Status of decontamination methods after using dentin adhesion inhibitors on indirect restorations: An integrative review of 19 publications.

ABSTRACT: The purpose of this review was to assess the literature regarding the decontamination of resin cement before the luting procedure in order to provide clinicians with a comparative overview of decontamination effects. A total of 19 articles were selected for inclusion in this review. The results indicated that bonding effectiveness is reduced due to residual adhesion inhibitors such as saliva, blood, hemostatic agents, and temporary/provisional cement. Self-etching and self-adhesive systems tend to be more negatively affected by adhesion inhibitors than do etch and rinse systems. Cleaning with an ultrasonic scaler or rotating brush have demonstrated conflicting effects in several studies. Some studies have reported that phosphoric acid has negative effects and recommend mild acid for decontamination. The application of phosphoric acid followed by sodium hypochlorite has been shown to help avoid negative effects. Alumina blasting has been investigated as a mechanical cleaning method in a relatively large number of experiments, most of which have confirmed its effectiveness. An intraoral cleaner containing functional monomers that has become commercially available in recent years is a promising method in clinical practice because it can easily and effectively remove temporary adhesive material. In addition, adhesion inhibitors can be easily removed from resin-coated dentin surfaces.

SUBMITTER: Mine A

PROVIDER: S-EPMC8424590 | biostudies-literature | 2021 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Status of decontamination methods after using dentin adhesion inhibitors on indirect restorations: An integrative review of 19 publications.

Mine Atsushi A Nikaido Toru T Matsumoto Mariko M Takagaki Tomohiro T Ishida Masaya M Ban Shintaro S Yamanaka Azusa A Takaishi Munechika M Yumitate Masahiro M Hagino Ryosuke R Van Meerbeek Bart B Yatani Hirofumi H

The Japanese dental science review 20210904

The purpose of this review was to assess the literature regarding the decontamination of resin cement before the luting procedure in order to provide clinicians with a comparative overview of decontamination effects. A total of 19 articles were selected for inclusion in this review. The results indicated that bonding effectiveness is reduced due to residual adhesion inhibitors such as saliva, blood, hemostatic agents, and temporary/provisional cement. Self-etching and self-adhesive systems tend ...[more]

PMID: 34522239

Similar Datasets

Project description:Immediate dentin sealing (IDS) involves applying an adhesive system to dentin directly after tooth preparation, before impression. This was considered an alternate to delayed dentin sealing (DDS), a technique in which hybridization is performed following the provisional phase and just before the indirect restoration luting procedure. This study aimed to compare the bond strength of restorations to dentin of the IDS and the DDS techniques throughout a systematic review and meta-analysis. The following PICOS framework was used: population, indirect restorations; intervention, IDS; control, DDS; outcomes, bond strength; and study design, in vitro studies. PubMed (MedLine), The Cochrane Library, ISI Web of Science, Scielo, Scopus, and Embase were screened up to January 2022 by two reviewers (L.H. and R.B.). In vitro papers studying the bond strength to human dentin of the IDS technique compared to the DDS technique were considered. Meta-analyses were carried out by using a software program (Review Manager v5.4.1; The Cochrane Collaboration). Comparisons were made by considering the adhesive used for bonding (two-step etch-and-rinse, three step etch-and-rinse, one-step self-etch, two-step self-etch, and universal adhesives). A total of 3717 papers were retrieved in all databases. After full-text assessment, 22 potentially eligible studies were examined for qualitative analysis, leaving a total of 21 articles for the meta-analysis. For the immediate bond strength, regardless of the adhesive strategy used, the IDS technique improved the bond strength of restorations to the dentin (p < 0.001). Taking into account the subgroup analysis, it seems that the use of the IDS technique with a two-step etch-and-rinse or a one-step self-etch adhesive system does not represent any advantage over the DDS technique (p = 0.07, p = 0.15). On the other hand, for the aged bond strength, regardless of the adhesive strategy used, the IDS technique improved the bond strength of restorations to the dentin (p = 0.001). The subgroups analysis shows that this improvement is observed only when a three-step etch-and-rinse adhesive system (p < 0.001) or when a combination of an adhesive system plus a layer of flowable resin (p = 0.01) is used. The in vitro evidence suggests that the use of the IDS technique improves the bond strength of dentin to resin-based restorations regardless of the adhesive strategy used. The use of a three-step etch-and-rinse adhesive system or the combination of an adhesive system plus a layer of flowable resin seems to considerably enhance the bond strength in the long term.

Project description:Dental caries, i.e., tooth decay mediated by bacterial activity, is the most widespread chronic disease worldwide. Carious lesions are commonly treated using dental resin composite restorations. However, resin composite restorations are prone to recurrent caries, i.e., reinfection of the surrounding dental hard tissues. Recurrent caries is mainly a consequence of waterborne and/or biofilm-mediated degradation of the tooth-restoration interface through hydrolytic, acidic and/or enzymatic challenges. Here we use amphipathic antimicrobial peptides to directly coat dentin to provide resin composite restorations with a 2-tier protective system, simultaneously exploiting the physicochemical and biological properties of these peptides. Our peptide coatings modulate dentin's hydrophobicity, impermeabilize it, and are active against multispecies biofilms derived from caries-active individuals. Therefore, the coatings hinder water penetration along the otherwise vulnerable dentin/restoration interface, even after in vitro aging, and increase its resistance against degradation by water, acids, and saliva. Moreover, they do not weaken the resin composite restorations mechanically. The peptide-coated highly-hydrophobic dentin is expected to notably improve the service life of resin composite restorations and to enable the development of entirely hydrophobic restorative systems. The peptide coatings were also antimicrobial and thus, they provide a second tier of protection preventing re-infection of tissues in contact with restorations. STATEMENT OF SIGNIFICANCE: We present a technology using designer peptides to treat the most prevalent chronic disease worldwide; dental caries. Specifically, we used antimicrobial amphipathic peptides to coat dentin with the goal of increasing the service life of the restorative materials used to treat dental caries, which is nowadays 5 years on average. Water and waterborne agents (enzymes, acids) degrade restorative materials and enable re-infection at the dentin/restoration interface. Our peptide coatings will hinder degradation of the restoration as they produced highly hydrophobic and antimicrobial dentin/material interfaces. We anticipate a high technological and economic impact of our technology as it can notably reduce the lifelong dental bill of patients worldwide. Our findings can enable the development of restorations with all-hydrophobic and so, more protective components.

Project description:ObjectivesThe aim was to assess how incorporating a short-fiber composite (SFC) core would affect the fracture behavior of direct and indirect overlays. Furthermore, to examine the relationship between the thickness ratio of SFC core to particulate-filled composite (PFC) veneering and the fracture-behavior of bilayered-structured restorations.Materials and methodsA total of 120 molars were used to create MOD cavities, with palatal cusps removed. Four different groups of direct overlays were then made (n = 15/group), all of which featured a SFC core (everX Flow) with varying thicknesses (0, 1, 4, and 5 mm), as well as a surface layer of PFC (G-aenial Posterior), with the overall thickness of the bilayered-structured restoration set at 5 mm. Additionally, four groups of CAD/CAM restorations were created (Cerasmart 270 and Initial LiSi Block), with or without 2 mm of SFC core reinforcement. Following the fabrication of these restorations, cyclic fatigue aging was carried out for a total of 500,000 cycles, with an applied maximum load (Fmax) of 150 N. Subsequently, each restoration underwent quasi-static loading until fracture. The fracture mode was subsequently evaluated using optical microscopy and SEM.ResultsThere were no statistically significant differences (p > 0.05) observed in the fracture resistance of indirect overlays reinforced with a 2-mm SFC core compared to those made solely from restorative materials. Direct overlays constructed using plain SFC or with a 4-mm layer thickness of SFC core exhibited significantly higher fracture resistance values (2674 ± 465 and 2537 ± 561 N) (p < 0.05) when compared to all other groups tested, according to the statistical analysis ANOVA.ConclusionsThe most effective method for restoring large MOD cavities was found to be direct restoration using SFC either alone or as a bulk core in combination with PFC composite.Clinical relevanceThe use of SFC as bulk reinforcing base will significantly improve the loading performance of directly layered restorations.

Project description:ObjectivesThis study was conducted to evaluate the effect of ethanolic extract of propolis on antibacterial and microshear bond strength of glass ionomer restorations to dentin.Materials and methodsConventional glass ionomer cement (Equia forte, GC Tokyo, Japan), resin-modified glass ionomer (Fuji II LC, GC Tokyo, Japan) and propolis powder (dried extract from honey bees) materials were used in this study. Both conventional glass ionomer and resin-modified glass ionomer were modified by two different concentrations of ethanolic extract of propolis (10 % and 25 % EEP). For antibacterial test, Streptococcus mutans strain was spread on agar petri dishes using a sterile swab. Discs of both glass ionomer restorative materials (without adding EEP, with 10 % EEP and with 25 % EEP) were fabricated within the agar plates. Antibacterial activity was evaluated by measuring the inhibition zones around each disc. For microshear bond strength test, 60 healthy human permanent molars were prepared by cutting occlusal surface and expose the dentin at the height of contour of all teeth then conditioned using poly acrylic acid conditioner, both glass ionomer restorative materials (without adding EEP, with 10 % EEP and with 25 % EEP) were mixed and applied on conditioned dentin surface by using tygon tube. Microshear bond strength was evaluated by the universal testing machine.ResultsTwo-way ANOVA test revealed that both glass ionomer type and different concentrations of EEP had significant effect on the antibacterial test results and microshear bond strength values (p < 0,05). Glass ionomer restorative material with 25%EEP had the highest antibacterial values whereas glass ionomer restorative material without modifications (control groups) had the lowest values. Resin-modified glass ionomer without any modification (control group) had the highest bond strength while resin-modified glass ionomer with 25%EEP had the lowest bond strength.ConclusionsIncorporation of ethanolic extract of propolis to glass ionomer restorative material increases the antibacterial effects of both conventional GIC and RMGI. Inspite of this advantage, it seems that it has deleterious effect on microshear bond strength to dentin.

Dataset Information

Status of decontamination methods after using dentin adhesion inhibitors on indirect restorations: An integrative review of 19 publications.

Publications

Status of decontamination methods after using dentin adhesion inhibitors on indirect restorations: An integrative review of 19 publications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets