Nickel-Doped ZnO Nanowalls with Enhanced Electron Transport Ability for Electrochemical Water Splitting.

ABSTRACT: This article reports on the growth of 3 mol% nickel (Ni)-doped zinc oxide nanowalls (ZnO NWLs) using the hydrothermal method. Morphological investigation as well as electrical conductivity of the undoped and Ni-doped ZnO NWLs was also discussed. The surface roughness of the formed ZnO NWLs was reduced after Ni-doping. The pore size of Ni-doped ZnO NWLs can be controlled by changing the concentration of hexamethylenetetramine (HMT). As the HMT concentration increased, the pores became larger with increasing surface roughness. The electrical conductivity of the electron-only device based on the Ni-doped ZnO NWLs was higher than that of the undoped one, and it was decreased with increasing the HMT concentration. Our results reveal that Ni-doping and adjustment of the HMT concentration are two key approaches to tune the morphology and electrical properties of ZnO NWLs. Finally, the undoped and Ni-doped ZnO NWLs were used as the catalyst for electrochemical water splitting. The Ni-doped ZnO NWLs with the HMT concentration of 1 mM showed the highest electrochemical performance, which can be attributed to the increased surface area and electrical conductivity.

SUBMITTER: Jiang BC

PROVIDER: S-EPMC8398548 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Photocorrosion of ZnO Single Crystals during Electrochemical Water Splitting.

Project description:Degradation and dissolution of transparent semiconducting oxides is central to various areas, including design of catalysts and catalysis conditions, as well as passivation of metal surfaces. In particular, photocorrosion can be significant and plays a central role during photoelectrochemical activity of transparent semiconducting oxides. Here, we utilize an electrochemical flow cell combined with an inductively coupled plasma mass spectrometer (ICP-MS) to enable the in situ study of the time-resolved release of zinc into solution under simultaneous radiation of UV-light. With this system we study the dissolution of zinc oxide single crystals with (0001) and (101̅0) orientations. At acidic and alkaline pH, we characterized potential dependent dissolution rates into both the oxygen and the hydrogen evolving conditions. A significant influence of the UV radiation and the pH of the electrolyte was observed. The observed dissolution behavior agrees well with the surface chemistry and stabilization mechanism of ZnO surfaces. In particular, polar ZnO(0001) shows ideal stability at low potentials and under hydrogen evolution conditions. Whereas ZnO(101̅0) sustains higher dissolution rates, while it is inactive for water splitting. Our data demonstrates that surface design and fundamental understanding of surface chemistry provides an effective path to rendering electroactive surfaces stable under operating conditions.

| S-EPMC7688208 | biostudies-literature

Colloidal Synthesis of Nickel Arsenide Nanocrystals for Electrochemical Water Splitting.

Project description:We report a detailed study on the first colloidal synthesis of NiAs nanocrystals. By optimizing the synthesis parameters, we were able to obtain trioctylphosphine-capped NiAs nanoplatelets with an average diameter of ∼10 nm and a thickness of ca. 4 nm. We then studied the performance of such NiAs nanocrystals as electrocatalysts for electrochemical water splitting reactions, namely, acidic hydrogen evolution reaction (HER) and alkaline oxygen evolution reaction (OER). These nanocrystals were found to be the most HER active ones among the transition metal arsenides reported to date despite exhibiting less than 40 h of stability under benchmark operative conditions (i.e., -10 mA cmgeo -2). When tested as alkaline OER electrocatalysts, our NiAs nanocrystals behaved as a pre-catalyst and transformed superficially into an active Ni-oxy/hydroxide. As a result, NiAs nanocrystals featured an OER activity higher than that of benchmark Ni0 nanocrystals. Noticeably, the OER performance, in terms of , was retained for up to 60 h of continuous operation. The present study highlights how transition metal arsenides, whose structural features could be successfully controlled through a proper tuning of the synthetic parameters, might represent an emerging class of materials for electrocatalytic applications.

| S-EPMC9832430 | biostudies-literature

P–N Heterojunction System Eu‐Doped ZnO@GO for Photocatalytic Water Splitting

Project description:Abstract Here, a feather‐like Eu‐doped ZnO (particle size ≈ 34.87 µm and Eg ≈ 3.13 eV) nanoassembly is synthesized by using the capping agent cetyltrimethylammonium bromide‐supported hydrothermal method. The Eu‐doped ZnO is loaded onto the graphene oxide (GO) surface as Eu‐doped ZnO@GO (particle size ≈ 23.07 µm and Eg ≈ 0.79 eV) and applied to measure the photocatalytic water splitting activity in 20% CH3OH under a 300 W Xe light source. Eu‐doped ZnO@GO exhibits the higher hydrogen generation activity of 255.8 µmol h−1 g−1 that is 159 and 1.5 times more than the pristine GO and Eu‐doped ZnO systems, respectively. Eu‐doped ZnO enhances the photocatalytic activity of GO because the p–n junction formed between GO and Eu‐doped ZnO might support the charge‐transfer and suppress charge recombination. The light harvesting power of Eu‐doped ZnO@GO makes the charge transfer smooth through the GO network. Surface photovoltage and electrochemical impedance studies of the Eu‐doped ZnO@GO composite, reveal that GO acts as the p‐type semiconductor and Eu‐doped ZnO works as an n‐type semiconductor and their interface facilitates the p–n junction to ease charge separation and results in enhanced the water‐splitting efficiency. Eu‐doped ZnO@GO (graphene oxide) with p–n junction is fabricated by a hydrothermal method and used for photocatalytic water splitting. The Eu‐doped ZnO@GO composite exhibits 159 and 1.5 times higher rate of hydrogen generation than the pristine GO and Eu‐doped ZnO systems, respectively. Here, GO acts as the p‐type and Eu‐doped ZnO worked as an n‐type semiconductor to suppress the charge‐carrier's recombination.

