Mechanical and Compositional Implications of Gallium Ion Milling on Epoxy Resin.

ABSTRACT: Focused Ion Beam (FIB) is one of the most common methods for nanodevice fabrication. However, its implications on mechanical properties of polymers have only been speculated. In the current study, we demonstrated flexural bending of FIB-milled epoxy nanobeam, examined in situ under a transmission electron microscope (TEM). Controllable displacement was applied, while real-time TEM videos were gathered to produce morphological data. EDS and EELS were used to characterize the compositions of the resultant structure, and a computational model was used, together with the quantitative results of the in situ bending, to mechanically characterize the effect of Ga⁺ ions irradiation. The damaged layer was measured at 30 nm, with high content of gallium (40%). Examination of the fracture revealed crack propagation within the elastic region and rapid crack growth up to fracture, attesting to enhanced brittleness. Importantly, the nanoscale epoxy exhibited a robust increase in flexural strength, associated with chemical tempering and ion-induced peening effects, stiffening the outer surface. Young's modulus of the stiffened layer was calculated via the finite element analysis (FEA) simulation, according to the measurement of 30 nm thickness in the STEM and resulted in a modulus range of 30-100 GPa. The current findings, now established in direct measurements, pave the way to improved applications of polymers in nanoscale devices to include soft materials, such as polymer-based composites and biological samples.

SUBMITTER: Samira R

PROVIDER: S-EPMC8398473 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Enhancing the Mechanical Toughness of Epoxy-Resin Composites Using Natural Silk Reinforcements.

Project description:Strong and tough epoxy composites are developed using a less-studied fibre reinforcement, that of natural silk. Two common but structurally distinct silks from the domestic B. mori/Bm and the wild A. pernyi/Ap silkworms are selected in fabric forms. We show that the toughening effects on silk-epoxy composites or SFRPs are dependent on the silk species and the volume fraction of silk. Both silks enhance the room-temperature tensile and flexural mechanical properties of the composite, whereas the more resilient Ap silk shows a more pronounced toughening effect and a lower critical reinforcement volume for the brittle-ductile transition. Specifically, our 60 vol.% Ap-SFRP displays a three-fold elevation in tensile and flexural strength, as compared to pure epoxy resin, with an order of magnitude higher breaking energy via a distinct, ductile failure mode. Importantly, the 60 vol.% Ap-SFRP remains ductile with 7% flexural elongation at lower temperatures (-50?°C). Under impact, these SFRPs show significantly improved energy absorption, and the 60 vol.% Ap-SFRP has an impact strength some eight times that of pure epoxy resin. The findings demonstrate both marked toughening and strengthening effects for epoxy composites from natural silk reinforcements, which presents opportunities for mechanically superior and "green" structural composites.

| S-EPMC5607334 | biostudies-literature

A Comparative Study of Gallium-, Xenon-, and Helium-Focused Ion Beams for the Milling of GaN.

Project description:The milling profiles of single-crystal gallium nitride (GaN) when subjected to focused ion beams (FIBs) using gallium (Ga), xenon (Xe), and helium (He) ion sources were investigated. An experimental analysis via annular dark-field scanning transmission electron microscopy (ADF-STEM) and high-resolution transmission electron microscopy (HRTEM) revealed that Ga-FIB milling yields trenches with higher aspect ratios compared to Xe-FIB milling for the selected ion beam parameters (30 kV, 42 pA), while He-FIB induces local lattice disorder. Molecular dynamics (MD) simulations were employed to investigate the milling process, confirming that probe size critically influences trench aspect ratios. Interestingly, the MD simulations also showed that Xe-FIB generates higher aspect ratios than Ga-FIB with the same probe size, indicating that Xe-FIB could also be an effective option for nanoscale patterning. Atomic defects such as vacancies and interstitials in GaN from He-FIB milling were suggested by the MD simulations, supporting the lattice disorder observed via HRTEM. This combined experimental and simulation approach has enhanced our understanding of FIB milling dynamics and will benefit the fabrication of nanostructures via the FIB technique.

| S-EPMC10647709 | biostudies-literature

Modified Epoxy Resin on the Burning Behavior and Mechanical Properties of Aramid Fiber Composite.

Project description:Aramid fiber/epoxy resin (AF/EP) composite has been heavily used as an impact protection material due to its excellent mechanical properties and lightweight merits. Meanwhile, it is also necessary to concern the flammability of matrix resin and the wick effect of aramid fiber, which would constitute a fire risk in harsh environments. In this work, a multifunctional flame-retardant modifier (EAD) was incorporated into the AF/EP system to improve the flame retardation. The addition of 5 wt% EAD made the AF/EP composite exhibit a high limiting oxygen index (LOI) value of 37.5%, self-extinguishment, as well as decreased total heat release and total smoke release. The results from thermogravimetric analysis (TGA) and dynamic mechanical analysis (DMA) demonstrated that the treated composites maintained good thermal stability. Due to the combined action of covalent and noncovalent bonds in the matrix-rich region, the interfacial bonding improved, which endowed AF/EP composite with strengthening and toughening effects. Compared with the control sample AF/EP, the tensile strength and ballistic parameter (V50) of the sample with 5 wt% EAD increased by 17% and 10%, accompanied with ductile failure mode. Furthermore, the flame-retardant mechanism was obtained by analyzing the actions in condensed and gaseous phases. Thanks to good compatibility and interfacial adhesion, the incorporation of EAD solved the inconsistent issue between flame retardancy and mechanical properties, which further expanded the application of AF/EP composite in the protection field.

| S-EPMC11356078 | biostudies-literature

Mechanical Properties of Epoxy Resin Mortar with Sand Washing Waste as Filler.

Project description:The objective of this study was to investigate the potential use of sand washing waste as filler for epoxy resin mortar. The mechanical properties of four series of mortars containing epoxy binder at 10, 15, 20, and 25 wt. % mixed with sand blended with sand washing waste filler in the range of 0-20 wt. % were examined. The compressive and flexural strength increased with the increase in epoxy and filler content; however, above epoxy 20 wt. %, slight change was seen in strength due to increase in epoxy and filler content. Modulus of elasticity also linearly increased with the increase in filler content, but the use of epoxy content beyond 20 wt. % decreased the modulus of elasticity of the mortar. For epoxy content at 10 wt. %, poor bond strength lower than 0.8 MPa was observed, and adding filler at 20 wt. % adversely affected the bond strength, in contrast to the mortars containing epoxy at 15, 20, 25 wt. %. The results indicate that the sand washing waste can be used as potential filler for epoxy resin mortar to obtain better mechanical properties by adding the optimum level of sand washing waste filler.

| S-EPMC5503406 | biostudies-other

Influence of crosslinking density on the mechanical and thermal properties of plant oil-based epoxy resin.

Project description:Plant oil-based epoxy resins are of great interest due to their ecological and economic necessity. Previous studies suggested that the crosslinking density had a considerable influence on the mechanical and thermal properties of plant oil-based epoxy resins. However, so far, the relationship between the crosslinking density and the thermo-mechanical properties of plant oil-based epoxy resins is not clear. To address this issue, model tung oil-based epoxy resins with different crosslinking densities were fabricated to investigate the influence of crosslinking density on the mechanical and thermal properties of tung oil-based epoxy resins. Results show that the tensile strength, Young's modulus, and glass transition temperature are linearly increased with increasing crosslinking density. The elongation at break and tensile toughness show nonlinear downward trends as the crosslinking density increases. The elongation at break decreases gently at first, then dramatically, and finally slowly as the crosslinking density increases. The tensile toughness declines sharply at first and then slowly with increasing crosslinking density. The relationship between the thermostability and the crosslinking density is complex, because the thermostability is determined by both the molecular structure of the curing system and the crosslinking density. These results provide some information for designing plant oil-based epoxy resins according to the requirements of their applications.

| S-EPMC9379777 | biostudies-literature

Liquid Oxygen Compatibility and Ultra-Low-Temperature Mechanical Properties of Modified epoxy Resin Containing Phosphorus and Nitrogen.

Project description:Endowing epoxy resin (EP) with prospective liquid oxygen compatibility (LOC) as well as enhanced ultra-low-temperature mechanical properties is urgently required in order to broaden its applications in aerospace engineering. In this study, a reactive phosphorus/nitrogen-containing aromatic ethylenediamine (BSEA) was introduced as a reactive component to enhance the LOC and ultra-low-temperature mechanical properties of an EP/biscitraconimide resin (BCI) system. The resultant EP thermosets showed no sensitivity reactions in the 98J liquid oxygen impact test (LOT) when the BSEA content reached 4 wt% or 5 wt%, indicating that they were compatible with liquid oxygen. Moreover, the bending properties, fracture toughness and impact strength of BSEA-modified EP were greatly enhanced at RT and cryogenic temperatures (77 K) at an appropriate level of BSEA content. The bending strength (251.64 MPa) increased by 113.67%, the fracture toughness (2.97 MPa·m1/2) increased by 81.10%, and the impact strength (31.85 kJ·m-2) increased by 128.81% compared with that of pure EP at 77 K. All the above results demonstrate that the BSEA exhibits broad application potential in liquid oxygen tanks and in the cryogenic field.

| S-EPMC9610556 | biostudies-literature

Quantification of gallium cryo-FIB milling damage in biological lamellae.

