A saccharide-based binder for efficient polysulfide regulations in Li-S batteries.

ABSTRACT: The viability of lithium-sulfur batteries as an energy storage technology depends on unlocking long-term cycle stability. Most instability stems from the release and transport of polysulfides from the cathode, which causes mossy growth on the lithium anode, leading to continuous consumption of electrolyte. Therefore, development of a durable cathode with minimal polysulfide escape is critical. Here, we present a saccharide-based binder system that has a capacity for the regulation of polysulfides due to its reducing properties. Furthermore, the binder promotes the formation of viscoelastic filaments during casting which endows the sulfur cathode with a desirable web-like microstructure. Taken together this leads to 97% sulfur utilisation with a cycle life of 1000 cycles (9 months) and capacity retention (around 700 mAh g^-1 after 1000 cycles). A pouch cell prototype with a specific energy of up to 206 Wh kg^-1 is produced, demonstrating the promising potential for practical applications.

SUBMITTER: Huang Y

PROVIDER: S-EPMC8433142 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Mastering Surface Sulfidation of MnP-MnO<sub>2</sub> Heterostructure to Facilitate Efficient Polysulfide Conversion in Li─S Batteries.

Project description:The development of lithium-sulfur (Li─S) batteries has been hampered by the shuttling effect of lithium polysulfides (LiPSs). An effective method to address this issue is to use an electrocatalyst to accelerate the catalytic conversion of LiPSs. In this study, heterogeneous MnP-MnO2 nanoparticles are uniformly synthesized and embedded in porous carbon (MnP-MnO2/C) as core catalysts to improve the reaction kinetics of LiPSs. In situ characterization and density functional theory (DFT) calculations confirm that the MnP-MnO2 heterostructure undergo surface sulfidation during the charge/discharge process, forming the MnS2 phase. Surface sulfidation of the MnP-MnO2 heterostructure catalyst significantly accelerated the SRR and Li2S activation, effectively inhibiting the LiPSs shuttling effect. Consequently, the MnP-MnO2/C@S cathode achieves outstanding rate performance (10 C, 500 mAh g-1) and ultrahigh cycling stability (0.017% decay rate per cycle for 2000 cycles at 5 C). A pouch cell with MnP-MnO2/C@S cathode delivers a high energy density of 429 Wh kg-1. This study may provide a new approach to investigating the surface sulfidation of electrocatalysts, which is valuable for advancing high-energy-density Li-S batteries.

| S-EPMC11348264 | biostudies-literature

Lignin as a Binder Material for Eco-Friendly Li-Ion Batteries.

Project description:The industrial lignin used here is a byproduct from Kraft pulp mills, extracted from black liquor. Since lignin is inexpensive, abundant and renewable, its utilization has attracted more and more attention. In this work, lignin was used for the first time as binder material for LiFePO₄ positive and graphite negative electrodes in Li-ion batteries. A procedure for pretreatment of lignin, where low-molecular fractions were removed by leaching, was necessary to obtain good battery performance. The lignin was analyzed for molecular mass distribution and thermal behavior prior to and after the pretreatment. Electrodes containing active material, conductive particles and lignin were cast on metal foils, acting as current collectors and characterized using scanning electron microscopy (SEM), electrochemical impedance spectroscopy (EIS) and galvanostatic charge-discharge cycles. Good reversible capacities were obtained, 148 mAh·g-1 for the positive electrode and 305 mAh·g-1 for the negative electrode. Fairly good rate capabilities were found for both the positive electrode with 117 mAh·g-1 and the negative electrode with 160 mAh·g-1 at 1C. Low ohmic resistance also indicated good binder functionality. The results show that lignin is a promising candidate as binder material for electrodes in eco-friendly Li-ion batteries.

| S-EPMC5456705 | biostudies-other

Hierarchical TiO2 spheres as highly efficient polysulfide host for lithium-sulfur batteries.

Project description:Hierarchical TiO2 micron spheres assembled by nano-plates were prepared through a facile hydrothermal route. Chemical tuning of the TiO2 through hydrogen reduction (H-TiO2) is shown to increase oxygen-vacancy density and thereby modifies the electronic properties. H-TiO2 spheres with a polar surface serve as the surface-bound intermediates for strong polysulfides binding. Under the restricting and recapturing effect, the sulfur cathode could deliver a high reversible capacity of 928.1?mA h g(-1) after 50 charge-discharge cycles at a current density of 200?mA g(-1). The H-TiO2 additive developed here is practical for restricting and recapturing the polysulfide from the electrolyte.

| S-EPMC4786857 | biostudies-other

A Natural Polymer Captor for Immobilizing Polysulfide/Polyselenide in Working Li-SeS<sub>2</sub> Batteries.

