Voltage-controlled NiO/ZnO p-n heterojunction diode: a new approach towards selective VOC sensing.

ABSTRACT: Metal oxide resistive gas sensors suffer from poor selectivity that restricts their practical applicability. Conventional sensor arrays are used to improve selectivity which increased the system complexity. Here, we have proposed a novel NiO/ZnO-based p-n junction single-diode device for selective sensing of several volatile organic compounds (VOCs) simultaneously by tuning bias voltage. The operating voltage was varied between 3 and 5 volts to achieve selective sensing of 2-propanol (19.1 times for 95 ppm with response and recovery times of 70 s and 55 s respectively' at 3 volts), toluene (20.1 times for 95 ppm with response and recovery times of 100 s and 60 s respectively, at 4 volts), and formaldehyde (11.2 times for 95 ppm with response and recovery times of 88 s and 54 s respectively, at 5 volts). A probable mechanism of the tunable selectivity with operating bias voltage due to increase in surface carriers with increasing voltage was hence put forth. Thus, this device may play an important role to develop future selective multiple VOC sensor thereby replacing standard sensor arrays.

SUBMITTER: Dey S

PROVIDER: S-EPMC8433462 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Integrated spectral photocurrent density and reproducibility analyses of excitonic ZnO/NiO heterojunction.

Project description:In this data article, the excitonic ZnO/NiO heterojunction device (Patel et al., 2017) [1] was measured for the integrated photocurrent density and reproducibility. Photograph of the prepared devices of ZnO/NiO on the FTO/glass is presented. Integrated photocurrent density as a function of photon energy from the sunlight is presented. Quantum efficiency measurement system (McScienceK3100, Korea) compliance with International Measurement System was employed to measure ZnO/NIO devices. These data are shown for the 300-440 nm of segment of the sunlight (AM1.5G, http://rredc.nrel.gov/solar/spectra/am1.5/). Reproducibility measure of ZnO/NiO device was presented for nine devices with the estimated device performance parameters including the open circuit voltage, short circuit current density, fill factor and power conversion efficiency.

| S-EPMC5614732 | biostudies-literature

Self-powered p-NiO/n-ZnO heterojunction ultraviolet photodetectors fabricated on plastic substrates.

Project description:A self-powered ultraviolet (UV) photodetector (PD) based on p-NiO and n-ZnO was fabricated using low-temperature sputtering technique on indium doped tin oxide (ITO) coated plastic polyethylene terephthalate (PET) substrates. The p-n heterojunction showed very fast temporal photoresponse with excellent quantum efficiency of over 63% under UV illumination at an applied reverse bias of 1.2 V. The engineered ultrathin Ti/Au top metal contacts and UV transparent PET/ITO substrates allowed the PDs to be illuminated through either front or back side. Morphology, structural, chemical and optical properties of sputtered NiO and ZnO films were also investigated.

| S-EPMC4759661 | biostudies-literature

New Insights towards High-Temperature Ethanol-Sensing Mechanism of ZnO-Based Chemiresistors.

Project description:In this work, we investigate ethanol (EtOH)-sensing mechanisms of a ZnO nanorod (NRs)-based chemiresistor using a near-ambient-pressure X-ray photoelectron spectroscopy (NAP-XPS). First, the ZnO NRs-based sensor was constructed, showing good performance on interaction with 100 ppm of EtOH in the ambient air at 327 °C. Then, the same ZnO NRs film was investigated by NAP-XPS in the presence of 1 mbar oxygen, simulating the ambient air atmosphere and O2/EtOH mixture at the same temperature. The partial pressure of EtOH was 0.1 mbar, which corresponded to the partial pressure of 100 ppm of analytes in the ambient air. To better understand the EtOH-sensing mechanism, the NAP-XPS spectra were also studied on exposure to O2/EtOH/H2O and O2/MeCHO (MeCHO = acetaldehyde) mixtures. Our results revealed that the reaction of EtOH with chemisorbed oxygen on the surface of ZnO NRs follows the acetaldehyde pathway. It was also demonstrated that, during the sensing process, the surface becomes contaminated by different products of MeCHO decomposition, which decreases dc-sensor performance. However, the ac performance does not seem to be affected by this phenomenon.

| S-EPMC7582869 | biostudies-literature

Gate-tunable carbon nanotube-MoS2 heterojunction p-n diode.

