Synthesis of chitosan-grafted poly-acrylic acid (CTS-g-PAA) hydrogel and its potential application in biosensors for signal enhancing and bioanalysis

ABSTRACT: Nowadays, hydrogels have been attracted a lot of interest due to their immense potential in different fields such as biomedicine and biotechnology. Biodegradable and biocompatible pH-sensitive chitosan-grafted polyacrylic acid (CTS-g-PAA) hydrogel was synthesized by grafting an acrylic acid monomer onto chitosan at the presence of methylene bisacrylamide as a cross-linking agent and ammonium persulphate as an initiator. FT-IR spectroscopy and scanning electron microscopy (SEM) were used to analyze the properties of the obtained hydrogel. The synthesized hydrogel is suitable for the delivery of many hydrophilic drugs or species. Using a multi-walled carbon nanotube modified-glassy carbon electrode (CNT-GCE), the loading and release conditions of Nile Blue (NB) as an electroactive compound were evaluated utilizing the differential pulse voltammetry (DPV) and cyclic voltammetry (CV). The effect of various parameters on the electrochemical signal of NB was investigated, and the optimal conditions for the efficient performance of hydrogel to delivery of NB were obtained. The electrocatalytic current values show linear dependence to NB concentration in the range of 0.098 – 0.971 μM while the detection limit of this electrochemical platform was 12.3 nM. The unique proposed hydrogel with the electroactive NB has a broad range of possible applications in biosensors for signal enhancement and bioanalysis.

Supplementary Information

The online version contains supplementary material available at 10.1007/s10854-021-06939-7.

SUBMITTER: Alipour E

PROVIDER: S-EPMC8421459 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Background: The repair of wounds usually caused by trauma or other chronic diseases remained challenging in clinics due to the potential risk of inflammation and inadequate tissue regenerative properties. Among them, the behaviour of immune cells, such as macrophages, is critical in tissue repair. Materials and methods: In this study, a water-soluble phosphocreatine-grafted methacryloyl chitosan (CSMP) was synthesized with a one-step lyophilization method, followed by the fabrication of CSMP hydrogel with a photocrosslinked method. The microstructure, water absorption and mechanical properties for the hydrogels were investigated. Then, the macrophages were co-cultured with hydrogels and the pro-inflammatory factors and polarization markers for these macrophages were detected through real-time quantitative polymerase chain reaction (RT-qPCR), Western blot (WB), and flow cytometry methods. Finally, the CSMP hydrogel was implanted in a wound defect area in mice to test its ability to promote wound healing. Results: The lyophilized CSMP hydrogel had a porous structure with pores ranging in size from 200 to 400 μm, which was larger than the CSM hydrogel’s. The lyophilized CSMP hydrogel possessed a higher water absorption rate compared with the CSM hydrogel. The compressive stress and modulus of these hydrogels were increased in the initial 7 days immersion and then gradually decreased during the in vitro immersion in PBS solution up to 21 days; the CSMP hydrogel showed a higher value in these parameters versus the CSM hydrogel. The CSMP hydrogel inhibited the expression of inflammatory factors such as interleukin-1β (IL-1β), IL-6, IL-12, and tumor necrosis factor-α (TNF-α) in an in vitro study cocultured with pro-inflammatory factors in pre-treated bone marrow-derived macrophages (BMM). The mRNA sequencing results showed that the CSMP hydrogel might inhibit the macrophages’ M1 type polarization through the NF-κB signaling pathway. Furthermore, when compared to the control group, the CSMP hydrogel promoted more skin area repair in the mouse wound defect area, and inflammatory factors such as IL-1β, IL-6, and TNF-α were lower in the repaired tissue for the CSMP group. Conclusion: This phosphate-grafted chitosan hydrogel showed great promise for wound healing through regulating the macrophage’s phenotype via the NF-κB signaling pathway.

Dataset Information

Synthesis of chitosan-grafted poly-acrylic acid (CTS-g-PAA) hydrogel and its potential application in biosensors for signal enhancing and bioanalysis

Supplementary Information

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets