Electrochemical and quantum mechanical investigation of various small molecule organic compounds as corrosion inhibitors in mild steel.

ABSTRACT: The corrosion inhibition property of selected small organic compounds was investigated using electrochemical measurements, including potentiodynamic polarization (PDP), linear polarization resistance (LPR), electrochemical impedance spectroscopy (EIS), and density functional theory (DFT) calculations. The inhibition efficiency (IE %) of the inhibitor on mild steel (MS) in 1 M HCl was then determined. Results show that the presence of the inhibitors resulted in decreased corrosion current density (I _corr) values and increased polarization resistance (R _p). Furthermore, the use of higher concentrations of inhibitors led to an increased inhibition efficiency. Tafel slopes and shifts in the E _corr values suggested that the inhibitors tested are mixed-type inhibitors that form a protective layer on the surface of the substrate. Of the organic compound inhibitors tested, the inhibitor 4-ethylpyridine (EP) exhibited the highest R _p values and inhibition efficiency values from the PDP, LPR, and EIS analyses, respectively. DFT calculations showed negative adsorption energies and confirmed the chemisorption of the inhibitors allowing for the formation of a hydrophobic protective film against corrosion and correlations between the quantum chemical values and electrochemical data were demonstrated. The results show the influence of the presence of electronegative O, S, and N atoms, as well as the role of aromatic rings in the promotion of surface protection by preventing aggressive ionic species from binding onto MS.

SUBMITTER: Carranza MSS

PROVIDER: S-EPMC8441079 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Chromeno-carbonitriles as corrosion inhibitors for mild steel in acidic solution: electrochemical, surface and computational studies.

Project description:Three novel N-hydrospiro-chromeno-carbonitriles namely, 2-amino-7,7-dimethyl-1',3',5-trioxo-1',3',5,6,7,8-hexahydrospiro[chromene-4,2'-indene]-3-carbonitrile (INH-1), 3-amino-7,7-dimethyl-2',5-dioxo-5,6,7,8-tetrahydrospiro[chromene-4,3'-indoline]-2-carbonitrile (INH-2) and 3'-amino-7',7'-dimethyl-2,5'-dioxo-5',6',7',8'-tetrahydro-2H-spiro[acenaphthylene-1,4'-chromene]-2'-carbonitrile (INH-3) were synthesized using the principles of green chemistry and applied as corrosion inhibitors for mild steel in acidic medium using computational simulations and experimental methods. Experimental and computational studies revealed that inhibition effectiveness of the INHs followed the sequence: INH-3 (95.32%) > INH-2 (93.02%) > INH-1 (89.16%). The investigated compounds exhibit mixed-type corrosion inhibition characteristics by blocking the active sites on the surface of mild steel. EIS study revealed that the INHs behave as interface-type corrosion inhibitors. EDX analyses supported the adsorption mechanism of corrosion inhibition. A DFT study carried out for gaseous and aqueous forms of inhibitor molecules indicated that interactions of INHs with the mild steel surface involve charge transfer phenomenon or donor-acceptor interactions. A Monte Carlo (MC) simulation study revealed that only a fractional segment of the molecule lies parallel to the steel surface, since the INH molecules are not completely planar. The results of computational studies and experimental analyses were in good agreement.

| S-EPMC8693851 | biostudies-literature

Cysteine as an Eco-Friendly Anticorrosion Inhibitor for Mild Steel in Various Acidic Solutions: Electrochemical, Adsorption, Surface Analysis, and Quantum Chemical Calculations.

Project description:The corrosion of iron in acidic environments has a negative impact on global industry. Herewith, the inhibitory effect of cysteine (Cys.) on mild steel (MSL) corrosion in different acidic solutions (1 M HCl, 1 M H2SO4, and 1 M H3PO4) was investigated through weight loss, potentiodynamic polarization (PDP), electrochemical impedance spectroscopy, scanning electron microscopy (SEM), and theoretical calculations. The measurement results indicated that the adsorption of Cys. molecules on the metal surface caused corrosion inhibition. As a result, a protective layer or insoluble compound, or both, is obtained, blocking the active sites, preventing corrosion. The effectiveness (IE %) of the Cys. was enhanced by increasing concentration and lowering temperature. The maximum IE % of inhibition at 1 × 10-2 M of Cys. obtained are 97.3, 89.7, and 84.4% in HCl, H3PO4, and H2SO4 solutions, respectively. At the same inhibitor concentration, the double-layer capacity decreased, and the charge-transfer resistance increased from 17.17 to 188.5, 3.564 to 31.91, and 1.325 to 8.715 Ω cm2 in HCl, H3PO4, and H2SO4 solutions, respectively. Adsorption and PDP studies confirmed that it obeys the Langmuir adsorption isotherm and acts as a mixed-type inhibitor of physicochemical nature. The corresponding thermodynamic and kinetic parameters were also calculated and discussed. Moreover, the inhibitory effect on the surface was inspected by SEM. The findings demonstrated that the order of IE % using Cys as anticorrosion agent for MSL is HCl > H3PO4 > H2SO4 solutions.

| S-EPMC10956117 | biostudies-literature

Novel porphyrin derivatives as corrosion inhibitors for stainless steel 304 in acidic environment: synthesis, electrochemical and quantum calculation studies.

Project description:A Novel 5,10,15,20-tetra (thiophen-2-yl) porphyrin (P1) and 5,10,15,20-tetrakis (5-Bromothiophen-2-yl) porphyrin (P2) were successfully synthesized, and their chemical structures were proved based on its correct elemental analysis and spectral data (IR and 1H-NMR). These compounds were examined as corrosion inhibitors for stainless steel 304 (SS304) in 2 M HCl utilizing mass reduction (MR) and electrochemical tests at inhibitor concentration (1 × 10-6-21 × 10-6 M). The protection efficiency (IE %) was effectively enhanced with improving the concentration of investigated compounds and reached 92.5%, 88.5% at 21 × 10-6 M for P1 & P2, respectively and decreases with raising the temperature. Langmuir's isotherm was constrained as the best fitted isotherm depicts the physical-chemical adsorption capabilities of P1 & P2 on SS304 surface with change in ΔGoads = 22.5 kJ mol-1. According to the PDP data reported, P1 and P2 work as mixed find inhibitors to suppress both cathodic and anodic processes. Porphyrin derivatives (P1 & P2) are included on the surface of SS304, according to surface morphology techniques SEM/EDX and AFM. Quantum calculations (DFT) and Monte Carlo simulation (MC) showed the impact of the chemical structure of porphyrin derivatives on their IE %.

| S-EPMC10579412 | biostudies-literature

The Effect of Microstructural Changes on Mechanical and Electrochemical Corrosion Properties of Duplex Stainless Steel Aged for Short Periods.

Project description:This work reports the effects of microstructural changes due to the secondary phases, in particular sigma (σ), on the mechanical properties and electrochemical behavior of thermally aged duplex stainless steel (DSS). Structural, morphological, mechanical, and electrochemical characterizations were performed. Sigma phase content increased with increasing aging treatment time. It had a net-like shape, as observed by electron backscatter diffractometry (EBSD). Its presence directly damaged mechanical properties. The corrosion assessment included electrochemical impedance spectroscopy (EIS) in 1 M NaCl solution at temperatures of 25, 40, and 65 °C. EIS results demonstrate that an increase in the σ phase content decreased the corrosion resistance (21.1-0.8, 3.5-0.3, and 3.1-0.2 kΩ cm2 at 25, 40, and 60 °C, respectively).

| S-EPMC7730082 | biostudies-literature

Electrochemical Study on Newly Synthesized Chlorocurcumin as an Inhibitor for Mild Steel Corrosion in Hydrochloric Acid.

Project description:A new curcumin derivative, i.e., (1E,4Z,6E)-5-chloro-1,7-bis(4-hydroxy-3-methoxyphenyl)hepta-1,4,6-trien-3-one (chlorocurcumin), was prepared starting with the natural compound curcumin. The newly synthesized compound was characterized by elemental analysis and spectral studies (IR, ¹H-NMR and 13C-NMR). The corrosion inhibition of mild steel in 1 M HCl by chlorocurcumin has been studied using potentiodynamic polarization (PDP) measurements and electrochemical impedance spectroscopy (EIS). The inhibition efficiency increases with the concentration of the inhibitor but decreases with increases in temperature. The potentiodynamic polarization reveals that chlorocurcumin is a mixed-type inhibitor. The kinetic parameters for mild steel corrosion were determined and discussed.

| S-EPMC5452761 | biostudies-other

Adsorption and Corrosion Inhibition Studies of Some Selected Dyes as Corrosion Inhibitors for Mild Steel in Acidic Medium: Gravimetric, Electrochemical, Quantum Chemical Studies and Synergistic Effect with Iodide Ions.

