Molecular Precursor Route to Bournonite (CuPbSbS₃) Thin Films and Powders.

ABSTRACT: Quaternary metal chalcogenides have attracted attention as candidates for absorber materials for inexpensive and sustainable solar energy generation. One of these materials, bournonite (orthorhombic CuPbSbS₃), has attracted much interest of late for its properties commensurate with photovoltaic energy conversion. This paper outlines the synthesis of bournonite for the first time by a discrete molecular precursor strategy. The metal dithiocarbamate complexes bis(diethyldithiocarbamato)copper (II) (Cu(S₂CNEt₂)₂, (1)), bis(diethyldithiocarbamato)lead (II) (Pb(S₂CNEt₂)₂, (2)), and bis(diethyldithiocarbamato)antimony (III) (Sb(S₂CNEt₂)₃, (3)) were prepared, characterized, and employed as molecular precursors for the synthesis of bournonite powders and the thin film by solvent-less pyrolysis and spray-coat-pyrolysis techniques, respectively. The polycrystalline powders and thin films were characterized by powder X-ray diffraction (p-XRD), which could be indexed to orthorhombic CuPbSbS₃. The morphology of the powder at the microscale was studied using scanning electron microscopy (SEM). Energy-dispersive X-ray spectroscopy (EDX) was used to elucidate an approximately 1:1:1:3 Cu/Pb/Sb/S elemental ratio. An optical band gap energy of 1.55 eV was estimated from a Tauc plot, which is close to the theoretical value of 1.41 eV.

SUBMITTER: Alharbi YT

PROVIDER: S-EPMC8424643 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

A molecular precursor route to quaternary chalcogenide CFTS (Cu2FeSnS4) powders as potential solar absorber materials.

Project description:In the present work we report on the synthesis of tetragonal stannite Cu2FeSnS4 powders using a solvent free melt method using a mixture of Cu, Fe, and Sn(ii)/Sn(iv) O-ethylxanthates heated at different temperatures. The as-synthesized powders were characterized by powder X-ray diffraction (p-XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), UV-Vis absorption spectroscopy, scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) spectroscopy, which confirm the successful synthesis of stannite CFTS. Optical measurements show that Cu2FeSnS4 powders have visible light absorption onsets in the far red with direct band gap energies in the range 1.32-1.39 eV which are suitable for acting as efficient absorber layers in solar cells. Electronic characterisation of these materials deposited as thin films by spin coating show that they are p type semiconductors with respectable carrier mobilities of ca. 60 cm2 V-1 s-1 with carrier densities on the order of 1014 cm-1.

| S-EPMC9069629 | biostudies-literature

Thiourea-Derived Single-Source Molecular Precursor For Spin-Coated PbS Thin Films.

Project description:In search of a suitable single-source precursor for the deposition of nanostructured PbS thin films at moderate temperatures under ambient conditions, we have synthesized the ligand N-(thiomorpholine-4-carbothioyl)benzamide and its corresponding lead(II) complex. The structures of both compounds were determined by single-crystal X-ray diffraction. In the complex, two ligands coordinate to a lead(II) atom in hemi-directed geometry through S and O atoms. Secondary intermolecular Pb⋅⋅⋅S interactions group the complexes into pairs. As bulk powders, both the ligand and complex show nominal composition and purity as evidenced by elemental analysis, 1 H NMR and IR spectroscopy. Thermal analysis of the lead(II) complex was carried out to understand its thermal decomposition behaviour for establishing a thin film fabrication protocol. Thin films of phase-pure PbS were fabricated using this new molecular precursor at the comparatively low annealing temperature of 250 °C. The film showed nanoparticles with cuboidal morphology and a blue-shifted optical absorption.

| S-EPMC10104949 | biostudies-literature

Antiferroelectric PbSnO3 Epitaxial Thin Films.

Project description:In condensed matter physics, oxide materials show various intriguing physical properties. Therefore, many efforts are made in this field to develop functional oxides. Due to the excellent potential for tin-based perovskite oxides, an expansion of new related functional compounds is crucial. This work uses a heteroepitaxial approach supported by theoretical calculation to stabilize PbSnO3 thin films with different orientations. The analyses of X-ray diffraction and transmission electron microscopy unveil the structural information. A typical antiferroelectric feature with double hysteresis and butterfly loops is observed through electrical characterizations consistent with the theoretical prediction. The phase transition is monitored, and the transition temperatures are determined based on temperature-dependent structural and electrical characterizations. Furthermore, the microscopic antiferroelectric order is noticed under atomic resolution images via scanning transmission electron microscopy. This work offers a breakthrough in synthesizing epitaxial PbSnO3 thin films and comprehensively understanding its anisotropic antiferroelectric behavior.

| S-EPMC9762279 | biostudies-literature

Scalable Route to the Fabrication of CH3NH3PbI3 Perovskite Thin Films by Electrodeposition and Vapor Conversion.

