Rubrene Thin Films with Viably Enhanced Charge Transport Fabricated by Cryo-Matrix-Assisted Laser Evaporation.

ABSTRACT: Among organic semiconductors, rubrene (RB; C₄₂H₂₈) is of rapidly growing interest for the development of organic and hybrid electronics due to exceptionally long spin diffusion length and carrier mobility up to 20 cm²V^-1s^-1 in single crystals. However, the fabrication of RB thin films resembling properties of the bulk remains challenging, mainly because of the RB molecule's twisted conformation. This hinders the formation of orthorhombic crystals with strong π-π interactions that support the band transport. In this work, RB films with a high crystalline content were fabricated by matrix-assisted laser evaporation and the associated structure, composition, and transport properties are investigated. Enhanced charge transport is ascribed to the crystalline content of the film. Spherulitic structures are observed on top of an amorphous RB layer formed in the initial deposition stage. In spherulites, orthorhombic crystals dominate, as confirmed by X-ray diffraction and the absorption and Raman spectra. Surprisingly, nanowires several microns in length are also detected. The desorption/ionization mass and X-ray photoelectron spectra consistently show minimal material decomposition and absence of RB peroxides. The observed carrier mobility up to 0.13 cm²V^-1s^-1, is close to the technologically accepted level, making these rubrene films attractive for spintronic and optoelectronic applications.

SUBMITTER: Jendrzejewski R

PROVIDER: S-EPMC8400232 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Thin Films of Metal-Organic Framework Interfaces Obtained by Laser Evaporation.

Project description:Properties such as large surface area, high pore volume, high chemical and thermal stability, and structural flexibility render zeolitic imidazolate frameworks (ZIFs) well-suited materials for gas separation, chemical sensors, and optical and electrical devices. For such applications, film processing is a prerequisite. Herein, matrix-assisted pulsed laser evaporation (MAPLE) was successfully used as a single-step deposition process to fabricate ZIF-8 films. By correlating laser fluency and controlling the specific transfer of lab-synthesized ZIF-8, films with user-controlled physical and chemical properties were obtained. Films' characteristics were evaluated by scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) spectroscopy, X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and X-ray photoelectron spectroscopy (XPS). The analysis showed that frameworks of ZIF-8 can be deposited successfully and controllably to yield polycrystalline films. The deposited films maintained the integrity of the individual ZIF-8 framework, while undergoing minor crystalline and surface chemistry changes. No significant changes in particle size were observed. Our study demonstrated control over both the MAPLE deposition conditions and the outcome, as well as the suitability of the listed deposition method to create composite architectures that could potentially be used in applications ranging from selective membranes to gas sensors.

| S-EPMC8224316 | biostudies-literature

Morphology and transport characterization of solution-processed rubrene thin films on polymer-modified substrates.

Project description:In this report, the morpho-structural peculiarities and the crystallization mechanisms in solution-processed, solvent vapor annealed (SVA) thin films of rubrene (5,6,11,12-tetraphenylnaphthacene) on different substrates were investigated. The high-quality rubrene crystal films with a triclinic crystal structure were successfully prepared on the FTO substrates (glass slide coated with fluorine-tin-oxide) modified by PLA (polylactic acid) for the first time. The area coverage of rubrene crystal and the sizes of rubrene dendritic crystals increased with increasing thickness of PLA film and concentration of rubrene solution. For rubrene molecules, FTO wafers with rough surface provided the possibility of heterogeneous nucleation. During the SVA process, there were two kinds of forces acting on the diffusion of rubrene molecules: one force was provided by the residual chloroform solvent, which was perpendicular to the substrate, and the other force was provided by gaseous dichloromethane, which was parallel to the substrate. The synergy of these two forces was proposed to explain the nucleation and the crystallization processes of rubrene films. The higher nucleus of PLA/rubrene dendrites and the layer-by-layer stacking of needle-shaped nanocrystalline PLA/rubrene were important for exploring their kinetic formation process.

| S-EPMC7376014 | biostudies-literature

Regulating strain in perovskite thin films through charge-transport layers.

