Optimizing the PMMA Electron-Blocking Layer of Quantum Dot Light-Emitting Diodes.

ABSTRACT: Quantum dots (QDs) are promising candidates for producing bright, color-pure, cost-efficient, and long-lasting QD-based light-emitting diodes (QDLEDs). However, one of the significant problems in achieving high efficiency of QDLEDs is the imbalance between the rates of charge-carrier injection into the emissive QD layer and their transport through the device components. Here we investigated the effect of the parameters of the deposition of a poly (methyl methacrylate) (PMMA) electron-blocking layer (EBL), such as PMMA solution concentration, on the characteristics of EBL-enhanced QDLEDs. A series of devices was fabricated with the PMMA layer formed from acetone solutions with concentrations ranging from 0.05 to 1.2 mg/mL. The addition of the PMMA layer allowed for an increase of the maximum luminance of QDLED by a factor of four compared to the control device without EBL, that is, to 18,671 cd/m², with the current efficiency increased by an order of magnitude and the turn-on voltage decreased by ~1 V. At the same time, we have demonstrated that each particular QDLED characteristic has a maximum at a specific PMMA layer thickness; therefore, variation of the EBL deposition conditions could serve as an additional parameter space when other QDLED optimization approaches are being developed or implied in future solid-state lighting and display devices.

SUBMITTER: Zvaigzne M

PROVIDER: S-EPMC8401809 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Effect of Air Exposure of ZnMgO Nanoparticle Electron Transport Layer on Efficiency of Quantum-Dot Light-Emitting Diodes.

Project description:We demonstrate the effect of air exposure on optical and electrical properties of ZnMgO nanoparticles (NPs) typically exploited as an electron transport layer in Cd-based quantum-dot light-emitting diodes (QLEDs). We analyze the roles of air components in modifying the electrical properties of ZnMgO NPs, which reveals that H2O enables the reduction of hole leakage while O2 alters the character of charge transport due to its ability to trap electrons. As a result, the charge balance in the QDs layer is improved, which is confirmed by voltage-dependent measurements of photoluminescence quantum yield. The maximum external quantum efficiency is improved over 2-fold and reaches the value of 9.5% at a luminance of 104 cd/m2. In addition, we investigate the problem of electron leakage into the hole transport layer and show that trap-mediated electron transport in the ZnMgO layer caused by adsorbed O2 ensures a higher leakage threshold. This work also provides an insight into the possible disadvantages of device contact with air as well as problems and challenges that might occur during open-air fabrication of QLEDs.

| S-EPMC8288913 | biostudies-literature

Effects of ZnMgO Electron Transport Layer on the Performance of InP-Based Inverted Quantum Dot Light-Emitting Diodes.

Project description:An environment-friendly inverted indium phosphide red quantum dot light-emitting diode (InP QLED) was fabricated using Mg-doped zinc oxide (ZnMgO) as the electron transport layer (ETL). The effects of ZnMgO ETL on the performance of InP QLED were investigated. X-ray diffraction (XRD) analysis indicated that ZnMgO film has an amorphous structure, which is similar to zinc oxide (ZnO) film. Comparison of morphology between ZnO film and ZnMgO film demonstrated that Mg-doped ZnO film remains a high-quality surface (root mean square roughness: 0.86 nm) as smooth as ZnO film. The optical band gap and ultraviolet photoelectron spectroscopy (UPS) analysis revealed that the conduction band of ZnO shifts to a more matched position with InP quantum dot after Mg-doping, resulting in the decrease in turn-on voltage from 2.51 to 2.32 V. In addition, the ratio of irradiation recombination of QLED increases from 7% to 25% using ZnMgO ETL, which can be attributed to reduction in trap state by introducing Mg ions into ZnO lattices. As a result, ZnMgO is a promising material to enhance the performance of inverted InP QLED. This work suggests that ZnMgO has the potential to improve the performance of QLED, which consists of the ITO/ETL/InP QDs/TCTA/MoO3/Al, and Mg-doping strategy is an efficient route to directionally regulate ZnO conduction bands.

| S-EPMC8151885 | biostudies-literature

Double Metal Oxide Electron Transport Layers for Colloidal Quantum Dot Light-Emitting Diodes.

