The Phase Structural Evolution and Gas Separation Performances of Cellulose Acetate/Polyimide Composite Membrane from Polymer to Carbon Stage.

ABSTRACT: Blending and heat-treatment play significant roles in adjusting gas separation performances of membranes, especially for incorporating thermally labile polymers into carbon molecular sieve membranes (CMSMs). In this work, cellulose acetate (CA) is introduced into polyimide (PI) as a sacrificial phase to adjust the structure and gas separation performance from polymer to carbon. A novel result is observed that the gas permeability is reduced, even when the immiscible CA phase decomposes and forms pores after heat treatment at 350 °C. After carbonization at 600 °C, the miscible CA has changed without contribution, while the role of the immiscible CA phase has changed from original hindrance to facilitation, the composite-based CMSM at a CA content of 10 wt.% shows highest performances, a H₂ permeability of ~5300 Barrer (56% enhancement) with a similar H₂/N₂ permselectivity of 42. The structural analyses reveal that the chain interactions and phase separation behaviors between CA and PI play critical roles on membrane structures and gas diffusion, and the corresponding phase structural evolutions during heat treatment and carbonization determine gas separation properties.

SUBMITTER: Li H

PROVIDER: S-EPMC8399511 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Molecularly Mixed Composite Membranes for Gas Separation Based on Macrocycles Embedded in a Polyimide

Project description: Not available

| S-EPMC10892679 | biostudies-literature

Metal-organic framework nanosheets in polymer composite materials for gas separation.

Project description:Composites incorporating two-dimensional nanostructures within polymeric matrices have potential as functional components for several technologies, including gas separation. Prospectively, employing metal-organic frameworks (MOFs) as versatile nanofillers would notably broaden the scope of functionalities. However, synthesizing MOFs in the form of freestanding nanosheets has proved challenging. We present a bottom-up synthesis strategy for dispersible copper 1,4-benzenedicarboxylate MOF lamellae of micrometre lateral dimensions and nanometre thickness. Incorporating MOF nanosheets into polymer matrices endows the resultant composites with outstanding CO2 separation performance from CO2/CH4 gas mixtures, together with an unusual and highly desired increase in the separation selectivity with pressure. As revealed by tomographic focused ion beam scanning electron microscopy, the unique separation behaviour stems from a superior occupation of the membrane cross-section by the MOF nanosheets as compared with isotropic crystals, which improves the efficiency of molecular discrimination and eliminates unselective permeation pathways. This approach opens the door to ultrathin MOF-polymer composites for various applications.

| S-EPMC4270742 | biostudies-literature

Cellulose-Based Carbon Molecular Sieve Membranes for Gas Separation: A Review.

Project description:In the field of gas separation and purification, membrane technologies compete with conventional purification processes on the basis of technical, economic and environmental factors. In this context, there is a growing interest in the development of carbon molecular sieve membranes (CMSM) due to their higher permeability and selectivity and higher stability in corrosive and high temperature environments. However, the industrial use of CMSM has been thus far hindered mostly by their relative instability in the presence of water vapor, present in a large number of process streams, as well as by the high cost of polymeric precursors such as polyimide. In this context, cellulosic precursors appear as very promising alternatives, especially targeting the production of CMSM for the separation of O2/N2 and CO2/CH4. For these two gas separations, cellulose-based CMSM have demonstrated performances well above the Robeson upper bound and above the performance of CMSM based on other polymeric precursors. Furthermore, cellulose is an inexpensive bio-renewable feed-stock highly abundant on Earth. This article reviews the major fabrication aspects of cellulose-based CMSM. Additionally, this article suggests a new tool to characterize the membrane performance, the Robeson Index. The Robeson Index, θ, is the ratio between the actual selectivity at the Robeson plot and the corresponding selectivity-for the same permeability-of the Robeson upper bound; the Robeson Index measures how far the actual point is from the upper bound.

| S-EPMC7435847 | biostudies-literature

"All Polyimide" Mixed Matrix Membranes for High Performance Gas Separation.