Project description:Thermally-induced tensile strain that remains in perovskite films following annealing results in increased ion migration and is a known factor in the instability of these materials. Previously-reported strain regulation methods for perovskite solar cells (PSCs) have utilized substrates with high thermal expansion coefficients that limits the processing temperature of perovskites and compromises power conversion efficiency. Here we compensate residual tensile strain by introducing an external compressive strain from the hole-transport layer. By using a hole-transport layer with high thermal expansion coefficient, we compensate the tensile strain in PSCs by elevating the processing temperature of hole-transport layer. We find that compressive strain increases the activation energy for ion migration, improving the stability of perovskite films. We achieve an efficiency of 16.4% for compressively-strained PSCs; and these retain 96% of their initial efficiencies after heating at 85?°C for 1000 hours-the most stable wide-bandgap perovskites (above 1.75?eV) reported so far.

| S-EPMC7090003 | biostudies-literature

Thin Films Based on Cobalt Phthalocyanine:C60 Fullerene:ZnO Hybrid Nanocomposite Obtained by Laser Evaporation.

Project description:Matrix-assisted pulsed laser evaporation (MAPLE) was used to deposit hybrid nanocomposite thin films based on cobalt phthalocyanine (CoPc), C60 fullerene and ZnO nanoparticles. The inorganic nanoparticles, with a size of about 20 nm, having the structural and optical properties characteristic of ZnO, were chemically synthesized by a simple precipitation method. Furthermore, ZnO nanoparticles were dispersed in a dimethyl sulfoxide solution in which CoPc and C60 had been dissolved, ready for the freezing MAPLE target. The effect of the concentration of ZnO nanoparticles on the structural, morphological, optical and electrical properties of the CoPc:C60:ZnO hybrid nanocomposite layers deposited by MAPLE was evaluated. The infrared spectra of the hybrid nanocomposite films confirm that the CoPc and C60 preserve their chemical structure during the laser deposition process. The CoPc optical signature is recognized in the ultraviolet-visible (UV-Vis) spectra of the obtained layers, these being dominated by the absorption bands associated to this organic compound while the ZnO optical fingerprint is identified in the photoluminescence spectra of the prepared layers, these disclosing the emission bands linked to this inorganic semiconductor. The hybrid nanocomposite layers exhibit globular morphology, which is typical for the thin films deposited by MAPLE. Current-voltage (J-V) characteristics of the structures developed on CoPc:C60:ZnO layers reveal that the addition of an appropriate amount of ZnO nanoparticles in the CoPc:C60 mixture leads to a more efficient charge transfer between the organic and inorganic components. Due to their photovoltaic effect, structures featuring such hybrid nanocomposite thin films deposited by MAPLE can have potential applications in the field of photovoltaic devices.

| S-EPMC7153592 | biostudies-literature

Directional Charge-Carrier Transport in Oriented Benzodithiophene Covalent Organic Framework Thin Films.

Project description:Charge-carrier transport in oriented COF thin films is an important factor for realizing COF-based optoelectronic devices. We describe how highly oriented electron-donating benzodithiophene BDT-COF thin films serve as a model system for a directed charge-transport study. Oriented BDT-COF films were deposited on different electrodes with excellent control over film roughness and topology, allowing for high-quality electrode-COF interfaces suitable for device fabrication. Hole-only devices were constructed to study the columnar hole mobility of the BDT-COF films. The transport measurements reveal a clear dependency of the measured hole mobilities on the BDT-COF film thickness, where thinner films showed about two orders of magnitude higher mobilities than thicker ones. Transport measurements under illumination yielded an order of magnitude higher mobility than in the dark. In-plane electrical conductivity values of up to 5 × 10-7 S cm-1 were obtained for the oriented films. Impedance measurements of the hole-only devices provided further electrical description of the oriented BDT-COF films in terms of capacitance, recombination resistance, and dielectric constant. An exceptionally low dielectric constant value of approximately 1.7 was estimated for the BDT-COF films, a further indication of their highly porous nature. DFT and molecular-dynamics simulations were carried out to gain further insights into the relationships between the COF layer interactions, electronic structure, and the potential device performance.

| S-EPMC6400429 | biostudies-literature

Ultra Uniform Pb0.865La0.09(Zr0.65Ti0.35)O? Thin Films with Tunable Optical Properties Fabricated via Pulsed Laser Deposition.

Project description:Ferroelectric thin films have been utilized in a wide range of electronic and optical applications, in which their morphologies and properties can be inherently tuned by a qualitative control during growth. In this work, we demonstrate the evolution of the Pb0.865La0.09(Zr0.65Ti0.35)O? (PLZT) thin films on MgO (200) with high uniformity and optimized optical property via the controls of the deposition temperatures and oxygen pressures. The perovskite phase can only be obtained at the deposition temperature above 700 °C and oxygen pressure over 50 Pa due to the improved crystallinity. Meanwhile, the surface morphologies gradually become smooth and compact owing to spontaneously increased nucleation sites with the elevated temperatures, and the crystallization of PLZT thin films also sensitively respond to the oxygen vacancies with the variation of oxygen pressures. Correspondingly, the refractive indices gradually develop with variations of the deposition temperatures and oxygen pressures resulted from the various slight loss, and the extinction coefficient for each sample is similarly near to zero due to the relatively smooth morphology. The resulting PLZT thin films exhibit the ferroelectricity, and the dielectric constant sensitively varies as a function of electric filed, which can be potentially applied in the electronic and optical applications.

| S-EPMC5951371 | biostudies-literature

Tuning charge transport dynamics via clustering of doping in organic semiconductor thin films.