Project description:The performance of colloidal quantum dot light-emitting diodes (QD-LEDs) have been rapidly improved since metal oxide semiconductors were adopted for an electron transport layer (ETL). Among metal oxide semiconductors, zinc oxide (ZnO) has been the most generally employed for the ETL because of its excellent electron transport and injection properties. However, the ZnO ETL often yields charge imbalance in QD-LEDs, which results in undesirable device performance. Here, to address this issue, we introduce double metal oxide ETLs comprising ZnO and tin dioxide (SnO2) bilayer stacks. The employment of SnO2 for the second ETL significantly improves charge balance in the QD-LEDs by preventing spontaneous electron injection from the ZnO ETL and, as a result, we demonstrate 1.6 times higher luminescence efficiency in the QD-LEDs. This result suggests that the proposed double metal oxide ETLs can be a versatile platform for QD-based optoelectronic devices.

| S-EPMC7221608 | biostudies-literature

Stability of Quantum-Dot Light Emitting Diodes with Alkali Metal Carbonates Blending in Mg Doped ZnO Electron Transport Layer.

Project description:We report here the fabrication of highly efficient and long-lasting quantum-dot light emitting diodes (QLEDs) by blending various alkali metal carbonate in magnesium (Mg) doped zinc oxide (ZnO) (MZO) electron transport layer (ETL). Alkali metal carbonates blending in MZO, X2CO3:MZO, control the band-gap, electrical properties, and thermal stability. This can therefore enhance the operational lifetime of QLEDs. It is found that the conductivity of X2CO3:MZO film can be controlled and the thermal stability of ETLs could be improved by X2CO3 blending in MZO. The inverted red QLEDs (R-QLEDs) with Cs2CO3:MZO, Rb2CO3:MZO, and K2CO3:MZO ETLs exhibited the operational lifetime of 407 h for the R-QLEDs with Cs2CO3:MZO, 620 h with Rb2CO3:MZO and 94 h with K2CO3:MZO ETLs at T95 with the initial luminance of 1000 cd/m2. Note that all red QLEDs showed the high brightness over 150,000 cd/m2. But the R-QLEDs with Na2CO3:MZO and Li2CO3:MZO ETLs exhibited shorter operational lifetime and poor brightness than the R-QLED with pristine MZO ETL.

| S-EPMC7761844 | biostudies-literature

Light extraction from quantum dot light emitting diodes by multiscale nanostructures.

Project description:Improving the light extraction efficiency by introducing optical-functional structures outside of quantum dot light emitting diodes (QLEDs) for further enhancing the external quantum efficiency (EQE) is essential for their application in display and lighting industries. Although the efficiency of QLEDs has been optimized by controlling the synthesis of the quantum dots, the low outcoupling efficiency is indeed unresolved because of total internal reflections, waveguides and metal surface absorptions within the device. Here, we utilize multiscale nanostructures attached to the outer surface of the glass substrate to extract the trapped light from the emitting layers of QLEDs. The result indicates that both the EQE and luminance are improved from 12.29% to 17.94% and 122 400 cd m-2 to 178 700 cd m-2, respectively. The maximum EQE and current efficiency improve to 21.3% and 88.3 cd A-1, respectively, which are the best performances among reported green QLEDs with light outcoupling nanostructures. The improved performance is ascribed to the elimination of total internal reflection by multiscale nanostructures attached to the outer surface of the QLEDs. Additionally, the simulation results of the finite-difference time domain (FDTD) also demonstrate that the light trapping effect is reduced by the multiscale nanostructures. The design of novel light outcoupling nanostructures for further improving the efficiency of QLEDs can promote their application in display and lighting industries.

| S-EPMC9417338 | biostudies-literature

Origin of Positive Aging in Quantum-Dot Light-Emitting Diodes.

Project description:The phenomenon of positive aging, i.e., efficiency increased with time, is observed in quantum-dot light-emitting diodes (QLEDs). For example, the external quantum efficiency (EQE) of blue QLEDs is significantly improved from 4.93% to 12.97% after storage for 8 d. The origin of such positive aging is thoroughly investigated. The finding indicates that the interfacial reaction between Al cathode and ZnMgO electron transport layer accounts for such improvement. During shelf-aging, the Al slowly reacts with the oxygen from ZnMgO, and consequently, leads to the formation of AlO x and the production of oxygen vacancies in ZnMgO. The AlO x interlayer reduces the electron injection barrier while the oxygen vacancies increase the conductivity of ZnMgO and, as a result, the electron injection is effectively enhanced. Moreover, the AlO x can effectively suppress the quenching of excitons by metal electrode. Due to the enhancement of electron injection and suppression of exciton quenching, the aged blue, green, and red QLEDs exhibit a 2.6-, 1.3-, and 1.25-fold efficiency improvement, respectively. The studies disclose the origin of positive aging and provide a new insight into the exciton quenching mechanisms, which would be useful for further constructing efficient QLED devices.

| S-EPMC6193172 | biostudies-literature

On the degradation mechanisms of quantum-dot light-emitting diodes.