Project description:To improve the interfacial compatibility of mixed matrix membranes (MMMs) for gas separation, microporous polyimide particle (AP) was designed, synthesized, and introduced into intrinsic microporous polyimide matrix (6FDA-Durene) to form "all polyimide" MMMs. The AP fillers showed the feature of thermal stability, similar density with polyimide matrix, high porosity, high fractional free volume, large microporous dimension, and interpenetrating network architecture. As expected, the excellent interfacial compatibility between 6FDA-Durene and AP without obvious agglomeration even at a high AP loading of 10 wt.% was observed. As a result, the CO2 permeability coefficient of MMM with AP loading as low as 5 wt.% reaches up to 1291.13 Barrer, which is 2.58 times that of the pristine 6FDA-Durene membrane without the significant sacrificing of ideal selectivity of CO2/CH4. The improvement of permeability properties is much better than that of the previously reported MMMs, where high filler content is required to achieve a high permeability increase but usually leads to significant agglomeration or phase separation of fillers. It is believed that the excellent interfacial compatibility between the PI fillers and the PI matrix induce the effective utilization of porosity and free volume of AP fillers during gas transport. Thus, a higher diffusion coefficient of MMMs has been observed than that of the pristine PI membrane. Furthermore, the rigid polyimide fillers also result in the excellent anti-plasticization ability for CO2. The MMMs with a 10 wt.% AP loading shows a CO2 plasticization pressure of 300 psi.

| S-EPMC8073420 | biostudies-literature

A cellulose acetate/<i>Amygdalus pedunculata</i> shell-derived activated carbon composite monolith for phenol adsorption.

Project description:Amygdalus pedunculata is expected to be a good candidate plant for desert reclamation ("greening") since it has notable tolerance to cold and drought and can grow in a wide range of areas with different soil types and moisture contents. In this study, we have developed a single-step method to fabricate a cellulose acetate (CA)/A. pedunculata shell (APS)-derived activated carbon (AC) composite monolith by thermally induced phase separation (TIPS) for removal of toxic phenol from aqueous solution. The composite monolith was easily fabricated by TIPS of a CA solution in the presence of the dispersed AC, in which AC was well loaded onto the monolithic skeleton of CA. The as-obtained monolith showed a maximum adsorption capacity of 45 mg g-1 at the initial phenol concentration of 0.8 mg mL-1. The present composite can be prepared with an arbitrary shape by a facile method from cheap materials, and is more convenient to recycle than powder adsorbents. Therefore, the present CA/APS-derived AC composite monolith has great potential as a promising adsorbent of low cost with convenient separation for toxic phenol-containing wastewater.

| S-EPMC9078407 | biostudies-literature

A Facile Synthesis of (PIM-Polyimide)-(6FDA-Durene-Polyimide) Copolymer as Novel Polymer Membranes for CO2 Separation.

Project description:Random copolymers made of both (PIM-polyimide) and (6FDA-durene-PI) were prepared for the first time by a facile one-step polycondensation reaction. By combining the highly porous and contorted structure of PIM (polymers with intrinsic microporosity) and high thermomechanical properties of PI (polyimide), the membranes obtained from these random copolymers [(PIM-PI)-(6FDA-durene-PI)] showed high CO2 permeability (>1047 Barrer) with moderate CO2/N2 (> 16.5) and CO2/CH4 (> 18) selectivity, together with excellent thermal and mechanical properties. The membranes prepared from three different compositions of two comonomers (1:4, 1:6 and 1:10 of x:y), all showed similar morphological and physical properties, and gas separating performance, indicating ease of synthesis and practicability for production in large scale. The gas separation performance of these membranes at various pressure ranges (100-1500 torr) was also investigated.

| S-EPMC6780089 | biostudies-literature

Polymer-Infiltrated Metal-Organic Frameworks for Thin-Film Composite Mixed-Matrix Membranes with High Gas Separation Properties.

Project description:Thin-film composite mixed-matrix membranes (TFC-MMMs) have potential applications in practical gas separation processes because of their high permeance (gas flux) and gas selectivity. In this study, we fabricated a high-performance TFC-MMM based on a rubbery comb copolymer, i.e., poly(2-[3-(2H-benzotriazol-2-yl)-4-hydroxyphenyl] ethyl methacrylate)-co-poly(oxyethylene methacrylate) (PBE), and metal-organic framework MOF-808 nanoparticles. The rubbery copolymer penetrates through the pores of MOF-808, thereby tuning the pore size. In addition, the rubbery copolymer forms a defect-free interfacial morphology with polymer-infiltrated MOF-808 nanoparticles. Consequently, TFC-MMMs (thickness = 350 nm) can be successfully prepared even with a high loading of MOF-808. As polymer-infiltrated MOF is incorporated into the polymer matrix, the PBE/MOF-808 membrane exhibits a significantly higher CO2 permeance (1069 GPU) and CO2/N2 selectivity (52.7) than that of the pristine PBE membrane (CO2 permeance = 431 GPU and CO2/N2 selectivity = 36.2). Therefore, the approach considered in this study is suitable for fabricating high-performance thin-film composite membranes via polymer infiltration into MOF pores.

| S-EPMC10053294 | biostudies-literature

On the Thermochemical Transition Depression of Cellulose Acetate Composite Membranes.