Project description:The corrosion inhibition properties of some organic dyes, namely Sunset Yellow (SS), Amaranth (AM), Allura Red (AR), Tartrazine (TZ) and Fast Green (FG), for mild steel corrosion in 0.5 M HCl solution, were investigated using gravimetric, potentiodynamic polarization techniques and quantum chemical calculations. The results showed that the studied dyes are good corrosion inhibitors with enhanced inhibition efficiencies. The inhibition efficiency of all the studied dyes increases with increase in concentration, and decreases with increase in temperature. The results showed that the inhibition efficiency of the dyes increases in the presence of KI due to synergistic interactions of the dye molecules with iodide (I(-)) ions. Potentiodynamic polarization results revealed that the studied dyes are mixed-type inhibitors both in the absence and presence of KI. The adsorption of the studied dyes on mild steel surface, with and without KI, obeys the Langmuir adsorption isotherm and involves physical adsorption mechanism. Quantum chemical calculations revealed that the most likely sites in the dye molecules for interactions with mild steel are the S, O, and N heteroatoms.

| S-EPMC6331870 | biostudies-other

Theoretical, thermodynamic and electrochemical analysis of biotin drug as an impending corrosion inhibitor for mild steel in 15% hydrochloric acid.

Project description:The corrosion mitigation efficiency of biotin drug for mild steel in 15% hydrochloric acid was thoroughly investigated by weight loss and electrochemical methods. The surface morphology was studied by the contact angle, scanning electrochemical microscopy, atomic force microscopy and scanning electron microscopy methods. Quantum chemical calculation and Fukui analysis were done to correlate the experimental and theoretical data. The influence of the concentration of inhibitor, immersion time, temperature, activation energy, enthalpy and entropy has been reported. The mitigation efficiency of biotin obtained by all methods was in good correlation with each other. Polarization studies revealed that biotin acted as a mixed inhibitor. The adsorption of biotin was found to obey the Langmuir adsorption isotherm. Surface studies showed the hydrophobic nature of the steel with inhibitor and vindicated the formation of a film on the metal surface that reduced the corrosion rate.

| S-EPMC5750002 | biostudies-literature

Synthesis, characterization and electrochemical analysis of cysteine modified polymers for corrosion inhibition of mild steel in aqueous 1 M HCl.

Project description:Butler's cyclopolymerization protocol was used to synthesize homo and copolymers of cysteine residues and diallyldimethylammonium chloride (DADMAC) using water as a solvent and excellent yields were obtained. The structural composition of the polymers was determined using nuclear magnetic resonance (NMR) and Fourier-transform infrared (FT-IR) spectroscopies. The thermal stability of the synthesized polymers was determined using thermogravimetric analysis (TGA). The corrosion efficiencies and adsorption characteristics of these polymers on mild steel were evaluated using gravimetric weight loss and potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS). The copolymers of cysteine residues and DADMAC exhibited excellent inhibition efficiencies in arresting mild steel corrosion in 1 M hydrochloric acid (HCl) at 60 °C. The best fitted Langmuir, Temkin and Freundlich adsorption isotherms suggested that the adsorption process occurs through chemisorption and physisorption. The surface morphology of mild steel in the presence or absence of polymers was determined using atomic force microscopy (AFM), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX), and X-ray photoelectron spectroscopy (XPS). This systematic study might provide a way to design new inhibitor compounds that could be beneficial in the field of biomedical science as well as for anti-corrosion applications.

| S-EPMC9060476 | biostudies-literature

Biogenic corrosion inhibitor on mild steel protection in concentrated HCl medium.

Project description:Turbinaria ornata (TO) extract was tested as green corrosion inhibitor on mild steel (MS) coupons in conc. HCl medium with an efficiency of 100% at 25?g?l-1 during 5?min exposure. Antibacterial efficacy performed against 16?S rDNA identified marine biofilming bacteria (MBB) and human pathogenic bacteria (HPB). Maximum inhibition growth was 16?mm on MBB observed in Bacillus megaterium (MBF14 - AB894827) and 20?mm on HPB in Escherichia coli (B5 - NCIM 2931). Similarly, minimum of 10?mm on MBB witnessed in Pseudomonas sp., (MBF9 - AB894829). Toxicity studies proved 50.0% LC50 at 500??g?ml-1 in 24?hrs, whereas Balanus amphitrite resulted in 100% mortality within 12?hrs. Results including weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy, FT-IR and GC-MS confirm 10-Octadecaonic acid as a major corrosion inhibitor from T. ornata and is discovered as a novel antifoulant. Anticorrosion formulation will become available soon.

| S-EPMC5805700 | biostudies-literature

Novel Corrosion Inhibitor for Mild Steel in HCl.

Project description:Corrosion inhibitory effects of new synthesized compound namely 5,5'- ((1Z,1'Z)-(1,4-phenylenebis(methanylylidene))bis(azanylylidene))bis(1,3,4-thiadiazole-2-thiol) (PBB) on mild steel in 1.0 M HCl was investigated at different temperatures using open circuit potential (OCP), potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS). Results showed that PBB inhibited mild steel corrosion in acid solution and indicated that the inhibition efficiencies increased with the concentration of inhibitor, but decreased proportionally with temperature. Changes in impedance parameters suggested the adsorption of PBB on the mild steel surface, leading to the formation of protective films.

| S-EPMC5453103 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data