Project description:SeS2 has become a promising cathode material owing to its enhanced electrical conductivity over sulfur and higher theoretical specific capacity than selenium; however, the working Li-SeS2 batteries have to face the practical challenges from the severe shuttling of soluble dual intermediates of polysulfide and polyselenide, especially in high-SeS2-loading cathodes. Herein, a natural organic polymer, Nicandra physaloides pectin (NPP), is proposed to serve as an effective polysulfide/polyselenide captor to address the shuttling issues. Informed by theoretical calculations, NPP is competent to provide a Lewis base-based strong binding interaction with polysulfides/polyselenides via forming lithium bonds, and it can be homogeneously deposited onto a three-dimensional double-carbon conductive scaffold to finally constitute a polysulfide/polyselenide-immobilizing interlayer. Operando spectroscopy analysis validates the enhanced polysulfide/polyselenide trapping and high conversion efficiency on the constructed interlayer, hence bestowing the Li-SeS2 cells with ultrahigh rate capability (448 mAh g-1 at 10 A g-1), durable cycling lifespan (≈ 0.037% capacity attenuation rate per cycle), and high areal capacity (> 6.5 mAh cm-2) at high SeS2 loading of 15.4 mg cm-2. Importantly, pouch cells assembled with this interlayer exhibit excellent flexibility, decent rate capability with relatively low electrolyte-to-capacity ratio, and stable cycling life even under a low electrolyte condition, promising a low-cost, viable design protocol toward practical Li-SeS2 batteries.

| S-EPMC8021686 | biostudies-literature

A Nacre-Like Carbon Nanotube Sheet for High Performance Li-Polysulfide Batteries with High Sulfur Loading.

Project description:Lithium-sulfur (Li-S) batteries are considered as one of the most promising energy storage systems for next-generation electric vehicles because of their high-energy density. However, the poor cyclic stability, especially at a high sulfur loading, is the major obstacles retarding their practical use. Inspired by the nacre structure of an abalone, a similar configuration consisting of layered carbon nanotube (CNT) matrix and compactly embedded sulfur is designed as the cathode for Li-S batteries, which are realized by a well-designed unidirectional freeze-drying approach. The compact and lamellar configuration with closely contacted neighboring CNT layers and the strong interaction between the highly conductive network and polysulfides have realized a high sulfur loading with significantly restrained polysulfide shuttling, resulting in a superior cyclic stability and an excellent rate performance for the produced Li-S batteries. Typically, with a sulfur loading of 5 mg cm-2, the assembled batteries demonstrate discharge capacities of 1236 mAh g-1 at 0.1 C, 498 mAh g-1 at 2 C and moreover, when the sulfur loading is further increased to 10 mg cm-2 coupling with a carbon-coated separator, a superhigh areal capacity of 11.0 mAh cm-2 is achieved.

| S-EPMC6010878 | biostudies-literature

Pitch-based carbon/nano-silicon composite, an efficient anode for Li-ion batteries.

Project description:As silicon-carbon electrodes with low silicon ratio are the negative electrode foreseen by battery manufacturers for the next generation of Li-ion batteries, a great effort has to be made to improve their efficiency and decrease their cost. Pitch-based carbon/nano-silicon composites are proposed as a high performance and realistic electrode material of Li-ion battery anodes. Composites are prepared in a simple way by the pyrolysis under argon atmosphere of silicon nanoparticles, obtained by a laser pyrolysis technique, and a low cost carbon source: petroleum pitch. The effect of the size and the carbon coating of the silicon nanoparticles on the electrochemical performance in Li-ion batteries is highlighted, proving that the carbon coating enhances cycling stability. Helped by a homogeneous dispersion of silicon nanoparticles into the amorphous carbon matrix, a high coulombic efficiency (especially in the first cycle) and a high stability over cycling is observed (over 1100 mA h g-1 after 100 cycles at relatively high current density 716 mA g-1 for Si based electrodes), which are superior to pitch-based carbon/silicon composites found in literature. This simple synthesis method may be extrapolated to other electrode active materials.

| S-EPMC9062498 | biostudies-literature

The Effects of the Binder and Buffering Matrix on InSb-Based Anodes for High-Performance Rechargeable Li-Ion Batteries.