Project description:The p-n junction diode and field-effect transistor are the two most ubiquitous building blocks of modern electronics and optoelectronics. In recent years, the emergence of reduced dimensionality materials has suggested that these components can be scaled down to atomic thicknesses. Although high-performance field-effect devices have been achieved from monolayered materials and their heterostructures, a p-n heterojunction diode derived from ultrathin materials is notably absent and constrains the fabrication of complex electronic and optoelectronic circuits. Here we demonstrate a gate-tunable p-n heterojunction diode using semiconducting single-walled carbon nanotubes (SWCNTs) and single-layer molybdenum disulfide as p-type and n-type semiconductors, respectively. The vertical stacking of these two direct band gap semiconductors forms a heterojunction with electrical characteristics that can be tuned with an applied gate bias to achieve a wide range of charge transport behavior ranging from insulating to rectifying with forward-to-reverse bias current ratios exceeding 10(4). This heterojunction diode also responds strongly to optical irradiation with an external quantum efficiency of 25% and fast photoresponse <15 ?s. Because SWCNTs have a diverse range of electrical properties as a function of chirality and an increasing number of atomically thin 2D nanomaterials are being isolated, the gate-tunable p-n heterojunction concept presented here should be widely generalizable to realize diverse ultrathin, high-performance electronics and optoelectronics.

| S-EPMC3831469 | biostudies-literature

Ag<sub>2</sub>S-Sensitized NiO-ZnO Heterostructures with Enhanced Visible Light Photocatalytic Activity and Acetone Sensing Property.

Project description:Visible light-driven Ag2S-grafted NiO-ZnO ternary nanocomposites are synthesized using a facile and cost-effective homogeneous precipitation method. The structural, morphological, and optical properties were extensively studied, confirming the formation of ternary nanocomposites. The surface area of the synthesized nanocomposites was calculated by electrochemical double-layer capacitance (C dl). Ternary Ag2S/NiO-ZnO nanocomposites showed excellent visible light photocatalytic property which increases further with the concentration of Ag2S. The maximum photocatalytic activity was shown by 8% Ag2S/NiO-ZnO with a RhB degradation efficiency of 95%. Hydroxyl and superoxide radicals were found to be dominant species for photodegradation of RhB, confirmed by scavenging experiments. It is noteworthy that the recycling experiments demonstrated high stability and recyclable nature of the photocatalyst. Moreover, the electrochemical results indicated that the prepared nanocomposite exhibits remarkable activity toward detection of acetone. The fabricated nanocomposite sensor showed high sensitivity (4.0764 ?A mmol L-1 cm-2) and a lower detection limit (0.06 mmol L-1) for the detection of acetone. The enhanced photocatalytic and the sensing property of Ag2S/NiO-ZnO can be attributed to the synergistic effects of strong visible light absorption, excellent charge separation, and remarkable surface properties.

| S-EPMC6682037 | biostudies-literature

High-Performance Deep Ultraviolet Photodetector Based on NiO/β-Ga2O3 Heterojunction.

Project description:Ultraviolet (UV) photodetector has attracted extensive interests due to its wide-ranging applications from defense technology to optical communications. The use of wide bandgap metal oxide semiconductor materials is of great interest in the development of UV photodetector due to their unique electronic and optical properties. In this work, deep UV photodetector based on NiO/β-Ga2O3 heterojunction was developed and investigated. The β-Ga2O3 layer was prepared by magnetron sputtering and exhibited selective orientation along the family of ([Formula: see text] 01) crystal plane after annealing. The photodetector demonstrated good performance with a high responsivity (R) of 27.43 AW-1 under a 245-nm illumination (27 μWcm-2) and the maximum detectivity (D*) of 3.14 × 1012 cmHz1/2 W-1, which was attributed to the p-NiO/n-β-Ga2O3 heterojunction.

| S-EPMC7036083 | biostudies-literature

NH3 Sensor Based on 3D Hierarchical Flower-Shaped n-ZnO/p-NiO Heterostructures Yields Outstanding Sensing Capabilities at ppb Level.

Project description:Hierarchical three-dimensional (3D) flower-like n-ZnO/p-NiO heterostructures with various ZnxNiy molar ratios (Zn5Ni1, Zn2Ni1, Zn1Ni1, Zn1Ni2 and Zn1Ni5) were synthesized by a facile hydrothermal method. Their crystal phase, surface morphology, elemental composition and chemical state were comprehensively investigated by XRD, SEM, EDS, TEM and XPS techniques. Gas sensing measurements were conducted on all the as-developed ZnxNiy-based sensors toward ammonia (NH3) detection under various working temperatures from 160 to 340 °C. In particular, the as-prepared Zn1Ni2 sensor exhibited superior NH3 sensing performance under optimum working temperature (280 °C) including high response (25 toward 100 ppm), fast response/recovery time (16 s/7 s), low detection limit (50 ppb), good selectivity and long-term stability. The enhanced NH3 sensing capabilities of Zn1Ni2 sensor could be attributed to both the specific hierarchical structure which facilitates the adsorption of NH3 molecules and produces much more contact sites, and the improved gas response characteristics of p-n heterojunctions. The obtained results clear demonstrated that the optimum n-ZnO/p-NiO heterostructure is indeed very promising sensing material toward NH3 detection for different applications.

| S-EPMC7506851 | biostudies-literature

A two-step synthesis of nanosheet-covered fibers based on ?-Fe2O3/NiO composites towards enhanced acetone sensing.

Project description:A novel hierarchical heterostructures based on ?-Fe2O3/NiO nanosheet-covered fibers were synthesized using a simple two-step process named the electrospinning and hydrothermal techniques. A high density of ?-Fe2O3 nanosheets were uniformly and epitaxially deposited on a NiO nanofibers. The crystallinity, morphological structure and surface composition of nanostructured based on ?-Fe2O3/NiO composites were investigated by XRD, SEM, TEM, EDX, XPS and BET analysis. The extremely branched ?-Fe2O3/NiO nanosheet-covered fibers delivered an extremely porous atmosphere with huge specific surface area essential for superior gas sensors. Different nanostructured based on ?-Fe2O3/NiO composites were also explored by adjusting the volume ratio of the precursors. The as-prepared samples based on ?-Fe2O3/NiO nanocomposite sensors display apparently enhanced sensing characteristics, including higher sensing response, quick response with recovery speed and better selectivity towards acetone gas at lower operating temperature as compared to bare NiO nanofibers. The sensing response of S-2 based ?-Fe2O3/NiO nanosheet-covered fibers were 18.24 to 100?ppm acetone gas at 169?°C, which was about 6.9 times higher than that of bare NiO nanofibers. The upgraded gas sensing performance of composites based on ?-Fe2O3/NiO nanosheet-covered fibers might be ascribed to the exclusive morphologies with large surface area, p-n heterojunctions and the synergetic performance of ?-Fe2O3 and NiO.

| S-EPMC5786040 | biostudies-literature

NiO/Perovskite Heterojunction Contact Engineering for Highly Efficient and Stable Perovskite Solar Cells.

Project description:Recent research shows that the interface state in perovskite solar cells is the main factor which affects the stability and performance of the device, and interface engineering including strain engineering is an effective method to solve this issue. In this work, a CsBr buffer layer is inserted between NiO x hole transport layer and perovskite layer to relieve the lattice mismatch induced interface stress and induce more ordered crystal growth. The experimental and theoretical results show that the addition of the CsBr buffer layer optimizes the interface between the perovskite absorber layer and the NiO x hole transport layer, reduces interface defects and traps, and enhances the hole extraction/transfer. The experimental results show that the power conversion efficiency of optimal device reaches up to 19.7% which is significantly higher than the efficiency of the device without the CsBr buffer layer. Meanwhile, the device stability is also improved. This work provides a deep understanding of the NiO x /perovskite interface and provides a new strategy for interface optimization.

| S-EPMC7284208 | biostudies-literature

Broadband photoresponse data of transparent all-oxide photovoltaics of ZnO/NiO.

Project description:In this data article, the properties of all transparent metal oxide of ZnO/NiO heterostructure "Transparent all-oxide photovoltaics and broadband high-speed energy-efficient optoelectronics" [1] are presented by characteristics of ZnO and NiO layers, open circuit voltage decay (OCVD), broadband light with intensity dependent current-voltage plots. The device performances under the effect of various optical excitation of intermediated-band, bound excitonic, free-excitonic and band-to-band are presented. The ZnO/NiO heterostructure direction grown on ITO/glass substrate by large area sputtering method [1] was characterized by UV-visible plots and scanning electron microscope (SEM). Carrier lifetime using OCVD of ZnO/NiO devices with carbon paint metal contact is presented. Prolonged open circuit voltage plots under UV light intensity are shown for stability and repeatability studies. I-V characteristics of ZnO/NiO heterostructure under the light wavelength from 623 nm to 365 nm are presented for energy efficient broadband optoelectronics.

| S-EPMC6598871 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data