A Highly Sensitive Electrochemical Glucose Sensor Based on Room Temperature Exfoliated Graphite-Derived Film Decorated with Dendritic Copper.

ABSTRACT: An ultrasensitive enzyme-free glucose sensor was facilely prepared by electrodepositing three-dimensional dendritic Cu on a room temperature exfoliated graphite-derived film (RTEG-F). An excellent electrocatalytic performance was demonstrated for glucose by using Cu/RTEG-F as an electrode. In terms of the high conductivity of RTEG-F and the good catalytic activity of the dendritic Cu structures, the sensor demonstrates high sensitivities of 23.237 mA/mM/cm², R² = 0.990, and 10.098 mA/mM/cm², R² = 0.999, corresponding to the concentration of glucose ranging from 0.025 mM to 1.0 mM and 1.0 mM to 2.7 mM, respectively, and the detection limit is 0.68 μM. In addition, the Cu/RTEG-F electrode demonstrates excellent anti-interference to interfering species and a high stability. Our work provides a new idea for the preparation of high-performance electrochemical enzyme-free glucose sensor.

SUBMITTER: Tang J

PROVIDER: S-EPMC8433722 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

An Exfoliated Graphite-Based Bisphenol A Electrochemical Sensor.

Project description:The use of an exfoliated graphite (EG) electrode in the square wave voltammetric detection of bisphenol A (a model phenolic pollutant) in water, whereby the phenolic electrode fouling challenge is mitigated, is described. The oxidation peak of BPA was observed at about 0.45 V in phosphate buffer solution at pH 10. The current response exhibited a linear relationship with the concentration over a range from 1.56 μM–50 μM. The detection limit was calculated to be 0.76 μM. The EG electrode surface was renewed after each measurement with excellent reproducibility. A real sample application was also investigated.

| S-EPMC3478800 | biostudies-other

A Silver-Loaded Exfoliated Graphite Nanocomposite Anti-Fouling Electrochemical Sensor for Bisphenol A in Thermal Paper Samples.

Project description:Silver nanoparticles (AgNPs) were synthesized separately and loaded onto the expanded layers of exfoliated graphite (EG) to form a silver nanoparticle-exfoliated graphite nanocomposite (AgNPs-EG). The AgNPs-EG was compressed into a pellet (0.6 cm in diameter) and used to prepare an electrochemical sensor for bisphenol A (BPA) in standard samples and in thermal paper. The synthesized materials were characterized by ultraviolet-visible spectrophotometry, X-ray diffraction spectroscopy, scanning electron microscopy, and energy-dispersive X-ray. The electrochemical behavior of BPA on the AgNPs-EG sensor was investigated by cyclic voltammetry and square wave voltammetry. Under optimized experimental conditions, the oxidation peak current was linearly proportional to bisphenol A concentrations in the range from 5.0 to100 μM, with a coefficient of determination (R2 ) of 0.9981. The obtained limit of detection of the method was 0.23 μM. The fabricated sensor was able to overcome electrode fouling with good reproducibility (RSD = 2.62%, n = 5) by mechanical polishing of the electrode on emery paper. The proposed method was successfully applied to determine bisphenol A in thermal paper samples and demonstrated good accuracy of 93.1 to 113% recovery.

| S-EPMC8047760 | biostudies-literature

A Nanometer-Sized Graphite/Boron-Doped Diamond Electrochemical Sensor for Sensitive Detection of Acetaminophen.

Project description:A boron-doped diamond (BDD) has been widely used as an outstanding electrode for constructing high-performance electrochemical biosensors. In this paper, we fabricated a novel electrode combined of nanometer-sized graphite-BDD film (NG-BDD) by chemical vapor deposition. The nanometer-sized graphite (NG) is formed on the (111) facet of BDD via converting an sp3 diamond structure to an sp2 graphitic phase at high temperature in boron-rich ambient. The electrode was characterized by means of scanning electron microscopy, Raman spectroscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. This NG-BDD was performed as an electrode of electrochemical biosensor to detect trace acetaminophen (APAP) accurately. Cyclic voltammetry and differential normal pulse voltammetry are used to investigate the overall performance of the electrochemical device. The sensor has a linear electrochemical response to APAP in the concentration range of 0.02-50 μM, and the detection limit is estimated to be as low as 5 nM. The research has resulted in a solution of constructing a reusable NG-BDD sensor to detect APAP with stability and show potential in extensive application.

| S-EPMC7948231 | biostudies-literature

Highly Sensitive Electrochemical Sensor for Anticancer Drug by a Zirconia Nanoparticle-Decorated Reduced Graphene Oxide Nanocomposite.

Project description:Because of their large surface area and conductivity, some inorganic materials have emerged as good candidates for the trace-level detection of pharmaceutical drugs. In the present work, we demonstrate the detection of an anticancer drug (regorafenib, REG) by using an electrochemical sensor based on a nanocomposite material. We synthesized a zirconia-nanoparticle-decorated reduced graphene oxide composite (ZrO2/rGO) using a one-pot hydrothermal method. Reduction of the graphene oxide supports of the Zr2+ ions with hydrazine hydrate helped in preventing the agglomeration of the zirconia nanoparticles and in obtaining an excellent electrocatalytic response of the nanostructure ZrO2/rGO-based electrochemical sensor. Structural and morphological characterization of the nanostructure ZrO2/rGO was performed using various analytical methods. A novel regorafenib (REG) electrochemical sensor was fabricated by immobilizing the as-prepared nanostructure ZrO2/rGO on to a glassy carbon electrode (GCE). The resulting ZrO2/rGO/GCE could be used for the rapid and selective determination of REG in the presence of ascorbic acid and uric acid. The ZrO2/rGO/GCE showed a linear response for the REG analysis in the dynamic range 11-343 nM, with a remarkable lower detection limit and limit of quantifications of 17 and 59 nM, respectively. The newly developed sensor was used for the accurate determination of REG in both serum samples and pharmaceutical formulations, with satisfactory results.

| S-EPMC6289492 | biostudies-literature

An Electrochemical Sensor Based on Carbon Paper Modified with Graphite Powder for Sensitive Determination of Sunset Yellow and Tartrazine in Drinks.

Project description:The paper describes the development of an electrochemical sensor to be used for the determination of synthetic food colorants such as Sunset Yellow FCF (SY) and Tartrazine (TZ). The sensor is a carbon paper (CP) electrode, manufactured by using hot lamination technology and volume modified with fine-grained graphite powder (GrP). The sensor (GrP/CP) was characterized by scanning electron microscopy, energy dispersive spectrometry, electrochemical impedance analysis, cyclic, linear sweep and differential pulse voltammetry. The mechanism of SY and TZ electrochemical oxidation on GrP/CP was studied. The developed sensor has good electron transfer characteristics and low electron resistance, high sensitivity and selectivity. Applying the differential pulse mode, linear dynamic ranges of 0.005-1.0 μM and 0.02-7.5 μM with limits of detection of 0.78 nM and 8.2 nM for SY and TZ, respectively, were obtained. The sensor was used to detect SY and TZ in non-alcoholic and alcoholic drinks. The results obtained from drink analysis prove good reproducibility (RSD ≤ 0.072) and accuracy (recovery 96-104%).

| S-EPMC9185310 | biostudies-literature

Near Room Temperature Light-Activated WS2-Decorated rGO as NO2 Gas Sensor.

Project description:The NO2 response in the range of 200 ppb to 1 ppm of a chemoresistive WS2-decorated rGO sensor has been investigated at operating temperatures of 25 °C and 50 °C in dry and humid air (40% RH) under dark and Purple Blue (PB) light conditions (λ = 430 nm). Few-layers WS2, exfoliated by ball milling and sonication technique, with average dimensions of 200 nm, have been mixed with rGO flakes (average dimension 700 nm) to yield WS2-decorated rGO, deposited on Si3N4 substrates, provided with platinum (30 μm gap distance) finger-type electrodes. TEM analysis showed the formation of homogeneous and well-dispersed WS2 flakes distributed over a thin, continuous and uniform underlying layer of interconnected rGO flakes. XPS and STEM revealed a partial oxidation of WS2 flakes leading to the formation of 18% amorphous WO3 over the WS2 flakes. PB-light irradiation and mild heating of the sensor at 50 °C substantially enhanced the baseline recovery yielding improved adsorption/desorption rates, with detection limit of 400 ppb NO2 and reproducible gas responses. Cross sensitivity tests with humid air interfering vapor highlighted a negligible influence of water vapor on the NO2 response. A charge carrier mechanism between WS2 and rGO is proposed and discussed to explain the overall NO2 and H2O response of the WS2-rGO hybrids.

| S-EPMC6603724 | biostudies-literature

Ultrasensitive Electrochemical Sensor Based on Polyelectrolyte Composite Film Decorated Glassy Carbon Electrode for Detection of Nitrite in Curing Food at Sub-Micromolar Level.

Project description:To ensure food quality and safety, developing cost-effective, rapid and precision analytical techniques for quantitative detection of nitrite is highly desirable. Herein, a novel electrochemical sensor based on the sodium cellulose sulfate/poly (dimethyl diallyl ammonium chloride) (NaCS/PDMDAAC) composite film modified glass carbon electrode (NaCS/PDMDAAC/GCE) was proposed toward the detection of nitrite at sub-micromolar level, aiming to make full use of the inherent properties of individual component (biocompatible, low cost, good electrical conductivity for PDMDAAC; non-toxic, abundant raw materials, good film forming ability for NaCS) and synergistic enhancement effect. The NaCS/PDMDAAC/GCE was fabricated by a simple drop-casting method. Electrochemical behaviors of nitrite at NaCS/PDMDAAC/GCE were investigated by cyclic voltammetry (CV) and differential pulse voltammetry (DPV). Under optimum conditions, the NaCS/PDMDAAC/GCE exhibits a wide linear response region of 4.0 × 10-8 mol·L-1~1.5 × 10-4 mol·L-1 and a low detection 1imit of 43 nmol·L-1. The NaCS/PDMDAAC shows a synergetic enhancement effect toward the oxidation of nitrite, and the sensing performance is much better than the previous reports. Moreover, the NaCS/PDMDAAC also shows good stability and reproducibility. The NaCS/PDMDAAC/GCE was successfully applied to the determination of nitrite in ham sausage with satisfactory results.

| S-EPMC6222513 | biostudies-literature

Direct Electrochemical Detection of Bisphenol A Using a Highly Conductive Graphite Nanoparticle Film Electrode.