Project description:C-decorated intermetallic InSb (InSb-C) was developed as a novel high-performance anode material for lithium-ion batteries (LIBs). InSb nanoparticles synthesized via a mechanochemical reaction were characterized using X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and energy-dispersive X-ray spectroscopy (EDX). The effects of the binder and buffering matrix on the active InSb were investigated. Poly(acrylic acid) (PAA) was found to significantly improve the cycling stability owing to its strong hydrogen bonding. The addition of amorphous C to InSb further enhanced mechanical stability and electronic conductivity. As a result, InSb-C demonstrated good electrochemical Li-ion storage performance: a high reversible specific capacity (878 mAh·g-1 at 100 mA·g-1 after 140 cycles) and good rate capability (capacity retention of 98% at 10 A·g-1 as compared to 0.1 A·g-1). The effects of PAA and C were comprehensively studied using cyclic voltammetry, differential capacity plots, ex-situ SEM, and electrochemical impedance spectroscopy (EIS). In addition, the electrochemical reaction mechanism of InSb was revealed using ex-situ XRD. InSb-C exhibited a better performance than many recently reported Sb-based electrodes; thus, it can be considered as a potential anode material in LIBs.

| S-EPMC8707395 | biostudies-literature

Cofactor-Assisted Artificial Enzyme with Multiple Li-Bond Networks for Sustainable Polysulfide Conversion in Lithium-Sulfur Batteries.

Project description:Lithium-sulfur batteries possess high theoretical energy density but suffer from rapid capacity fade due to the shuttling and sluggish conversion of polysulfides. Aiming at these problems, a biomimetic design of cofactor-assisted artificial enzyme catalyst, melamine (MM) crosslinked hemin on carboxylated carbon nanotubes (CNTs) (i.e., [CNTs-MM-hemin]), is presented to efficiently convert polysulfides. The MM cofactors bind with the hemin artificial enzymes and CNT conductive substrates through FeN5 coordination and/or covalent amide bonds to provide high and durable catalytic activity for polysulfide conversions, while π-π conjugations between hemin and CNTs and multiple Li-bond networks offered by MM endow the cathode with good electronic/Li+ transmission ability. This synergistic mechanism enables rapid sulfur reaction kinetics, alleviated polysulfide shuttling, and an ultralow (<1.3%) loss of hemin active sites in electrolyte, which is ≈60 times lower than those of noncovalent crosslinked samples. As a result, the Li-S battery using [CNTs-MM-hemin] cathode retains a capacity of 571 mAh g-1 after 900 cycles at 1C with an ultralow capacity decay rate of 0.046% per cycle. Even under raising sulfur loadings up to 7.5 mg cm-2 , the cathode still can steadily run 110 cycles with a capacity retention of 83%.

| S-EPMC8787425 | biostudies-literature

Flame retardant high-power Li-S flexible batteries enabled by bio-macromolecular binder integrating conformal fractions.

Project description:Polymer binders for sulfur cathodes play a very critical role as they prerequisites for an in-situ immobilization against polysulfide shuttle and volume change, while ensuring good adhesion within active materials for ion conduction along with robust mechanical and chemical stability. Here, we demonstrate anionic surface charge facilitated bio-polymer binder for sulfur cathodes enabling excellent performance and fire safety improvement. The aqueous-processable tragacanth gum-based binder is adjusted to house high sulfur loading over 12 mg cm-2 without compromising the sulfur utility and reversibility, imparting high accessibility for Li-ions to sulfur particles about 80%. The intrinsic rod and sphere-like saccharidic conformal fraction's multifunctional polar units act as active channels to reach the sulfur particles. As a result, the binder entraps polysulfides with 46% improvement and restrains the volume changes within 16 % even at 4 C. Moreover, the flexible Li-S battery delivers a stack gravimetric energy density of 243 Wh kg-1, demonstrating high reactivity of sulfur along with good shape conformality, which would open an avenue for the potential development of the compact and flexible high-power device.

| S-EPMC8748741 | biostudies-literature

Discovery of Dual-Functional Amorphous Titanium Suboxide to Promote Polysulfide Adsorption and Regulate Sulfide Growth in Li-S Batteries.

Project description:Lithium-sulfur (Li-S) batteries are promising as next-generation energy storage systems. Adsorbents for sulfide species are favorably applied to the cathode, but this substrate often results in a surface-passivating lithium sulfide(Li2 S) film with a strong adsorption of Li2 S. Here, an amorphous titanium suboxide (a-TiOx) is presented that strongly adsorbs lithium polysulfides (Li2 Sx , x < 6) but relatively weakly adsorbs to Li2 S. With these characteristics, the a-TiOx achieves high conversion of Li2 Sx and high sulfur utilization accompanying the growth of particulate Li2 S. The DFT calculations present a mechanism for particulate growth driven by the promoted diffusion and favorable clustering of Li2 S. The a-TiOx -coated carbon nanotube-assembled film (CNTF) cathode substrate cell achieves a high discharge capacity equivalent to 90% sulfur utilization at 0.2 C. The cell also delivers a high capacity of 850 mAh g-1 even at the ultra-high-speed of 10 C and also exhibits high stability of capacity loss of 0.0226% per cycle up to 500 cycles. The a-TiOx /CNTF is stacked to achieve a high loading of 7.5 mg S cm-2 , achieving a practical areal capacity of 10.1 mAh cm-2 .

| S-EPMC9353452 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data