Project description:Gallic acid (GA) and quercetin (QU) are two important bioactive molecules with increased biomedical interest. Cellulose acetate (CA) is a polymer derived from cellulose and is used in various applications. In this work, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR) were used to study the thermal behavior of electrospun CA membranes loaded with quercetin or gallic acid. It was found that gallic acid and quercetin depress the thermochemical transition (simultaneous softening and decomposition) of CA, in a mechanism similar to that of the glass transition depression of amorphous polymers by plasticizers. The extensive hydrogen bonding, besides the well-known effect of constraining polymer's softening by keeping macromolecules close to each other, has a secondary effect on the thermochemical transition, i.e., it weakens chemical bonds and, inevitably, facilitates decomposition. This second effect of hydrogen bonding can provide an explanation for an unexpected observation of this study: CA membranes loaded with quercetin or gallic acid soften at lower temperatures; however, at the same time, they decompose to a higher extent than pure CA. Besides optimization of CA processing, the fundamental understanding of the thermochemical transition depression could lead to the design of more sustainable processes for biomass recycling and conversion.

| S-EPMC9416459 | biostudies-literature

3D Printing of Thermal Insulating Polyimide/Cellulose Nanocrystal Composite Aerogels with Low Dimensional Shrinkage.

Project description:Polyimide (PI)-based aerogels have been widely applied to aviation, automobiles, and thermal insulation because of their high porosity, low density, and excellent thermal insulating ability. However, the fabrication of PI aerogels is still restricted to the traditional molding process, and it is often challenging to prepare high-performance PI aerogels with complex 3D structures. Interestingly, renewable nanomaterials such as cellulose nanocrystals (CNCs) may provide a unique approach for 3D printing, mechanical reinforcement, and shape fidelity of the PI aerogels. Herein, we proposed a facile water-based 3D printable ink with sustainable nanofillers, cellulose nanocrystals (CNCs). Polyamic acid was first mixed with triethylamine to form an aqueous solution of polyamic acid ammonium salts (PAAS). CNCs were then dispersed in the aqueous PAAS solution to form a reversible physical network for direct ink writing (DIW). Further freeze-drying and thermal imidization produced porous PI/CNC composite aerogels with increased mechanical strength. The concentration of CNCs needed for DIW was reduced in the presence of PAAS, potentially because of the depletion effect of the polymer solution. Further analysis suggested that the physical network of CNCs lowered the shrinkage of aerogels during preparation and improved the shape-fidelity of the PI/CNC composite aerogels. In addition, the composite aerogels retained low thermal conductivity and may be used as heat management materials. Overall, our approach successfully utilized CNCs as rheological modifiers and reinforcement to 3D print strong PI/CNC composite aerogels for advanced thermal regulation.

| S-EPMC8588507 | biostudies-literature

Role of Cation Structure in CO2 Separation by Ionic Liquid/Sulfonated Polyimide Composite Membrane.

Project description:The development of suitable separation technologies for the separation of carbon dioxide is a pressing technological requirement. The application of ion gel membranes for this purpose continues to stimulate a great deal of research, and in this study we focus on the chemical structure of the ionic liquid component in the ion gel, and its interactions with the sulfonated polyimide polymer. Whilst such membranes are known to give promising carbon dioxide separation properties together with mechanical strength and thin-film-processability, we further elaborate on how changing the cation of the ionic liquid from a typical imidazolium cation to a protic variant effects the physicochemical, thermal, and structural properties of the membranes, and how these changes further influence the carbon dioxide separation properties. We compare and contrast our findings with our earlier study on protic and aprotic ammonium-based ionic liquids, and highlight that for CO2 absorption behavior in the imidazolium systems, the importance of directionality of interactions (ion pairs exhibit a large energy stabilization only for a specific geometrical arrangement of cation and anion, e.g., hydrogen bonding rather than Coulombic interaction) between cation and anion applies not only to the protic system, but also to the nominally aprotic cation. Finally, we demonstrate that the phase separation behavior in the ion gels is an important factor in determining the carbon dioxide separation behavior.

| S-EPMC6680971 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data