| S-EPMC10069305 | biostudies-literature

Synergistic effects of nitrogen-doped carbon and praseodymium oxide in electrochemical water splitting.

Project description:Hybrid materials featuring perovskite-type metal oxide in conjunction with heteroatom-doped graphene hold immense promise as alternatives to costly noble metal catalysts for electrochemical water splitting, facilitating the generation of environmentally friendly hydrogen. In this study, perovskite-type oxide containing praseodymium, barium, strontium, cobalt, and iron atoms dispersed in a carbon matrix as a catalyst is synthesized via annealing of the carbon material with substrates for the preparation of perovskite oxide. The mass ratio of reagents regulates the porous structure and elemental composition. The result of the hydrogen evolution reaction (HER), suggests that the hybrid catalysts exhibit intermediate HER kinetics compared to the commercial Pt/C and the catalyst without carbon. The Tafel slope for HER is lower for materials containing carbon, because of the improved reaction kinetics, facilitated proton transfer, and enhanced electrochemical surface area. Therefore, the study provides an effective strategy for the preparation of catalyst and their use as the active catalyst of water splitting.

| S-EPMC10616108 | biostudies-literature

Cobalt-Doped ZnO Nanorods Coated with Nanoscale Metal-Organic Framework Shells for Water-Splitting Photoanodes.

Project description:Developing highly efficient and stable photoelectrochemical (PEC) water-splitting electrodes via inexpensive, liquid phase processing is one of the key challenges for the conversion of solar energy into hydrogen for sustainable energy production. ZnO represents one the most suitable semiconductor metal oxide alternatives because of its high electron mobility, abundance, and low cost, although its performance is limited by its lack of absorption in the visible spectrum and reduced charge separation and charge transfer efficiency. Here, we present a solution-processed water-splitting photoanode based on Co-doped ZnO nanorods (NRs) coated with a transparent functionalizing metal-organic framework (MOF). The light absorption of the ZnO NRs is engineered toward the visible region by Co-doping, while the MOF significantly improves the stability and charge separation and transfer properties of the NRs. This synergetic combination of doping and nanoscale surface functionalization boosts the current density and functional lifetime of the photoanodes while achieving an unprecedented incident photon to current efficiency (IPCE) of 75% at 350 nm, which is over 2 times that of pristine ZnO. A theoretical model and band structure for the core-shell nanostructure is provided, highlighting how this nanomaterial combination provides an attractive pathway for the design of robust and highly efficient semiconductor-based photoanodes that can be translated to other semiconducting oxide systems.

| S-EPMC7493217 | biostudies-literature

Overall electrochemical splitting of water at the heterogeneous interface of nickel and iron oxide.

Project description:Efficient generation of hydrogen from water-splitting is an underpinning chemistry to realize the hydrogen economy. Low cost, transition metals such as nickel and iron-based oxides/hydroxides have been regarded as promising catalysts for the oxygen evolution reaction in alkaline media with overpotentials as low as ~200 mV to achieve 10 mA cm-2, however, they are generally unsuitable for the hydrogen evolution reaction. Herein, we show a Janus nanoparticle catalyst with a nickel-iron oxide interface and multi-site functionality for a highly efficient hydrogen evolution reaction with a comparable performance to the benchmark platinum on carbon catalyst. Density functional theory calculations reveal that the hydrogen evolution reaction catalytic activity of the nanoparticle is induced by the strong electronic coupling effect between the iron oxide and the nickel at the interface. Remarkably, the catalyst also exhibits extraordinary oxygen evolution reaction activity, enabling an active and stable bi-functional catalyst for whole cell water-splitting with, to the best of our knowledge, the highest energy efficiency (83.7%) reported to date.

| S-EPMC6898202 | biostudies-literature

An electron-hole rich dual-site nickel catalyst for efficient photocatalytic overall water splitting.

Project description:Photocatalysis offers an attractive strategy to upgrade H2O to renewable fuel H2. However, current photocatalytic hydrogen production technology often relies on additional sacrificial agents and noble metal cocatalysts, and there are limited photocatalysts possessing overall water splitting performance on their own. Here, we successfully construct an efficient catalytic system to realize overall water splitting, where hole-rich nickel phosphides (Ni2P) with polymeric carbon-oxygen semiconductor (PCOS) is the site for oxygen generation and electron-rich Ni2P with nickel sulfide (NiS) serves as the other site for producing H2. The electron-hole rich Ni2P based photocatalyst exhibits fast kinetics and a low thermodynamic energy barrier for overall water splitting with stoichiometric 2:1 hydrogen to oxygen ratio (150.7 μmol h-1 H2 and 70.2 μmol h-1 O2 produced per 100 mg photocatalyst) in a neutral solution. Density functional theory calculations show that the co-loading in Ni2P and its hybridization with PCOS or NiS can effectively regulate the electronic structures of the surface active sites, alter the reaction pathway, reduce the reaction energy barrier, boost the overall water splitting activity. In comparison with reported literatures, such photocatalyst represents the excellent performance among all reported transition-metal oxides and/or transition-metal sulfides and is even superior to noble metal catalyst.

| S-EPMC10060254 | biostudies-literature

Phosphorus-Doped 3D RuCo Nanowire Arrays on Nickel Foam with Enhanced Electrocatalytic Activity for Overall Water Splitting.

Project description:It is especially significant to design and construct high-performance and stable three-dimensional (3D) bifunctional nanoarchitecture electrocatalysts toward overall water splitting. Herein, we have constructed 3D self-supported phosphorus-doped ruthenium-cobalt nanowires on nickel foams (RuCoP/NF) via a simple hydrothermal reaction followed by a low-temperature phosphating reaction. Doping P can not merely enhance the intrinsic activity of electrocatalysts for overall water splitting but at the same time increase electrochemical surface areas (ECSAs) to expose more accessible active sites. As a 3D bifunctional catalyst, RuCoP/NF demonstrates superior performance for HER (44 mV@10 mA cm-2) and OER (379 mV@50 mA cm-2) in 1.0 M KOH electrolyte solution. The overall water-splitting system was assembled using RuCoP/NF as both anode and cathode. Besides, it exhibits a voltage of 1.533 V at a current density of 10 mA cm-2 and long-term durability within 24 h. P-dopant changes the electron structure of Ru and Co, which is conducive to the formation of Ruδ- and Coδ+, resulting in the adjustment of binding H*/OH* and the improvement of the overall water-splitting reaction kinetics. This work provides a facile method to produce heteroatom-doped and high-performance catalysts for efficient overall water splitting.

| S-EPMC8153743 | biostudies-literature

Urea-Doped ZnO Films as the Electron Transport Layer for High Efficiency Inverted Polymer Solar Cells.

Project description:In this paper, urea-doped ZnO (U-ZnO) is investigated as a modified electron transport layer (ETL) in inverted polymer solar cells (PSCs). Using a blend of Poly{4,8-bis[(2-ethylhexyl)oxy] benzo [1,2-b:4,5-b'] dithiophene-2,6-diyl-alt-3-fluoro-2-[(2-ethylhexyl)carbonyl] thieno [3,4-b] thiophene-4,6-diyl}(PTB7), and [6,6]-phenyl-C71-butyric acid methyl ester (PC71BM) as light absorber, a champion power conversion efficiency (PCE) of 9.15% for U-ZnO ETL based PSCs was obtained, which is 15% higher than that of the pure ZnO ETL based PSCs (7.76%). It was demonstrated that urea helps to passivate defects in ZnO ETL, resulting in enhanced exciton dissociation, suppressed charge recombination and efficient charge extraction efficiency. This work suggests that the utilization of the U-ZnO ETL offer promising potential for achieving highly efficient PSCs.

| S-EPMC6138008 | biostudies-literature

Enhanced Charge Separation in Nanoporous BiVO4 by External Electron Transport Layer Boosts Solar Water Splitting.

Project description:The optimization of charge transport with electron-hole separation directed toward specific redox reactions is a crucial mission for artificial photosynthesis. Bismuth vanadate (BiVO4 , BVO) is a popular photoanode material for solar water splitting, but it faces tricky challenges in poor charge separation due to its modest charge transport properties. Here, a concept of the external electron transport layer (ETL) is first proposed and demonstrated its effectiveness in suppressing the charge recombination both in bulk and at surface. Specifically, a conformal carbon capsulation applied on BVO enables a remarkable increase in the charge separation efficiency, thanks to its critical roles in passivating surface charge-trapping sites and building external conductance channels. Through decorated with an oxygen evolution catalyst to accelerate surface charge transfer, the carbon-encased BVO (BVO@C) photoanode manifests durable water splitting over 120 h with a high current density of 5.9 mA cm-2 at 1.23 V versus the reversible hydrogen electrode (RHE) under 1 sun irradiation (100 mW cm-2 , AM 1.5 G), which is an activity-stability trade-off record for single BVO light absorber. This work opens up a new avenue to steer charge separation via external ETL for solar fuel conversion.

| S-EPMC10837342 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data