Project description:Hybrid halide perovskite thin films are applicable in a wide range of devices such as light-emitting diodes, solar cells, and photodetectors. The optoelectronic properties of perovskites together with their simple and inexpensive film deposition methods make these materials a viable alternative to established materials in these devices. However, the potential of perovskite materials is compromised by the limitations of the existing deposition methods, which suffer from trade-off among suitability for large-scale industrial production in a batch or roll-to-roll manner, deposition area, film quality, and costs. We addressed these limitations by developing a deposition method that is inexpensive, applicable to large substrate areas, scalable, and yields high-quality perovskite films. In this study, the low-cost electrodeposition (ED) method and sequential exposure to reagent vapors produce CH3NH3PbI3 perovskite films with thickness nonuniformity below 9% on a centimeter scale. PbO2 films are electrodeposited first and then undergo two vapor conversion steps, with HI vapor in the first step and CH3NH3I vapor in the second step. The second step yields CH3NH3PbI3 films that are continuous and consist of micrometer-sized grains. This process allows the preparation of both α- and β-phase CH3NH3PbI3 films, offers a simple means to control the film thickness, and works over a wide range of film thicknesses. In this work, films with thicknesses ranging from 100 nm to 10 μm were prepared. ED and vapor conversion are inherently scalable techniques and hence the process described herein could benefit application areas in which large device areas and throughput are required, such as the production of solar cells.

| S-EPMC6640741 | biostudies-literature

Atomic layer deposition of dielectric Y2O3 thin films from a homoleptic yttrium formamidinate precursor and water.

Project description:We report the application of tris(N,N'-diisopropyl-formamidinato)yttrium(iii) [Y(DPfAMD)3] as a promising precursor in a water-assisted thermal atomic layer deposition (ALD) process for the fabrication of high quality Y2O3 thin films in a wide temperature range of 150 °C to 325 °C. This precursor exhibits distinct advantages such as improved chemical and thermal stability over the existing Y2O3 ALD precursors including the homoleptic and closely related yttrium tris-amidinate [Y(DPAMD)3] and tris-guanidinate [Y(DPDMG)3], leading to excellent thin film characteristics. Smooth, homogeneous, and polycrystalline (fcc) Y2O3 thin films were deposited at 300 °C with a growth rate of 1.36 Å per cycle. At this temperature, contamination levels of C and N were under the detectable limits of nuclear reaction analysis (NRA), while X-ray photoelectron spectroscopy (XPS) measurements confirmed the high purity and stoichiometry of the thin films. From the electrical characterization of metal-insulator-semiconductor (MIS) devices, a permittivity of 13.9 at 1 MHz could be obtained, while the electric breakdown field is in the range of 4.2 and 6.1 MV cm-1. Furthermore, an interface trap density of 1.25 × 1011 cm-2 and low leakage current density around 10-7 A cm-2 at 2 MV cm-1 are determined, which satisfies the requirements of gate oxides for complementary metal-oxide-semiconductor (CMOS) based applications.

| S-EPMC8693876 | biostudies-literature

LiNbO3 Thin Films through a Sol-Gel/Spin-Coating Approach Using a Novel Heterobimetallic Lithium-Niobium Precursor.

Project description:Lithium niobate is a lead-free material which has attracted considerable attention due to its excellent optical, piezoelectric, and ferroelectric properties. This research is devoted to the synthesis through an innovative sol-gel/spin-coating approach of polycrystalline LiNbO3 films on Si substrates. A novel single-source hetero-bimetallic precursor containing lithium and niobium was synthesized and applied to the sol-gel synthesis. The structural, compositional, and thermal characteristics of the precursor have been tested through attenuated total reflection, X-ray photoelectron spectroscopy, thermogravimetric analysis, and differential scanning calorimetry. The LiNbO3 films have been characterized from a structural point of view with combined X-ray diffraction and Raman spectroscopy. Field-emission scanning electron microscopy, energy dispersive X-ray analysis, and X-ray photoelectron spectroscopy have been used to study the morphological and compositional properties of the deposited films.

| S-EPMC10892834 | biostudies-literature

CO2-based atomic/molecular layer deposition of lithium ethylene carbonate thin films.