Project description:Cryogenic electron microscopy (cryo-EM) can reveal the molecular details of biological processes in their native, cellular environment at atomic resolution. However, few cells are sufficiently thin to permit imaging with cryo-EM. Thinning of frozen cells to <500 nm lamellae by focused-ion-beam (FIB) milling has enabled visualization of cellular structures with cryo-EM. FIB milling represents a significant advance over prior approaches because of its ease of use, scalability, and lack of large-scale sample distortions. However, the amount of damage it causes to a thinned cell section has not yet been determined. We recently described an approach for detecting and identifying single molecules in cryo-EM images of cells using 2D template matching (2DTM). 2DTM is sensitive to small differences between a molecular model (template) and the detected structure (target). Here, we use 2DTM to demonstrate that under the standard conditions used for machining lamellae of biological samples, FIB milling introduces a layer of variable damage that extends to a depth of 60 nm from each lamella surface. This layer of damage limits the recovery of information for in situ structural biology. We find that the mechanism of FIB milling damage is distinct from radiation damage during cryo-EM imaging. By accounting for both electron scattering and FIB milling damage, we estimate that FIB milling damage with current protocols will negate the potential improvements from lamella thinning beyond 90 nm.

| S-EPMC10266028 | biostudies-literature

Effect of Ion Irradiation Introduced by Focused Ion-Beam Milling on the Mechanical Behaviour of Sub-Micron-Sized Samples.

Project description:The development of xenon plasma focused ion-beam (Xe+ PFIB) milling technique enables site-specific sample preparation with milling rates several times larger than the conventional gallium focused ion-beam (Ga+ FIB) technique. As such, the effect of higher beam currents and the heavier ions utilized in the Xe+ PFIB system is of particular importance when investigating material properties. To investigate potential artifacts resulting from these new parameters, a comparative study is performed on transmission electron microscopy (TEM) samples prepared via Xe+ PFIB and Ga+ FIB systems. Utilizing samples prepared with each system, the mechanical properties of CrMnFeCoNi high-entropy alloy (HEA) samples are evaluated with in situ tensile straining TEM studies. The results show that HEA samples prepared by Xe+ PFIB present better ductility but lower strength than those prepared by Ga+ FIB. This is due to the small ion-irradiated volumes and the insignificant alloying effect brought by Xe irradiation. Overall, these results demonstrate that Xe+ PFIB systems allow for a more efficient material removal rate while imparting less damage to HEAs than conventional Ga+ FIB systems.

| S-EPMC7316792 | biostudies-literature

Effect of the alumina micro-particle sizes on the thermal conductivity and dynamic mechanical property of epoxy resin.

Project description:Epoxy thermal conductive adhesives with high thermal conductivity and dynamic mechanical properties are important thermally conductive materials for fabricating highly integrated electronic devices. In this paper, micro-Al2O3 is used as a thermally conductive filler for the epoxy resin composite and investigated the effect of micron-sized alumina particle size on the thermal conductivity and dynamic mechanical property of epoxy resin by the transient planar hot plate method and DMA (Dynamic mechanical analysis). The experimental results show that with the same amount of alumina filling, the thermal conductivity and Tg (glass transition temperature) of epoxy/Al2O3 composite material decrease with the increase of alumina particle size. The maximum thermal conductivity of the composite material is 0.679 (W/mK), while the energy storage modulus of epoxy/Al2O3 composite material increases with the increase of alumina particle size, and the maximum energy storage modulus of the composite material is 160MPa. Compared with pure epoxy resin, the thermal conductivity and energy storage modulus have increased by 2.7 and 3.2 times, respectively. The epoxy/Al2O3 composite was applied to the COB (Chips On Board) type LED package, and the substrate temperature of the LED dropped to the lowest after 1.5 hours of operation using EP-A5 composite, and the temperature was stabilized at 38.2°C, indicating that the addition of 5-micron alumina composite has the best heat dissipation in the COB type LED package. These results are critical for the implementation of particulate-filled polymer composites in practical applications because relaxed material specifications and handling procedures can be incorporated in production environments to improve efficiency.

| S-EPMC10575537 | biostudies-literature

Eco-Friendly Epoxy-Terminated Polyurethane-Modified Epoxy Resin with Efficient Enhancement in Toughness.

Project description:Polyurethane is widely used to toughen epoxy resins due to its excellent comprehensive properties and compatibility. However, some demerits of polyurethanes limit their applications, such as the harsh storage condition of isocyanate-terminated polyurethane (ITPU), the limited amount of ITPU in epoxy resin, and using solvents during the preparation of polyurethane-modified epoxy resins. To address these issues, in this study, we reported a facile and green approach for preparing epoxy-terminated polyurethane (EPU)-modified epoxy resins with different EPU contents. It was found that the toughness of the epoxy resin was significantly improved after the addition of EPU. When the EPU content was 30 wt%, the elongation at break and toughness were improved by 358.36% and 73.56%, respectively. In comparison, the toughening effect of EPU outperformed that of ITPU. Moreover, the high content of EPU did not significantly decrease the glass transition temperature and had little effect on the thermal stability of the epoxy resin.

| S-EPMC10346895 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data