Project description:The operating lifetime of blue quantum-dot light-emitting diodes (QLED) is currently a short slab for this emerging display technology. To pinpoint the origin of device degradation, here we apply multiple techniques to monitor the electric-field distribution and space-charge accumulation across the multilayered structure before and after lifetime tests. Evident by charge-modulated electro-absorption and capacitance-voltage characteristics, the excited electrons in blue quantum dots (QD) are prone to cross the type II junction between the QD emission layer and the electron-transporting layer (ETL) due to the offset of conduction band minimum, leading to space-charge accumulation and operating-voltage rise in the ETL. Therefore, unlike those very stable red devices, of which the lifetime is primarily limited by the slow degradation of hole-transporting layer, the poor lifetime of blue QLED originates from the fast degradation at the QD-ETL junction. Materials engineering for efficient electron injection is prerequisite for the boost of operating lifetime.

| S-EPMC6377672 | biostudies-literature

Utilization of Nanoporous Nickel Oxide as the Hole Injection Layer for Quantum Dot Light-Emitting Diodes.

Project description:Nickel oxide (NiOx) has been extensively investigated as the hole injection layer (HIL) for many optoelectronic devices because of its excellent hole mobility, high environmental stability, and low-cost fabrication. In this research, a NiOx thin film and nanoporous layers (NPLs) have been utilized as the HIL for the fabrication of quantum dot light-emitting diodes (QLEDs). The obtained NiOx NPLs have spongelike nanostructures that possess a larger surface area to enhance carrier injection and to lower the turn-on voltage as compared with the NiOx thin film. The energy levels of NiOx were slightly downshifted by incorporating the nanoporous structure. The amount of Ni2O3 species is higher than that of NiO in the NiOx NPL, confirming its good hole transport ability. The best QLED was achieved with a 30 nm thick NiOx NPL, exhibiting a maximum brightness of 68 646 cd m-2, a current efficiency of 7.60 cd A-1, and a low turn-on voltage of 3.4 V. More balanced carrier transport from the NiOx NPL and ZnO NPs/polyethylenimine ethoxylated (PEIE) is responsible for the improved device performance.

| S-EPMC8158834 | biostudies-literature

Quantum-Dot Light-Emitting Diodes with Nitrogen-Doped Carbon Nanodot Hole Transport and Electronic Energy Transfer Layer.

Project description:Electroluminescence efficiency is crucial for the application of quantum-dot light-emitting diodes (QD-LEDs) in practical devices. We demonstrate that nitrogen-doped carbon nanodot (N-CD) interlayer improves electrical and luminescent properties of QD-LEDs. The N-CDs were prepared by solution-based bottom up synthesis and were inserted as a hole transport layer (HTL) between other multilayer HTL heterojunction and the red-QD layer. The QD-LEDs with N-CD interlayer represented superior electrical rectification and electroluminescent efficiency than those without the N-CD interlayer. The insertion of N-CD layer was found to provoke the Förster resonance energy transfer (FRET) from N-CD to QD layer, as confirmed by time-integrated and -resolved photoluminescence spectroscopy. Moreover, hole-only devices (HODs) with N-CD interlayer presented high hole transport capability, and ultraviolet photoelectron spectroscopy also revealed that the N-CD interlayer reduced the highest hole barrier height. Thus, more balanced carrier injection with sufficient hole carrier transport feasibly lead to the superior electrical and electroluminescent properties of the QD-LEDs with N-CD interlayer. We further studied effect of N-CD interlayer thickness on electrical and luminescent performances for high-brightness QD-LEDs. The ability of the N-CD interlayer to improve both the electrical and luminescent characteristics of the QD-LEDs would be readily exploited as an emerging photoactive material for high-efficiency optoelectronic devices.

| S-EPMC5388879 | biostudies-literature

Thermal assisted up-conversion electroluminescence in quantum dot light emitting diodes.

Project description:Up-conversion electroluminescence, in which the energy of a emitted photon is higher than that of the excitation electron, is observed in quantum-dot light-emitting diodes. Here, we study its mechanism by investigating the effect of thermal energy on the charge injection dynamic. Based on the results of temperature-dependent electroluminescence and theoretical analysis, we reveal that at sub-bandgap voltage, holes can be successfully injected into quantum-dots via thermal-assisted thermionic-emission mechanism, thereby enabling the sub-bandgap turn-on and up-conversion electroluminescence of the devices. Further theoretical deduction and experimental results confirm that thermal-assisted hole-injection is the universal mechanism responsible for the up-conversion electroluminescence. This work uncovers the charge injection process and unlocks the sub-bandgap turn-on mechanism, which paves the road for the development of up-conversion devices with power conversion efficiency over 100%.

| S-EPMC8766545 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data