Project description:We developed an accurate and sensitive sensor for electrochemical detection of bisphenol A (BPA) with a high-conductivity graphite nanoparticle (GN) film electrode. The GNs consisted of several stacked graphene sheets and showed a homogenous spherical shape, high conductivity, large surface area and good adsorption properties to BPA. The constructed GN film electrode exhibited improved amperometric current responses such as decreased impedance and lowered BPA oxidation potential compared with those of a pristine electrode, and also possessed a large surface area to allow fast electron transfer and BPA accumulation. A pre-accumulation process with BPA adsorption resulted in considerable current signal enhancement during BPA detection. The loading amount of GNs on the film electrode and the time for target BPA enrichment were optimized. The GN film electrode-based sensor showed high reproducibility and high selectivity for BPA over other reagents. Differential pulse voltammetry experiments revealed that the concentrations of BPA were linearly correlated with the current changes, and the lowest limit of detection of the sensor was 35 nM. Furthermore, the sensor showed great accuracy and reliability, as confirmed by high-performance liquid chromatography measurements. The sensor was also successfully used for BPA determination in groundwater samples, demonstrating its potential for real environmental analysis.

| S-EPMC5422197 | biostudies-literature

Laser Ablation on Isostatic Graphite-A New Way to Create Exfoliated Graphite.

Project description:In search of a new way to fabricate graphene-like materials, isostatic graphite targets were ablated using high peak power with a nanosecond-pulsed infrared laser. We conducted dry ablations in an argon atmosphere and liquid-phase ablations in the presence of a liquid medium (water or toluene). After the dry ablation, the SEM images of the target showed carbon in the form of a volcano-like grain structure, which seemed to be the result of liquid carbon ejected from the ablation center. No graphite exfoliation could be achieved using dry ablation. When using liquid phase ablation with water or toluene as a liquid medium, no traces of the formation of liquid carbon were found, but cleaner and deeper craters were observed. In particular, when using toluene as a liquid medium, typical graphite exfoliation was found. We believe that due to the extremely high pressure and high temperature induced by the laser pulses, toluene was able to intercalate into the graphite layers. Between the laser pulses, the intercalated toluene was able to flash evaporate and blow-up the graphite, which resulted in exfoliated graphite. Exfoliated graphite was found on the ablated graphite surface, as well as in the toluene medium. The ablation experiments with toluene undertaken in this study demonstrated an effective method of producing micrometer-sized graphene material. When using water as a liquid medium, no massive graphite exfoliation was observed. This meant that under the used laser conditions, toluene was a better intercalant for graphite exfoliation than water.

| S-EPMC9410218 | biostudies-literature

Spherulitic copper-copper oxide nanostructure-based highly sensitive nonenzymatic glucose sensor.

Project description:In this work, three different spherulitic nanostructures Cu-CuOA, Cu-CuOB, and Cu-CuOC were synthesized in water-in-oil microemulsions by varying the surfactant concentration (30 mM, 40 mM, and 50 mM, respectively). The structural and morphological characteristics of the Cu-CuO nanostructures were investigated by ultraviolet-visible (UV-vis) spectroscopy, X-ray diffraction, scanning electron microscopy, and high-resolution transmission electron microscopy techniques. The synthesized nanostructures were deposited on multiwalled carbon nanotube (MWCNT)-modified indium tin oxide (ITO) electrodes to fabricate a nonenzymatic highly sensitive amperometric glucose sensor. The performance of the ITO/MWCNT/Cu-CuO electrodes in the glucose assay was examined by cyclic voltammetry and chronoamperometric studies. The sensitivity of the sensor varied with the spherulite type; Cu-CuOA, Cu-CuOB, and Cu-CuOC exhibited a sensitivity of 1,229, 3,012, and 3,642 µA mM(-1)·cm(-2), respectively. Moreover, the linear range is dependent on the structure types: 0.023-0.29 mM, 0.07-0.8 mM, and 0.023-0.34 mM for Cu-CuOA, Cu-CuOB, and Cu-CuOC, respectively. An excellent response time of 3 seconds and a low detection limit of 2 µM were observed for Cu-CuOB at an applied potential of +0.34 V. In addition, this electrode was found to be resistant to interference by common interfering agents such as urea, cystamine, L-ascorbic acid, and creatinine. The high performance of the Cu-CuO spherulites with nanowire-to-nanorod outgrowths was primarily due to the high surface area and stability, and good three-dimensional structure. Furthermore, the ITO/MWCNT/Cu-CuOB electrode applied to real urine and serum sample showed satisfactory performance.

| S-EPMC4556295 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data