy impacting during high energy mechanical milling (HEMM). Upon carbonization at 800 °C, heating energy induces Cu3Si to crystallize in nanocrystalline/amorphous Si-rich matrix enhancing composite rigidity and conductivity. In addition, residual carbon formed on outside surface of composite powder as a buff space further alleviates volume change upon lithiation/delithiation. Thus, coin cell made of C-coated Si/Cu3Si-based composite as negative electrode (active materials loading, 2.3 mg cm-2) conducted at 100 mA g-1 performs the initial charge capacity of 1812 mAh g-1 (4.08 mAh cm-2) columbic efficiency of 83.7% and retained charge capacity of 1470 mAh g-1 (3.31 mAh cm-2) at the end of the 100th cycle, opening a promised window as negative electrode materials for lithium ion batteries.

| S-EPMC6107536 | biostudies-literature

Ionic and Electronic Conductivities of Lithium Argyrodite Li6PS5Cl Electrolytes Prepared via Wet Milling and Post-Annealing.

Project description:Lithium argyrodite Li6PS5Cl powders are synthesized from Li2S, P2S5, and LiCl via wet milling and post-annealing at 500°C for 4 h. Organic solvents such as hexane, heptane, toluene, and xylene are used during the wet milling process. The phase evolution, powder morphology, and electrochemical properties of the wet-milled Li6PS5Cl powders and electrolytes are studied. Compared to dry milling, the processing time is significantly reduced via wet milling. The nature of the solvent does not affect the ionic conductivity significantly; however, the electronic conductivity changes noticeably. The study indicates that xylene and toluene can be used for the wet milling to synthesize Li6PS5Cl electrolyte powder with low electronic and comparable ionic conductivities. The all-solid-state cell with the xylene-processed Li6PS5Cl electrolyte exhibits the highest discharge capacity of 192.4 mAh·g-1 and a Coulombic efficiency of 81.3% for the first discharge cycle.

| S-EPMC8717468 | biostudies-literature

Thermal Decomposition Study on Li2O2 for Li2NiO2 Synthesis as a Sacrificing Positive Additive of Lithium-Ion Batteries.

Project description:Herein, thermal decomposition experiments of lithium peroxide (Li2O2) were performed to prepare a precursor (Li2O) for sacrificing cathode material, Li2NiO2. The Li2O2 was prepared by a hydrometallurgical reaction between LiOH·H2O and H2O2. The overall reaction during annealing was found to involve the following three steps: (1) dehydration of LiOH·H2O, (2) decomposition of Li2O2, and (3) pyrolysis of the remaining anhydrous LiOH. This stepwise reaction was elucidated by thermal gravimetric and quantitative X-ray diffraction analyses. Furthermore, over-lithiated lithium nickel oxide (Li2NiO2) using our lithium precursor was synthesized, which exhibited a larger yield of 90.9% and higher irreversible capacity of 261 to 265 mAh g-1 than the sample prepared by commercially purchased Li2O (45.6% and 177 to 185 mAh g-1, respectively) due to optimal powder preparation conditions.

| S-EPMC6943730 | biostudies-literature

Sub-micro droplet reactors for green synthesis of Li3VO4 anode materials in lithium ion batteries.

Project description:The conventional solid-state reaction suffers from low diffusivity, high energy consumption, and uncontrolled morphology. These limitations are competed by the presence of water in solution route reaction. Herein, based on concept of combining above methods, we report a facile solid-state reaction conducted in water vapor at low temperature along with calcium doping for modifying lithium vanadate as anode material for lithium-ion batteries. The optimized material, delivers a superior specific capacity of 543.1, 477.1, and 337.2 mAh g-1 after 200 and 1000 cycles at current densities of 100, 1000 and 4000 mA g-1, respectively, which is attributed to the contribution of pseudocapacitance. In this work, we also use experimental and theoretical calculation to demonstrate that the enhancement of doped lithium vanadate is attributed to particles confinement of droplets in water vapor along with the surface and structure variation of calcium doping effect.

| S-EPMC8149873 | biostudies-literature

Low dimensional nanostructures of fast ion conducting lithium nitride.

Project description:As the only stable binary compound formed between an alkali metal and nitrogen, lithium nitride possesses remarkable properties and is a model material for energy applications involving the transport of lithium ions. Following a materials design principle drawn from broad structural analogies to hexagonal graphene and boron nitride, we demonstrate that such low dimensional structures can also be formed from an s-block element and nitrogen. Both one- and two-dimensional nanostructures of lithium nitride, Li3N, can be grown despite the absence of an equivalent van der Waals gap. Lithium-ion diffusion is enhanced compared to the bulk compound, yielding materials with exceptional ionic mobility. Li3N demonstrates the conceptual assembly of ionic inorganic nanostructures from monolayers without the requirement of a van der Waals gap. Computational studies reveal an electronic structure mediated by the number of Li-N layers, with a transition from a bulk narrow-bandgap semiconductor to a metal at the nanoscale.

| S-EPMC7479578 | biostudies-literature