Project description:A significant challenge in the rational design of organic thermoelectric materials is to realize simultaneously high electrical conductivity and high induced-voltage in response to a thermal gradient, which is represented by the Seebeck coefficient. Conventional wisdom posits that the polymer alone dictates thermoelectric efficiency. Herein, we show that doping - in particular, clustering of dopants within conjugated polymer films - has a profound and predictable influence on their thermoelectric properties. We correlate Seebeck coefficient and electrical conductivity of iodine-doped poly(3-hexylthiophene) and poly[2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione-3,6-diyl)-alt-(2,2';5',2'';5'',2'''-quaterthiophen-5,5'''-diyl)] films with Kelvin probe force microscopy to highlight the role of the spatial distribution of dopants in determining overall charge transport. We fit the experimental data to a phonon-assisted hopping model and found that the distribution of dopants alters the distribution of the density of states and the Kang-Snyder transport parameter. These results highlight the importance of controlling dopant distribution within conjugated polymer films for thermoelectric and other electronic applications.

| S-EPMC6610129 | biostudies-literature

Enhanced Ballistic Transport of Charge Carriers in Alloyed and K-Passivated Alloyed Perovskite Thin Films.

Project description:Hybrid organic-inorganic perovskites show remarkable charge transport properties despite their deposition via low-temperature solution phase methods. It has recently been shown that this includes the ballistic transport of charges following photoexcitation, with ballistic transport lengths as large as 150 nm measured in MAPI3 films, which is almost twice the value reported for GaAs. Here we explore the ballistic transport regime in high-performance triple-cation and K-passivated triple-cation perovskite films, using femtosecond transient absorption microscopy, which allows us to image carrier motion with 10 fs temporal resolution and 10 nm spatial precision. We observe ballistic transport lengths of 160 and 220 nm in triple-cation and K-passivated triple-cation perovskite films, respectively. We propose that the ballistic transport is limited by nanoscale trap clusters at grain boundaries and interfaces, which can be passivated via chemical treatments to enhance the ballistic transport length, which implies that further enhancements are possible as passivation methods are improved.

| S-EPMC7467737 | biostudies-literature

Spatial and temporal imaging of long-range charge transport in perovskite thin films by ultrafast microscopy.

Project description:Charge carrier diffusion coefficient and length are important physical parameters for semiconducting materials. Long-range carrier diffusion in perovskite thin films has led to remarkable solar cell efficiencies; however, spatial and temporal mechanisms of charge transport remain unclear. Here we present a direct measurement of carrier transport in space and in time by mapping carrier density with simultaneous ultrafast time resolution and ∼50-nm spatial precision in perovskite thin films using transient absorption microscopy. These results directly visualize long-range carrier transport of ∼220 nm in 2 ns for solution-processed polycrystalline CH3NH3PbI3 thin films. Variations of the carrier diffusion coefficient at the μm length scale have been observed with values ranging between 0.05 and 0.08 cm(2) s(-1). The spatially and temporally resolved measurements reported here underscore the importance of the local morphology and establish an important first step towards discerning the underlying transport properties of perovskite materials.

| S-EPMC4557372 | biostudies-literature

Kondo-like transport and magnetic field effect of charge carrier fluctuations in granular aluminum oxide thin films.

Project description:Granular aluminum oxide is an attractive material for superconducting quantum electronics. However, its low-temperature normal state transport properties are still not fully understood, while they could be related to the unconventional phenomenon of the superconductivity in this material. In order to obtain useful information on this aspect, a detailed study of charge carrier fluctuations has been performed in granular aluminum oxide films. The results of electric noise measurements indicate the presence of a Kondo-type spin-flip scattering mechanism for the conducting electrons in the normal state, at low temperatures. Moreover, the magnetic field dependence of the noise amplitude suggests that interface magnetic moments are the main source of fluctuations. The identification of the nature of fluctuation processes is a mandatory requirement for the improvement of quality and performance of quantum devices.

| S-EPMC6141613 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data