Project description:When a conventional lithium-ion battery (LIB) is cycled, a solid electrolyte interphase (SEI) forms on the surface of a negative electrode, passivating it but also depleting the capacity of the battery. Most commercial LIBs utilize a carbonate-based electrolyte, which at least temporarily leads to the formation of lithium alkyl carbonates (ROCO2Li) as the main organic SEI component. Here, we pioneer the use of atomic/molecular layer deposition (ALD/MLD) for the fabrication of lithium ethyl glycoxide (LiEG) and lithium ethylene carbonate (LiEGCO) thin films, to mimic the lithium alkyl carbonate component of the SEI. For the in situ growth of LiEGCO, we employ for the first time CO2 as an ALD/MLD precursor. The films are characterized using XRR, GIXRD, FTIR, AFM and SEM.

| S-EPMC9417553 | biostudies-literature

Fabrication of Transparent and Conductive SWCNT/SiO2 Composite Thin-Film by Photo-Irradiation of Molecular Precursor Films.

Project description:A single-walled carbon nanotube (SWCNT)-silica composite thin film on a quartz glass was formed by ultraviolet irradiation (20-40 °C) onto a spin-coated precursor film. With 7.4 mass% SWCNTs, the electrical resistivity reached 7.7 × 10-3 Ω·cm after UV-irradiation. The transmittance was >80% at 178-2600 nm, and 79%-73% at 220-352 nm. Heat treatment increased the transparency and pencil hardness, without affecting the low electrical resistivity. Raman spectroscopy and microscopic analyses revealed the excellent film morphology with good SWCNT dispersal. The low refractive index (1.49) and haze value (<1.5%) are invaluable for transparent windows for novel optoelectronic devices.

| S-EPMC8707605 | biostudies-literature

A Fast Route Towards Freestanding Single-Crystalline Oxide Thin Films by Using YBa2Cu3O7-x as a Sacrificial Layer.

Project description:Researchers have long been seeking multifunctional materials that can be adopted for next-generation nanoelectronics, and which, hopefully, are compatible with current semiconductor processing for further integration. Along this vein, complex oxides have gained numerous attention due to their versatile functionalities. Despite the fact that unbounded potential of complex oxides has been examined over the past years, one of the major challenges lies in the direct integration of these functional oxides onto existing devices or targeted substrates that are inherently incompatible in terms of oxide growth. To fulfill this goal, freestanding processes have been proposed, in which wet etching of inserted sacrificial layers is regarded as one of the most efficient ways to obtain epitaxial high-quality thin films. In this study, we propose using an alternative oxide, YBa2Cu3O7 (YCBO), as a sacrificial layer, which can be easily dissolved in light hydrochloric acid in a more efficient way, while protecting selected complex oxides intact. The high epitaxial quality of the selected complex oxide before and after freestanding process using YBCO as a sacrificial layer is comprehensively studied via a combination of atomic force microscopy, X-ray diffraction, transmission electron microscopy, and electrical transports. This approach enables direct integration of complex oxides with arbitrary substrates and devices and is expected to offer a faster route towards the development of low-dimensional quantum materials.

| S-EPMC7455685 | biostudies-literature

Quantized anomalous Hall resistivity achieved in molecular beam epitaxy-grown MnBi2Te4 thin films.

Project description:The intrinsic magnetic topological insulator MnBi2Te4 provides a feasible pathway to the high-temperature quantum anomalous Hall (QAH) effect as well as various novel topological quantum phases. Although quantized transport properties have been observed in exfoliated MnBi2Te4 thin flakes, it remains a big challenge to achieve molecular beam epitaxy (MBE)-grown MnBi2Te4 thin films even close to the quantized regime. In this work, we report the realization of quantized anomalous Hall resistivity in MBE-grown MnBi2Te4 thin films with the chemical potential tuned by both controlled in situ oxygen exposure and top gating. We find that elongated post-annealing obviously elevates the temperature to achieve quantization of the Hall resistivity, but also increases the residual longitudinal resistivity, indicating a picture of high-quality QAH puddles weakly coupled by tunnel barriers. These results help to clarify the puzzles in previous experimental studies on MnBi2Te4 and to find a way out of the big difficulty in obtaining MnBi2Te4 samples showing quantized transport properties.

| S-EPMC10776363 | biostudies-literature